• 한국에너지공학회:학술대회논문집
• /
• 한국에너지공학회 1992년도 학술발표회 초록집
• /
• pp.39-40
• /
• 1992

This paper dealt with the manufacturing of binary alloy catalyst and showed simple electrochemical method for determing catalytic activity of oxygen reduction in acid or alkaline electrolyte. The catalyst was prepared by impregnating transition metal salts on platinum or silver particles adsorbed before on carbon paper substrate. The electrochemical characteristics of the catalysts was investigated with carbon paper electrode or PTFE-boned porous electrode and then cathodic current densities and tafel slopes were compared. As a result, of all binary catalysts utilized in this work, Pt-Fe, Pt-Mo showed better oxygen reduction activity than pure platinum catalyst in acid electrolyte and Ag-Fe, Ag-Pt, and Ag-Ni-Bi-Ti catalyst did than pure silver catalyst in alkaline electrolyte. The current density of Pt-Fe electrode in acid electrolyte was one and half times higher than that of Pt electrode(~500mA/$\textrm{cm}^2$ at 0.7VvsNHE).

• 한국지구과학회지
• /
• 제22권3호
• /
• pp.208-222
• /
• 2001

이 연구는 전남 광양광산과 그 주변의 하천에 형성되어 있는 부유성 비정질 퇴적물의 지구화학적 특성을 밝히기 위해 수행되었다. 부유성 비정질 퇴적물의 주요성분은 Fe$_2$O$_3$이며, Fe$_2$O$_3$의 함량은 17.9${\cdot}$72.3wt.% 범위로 나타난다. Fe함량이 증가하면 Si, Al, Mg, Na, K, Mn 및 Ti 함량이 감소하며 Te, Au, Ga, Bi, Cd, Hg, Sb, 및 Se등의 함량은 증가한다. 하상 침전물인 비정질 퇴적물에는 As(최대 54.9ppm), Bi(최대 3.77ppm), Cd(최대 3.65ppm), Hg(최대64ppm), Sb(최대 10.1ppm), Cu (최대 37.1ppm), Mo(최대 8.86ppm), Pb(최대 9.45ppm) 및 Zn(최대 29.7ppm) 등의 중금속원소가 농집되어 있다. 황갈색 침전물에는 Au(최대 4.40ppm)와 Ag(최대 0.24ppm) 함량이 매우 높게 나타나며, Au함량은 하천의 상류지역에 높은 함량을 보이다가 하류지역으로 갈수록 그 함량이 감소한다. 반면에 Ag 함량은 상류지역의 하천에 낮은 함량을 보이다가 하류지역으로 갈수록 그 함량이 증가하여 나타난다. XRD분석에서 하상의 황갈색 침전물은 X-선회절선이 뚜렷하지 않은 비정질이거나 결정도가 미약한 철수산화물로 밝혀졌으며, 석영, 침철석, 고령토, 일라이트 등이 관찰된다. IR분석에서 비정질 하상 퇴적물은 OH기, H$_2$O, SO$_4$ 및 Fe-O 기에 의한 흡수밴드가 관찰된다.

• 한국세라믹학회지
• /
• 제25권5호
• /
• pp.443-448
• /
• 1988

Colored Cubic Zircona(CCZ) single crystals were grown by the skull melting method. The grown crystals were doped with up to 0.1wt% transition (Cu, Ni, Co, Ti, Fe, Mo, Cr, V, Mn) metal ions on ZrO2-Y2O3(9.5~10mol%) and their Optical transmission spectra(λ=300~800nm)data were obtained. Various colors were pronounced due to dopant effects in the grown Crystals.

• 열처리공학회지
• /
• 제34권1호
• /
• pp.17-24
• /
• 2021

In this study, Ti-X (X=Mn, Fe, Mo) powder alloys were designed and manufactured by both powder metallurgy (PM) and metal powder injection molding (MIM) process to improve strength and formability compared to CP-Ti powder materials. It was found that the lamellar microstructure consisted of α and β phases was formed in PM-processed alloys. However, MIM-processed alloys showed not the lamellar microstucture but the equiaxed α + β microstructure. It was also revealed that the contents of X component and feedstock were not affected to microstructure evolution. The reason why different microstructure was appeared between PM-processed and MIM-processed alloys is not clear yet, but supposed to be the effect of intersticial elements such as C, H and N derived from feedstock during debinding process of MIM.

• 대한금속재료학회지
• /
• 제47권2호
• /
• pp.129-137
• /
• 2009

Corrosion behaviors of TiN coated dental casting alloys have been researched by using various electrochemical methods. Three casting alloys (Alloy 1: 63Co-27Cr-5.5Mo, Alloy 2: 63Ni-16Cr-5Mo, Alloy 3: 63Co-30Cr-5Mo) were prepared for fabricating partial denture frameworks with various casting methods; centrifugal casting(CF), high frequency induction casting(HFI) and vacuum pressure casting(VP). The specimens were coated with TiN film by RF-magnetron sputtering method. The corrosion behaviors were investigated using potentiostat (EG&G Co, 263A. USA) in 0.9% NaCl solution at $36.5{\pm}1^{\circ}C$. The corrosion morphologies were analyzed using FE-SEM and EDX. Alloy 1 and Alloy 2 showed the ${\alpha}-Co$ and ${\varepsilon}-Co$ phase on the matrix, and it was disappeared in case of TiN coated Alloy 1 and 2. In the Alloy 3, $Ni_2Cr$ second phases were appeared at matrix. Corrosion potentials of TiN coated alloy were higher than that of non-coated alloy, but current density at passive region of TiN coated alloy was lower than that of non-coated alloy. Pitting corrosion resistances were increased in the order of centrifugal casting, high frequency induction casting and vacuum pressure casting method from cyclic potentiodynamic polarization test.

