• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.32 no.9
• /
• pp.788-795
• /
• 2008

To understand the tensile behaviors of GFRP at low temperature, three types of specimen have been used in this study. Tensile properties and fracture mechanisms for three orthogonal orientations of plain weave glass fabric reinforced epoxy resin laminate were investigated at temperature range of about -30 to $15^{\circ}C$. The tensile properties of axial and edge type specimen decrease slightly with decreasing temperature to $-20^{\circ}C$. However, at $-30^{\circ}C$ the decreases in the tensile properties increased considerably. Below $-20^{\circ}C$, thickness type specimen showed a marked decreases in the tensile properties. It was obvious that the fracture manner of thickness type specimen was adhesive failure at above $-10^{\circ}C$ and a mixed adhesive and cohesive failure at below $-20^{\circ}C$.

• Nuclear Engineering and Technology
• /
• v.51 no.3
• /
• pp.769-775
• /
• 2019

The tensile strength of irradiated 3C-SiC, SiC with artificial point defects, SiC with symmetric tilt grain boundaries (GBs), irradiated SiC with GBs are investigated using molecular dynamics simulations at 300 K. For an irradiated SiC sample, the tensile strength decreases with the increase of irradiation dose. The Young's modulus decreases with the increase of irradiation dose which agrees well with experiment and simulation data. For artificial point defects, the designed point defects dramatically decrease the tensile strength of SiC at low concentration. Among the point defects studied in this work, the vacancies drop the strength the most seriously. SiC symmetric tilt GBs decrease the tensile strength of pure SiC. Under irradiated condition, the tensile strengths of all SiC samples with grain boundaries decrease and converge to certain value because the structures become amorphous and the grain boundaries disappear after high dose irradiation.

• Journal of the Korea Concrete Institute
• /
• v.21 no.6
• /
• pp.789-796
• /
• 2009

The randomness in the strength of a RC member is caused mainly by the variability of the mechanical properties of concrete and steel, the dimensions of concrete cross sections, and the placement of reinforcing bars and so on . Among those variations, the randomness and uncertainty of mechanical properties of concrete, such as compressive strength, tensile strength, and elastic modulus give the most significant influences and show relatively large statistical variations. In Korea, there has been little effort for the construction of its own statistical models for mechanical properties of concrete and steel, thus the foreign data have been utilized till now. In this paper, variability of compressive strength, tensile strength and elastic modulus of normal-weight structural concrete with various specified design compressive strength levels are examined based on the data obtained from a number of published and unpublished sources in this country and additional laboratory tests done by the authors. The inherent probabilistic models for compressive and tensile strength of normal-weight concrete are proposed as Gaussian distribution. Also, the relationships between compressive and splitting tensile strength and between compressive strength and elastic modulus in current KCI Code are verified and new ones are suggested based on local data.

• Composites Research
• /
• v.35 no.1
• /
• pp.42-46
• /
• 2022

In this study, when the carbon fiber composite was manufactured, the correlation between the porosity and mechanical properties according to the number of glass fiber felts laminated together and the stacking sequence was confirmed. The carbon fiber composite was manufactured by stacking glass fiber felts, which are highly permeable materials, and using vacuum assisted resin transfer molding (VARTM). Porosity was measured by photographing the cross-section of the specimen with an optical microscope and then using porosity calculation code of MATLAB, and mechanical properties were measured for tensile strength, modulus by tensile test. Furthermore, Pearson correlation coefficient between porosity and mechanical properties was calculated to confirm the correlation between two variables. As a result, the number of glass fiber felt increased and the distance from the center of laminated composites increased, the porosity increasing were confirmed. In addition, tensile strength/modulus showed a weak positive correlation with porosity. Also, in order to confirm the effect of only porosity on tensile strength and modulus, mechanical properties calculated by CLPT (Classical Laminate Plate Theory) and experimental values were compared, and the difference in tensile strength showed a strong positive correlation with porosity and the difference in modulus showed a weak positive correlation with porosity.

• Bulletin of the Korean Chemical Society
• /
• v.30 no.10
• /
• pp.2253-2258
• /
• 2009

wet spun polyacrylonitrile (PAN) fiber precursors. The process variables chosen were treatment temperature, applied tension in stabilization process. The temperature profile of the stabilization was set on the basis of exothermic peaks of the differential scanning calorimetry (DSC) result. Both tensile strength and modulus increased with holding at onset temperatures of the exothermic peaks for extended duration, and with a higher heating rate up to the onset temperatures at a given applied tension among the experimental conditions. The increase in load monotonously increased the tensile modulus, on the other hand, the tensile strength was maximum at the load of 15 mg/filament (T15). The load 20 mg/ filament (T20) was considered to be exceeded to form oriented crystalline structure, possibly introducing more defects in the fiber than under load of T15. The sample CP3-T15 O5 H30 showed the best tensile properties among the samples experimented whose tensile properties are compatible with the commercialized grade of general purpose carbon fibers even at low carbonization temperature such as $800\;{^{\circ}C}$ (the carbonization temperature in the commercial process. 1300∼$1500\;{^{\circ}C}$).

