• Journal of Powder Materials
• /
• v.13 no.3 s.56
• /
• pp.192-198
• /
• 2006

The nanostructured cerium oxide powders were synthesized by spray thermal decomposition process for the use as the raw materials of resistive oxygen sensor. The synthesis routes consisted of 1) spray drying of water based organic solution made from cerium nitrate hydrate ($Ce(NO_3){_3}6H_2O$) and 2) heat treatment of spray dried precursor powders at $400^{\circ}C$ in air atmosphere to remove the volatile components and identically to oxidize the cerium component. The produced powders have shown the loose structure agglomerated with extremely fine cerium oxide particles with about 15 nm and very high specific surface area ($110m^2/g$). The oxygen sensitivity, n ($Log{\propto}Log (P_{O2}/P^o)^{-n}$ and the response time, $t_{90}$ measured at $600^{\circ}C$ in the sample sintered at $1000^{\circ}C$, were about 0.25 and 3 seconds, respectively, which had much higher performances than those known in micron or $100{\sim}200nm$ sized sensors.

• Proceedings of the KAIS Fall Conference
• /
• 2000.10a
• /
• pp.39-41
• /
• 2000

Newly modified spray Pyrolysis system was developed to Produce ultra Pure and fine Powder by spray Pyrolysis Process. In this system, raw material solution was effectively atomized and sprayed into the reaction furnace. Also, thermal decomposition process fully completed in the three zone reaction furnace, and produced powder was effectively collected. A technology to reduce impurities in complex acid solution below 20ppm was also developed. The characteristics of produced powder were studied by changing the reaction conditions such as reaction temperature, the injection velocity of the solution and air, nozzle tip size and concentration of solution. The morphology of powder had spherical shape under the most experimental conditions, and the composition and the particle size distribution were almost uniform. Under the most experimental conditions average particle size of most produced powder was below 100nm.

• Journal of the Korean institute of surface engineering
• /
• v.45 no.1
• /
• pp.1-7
• /
• 2012

Multi-walled carbon nanotube (MWCNT) aluminum composite powders were deposited to form coatings using a high velocity oxygen fuel (HVOF) spraying process. High thermal energy and contact with atmospheric oxygen were supplied as the MWCNT aluminum composite particles were exposed to a gas flow field at high temperature (${\sim}3.0{\times}10^3$ K) during HVOF spraying. As a result, the particles underwent full or partial melting and rapid solidification due to the high thermal energy, and the exposure to oxygen induced the interfacial reaction of MWCNTs within the particle. The electrical and mechanical properties of MWCNT aluminum composite coatings were evaluated based on microstructure analysis. Electrical resistivity, elastic modulus, and micro-hardness, of the MWCNT aluminum composite coatings were higher than those of pure aluminum coating. The contribution of MWCNTs to the aluminum matrix can be attributed to their high electrical conductivity, dispersion hardening and anchoring effects. The relationship among the properties and the interaction of the MWCNTs with the aluminum matrix is discussed.

• Journal of Korea Foundry Society
• /
• v.17 no.4
• /
• pp.365-370
• /
• 1997

The effects of changes in microstructure of Si phase on the thermal expansion coefficients(CTEs) and tensile properties of the hypereutectic Al-Si foundry alloy(A390) were investigated experimentally. Specimens were prepared by various fabrication processes, such as a permanent mold casting, a squeeze casting and a spray casting process, and subsequently hot-extruded. CTEs of the spray-cast specimen were found to be about 10% lower than those of the permanent mold-cast specimen, and the CTEs of the hypereutectic Al-Si alloy(A390) were changed proportionally with the size of Si phase. Ultimate tensile strength of the spray-cast and hot-extruded specimen was dramatically improved about 100% with improved elongation, compared to that of permanent mold-cast specimen. These improvements are mainly attributed to the reduction in size and aspect ratio of the brittle Si phase, and the elimination of the microvoids/porosities formed during casting.

