• Journal of Technologic Dentistry
• /
• v.31 no.4
• /
• pp.31-36
• /
• 2009

This study evaluated the grindability of series of Ti-Cu alloys in order to develop a Ti alloy with better grindability than commercially pure titanium(CP Ti). Experimental Ti-Xwt%Cu alloys(X=2, 5, 10) were made in an argon-arc melting furnace. Slabs of experimental alloys were ground using a SiC abrasive wheel on an electric handpiece at circumferential speed(15000, 30000rpm) by applying a force(250, 300gr). Grindability was evaluated by measuring the amount of metal volume removed after grinding for 2 minutes. Data were compared to those for CP Ti and Ti-6wt%Al-4wt%V alloy. From results, It was observed that the grindability of Ti-Cu alloys increased with an increase in the Cu concentration compared to CP Ti, particularly the 10wt%Cu alloy exhibited the highest grindability at all speeds. By alloying with Cu, the Ti exhibited better grindability at high speed. The continuous precipitation of $Ti_2Cu$ among the ${\alpha}$-matrix grains made this material less ductile and facilitated more effective grinding because small segments more readily formed. The Ti-10wt%Cu alloy has a great potential for use as a dental machining alloy.

• Journal of Technologic Dentistry
• /
• v.25 no.1
• /
• pp.81-87
• /
• 2003

Ti-20%Zr-X%Cr(X=0,5) based alloys not containing hamful Al and V were newly designed in order to reveal their possibility for dental casting alloys, and melted in argon-arc casting machine. The mechanical properties were evaluated by using universal testing machine. The tensile strength and %elongaton of the alloys markedly increased with Cr content. The Ti-20%Zr-5%Cr alloy showed a similar tendency with Ti-6%Al-4%V alloy in tensile strength, but surpassed in %elongation. From these results, it was concluded that new alloys for successful dental casting materials should be designed as Ti-Zr-Cr based alloys.

• Corrosion Science and Technology
• /
• v.8 no.4
• /
• pp.139-142
• /
• 2009

Recently, quaternary titanium alloys of the system Ti-Nb-Ta-Zr received considerable research interest as potential implant materials because of their excellent mechanical properties and biocompatibility. However, only few reported works were available on the corrosion behavior of such alloys. Hence, in the present work, electrochemical corrosion of Ti-35Nb-5Ta-7Zr alloy, which has been fabricated by arc melting and heat treatment, was studied in 0.9 wt% NaCl at $37\pm1^{\circ}C$, along with biomedical grade Ti-6Al-4V and CP-Ti. The phase and microstructure of the alloys were investigated employing XRD and SEM. The results of electrochemical studies indicated that the corrosion resistance of the quaternary alloy was inferior to that of Ti-6Al-4V and CP Ti.

• Journal of Korea Foundry Society
• /
• v.18 no.6
• /
• pp.550-554
• /
• 1998

The microstructures of rapidly solidified binary Ti-Al alloys containing $45{\sim}58\;at%Al$ have been studied using C/S (carbon/sulfur), N/O (nitrogen/oxygen) analyser, X-ray fluorescence spectrometer (XRF), X-ray diffractometer (XRD), optical microscope (OM) and scanning electron microscope (SEM). The phases present in the alloys and their distribution were found to be a sensitive function of Al content. Essentially single-phase (${\gamma}$) microstructures were observed to alloys with 45 at%Al, 55 at%Al and 58 at%Al. In other content alloys, two phase (${\alpha}_2$, ${\gamma}$) microstructures were observed. The 48 at%Al, 52 at%Al alloys contain (${\gamma}+{\alpha}_2$) phase and ${\alpha}_2$ phase. These results indicate that rapid solidification affect the solidification path, then metastable phase forming during solidification.

