• Metals and materials international
• /
• 제24권6호
• /
• pp.1327-1332
• /
• 2018

In this study, a novel approach to the explosive synthesis of titanium carbide (TiC) is discussed. Nonstoichiometric $TiC_x$ powder was produced via the underwater explosion of a Ti powder encapsulated within a spherical explosive charge. The explosion process, bubble formation, and synthesis process were visualized using high-speed camera imaging. It was concluded that synthesis occurred within the detonation gas during the first expansion/contraction cycle of the bubble, which was accompanied by a strong emission of light. The recovered powders were studied using scanning electron microscopy and X-ray diffraction. Submicron particles were generated during the explosion. An increase in the carbon content of the starting powder resulted in an increase in the carbon content of the final product. No oxide byproducts were observed within the recovered powders.

• 열처리공학회지
• /
• 제22권1호
• /
• pp.3-7
• /
• 2009

Variation in oxidation behavior with heat treatment temperature is investigated for a Ni-Ti alloy using X-ray diffraction, DSC (differential scanning calorimetry) and Auger electron spectroscopy. And the effect of oxidation on transformation behavior and superelasticity is characterized. A cold-worked 50.6Ni-Ti alloy is oxidized at 300-$700^{\circ}C$ for 1 hr in the air atmosphere. With an increase in heating temperature, the structure of $TiO_2$ changes from amorphous (300 and $400^{\circ}C$) to anatase ($500^{\circ}C$), and to rutile ($700^{\circ}C$). Activation energy of oxidation for NiTi is measured to be 51 Kcal/mol when heating temperature is $500^{\circ}C$ or above. Since Ti reacts preferably with oxygen, Ni content increases between matrix and oxide, forming $Ni_{3}Ti$ compounds. The resultant of oxidation decreases significantly $M_s$ and $A_s$ temperature in the specimen oxidized at $900^{\circ}C$ with $B_2{\rightarrow}M$ transformation path. An extra is found on cooling between two peaks in the specimen with $B_2{\rightarrow}R{\rightarrow}M$ one which is oxidized at $900^{\circ}C$ and aged at $500^{\circ}C$. Oxidation deteriorates superelasticity due to formation of Ni-rich compound.

• 한국분말재료학회지
• /
• 제14권3호
• /
• pp.208-214
• /
• 2007

The microstructure and hardness of (W,Ti)C cemented carbides with a different metallic binder composition of Ni and Co fabricated by powder technology were investigated. The densifications of the prepared materials were accomplished by using vacuum sintering at $1450^{\circ}C$. Nearly full dense (W,Ti)C cemented carbides were obtained with a relative density of up to 99.7% with 30 wt.% Co and 99.9% with 30 wt.% Ni as a metallic binder. The average grain size of the (W,Ti)C-Co and the (W,Ti)C-Ni was decreased by increasing the metallic binder content. The hardness of the dense (W,Ti)C-15 wt%Co and (W,Ti)C-15 wt%Ni, was greater than that of the other related cemented carbides; in addition, the cobalt-based cemented carbides had greater hardness values than the nickel-based cemented carbides.

• The Korean Journal of Ceramics
• /
• 제5권2호
• /
• pp.189-194
• /
• 1999

Crystallization of glasses in the system (Ca, Sr, Ba)$O-Al_2O_3-B_2O_3-SiO_2-TiO_2$ and dielectric properties of crystallized glasses were investigated. As increasing B2O3 content and decreasing SiO2 content in the glass, the major crystalline phase changed from $(Sr, Ba)_2TiSi_2O_8$ to (Ca, Sr, Ba)TiO3, the dielectric constant of crystallized glasses increased and the Temperature Coefficient of Capacitance (TCC) changed to negative. The dielectric constant and TCC was estimated for (Sr, Ba)2TiSi2O8 phase as 18 and -440 $ppm/^{\circ}C$, respectively and for (Ca, Sr, Ba)TiO3 phase as 307 and -1900 $ppm/^{\circ}C$, respectively. The dielectric properties of (Ca, Sr, Ba)TiO3 phase (in this study) were similar to those of (Ca, Ba) TiO_3 solid-solution^12)$, but $(Sr, Ba)_2TiSi_2O_8$ phase (in this study) and $Sr_2TiSi_2O_\;8^4$ showed the different properties.

• 한국안광학회지
• /
• 제2권1호
• /
• pp.9-16
• /
• 1997

강유천체 $Pb_5Ge_{3-x}Ti_xO_{11}$ 단결정을 x=0.015, 0.021, 0.03의 조성에 대하여 Czochralski법으로 성장시켰으며, 성장시킨 단결정의 색상은 맑고 투명한 연한 노란색이었다. $Pb_5Ge_{3-x}Ti_xO_{11}$ 단결정의 유전완화에 관한 연구를 위한 측정은 주파수범위 100 Hz에서 10 MHz까지 온도범위 $20^{\circ}C$에서 $600^{\circ}C$까지 변화 시키면서 하였다. 측정결과 유전을 최대값이 되는 온도는 Ti 성분이 증가함으로 낮은 온도로 이동하였으며, 유전율의 최대값의 크기는 Ti 성분의 증가에 따라 감소하였다. $Pb_5Ge_{3-x}Ti_xO_{11}$ 단결정의 유전응답의 주파수 의존성은 완화시간 분포와, Debye 완화형태를 가졌으며, 유전적 거동은 캐리어가 우세한 반응의 특징을 나타내었다.

