• Proceedings of the KSME Conference
• /
• 2005.11a
• /
• pp.135.2-135.2
• /
• 2005

• Electrical & Electronic Materials
• /
• v.8 no.1
• /
• pp.13-20
• /
• 1995

To develope a high precision TiAIN thin film resistor, TiAIN films were deposited on A1$_{2}$03 substrates by reactive planar magnetron cosputtering from Ti and Al targets in an Ar-N$_{2}$ atmosphere. The characteristics of the TiAIN thin film were controlled by changing of the R.F. power on Ti and Al targets, and the N$_{2}$ partial pressure. The high precision TiAIN thin film resistor with TCR(Temperature Coefficient of Resistance) of less than 10ppm/.deg. C was obtained under the R.F. power condition of 160(w)/240(w) to Ti and Al targets at the N$_{2}$ partial pressure of 7*10$^{-5}$ Torr. The composition of these films were investigated by XRD, SEM and EDS.

• Korean Journal of Materials Research
• /
• v.12 no.8
• /
• pp.676-681
• /
• 2002

Microstructure, mechanical properties, and oxidation resistance of TiAIN thin films deposited on quenched and tempered STD61 tool steel by arc ion plating were studied using XRD, XPS and micro-balance. The TiAIN film was grown with the (200) orientation. The grain size of TiAIN thin film decreased with increasing Al contents, while chemical binding energy increased with Al contents. When hard coating films were oxidized at $850^{\circ}C$ in air, oxidation resistance of both TiN and TiCN films became relatively lower since the surface of films formed non-protective film such as $TiO_2$. However, oxidation resistance of TiAIN film was excellent because its surface formed protective layer such as $_A12$$O_3$ and $_Al2$$Ti_{7}$$O_{15}$, which suppressed oxygen intrusion.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1996.11a
• /
• pp.144-145
• /
• 1996

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2002.05a
• /
• pp.59-59
• /
• 2002

• Journal of Surface Science and Engineering
• /
• v.38 no.6
• /
• pp.207-211
• /
• 2005

In this work a multi-layered nanostructured TiAIN/CrN superlattice coatings was synthesized using closed-field unbalanced magnetron sputtering method and the relationships between their superlattice period (1), micro-structure, hardness and elastic modulus were investigated. In addition, wear test at $500^{\circ}C$ and oxidation resistance test at $900^{\circ}C$ were performed to investigate high temperature properties of these thin films. The coatings were characterized in terms of microstructure and mechanical properties by transmission electron microscopy (TEM) and nano-indentation test. Results from TEM analysis showed that superlattice periods was inversely proportional to the jig rotation speed. The maximum hardness and elastic modulus of 37 GPa and 375 GPa were observed at superalttice period of 6.1 nm and 4.4 nm, respectively. An higher value of microhardness from TiAIN/CrN thin films than either TiAIN (30 GPa) or CrN (26 GPa) was noted while the elastic modulus was approximately an average of TiAIN and CrN films. These enhancement effects in superlattice films could be attributed to the resistance to dislocation glide across interface between the CrN and TiAIN layers. Much improved plastic deformation resistance ($H^3/E^2$) of 0.36 from TiAIN/CrN coatings was observed, compared with 0.15 and 0.16 from TiAIN and CrN, respectively. Also the wear resistance at $500^{\circ}C$ was largely increased than those of single TiAIN and CrN coatings and TiAIN/CrN coatings showed much reduced weight gain after exposure at $900^{\circ}C$ for 20 hours.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2006.10a
• /
• pp.60-60
• /
• 2006

• Journal of Surface Science and Engineering
• /
• v.35 no.4
• /
• pp.199-205
• /
• 2002

