• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2009.05a
• /
• pp.143-143
• /
• 2009

본 연구에서는 Ti 합금에 Nb과 Zr을 첨가하여 Ti-29Nb-xZr(x : 3, 5, 7, 10, 15 wt %) 3원계 합금을 제조하고 Zr의 함량과 전압 그리고 용액의 농도를 다르게 하여 양극산화 시킨 후 합금의 표면을 관찰하고 특성을 조사하였다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2007.11a
• /
• pp.42-42
• /
• 2007

무독성 원소로 조성된 Ti-30Ta-xZr(x=3, 7, 10, 15) 합금을 제조하여, HA박막과 금속사이의 계면이 생기는 문제점을 개선하기 위해 합금 표면에 HA/TiN 및 HA/ZrN 이중층을 형성시킨 후 전기화학적 방법으로 코팅의 영향을 조사하였다.

• Journal of Korea Foundry Society
• /
• v.30 no.4
• /
• pp.147-150
• /
• 2010

An eco-friendly production technique of Al-8.6Ti-0.025C refiner was developed by melting a Al-Ti master alloy in a graphite crucible, in which the potential nucleation site, TiC effectively formed by the spontaneous in-situ reaction between excessive Ti and carbon from graphite crucible. The A3003 alloy refined by the Al-8.6Ti-0.025C showed effectively refined macrostructure and enhanced mechanical properties comparable to the commercial Al-Ti-B refiner. The effective refinement was achieved in a shorter compare to the melt-treating time commercial Al-Ti-B refiner.

• Journal of Powder Materials
• /
• v.11 no.3
• /
• pp.193-201
• /
• 2004

1960년 Au-Si계 합금에서 처음으로 비정질상이 급속 응고법에 의해 보고된 이래/sup 1)/ 지난 40년 간 많은 합금계에서 비정질상이 보고되어졌다. 대표적으로 Fe-, Ni-, Co기 합금 등 많은 합금계에서 비정질상이 보고되었으나, 비정질상의 형성을 위해서는 약 105 K/s이상의 높은 냉각속도를 필요로 하였다. 1980년대 수백 K/s의 낮은 냉각속도 하에서도 비정질상이 형성될 수 있는 다원계 합금(multi-component alloy)이 Mg-Ln-(Ni, Cu, Zn), Ln-Al-TM 합금에서 보고되어 졌으나 많은 관심을 받지 못하다가 1993년 Zr-Ti-Ni-Cu-Be 합금에서 수 ㎝ 크기의 비정질합금 제조가 보고되면서 전 세계적으로 많은 관심을 받게 되었다. Zr-Ti-Ni-Cu-Be계 벌크 비정질 합금이 보고된 후 Zr-(Nb,Pd)-Al-TM, Pd-Cu-Ni-P, Fe-Co-Zr-Mo-W-B, Ti-Zr-Ni-Cu-Sn등 여러 합금계에서 벌크 비정질 합금이 보고되었다. (중략)

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2018.06a
• /
• pp.69.2-69.2
• /
• 2018

전기화학적 양극산화법에 의해 형성하는 TiO2 나노튜브층은 넓은 비표면적과 규칙적인 구조를 가지고 있어 광촉매, 태양 전지, 생체재료 분야 등 다양한 분야에서의 응용이 되고 있으며, 국내 외 많은 연구가 보고 되고 있다. 특히, 나노튜브 층의 성장 거동에 미치는 인자로는 용액의 pH, 점도 등의 전해질의 물성, 인가전압, 시간 등이 있으며, 그에 대해 많은 연구가 이루어졌고 보고되고 있다. 최근 들어, 앞서 설명한 인자 이외에 양극산화에 사용되는 기판의 특성(미세구조, 결정구조, 결함, 첨가 원소 등)이 나노튜브층 성장거동에 영향을 미친다고 보고되었다. 따라서 본 연구에서는 전이금속으로 이루어진 Ti합금을 이용하여 첨가되는 합금원소가 산화막 성장 거동과 형태에 미치는 영향에 대해 조사 하였다. 본 연구에서는 Ti-Ni, Ti-Fe, Ti-Co 3종류 합금을 고진공 아크용해법으로 제조 하였으며, $1000^{\circ}C$에서 24시간 균질화 열처리를 하였다. 모든 합금은 최종 두께 2mm가지 냉간압연 하였으며, 양극산화는 동일한 조건에서 하였다. 생성된 나노튜브층의 표면 및 단면은 FE-SEM을 통해 관찰 하였다.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2009.05a
• /
• pp.40.2-40.2
• /
• 2009

일반적으로, 극미세 공정조직은 높은 강도를 나타내지만 낮은 연성을 가지는 단점을 보이고 있다. 극미세 공정합금의 연성을 증대시키고자, 상대적으로 연한 고용체 또는 경한 금속간 화합물을 마이크로 크기의 초정상으로 형성시키는 연구가 활발히 진행 되어지고 있다. 이러한 마이크로 크기의 초정상은 극미세 공정합금의 연성을 증가시키기에는 효과적이지만, 강도가 큰 폭으로 낮아지는 손실을 나타내고 있다. 최근, 공정조직 만으로 이루어진 극미세 공정합금의 연성을 증대시키고자, 공정조직의 형상 및 구성상을 조절하는 등의 연구가 발표되어지고 있다. 본, 연구에서는 Ti-, Mg-계 합금에 양극화 공정조직을 유도하여 극미세 공정조직 양극화 Ti-, Mg-합금을 개발, 이러한 불균일성을 내포한 양극화 공정조직이 극미세 공정조직 양극화 Ti-, Mg-합금의 기계적 성질에 미치는 영향을 체계적으로 연구하였다.