• 센서학회지
• /
• 제11권2호
• /
• pp.77-83
• /
• 2002

저비용과 휴대성을 고려한 알코올 경보기의 제작을 위해 동작온도가 낮고 감도가 높은 반도체 가스 센서를 제작하였다. $Fe_2O_3$에 금속 산화물인 $MoO_3$, $V_2O_5$, $TiO_2$, 그리고 CdO 등을 첨가하여 스크린 프린팅법을 이용하여 센서를 제작하였다. 센서의 전기적 안정성을 위하여 질소 분위기에서 $700^{\circ}C$, 2시간 동안 열처리를 하였다. 알코올, 탄화수소계 가스와 담배연기 등을 사용하여 센서의 가스 감도를 조사하였다. $V_2O_5$를 첨가한 센서가 알코올 가스 1,000 ppm에 대해서 약 $80{\sim}90%$의 감도를 보이며, 타 가스에 대한 선택성도 가짐을 알 수 있었다. 제작된 센서와 PIC-chip을 사용하여 휴대 가능한 경보기를 제작할 수 있었다.

• 분석과학
• /
• 제22권5호
• /
• pp.422-431
• /
• 2009

휴대용 X-선 형광 분석기의 개발을 위한 기초연구로서 휴대용 및 bench-top X-선 형광 분석기를 이용하여 오일 시료 중의 Na, Mg, Al, Si, P, Ca, Ti, V, Cr, Mn, Fe, Ni, Cu, Zn, Mo, Ag, Cd, Sn, Ba, Pb 등 20종의 마찰 금속 원소들을 비교 분석하였다. 마찰 금속 원소의 농도가 10~900 mg/kg으로 함유된 오일 인증표준물질을 구입하여 측정 시간 등에 따른 최적 분석조건을 확립하고, 각 마찰 금속 원소에 대한 검량곡선을 작성하였다. 마찰 금속 원소가 함유된 오일 인증표준물질 및 시판 중인 엔진오일 시료의 주행 전 후의 금속 원소 농도를 empirical 법 및 fundamental parameter 법으로 정량분석하고 그 결과를 비교하였다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2004년도 하계학술대회 논문집 Vol.5 No.2
• /
• pp.894-897
• /
• 2004

Sodum bismuth titanate $(Na_{0.5}Bi_{0.5}TiO_3$ or NBT) thin films coated on the $LaNiO_3$ (LNO) electrode by sol-gel methode and rapid thermal annealing (RTA) technique. The NBT (NBT/LNO/Si) thin films examined by x-ray diffraction (XRD). The orientation of NBT was observed for films coated at $900^{\circ}C$, 5 min and $600^{\circ}C$, 60 min. Filed emission scanning electron microscopy (FE-SEM) showed uniform surface composed of grains. The grain size of NBT thin films increased with increasing annealing temperature.

• Transactions on Electrical and Electronic Materials
• /
• 제11권2호
• /
• pp.54-60
• /
• 2010

Polymer-assisted deposition is a chemical solution route to high quality thin films. In this process, the polymer controls the viscosity and binds metal ions, resulting in a homogeneous distribution of metal precursors in the solution and the formation of crack-free and uniform films after thermal treatment. We review our recent effort to epitaxially grow metal-nitride thin films, such as hexagonal GaN, cubic TiN, AlN, NbN, and VN, mixed-nitride $Ti_{1-x}Al_xN$, ternary nitrides tetragonal $SrTiN_2$, $BaZrN_2$, and $BaHfN_2$, hexagonal $FeMoN_2$, and nanocomposite TiN-$BaZrN_2$.

• 전기전자학회논문지
• /
• 제20권2호
• /
• pp.177-180
• /
• 2016

본 연구에서는 4H-SiC(0001)기판 위에서 형성되는 나노구조화를 제어하기 위해 상지층과 하지층으로 구성된 이중층 금속을 증착하고 두께, 열처리 시간을 변화하였다. 또한 표면에너지와 응집현상의 상관관계를 분석하기 위해 SiC와는 다른 표면에너지를 갖는 Glass와 Si기판에도 같은 조건으로 실험하였다. FE-SEM을 통하여 금속이 나노구조화를 형성하는 두께가 Ag=20nm, Ti=2nm임을 확인 했으며 두께가 두꺼울 수록 나노 입자가 형성되지 않았다. 세기판의 표면에너지를 구하기 위해 접촉각 측정기를 통해 정접촉각법으로 측정하였다. 그 결과 표면에너지 값이 가장 높은 Glass(53.89 mN/m) 기판에서 나노 입자가 가장 고르게 분포된 형태를 보였으며 SiC(41.13 mN/m)에서 나노구조화 되는 양상을 보였고, Si(32.96 mN/m)에서는 NPs 형성이 되지 않았다. 표면에너지가 작을수록 나노 입자형성이 고르게 분포되는 현상을 Young equation으로 분석하였다.