• Proceedings of the KIEE Conference
• /
• 2011.07a
• /
• pp.1447-1448
• /
• 2011

The CSPE cables are used for three years in nuclear power plant. The accelerated thermal aging of chloro sulfonate polyethylene(CSPE) jacket of test cables were carried out for the period equal to 10, 20 and 30 years in air at 90 and $100^{\circ}C$, respectively. The electrical volume resistivity, density, XPS, FE-SEM, EDS and XRF of the accelerated thermal aging of CSPE were measured. The validation of condition monitering method of accelerated thermal aging CSPE was estimated by them. The best validation of condition monitoring method of accelerated aging CSPE is electrical volume resistivity because change thermal of the specimen showed distinction.

• Journal of Electrical Engineering and Technology
• /
• v.7 no.1
• /
• pp.103-108
• /
• 2012

The present study describes the considerations on the long-term reliability of the on-line partial discharge (PD) ceramic sensor for thermal power generators. Voltage acceleration aging tests were carried out under continuous and impulsive thermal aging at more than $100^{\circ}C$, considering the practical service environment. Experimental results show that the sensors have a life that could last for more than 100 years, excellent dielectric characteristics, and insulation strength. In addition, the ceramic on-line PD sensors were installed in a thermal power generator in Korea for demonstration. The results of the PD calibration and test voltage application prove that the on-line ceramic sensors have satisfactory performances for on-line PD measurement.

• The Journal of Korean Academy of Prosthodontics
• /
• v.37 no.5
• /
• pp.597-606
• /
• 1999

This study was performed to evaluate the effect of aging and thermal cycling on the biaxial flexure strength of low commercially available veneering resin composites for crown(Dentacolor : DC, Artglass : AG, Esternia : ET and Targis : TG). Disc specimens were fabricated in a teflon mold giving 12mm in diameter and 1mm in thickness. All samples were divided into 4 groups. Group 1 was dried in a dessicator at $25^{\circ}C$ for 30 days. Group 2 was immersed in distilled water at $37^{\circ}C$ for 30 days. Group 3 was immersed in distilled water at $65^{\circ}C$ for 30 days. Group 4 was subjected to 10,000 thermal cycles between $5^{\circ}C\;and\;55^{\circ}C$, and the immersion time in each bath was 15 seconds per cycle. Biaxial flexure test was conducted using the ball-on-three-ball method at the cross head speed of 0.5mm/min and fracture surfaces were observed with scanning electoron microscope. The results obtained were summarized as follows; 1. Weibull modulus values, except for the AG group, decreased after thermal cycling treatment. 2. Biaxial flexure strength values of aging group at $37^{\circ}C$ were the lowest in all sample groups. Except for the DC group, strength values were significantly decreased for the drying group. 3. After thermal cycling test, the highest value of biaxial flexure strength of 188.8 MPa was observed in the ET group and the lowest value of 73.2 MPa was observed in the DC group. The strength values showed the significant differences in each group (p<0.05). 4. Observation of surfaces after thermal cycling test revealed the ditching in the part of surrounding large fillers.

• Journal of the Korean institute of surface engineering
• /
• v.50 no.6
• /
• pp.492-497
• /
• 2017

In this study, we investigated the effect of thermal aging on mechanical characteristics of Inconel 600 nickel-based alloy. The thermal aging was conducted up to 1000 hours at an atmosphere of $650^{\circ}C$. The microstructure of thermally aged specimens was investigated by an optical microscope (OM), scanning electron microscope (SEM) and energy dispersive spectrometer (EDS). In addition, tensile test (strain rate: 2 mm/min) and micro Vickers hardness test were conducted to evaluate mechanical properties with time. As a result of the experiment, Cr-rich carbide continuously precipitated during thermal aging, leading to the change of the mechanical characteristics and fracture mode. With the increase of aging time, tensile strength, yield strength, and hardness gradually decreased. The fracture mode changed from ductile to brittle with the increase of grain boundary carbide.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.33 no.3
• /
• pp.855-864
• /
• 2013

The dynamic characteristics of natural rubber bearings, which are used as isolator, are dependent on the main rubber's dynamic behaviors and nonlinear properties. Rubber materials tend to undergo an aging process under the influence of mechanical or environmental factors, so they inevitably end up facing damage. A main cause of aging like this is known to be oxidization, which occurs through the heat of reaction at high temperatures. Accordingly, in this study an accelerated thermal aging test was carried out in order to compare the characteristic values of the bearings before and after thermal aging occurs. As a result of this experiment, it was found that a thermal aging phenomenon could have some effects on shear stiffness, energy absorption, and equivalent damping coefficients of the bearings. Furthermore, a deterioration in the dynamic properties of the natural rubber bearings caused by the thermal aging was applied to an actual bridge and then the effects of such thermal aging on the seismic performance of the bridge were also compared and analyzed based on numerical analysis. As a result of this analysis, it was found that the changes in the basic properties of the natural rubber bearings caused by the thermal aging bring only a minor effect on the seismic performance of bridges.