• Journal of the Korean Society of Propulsion Engineers
• /
• v.4 no.1
• /
• pp.1-12
• /
• 2000

This study summarizes the numerical analyses of a Ti alloy deformation under a back extrusion process. Amongst metallic parts in a small propulsion motor case, a Ti-6Al-4V alloy is used extensively. However, the Ti alloy shows a great deal of shear band formation which often leads to a fracture due to a narrow working temperature window. Moreover, the shear band tends to develop over an area where a contact occurs between the hot work piece and the die wall, due to localized cooling. Thus, heating the dies is often required to overcome the deformation localization. Therefore, it becomes necessary to investigate the internal temperature and strain rate distribution during forging process of a Ti alloy. Furthermore, a shear band analysis is peformed using a finite difference scheme and a comparison is made between steel and Ti alloy.

• Proceedings of the Korean Radioactive Waste Society Conference
• /
• 2003.11a
• /
• pp.395-400
• /
• 2003

For the long term storage safety study of the metallic spent fuel, U-Nb, U-Ti, U-Ni, U-Zr, and U-Hf simulated metallic uranium alloys, known as corrosion resistant alloys, were fabricated and oxidized in oxygen gas at $200^{\circ}C~300^{\circ}C$. Simulated metallic uranium alloys were more corrosion resistant than pure uranium metal, and corrosion resistance increases Nb, Ni, Ti in that order. The oxidation rates of uranium alloys determined and activation energy was calculated for each alloy. The matrix microstructure of the test specimens were analyzed using OM, SEM, and EPMA. It was concluded that Nb was the best acceptable alloying elements for reducing corrosion of uranium meta] considered to suitable as candidate.

• Resources Recycling
• /
• v.24 no.1
• /
• pp.21-27
• /
• 2015

The present study describes the process of producing low oxygen content alloy powder from Ti-6Al-4V and Ti-8Al-1Mo-1V (AMS 4972) alloy scraps using hydrogenation-dehydrogenation (HDH) and deoxidation in solid state (DOSS) processes. Each prepared powder was deoxidized with Ca contact and non-contact method to compare the deoxidation capability. It is known that the non-contact deoxidation method, using Ca vapor above the melting temperature $T_m$ of Ca, has greater deoxidation capability. However, Oxygen contents in Ti-6Al-4V and Ti-8Al-1Mo-1V powder after non-contact deoxidation method were higher than those after contact deoxidation method. Therefore, we investigate the effect of Al - the richest alloy element in theses Ti based metals - on the deoxidation processes.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.03a
• /
• pp.143-143
• /
• 2003

현대 산업이 발전함에 따라 다양한 기기들의 초소형화가 급속히 진행되고 있다. 이러한 요구에 부응하기 위하여 미세구동소자(Microelectromechanical system)의 개발이 많은 연구 그룹들에 의해서 이루어지고 있다. 미세구동소자에 응용을 하기 위해 개발되어지고 있는 여러 가지 소재들 중 $\ulcorner$형상기억합금 $\lrcorner$은 기존의 바이메탈이나 피에조 소자에 비하여 작동거리가 우수하기 때문에 그 가능성을 인정받고 있지만, 벌크재료는 느린 냉각속도 때문에 반응속도가 느린 단점이 있기 때문에 박막화 할 필요성이 있다. 이러한 이유로 여러 그룹들에 의해 형상기억합금의 박막화가 시도되고 있으나, 조성에 의해 특성의 변화가 심한 형상기억합금의 정밀한 조성제어가 힘들다고 알려져 있다. 몇몇 연구 그룹에서 RF magnetron sputtering법을 이용하여 Ti-Ni합금 박막을 성공적으로 제조하였다는 보고가 있지만, 타겟 조성 및 형태 등의 정밀한 제어가 필요하므로 3원 합금 박막 등을 제조할 경우에는 또 다시 타겟의 조건을 정밀하게 제어해야 할 필요성이 있다. 따라서 본 연구에서는 산화물 박막등의 제조에 있어서 타겟 조성과 제조된 박막 조성이 잘 일치하여 조성제어가 쉽게 이루어진다고 알려져 있는 PLD법을 도입하여 형상기억합금 박막제조에 적용가능한지를 검토하는 것을 목적으로 하였다.