• Corrosion Science and Technology
• /
• 제8권4호
• /
• pp.162-169
• /
• 2009

Pure titanium and its alloys are drastically used in implant materials due to their excellent mechanical properties, high corrosion resistance and good biocompatibility. However, the widely used Ti-6Al-4V is found to release toxic ions (Al and V) into the body, leading to undesirable long-term effects. Ti-6Al-4V has much higher elastic modulus than cortical bone. Therefore, titanium alloys with low elastic modulus have been developed as biomaterials to minimize stress shielding. For this reason, Ti-30Ta-xZr alloy systems have been studied in this study. The Ti-30Ta containing Zr(5, 10 and 15 wt%) were 10 times melted to improve chemical homogeneity by using a vacuum furnace and then homogenized for 24 hrs at $1000^{\circ}C$. The specimens were cut and polished for corrosion test and Ti coating and then coated with TiN, respectively, by using DC magnetron sputtering method. The analyses of coated surface were carried out by field emission scanning electron microscope(FE-SEM). The electrochemical characteristics were examined using potentiodynamic (- 1500 mV~+ 2000 mV) and AC impedance spectroscopy(100 kHz~10 mHz) in 0.9% NaCl solution at $36.5{\pm}1^{\circ}C$. The equiaxed structure was changed to needle-like structure with increasing Zr content. The surface defects and structures were covered with TiN/Ti coated layer. From the polarization behavior in 0.9% NaCl solution, The corrosion current density of Ti-30Ta-xZr alloys decreased as Zr content increased, whereas, the corrosion potential of Ti-30Ta-xZr alloys increased as Zr content increased. The corrosion resistance of TiN/Ti-coated Ti-30Ta-xZr alloys were higher than that of the TiN-coated Ti-30Ta-xZr alloys. From the AC impedance in 0.9% NaCl solution, polarization resistance($R_p$) value of TiN/Ti coated Ti-30Ta-xZr alloys showed higher than that of TiN-coated Ti-30Ta-xZr alloys.

• The Korean Journal of Ceramics
• /
• 제1권3호
• /
• pp.125-130
• /
• 1995

Electrical discharge machinable $SiC-TiB_2$ composites were fabricated by hot-pressing. Their mechanical and electrical properties were determined as a function of $TiB_2$ content. The addition of $TiB_2$ to SiC matrix increased the strength and toughness and decreased electrical resistivity. The flexural strength and fracture toughness of SiC-40 vol% $TiB_2$ composited were approximately 50% higher than those of monolithic SiC ceramics. Microstructural analysis showed that the toughening was mainly due to the crack deflection, with some possible contribution from crack branching or microcracking.

• Journal of Welding and Joining
• /
• 제18권5호
• /
• pp.98-104
• /
• 2000

Aluminum alloys are being employed in automobile parts as strive to reduce overall vehicle weight to meet demands for improved fuel economy and reduction in vehicle emissions. Al-based composites reinforced with ceramic ($Al_2O_3,\;SiC,\;TiC\;and\;B_4C$) applications in a variety of components in automotive engines, such as liners, where the tribological properties of the material are important. In this study, Al-base composites reinforced with TiC particle powders has been developed for producing plasma spray coatings. The composite plasma spray powders were prepared Al-13Si-3Mg(wt%) alloy with TiC(40, 60 and 80wt%) particles ($0.2~5{\mu}textrm{m}$) by drum type ball milling. The composite powders ($36~76{\mu}textrm{m}$) were sprayed with plasma torch. Plasma sprayed coatings were heat-treated at $500^{\circ}C$ for 3 hours. The wear resistances of the plasma sprayed coatings were found to decrease with increasing TiC content and improved with heat treatment. AlSiMg-40% TiC heat-treated coatings were showed the best wear resistance in this study.

• 한국세라믹학회지
• /
• 제50권6호
• /
• pp.372-377
• /
• 2013

Machinable SiC ceramics are prepared with the addition of $Al_2TiO_5$. Ready-to-press SiC and $Al_2TiO_5$ powders are mixed and pressureless sintered at $1750^{\circ}C$ and $1850^{\circ}C$ for 1 h. The weight ratios of the SiC and $Al_2TiO_5$ powders are 100 : 0, 100 : 10, and 100 : 20. After sintering, only SiC peaks are detected in the X-ray diffraction analyses. The density, strength, and grain size of the SiC increase with increases in the $Al_2TiO_5$ content and sintering temperature. The $Al_2TiO_5$-doped specimens are easy to micro-hole machine. Based on the density and strength data, the ceramics sintered at $1850^{\circ}C$ can be used as machinable ceramics.

• 한국분말재료학회지
• /
• 제24권1호
• /
• pp.29-33
• /
• 2017

Titanium carbide (TiC) powders are successfully synthesized by carburization of titanium hydride ($TiH_2$) powders. The $TiH_2$ powders with size lower than $45{\mu}m$ (-325 Mesh) are optimally produced by the hydrogenation process, and are mixed with graphite powder by ball milling. The mixtures are then heat-treated in an Ar atmosphere at $800-1200^{\circ}C$ for carburization to occur. It has been experimentally and thermodynamically determined that the de-hydrogenation, "$TiH_2=Ti+H_2$", and carburization, "Ti + C = TiC", occur simultaneously over the reaction temperature range. The unreacted graphite content (free carbon) in each product is precisely measured by acid dissolution and by the filtering method, and it is possible to conclude that the maximal carbon stoichiometry of $TiC_{0.94}$ is accomplished at $1200^{\circ}C$.