• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2016년도 추계학술대회 논문집
• /
• pp.107-107
• /
• 2016

TiCrAlSiN films were developed in order to improve the high-temperature oxidation resistance, corrosion resistance, and mechanical properties of conventional TiN films that are widely used as hard films to protect and increase the lifetime and performance of cutting tools or die molds. In this study, a nano-multilayered TiAlCrSiN film was deposited by cathodic arc plasma deposition. It displayed relatively good oxidation resistance at $700-900^{\circ}C$, owing to the formation protective oxides of $Al_2O_3$, $Cr_2O_3$, and $SiO_2$, and semiprotective $TiO_2$. At $1000^{\circ}C$, the increased temperature led to the formation of the imperfect oxide scale that consisted primarily of the outer ($TiO_2$,$Al_2O_3$)-mixed scale and inner ($TiO_2$, $Al_2O_3$, $Cr_2O_3$)-mixed scale.

• 한국표면공학회지
• /
• 제47권5호
• /
• pp.252-256
• /
• 2014

The TiAlCrSiN film was deposited on the WC-20%TiC-10%Co carbide, and its oxidation behavior was examined at $700-1000^{\circ}C$. It displayed relatively good oxidation resistance owing to the formation of $TiO_2$, $Al_2O_3$, $Cr_2O_3$, and $SiO_2$ up to $900^{\circ}C$. However, at $1000^{\circ}C$, the fast oxidation rate and partial oxidation of WC in the substrate led to the formation of the thick, fragile oxide scale.

• 한국표면공학회지
• /
• 제54권3호
• /
• pp.133-138
• /
• 2021

Ternary Ti-X-N coatings, where X = Al, Si, Cr, O, etc., have been widely used for machining tools and cutting tools such as inserts, end-mills, and etc. Ti-Al-N-O coatings were deposited onto silicon wafer and WC-Co substrates by a cathodic arc evaporation (CAE) technique at various negative substrate bias voltages. In this study, the influence of substrate bias voltages during deposition on the microstructure and mechanical properties of Ti-Al-N-O coatings were systematically investigated to optimize the CAE deposition condition. Based on results from various analyses, the Ti-Al-N-O coatings prepared at substrate bias voltage of -80 V in the process exhibited excellent mechanical properties with a higher compressive residual stress. The Ti-Al-N-O (-80 V) coating exhibited the highest hardness around 30 GPa and elastic modulus around 303 GPa. The improvement of mechanical properties with optimized bias voltage of -80 V can be explained with the diminution of macroparticles, film densification and residual stress induced by ion bombardment effect. However, the increasing bias voltage above -80 V caused reduction in film deposition rate in the Ti-Al-N-O coatings due to re-sputtering and ion bombardment phenomenon.

• 전자공학회논문지D
• /
• 제36D권7호
• /
• pp.17-25
• /
• 1999

PECVD 법을 이용하여 Tungsten Nitride($WN_x$) 박막을 $WSi_3N_4$ 기판위에 형성하였다. $WN_x$ 박막은 기관온도, 가스의 유량, rf power 등의 공정변수를 변화시키면서 형성되었고, 서로 다른 질소원으로 $NH_3$와 $N_2$를 각각 사용하여 박막의 특성을 조사하였다. $WN_x$ 막 내의 질소함량은 $NH_3$와 $N_2$의 유량에 따라 0~45% 정도로 변화하였으며, $NH_3$를 사용하였을 때, 최고 160nm/min의 높은 성장률을 나타내었다. $WSi_3N_4$ 기판 위에서는 TiN이나 Si 위에서보다 높은 성장률을 나타내었다. $WN_x$ 박막의 순도를 AES로 측정해 본 결과 $NH_3$를 사용했을 때 고순도의 박막을 얻을 수 있었다. XRD 분석으로 순수한 다결정의 W가 비정질의 $WN_x$로 변화되는 것을 알 수 있었으며, 이것은 $WN_x$가 식각 공정시 미세 패턴 형성이 W보다 유리할 것이라는 것을 보여준다. TiN, NiCr, Al 등의 다양한 기판 위에 형성해 본 결과 Al 위에서 최대 $1.6 {\mu}m$의 두꺼운 막이 형성되었다.