• Polymer(Korea)
• /
• v.27 no.3
• /
• pp.249-254
• /
• 2003

The variation of chemical structure and physical properties of crosslinked polyethylene (XLPE) during thermal aging process was investigated. The formation of carbonyl functional group resulting from thermal oxidation reaction of XLPE was monitored using X-ray photoelectron spectroscopy and near infrared (NIR) spectroscopy. It was observed that the intensity of carbonyl peak observed at 1715 nm linearly increased with aging time in NIR spectroscopy. The linear relationship between NIR peak absorbance and aging time confirmed that NIR spectroscopy might be used as a proper tool for monitoring the aging process of polymeric materials. Also the formation of crosslinks during the aging process was monitored using thermal mechanical analysis, stress-strain test, and Shore hardness test. The change in the physical properties, such as the increase in the glass transition temperature from 110 to 132$^{\circ}C$, the decrease in the strain from 265 to 110%, as well as the increase in the shore D hardness from 32 to 50, was observed during the aging process.

• Journal of the Korean Society for Heat Treatment
• /
• v.31 no.3
• /
• pp.91-96
• /
• 2018

Microstructural development of ferritic 11Cr-3.45W heat-resistance steel for ultra-supercritical power plant during creep and thermal aging was investigated using electron microscopy. The test samples were isothermally aged at $700^{\circ}C$ for up to 4000 hours and subjected to creep loading at $700^{\circ}C$ for predetermined periods of lifetime to prepare the damaged materials. In this structural material, a various secondary phases are the primary influence on mechanical properties of ferritic heat-resistance steel. The typical precipitates of $M_{23}C_6$, MX and $M_2X$ secondary phases had been analyzed through qualitative and quantitative manner. Coarsening of precipitates and increase of lath width were observed during creep and thermal aging. This phenomenon was remarkable for creep process compared with isothermal aging process.

• Fire Science and Engineering
• /
• v.18 no.3
• /
• pp.45-50
• /
• 2004

Thermal degradation of PVC which used for insulator of 600V vinyl insulated wire has been studied by thermo gravimetry analysis and accelerated thermal aging test. The activation energy using thermo gravimetry analysis was determined by the kinetic methods, such as Kissinger and Flynn-Wall-Ozawa. The activation energy was determined to from 89.29 kJ/mol to 111.39 kJ/mol in 600V PVC insulated wire and from 97.80 kJ/mol to 119.25 kJ/mol in 600v heat-resistant PVC insulated wire. And also, the activation energy through a long-term thermal aging test was calculated by using Arrhenius equation In the low temperature of 8$0^{\circ}C$, 9$0^{\circ}C$, 10$0^{\circ}C$. The results showed that 600V PVC insulated wire was 92.16 kJ/mol, and 600v heat-resistant PVC insulated wire was 97.52 kJ/mol. Consequently, the activation energy of 600V heat-resistant PVC insulated wire is larger than 600V PVC insulated wire. Therefore, it can be predicted that 600V heat-resistant PVC insulated wire has a long-term stability relatively.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.30 no.5A
• /
• pp.417-424
• /
• 2010

The dynamic properties of laminated rubber bearings used as isolators in structures could be significantly deteriorated because of the change of microstructure in rubber caused by thermal aging. As a result, a catastrophic failure of bridges and buildings unexpectedly occurs when they are subjected to earthquake attack. Here, the dynamic properties of laminated rubber bearings before and after different of compression-shear loading and repeated cycles loadings, ultimated failure test with thermal aging were first measured and compared to each other. The experimental results, the effects of thermal aging on the shear stiffness, energy absorption, and equivalent damping coefficient of laminated rubber bearings are investigated. It is found that the deterioration of dynamic properties of laminated rubber bearings caused by thermal aging is significant and should be taken into account in designing rubber bearings.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.28 no.12
• /
• pp.1968-1973
• /
• 2004

Structural degradations are often experienced on the components of nuclear power plants in reactor pressure vessels (RPV) and steam generators (SG) when these components are exposed to high temperature and high pressure for a long period of time. Such conditions result in the change of microstructures and of mechanical properties of materials, which requires an evaluation of the safeguards related to structural integrity. In a primary reactor cooling system (RCS), a dissimilar weld zone exists between cast stainless steel (CF8M) in a pipe and low-alloy steel (SA508 cl.3) in a nozzle. Thermal aging is observed in CF8M as the RCS is exposed for a long period of time under the operating temperature between 290 and 33$0^{\circ}C$. Under the same conditions, it is well known that degradation is not observed in low alloy steel. An investigation of the effect of thermal aging on the various mechanical properties of the dissimilar weld zone is required. The purpose of the present investigation is to find the effect of thermal aging on the dissimilar weld zone. The specimens are prepared by an artificially accelerated aging technique maintained for various times at 43$0^{\circ}C$, respectively. Then, The various mechanical test for the dissimilar welds are performed.