• Journal of Technologic Dentistry
• /
• v.36 no.4
• /
• pp.239-246
• /
• 2014

Purpose: The purpose of this study was to compare the tensile strength and mechanical properties of orthodontic wire joints made by gas soldering and laser welding, with and without filling material, to identify the effectiveness and potential clinical application of laser welded orthodontic wires. Methods: Three joint configurations of orthodontic wire were used: diameter 0.9 to 0.9 mm wire, diameter 0.9 to 0.5 wire and diameter 0.9 mm wire to band. The joints were made using three different methods: gas soldering, laser welding with and without filling material. For each kind of joint configuration or connecting method 7 specimens were carefully produced. The tensile strengths were measured with a universal testing machine (Zwick/Roell, Instron, USA). The hardness measurements were carried out with a hardness tester(Future-Tech Co. Tokyo, Japan). Data were analyzed by AVOVA(p= .05) and Turkey HD test(p= .05). Results: In all cases, gas soldering joints were ruptured on a low level on tensile bonding strength. Significant differences between laser welding and gas soldering(p< .05) were found in each joint configuration. The highest tensile strength means were observed for laser welding, with filling material, of 0.9 to 0.9 mm wire joint. Conclusion: In conclusion, the elastic modulus and tensile strength means of laser soldering with filling material were the highest, and the tensile strength means of laser soldering were higher than those of gas soldering.

• Journal of the Korean Wood Science and Technology
• /
• v.50 no.6
• /
• pp.392-403
• /
• 2022

Currently, composite board manufacturing using natural fibers has the potential to expand owing to environmental awareness. To produce a composite board, treatment is required to improve the mechanical and physical properties of the natural fibers. In this study, sodium chloride (NaCl) was used for the chemical treatment. However, studies on chemical treatments using NaCl are limited. This study aimed to investigate the characteristics of kenaf fibers after NaCl treatment. The NaCl treatment concentrations were 1, 3, and 5 wt.% at room temperature, with soaking durations of 1, 2, and 3 h. The tensile strength, strain, and Young's modulus were measured to evaluate the mechanical properties of the fibers. The fiber bundle diameter, weight change owing to treatment, and contact angle were determined to analyze the effect of NaCl treatment. The kenaf fiber bundle treated with 5 wt.% NaCl for 3 h exhibited the highest tensile strength, Young's modulus, reduction in fiber bundle diameter, weight change, and decrease in contact angle compared to those of untreated fiber bundles. The tensile properties of the fiber bundle exhibited a tendency to decrease with increasing fiber bundle diameter. Increasing the soaking duration from 1 to 2 h did not result in a significant decrease in the fiber bundle diameter or an increase in tensile strength. However, a further increase in the soaking duration from 2 to 3 h resulted in a considerable decrease in the fiber bundle diameter and an increase in the tensile strength.

• Journal of the Korean Society of Industry Convergence
• /
• v.9 no.4
• /
• pp.309-315
• /
• 2006

Important material properties of UCAS rod can divide by tension characteristic of base rod part and both end part of U type anchor. Tensile properties of base rod part need as concrete reinforcement material as an alternative material of reinforcing rod, and tensile properties of U type anchor is used at connection with UCAS rod. This treatise carry out tensile test of UCAS rod, examine necessary properties such as strength, elastic modulus and maximum capacity of UCAS rod as reinforcement material of concrete. Also, to examine material properties carry out tensile test of U type anchor.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2005.11a
• /
• pp.125-128
• /
• 2005

The dispersion of carbon nanofiber (CNF) was carried out by solution blending, mechanical mixing, and sonication. CNFs at levels of 5-50% fiber weight content were mixed with polypropylene (PP) powder, and then were melt-mixed using a twin-screw extruder. For the further alignment of fibers, extruded rods were stacked uni-directionally in the mold cavity for the compression molding. For the evaluation of mechanical properties of nanocomposites, tension, in-plane shear, and flexural tests were conducted. CNF/PP composites clearly showed reinforcing effect in the longitudinal direction. The tensile modulus and strength have improved by 100% and 40%, respectively for 50 % fiber weight content, and the flexural modulus and strength have increased by 120% and 25%, respectively for the same fiber weight content. The shear modulus showed 65% increase, but the strength dropped sharply by 40%. However, the property enhancement was not significant due to the poor adhesion between fiber and matrix. In the transverse direction, the tensile, flexural, and shear strength decreased as more fibers were added.

• Computers and Concrete
• /
• v.21 no.1
• /
• pp.87-94
• /
• 2018

This paper presents the results of an experimental study to investigate the influences of high temperatures on the mechanical properties of concrete containing recycled fine aggregate. A total of 150 concrete prisms ($100{\times}100{\times}300mm$) and 150 concrete cubes ($100{\times}100{\times}100mm$) are cast and heated under five different temperatures ($20^{\circ}C$, $200^{\circ}C$, $400^{\circ}C$, $600^{\circ}C$, $800^{\circ}C$) for test. The results show that the mass loss, compressive strength, elastic modulus, splitting tensile strength of concrete specimens containing recycled fine aggregate decline significantly as the temperature rise. At the same temperature, the compressive strength, splitting tensile strength, elastic modulus of concrete specimens containing recycled coarse aggregate and recycled fine aggregate (RHC) is lower than that of concrete specimens containing natural coarse aggregate and recycled fine aggregate (RFC). The shape of stress-strain curves of concrete specimens at different temperatures is different, and the shape of that become flatter as the temperature rises. Normal concrete has better energy absorption capacity than concrete containing recycled fine aggregate.