• Proceedings of the Korean Society of Marine Engineers Conference
• /
• 2011.06a
• /
• pp.314-314
• /
• 2011

• Journal of Korea Foundry Society
• /
• v.17 no.3
• /
• pp.292-301
• /
• 1997

• Journal of the Korean Ceramic Society
• /
• v.51 no.6
• /
• pp.598-604
• /
• 2014

Considerable research efforts have been explored attempting to enhance the thermal durability of thermal barrier coatings (TBCs) at the high operating temperatures of gas turbines. In this study, the suspension plasma spray (SPS) process was applied to produce TBCs with a segmented structure by using an yttria-stabilized zirconia (YSZ) suspension. Four different experiment sets were carried out by controlling the ratio between surface roughness of the bond coat and feed stock size ($R_a/D_{50}$) in order to examine the effect of $R_a/D_{50}$ ratio on the microstructure of SPS-prepared coatings. When the $R_a/D_{50}$ had a high value of 11.8, a deposited thick coating turned out to have a cone-type columnar microstructure. In contrast, at the low $R_a/D_{50}$ values of 2.9 and 0.18, a deposited thick coating appeared to have a dense, vertically-cracked microstructure. However, with the very low $R_a/D_{50}$ value of 0.05 the coating was delaminated.

• Journal of Welding and Joining
• /
• v.21 no.4
• /
• pp.39-45
• /
• 2003

Nano-TiO$_2$ photocatalytic coatings were deposited on the stainless steel 304(50$\times$70$\times$3mm) by the APS(Atmospheric Plasma Spraying). Photocatlytic reaction was tested in MB(methylene blue) aqueous solution. For applying nano-TiO$_2$ powders by thermal spray, the starting nano-TiO$_2$ powder with 100% anatase crystalline was agglomerated by spray drying. Plasma second gas(H$_2$) flow rate and spraying distance were used as principal process parameters which are known to control heat enthalpy(heat input). The relationship between process parameters and the characteristics of microstructure such as the anatase phase fraction and grain size of the TiO$_2$ coatings were investigated. The photo-decomposition efficiency of TiO$_2$ coatings was evaluated by the kinetics of MB aqueous solution decomposition. It was found that the TiO$_2$ coating with a lower heat input condition had a higher anatase fraction, smaller anatase grain size and a better photo-decomposition efficiency.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2023.05a
• /
• pp.59-60
• /
• 2023

The corrosion of steel rebar embedded in the coastal areas is corroding once the chloride ions ingress through the pores of the concrete. Therefore, in the present study, a 100 ㎛ thick Al and Zn coating was deposited by an arc thermal spray process onto the steel. The corrosion studies of these deposited coatings were assessed in 3.5 wt.% NaCl contaminated concrete pore (CP) solution with immersion periods. The results show that the Al coating is more corrosion resistance compared to the Zn coating attributed to the formation of gibbsite (γ-Al(OH)₃) whereas Zn coating exhibits Zn(OH)₂ onto the coating surface as passive layer. The Zn(OH)₂ is readily soluble in an alkaline solution. Alternatively, γ-Al(OH)₃ on the Al coating surface is less solubility in the alkaline pH, which further provides barrier protection against corrosion.

• Journal of the Korean institute of surface engineering
• /
• v.39 no.4
• /
• pp.179-189
• /
• 2006

High velocity oxygen fuel(HVOF) thermal spray coating of WC-Co powder is one of the most promising candidate for the replacement of the traditional hard chrome plating and ceramics coating because of the environmental problem of the very toxic $Cr^{6+}$ known as carcinogen and the brittleness of ceramics coating. WC-Co micron and nano powder were coated by HVOF thermal spraying method for the study of durability improvement of the high speed spindle. Coatings were planned by Taguchi program for the four spray parameters of spray distance, flow rates of hydrogen, oxygen and powder feed rate. Optimal coating process was obtained by the studies of coating properties such as porosity, surface roughness, micro hardness, and micro structure. WC-Co micron and nano powder were coated on the Inconel 718 substrate by the optimal coating process obtained in this study. The wear behaviors were studied by the sliding wear tester at room temperature and at an elevated temperature of $500^{\circ}C$ for the application to high speed spindle. Sliding wear test was carried out for four most promising hard coatings of chrome coating, ceramics coatings such as $A1_2O_3,\;Cr_2O_3$ and HVOF Co-alloy T800 for the comparison of their wear behaviors. HVOF WC-Co coating was better than other coatings showing highest micro hardness of 1400 Hv and comparable friction coefficients with others. HVOF WC-Co coating is a strong candidate for the replacement of the traditional hard chrome plating for the high speed spindle.