TiN and TiAlN films were deposited on SKD 11 steel substrates by an arc ion plating (AIP) technique. The crystallinity and morphology for the deposited films were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The mechanical properties of both films were investigated through the indentation, impact, and wear test. Those films fairly adherent to SKD 11 steel substrate, showed hardness values of 2300 $\pm$ 100kg/$\textrm{mm}^2$ and 3200 $\pm$ 100kg/$\textrm{mm}^2$ with a load of 25g, respectively. During impact test, TiAlN films showed much superior impact wear resistance to TiN films. It could be suggested that the TiN films was failed relatively by plastic deformation with oxidation during impact test, while TiAlN films was failed by brittle fracture and resisted the oxidation by the impact energy. The friction coefficient of TiAlN films became lower than that of TiN films at high sliding speed condition although it was higher than that of TiN films at low speed. Therefore, TiAlN films was suggested to be more advantageous than TiN films for high speed machining fields.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2001.11a
• /
• pp.28-28
• /
• 2001

$TiCl_44,{\;}AICl_3,{\;}H_2,{\;}Ar,{\;}NH_3$ 기체를 사용하여 플라즈마 화학 증착법으로 $(Ti_{1-x}AI_x)N$ 피막을 증착한 후 진공열처리 실험을 통해 열처리 전후에 나타나는 피막의 가계적 특성 변화 및 상변화 양상에 대해 연구하였다. 기판으로는 M2 고속도강과 알루미나(${\alpha}-Al_2O_3$)를 사용하였으며, 열처리 실험은 진공 열처리로를 이용하여 $800$ ~ $1100^{\circ}C$ 에서 진행하였다. M2 고속도강 위에 증착한 $(Ti_{1-x}AI_x)N$ 피막은 모두 (200) 우선 방위를 갖고 있었으며, AI의 함량이 높아짐에 따라 입자의 크기가 미세해져 $(Ti_{0.2}AI_{0.8})N$ 의 경우 수 nm의 업자들로 이루어져 있었다. 열처리 시간을 일정하게 하고, 그 온도를 증가시킬 경우 비교적 낮은 온도 영역($~900^{\circ}C$)에서는 경도 증가를 나타내지만, 열처리가 더욱 진행됨에 따라 다시 경도가 감소하는 양상을 나타내었으며, 열처리 온도를 일정하게 하고 열처리 시간을 변화 시킬 경우에도 초기에 경도가 증가하다가 열처리가 진행됨에 따라 경도가 다시 감소하는 현상을 관찰 하였다. 이때 경도증가 정도는 Al 함량이 높을 수록 뚜렷하고 오래 지속되었으며, $(Ti_{0.2}AI_{0.8})N$ 피막의 경우 열처리 전 $2000HK_{0.01}$에서 열처리 후 $4500HK_{0.01}$로, 매우 큰 경도 증가를 나타내었다. 이와 같은 열처리 전후의 기계적 특성 변화는 준 안정상의 $(Ti_{1-x}AI_{x})N$ 피막에서, 열처리가 진행됨에 따라 미세한 AlN 업자가 석출되면서 나타나는 현상으로, 고분해능 전자현미경(HRTEM) 분석을 통해 경도가 증가한 시편의 경우 석출상의 크기가 5nm 이하로 매우 작고 대체로 기지와 연속적인 계면을 형성하나, 열처리가 진행될수록 석 출상의 크기가 커지고 임계크기 이상에 이르면 연속적인 계면은 거의 발견되지 않고, 대부 분 불연속적이고 확연한 계면을 형성함을 관찰 할 수 있었다. 알루미나(${\alpha}-Al_2O_3$) 기판 위에 증착한 $(Ti_{1-x}AI_{x})N$ 피막은 마찬가지로 (200) 우선 방위를 나타내었으나, 그 입자의 크기가 수십 nm로 고속도강위에 증착한 피막에 비해 상당히 크게 형성되었다. 또한 열처리 후에 AIN의 석출이 진행됨에도 불구하고 경도 증가는 나타나지 않고, 열처리가 진행됨에 따라 경도가 감소하는 양상만을 나타내었다. 결국 $(Ti_{1-x}AI_{x})N$ 피막이 열처리 전후에 보아는 기계적 특성의 변화 양상은 열역학적으로 안정한 Wurzite-AlN의 석출에 따른 것으로 AlN 석출상의 크기에 의존하며, 또한 이러한 영향은 $(Ti_{1-x}AI_{x})N$ 피막에 존재하는 AI의 함량이 높고, 초기에 증착된 막의 업자 크기가 작을 수록 클 것으로 여겨진다.