• Journal of the Korean institute of surface engineering
• /
• v.39 no.6
• /
• pp.288-294
• /
• 2006

Alloys of TiAl-Mn-(0, 5, 10)wt.% $Y_2O_3$ were prepared by a powder metallurgical route, and their oxidation behavior was studied at 800, 900 and $1000^{\circ}C$ in 1 atm of air. The scale formed on the alloys consisted of $TiO_2$ and $Al_2O_3$ oxides. During oxidation, Mn tended to diffuse outward, whereas oxygen diffused inward. The dispersoids of $T_2O_3$, which segregated at the matrix grain boundaries, acted as a diffusion channel for cations and oxygen ions, nucleation sites for oxides, and vacancy annihilation sites. $T_2O_3$ increased the scale thickness, but improved the scale adherence.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2013.05a
• /
• pp.194-194
• /
• 2013

In order to investigate nanotube morphology change of Ti-6Al-4V alloys by heat treatments, the Ti-6Al-4V alloys were used in this study. In non-treated Ti-6Al-4V alloy case, nanotubes only exhibited at ${\alpha}$ phase region with dissolved V-oxide area of ${\beta}$ phase. However, in Ti-6Al-4V alloy at $800^{\circ}C$ WQ case, nanotubes exhibited at both ${\alpha}$ and ${\beta}$ phase region. Electrochemical corrosion studies showed that the nanotubular alloy at $800^{\circ}C$WQ possesses slightly higher corrosion resistance than non-treated nanotubular alloy.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.1030-1031
• /
• 2006

Titanium alloys and Titanium alloy-based particulate composites were synthesized using the blended elemental P/M route. First, processing conditions such as the fabrication of master alloy powder were investigated. Ti-6Al-4V, Ti-5Al-2.5Fe, Ti-6Al-2Sn-4Zr-2Mo, IMI685, IMI829, Timetal 1100 and Timetal 62S, and Ti-6Al-2Sn-4Zr-2Mo/ 10%TiB and Timetal 62S/10%TiB were then synthesized using the optimal processing conditions obtained. The microstructures and mechanical properties such as tensile strength and high cycle fatigue strength were evaluated.

• Korean Journal of Metals and Materials
• /
• v.49 no.8
• /
• pp.619-627
• /
• 2011

The poisoning effect of Zr in aluminum alloys was investigated by analyzing the filtered cakes of aluminum alloy melt taken with the $Prefil^{(R)}$ footprinter through a variety of analytic instruments, SEM/EDX, Auger, and TEM. Experimental results indicated that the morphology and chemical composition of the aluminum alloys were not modified with the addition of Zr, which is to previous belief that Zr poisoning is caused by modification of $(Ti_{1-x}Zr_x)Al_3$. On the other hand, $TiAl_3$ surroundig $TiB_2$ particles was modified and its lattice parameter was more mismatched by increasing Zr content, leading to less nucleation rate. This is also supported by the observation that the poisoning effect is reduced when Ti is added, resulting in a lower content ratio of Zr to Ti. These results suggest that extra Ti should be added to eliminate the poisoning effect of Zr in aluminum alloys containing Zr.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1994.05a
• /
• pp.59-60
• /
• 1994

• Journal of the Korean Ceramic Society
• /
• v.45 no.10
• /
• pp.638-643
• /
• 2008

Biomimetic apatite formation and deposition behaviors of Ti-6Al-7Nb and Ti-6Al-4V plates in simulated body fluids(SBF) under various conditions were examined. In case of regular samples without collagen treatments the weight gain due to apatite precipitation on the surface in Ti-6Al-4V was found to be higher than in Ti-6Al-7Nb. In case of collagen-coated samples, the weight gain in Ti-6Al-4V continued to be higher than in Ti-6Al-7Nb, but the difference between the two became smaller. Both Ti-6Al-7Nb and Ti-6Al-4V samples with collagen coating exhibited an appreciable increase of weight gain, which may be caused by the interaction between collagen and $Ca^{+2}$ ions. The weight gain was found to be not much affected by the addition of collagen to SBF. The ill-defined granular structure in the presence of collagen can be associated with the increasing volume fraction of amorphous calcium phosphate.