• Korean Chemical Engineering Research
• /
• v.46 no.5
• /
• pp.880-885
• /
• 2008

Spray pyrolysis was applied to prepare spherical silica particles with mesopores of a regular structure. The physical properties such as surface area, pore size, pore structure, particle size, and morphology were studied by BET, SEM, SAXS, and DLS analysis. At a fixed gas flow rate, the BET surface area changed from 200 to $1,290m^2/g$ as changing the CTAB/TEOS molar ratio from 0.05 to 0.3. At a fixed CTAB/TEOS ratio, the surface area of silica particles was varied from 1,062 to $1,305m^2/g$ with changing the gas flow rate from 10 to 40 l/min. The average pore size measured by BJH desorption was about $21{\sim}23{\AA}$ and not significantly influenced by the CTAB/TEOS ratio and the gas flow rate. Finally, the highest surface area which was $1,305m^2/g$ were obtained when the CTAB/TEOS ratio and the gas flow rate were 0.2 and 20 l/min, respectively. According to SAXS analysis, the prepared silica particles showed a strong peak at $2{\theta}=2.6^{\circ}$ and two minor peaks around $2{\theta}=4.4^{\circ}$ and $5.1^{\circ}$, which are due to regular mesopores of hexagonal structure. The morphology of silica particles prepared were spherical shape and the average particle size was $1.0{\mu}m$.

• Bulletin of the Korean Chemical Society
• /
• v.33 no.3
• /
• pp.1067-1070
• /
• 2012

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2000.11a
• /
• pp.26-26
• /
• 2000

• Journal of the Korean Applied Science and Technology
• /
• v.24 no.2
• /
• pp.174-181
• /
• 2007

In this study, $SiO_2/poly(ethylene-co-vinyl$ alcohol)(EVOH) hybrid coating materials with gas barrier property could be produced using sol-gel method. The biaxially oriented polypropylene (BOPP) substrate with surface pretreatment was coated with the prepared hybrid sols containing various inorganic silicate component by a spin coating method. Crystallization behavior of the hybrids was investigated in terms of analysis of X-ray diffraction and cooling thermogram from DSC experiment. From the morphological observation of the $SiO_2/EVOH$ hybrid gel, it was confirmed that there existed an optimum content of inorganic silicate precursor, Tetraethylorthosilicate (TEOS), to produce hybrid materials with dense microstructure, exhibiting uniformly dispersed silica particles with average size below 100 nm. When TEOS was added at below or above the optimum content, particle clusters with large domain were observed, resulting in phase separation. This morphological result was found to be in good agreement with that of oxygen permeability of the hybrid coated films. In the case of film coated with hybrid prepared from addition of 0.01 - 0.02mol of TEOS, a remarkable improvement in barrier property could be obtained, however, with the addition of TEOS more than 0.04 mol, the barrier property was dramatically reduced because of phase separation and micro-crack formation on the film surface.

• Journal of the Korean Ceramic Society
• /
• v.34 no.2
• /
• pp.216-224
• /
• 1997

Porous silica ceramics were prepared(with HCI catalyst) using H2O/TEOS molar ratios of 2.6~59.0, with the EtOH/TEOS ratio fixed. After preparing 9 kinds of sol, the followings were investigated; measurement of the gelation time, thermal analyses by TG/DTA, property analyses of the intermediates by FT-IR and X-ray diffractometry with dried samples, analyses of SiO2 polymer by FT-IR, the investigation of specific sur-face area and pore size distribution by N2-adsorption isotherm, and structural change of SiO2 polymer and pore morphology by TEM observation, with samples heat-treated to 50$0^{\circ}C$. In the concentrations of in-vestigated compositions and catalyst, gelation time showed a minimum at ca. 11 moles of water per one mole of TEOS, the highest degree of polymerization at ca. 8-18 moles, and the largest specific surface area at ca. 11 moles, which means that the polymerization proceeded fastest at ca. 11 moles of water. In con-clusion, the more water used, the faster the polymerization reaction up to ca. 11 moles, but more than ca. 11 moles of water caused retardation of gelation and resultant reduction of specific surface area.

• Membrane Journal
• /
• v.26 no.5
• /
• pp.391-400
• /
• 2016

In this work, novel thin film composite (TFC) forward osmosis (FO) membranes are developed via interfacial polymerization on the polysulfone (PS) substrate, using TEOS as the a sol-gel reagent to form hydrophilic interlayer polymer between PS and polyamide (PA). The PS substrate was cast on a very thin polyester nonwoven to reduce membrane resistance. With the incorporation of TEOS (tetraethoxy silane) polymer in the interface between PS and PA, the formed TFC FO membrane exhibits better hydrophilicity and improved water flux, and therefore superior membrane performance. By changing the polymerization sequence of PA interfacial polymerization and TEOS sol-gel condensation, the surface properties and performance of FO membranes are changed significantly. The permeability of FO membranes were estimated using the bench-scale FO test equipment. The distribution of the polysiloxane on composite membrane and morphology are also studied with FE-SEM and EDAX. The PS_PA_TEOS membrane showed highly enhanced water flux (79.2 LMH) but reverse salt flux (RSF) value (7.10 GMH) also increased. However, the flux of PS_TEOS_PA membrane increased moderately (54.1 LMH) without increasing RSF value (1.60 GMH) compare with PS_PA membrane.

• Journal of Environmental Science International
• /
• v.9 no.4
• /
• pp.311-318
• /
• 2000

To improve $CO_2$pemselectivity, a modified silica membrane was prepared by chemical vapor deposition with tetraethoxysilane(TEOS)-ethanol-water, and TEOS-ethanol-water-HCI solution at 300-$600^{\circ}C$. The silica was effectively deposited in the mesopores of a ${\gamma}$-alumina film coated on a porous $\alpha$-alumina tube by evacuating the reactants through the porous wall. In this membrane, $CO_2$interacts, to some extent, with the pore wall, and $CO_2$/$N_2$selectivity then exceeds the value of the Knudsen diffusion mechanism, while the membrane derived from TEOS alone has no $CO_2$selectivity. The silica membrane prepared from TEOS-ethanol-water-HCI solution showed that $CO_2$permeance was $2.5$\times$10^{-7}mol/s^{-1}.m^{-2}.Pa^{-1} at 30{\circ}C$ and $CO_2$/$N_2$selectivity was approximately 3. The $CO_2$permeance and selectivity was improved by enlarging the surface diffusion with modification of chemical affinity of the silica pores.

• Proceedings of the KSME Conference
• /
• 2000.11b
• /
• pp.174-179
• /
• 2000

Ultrafine particles have been used widely in many high technology industrial areas. The spherical nonagglomerated and uniform nanometer-size $SiO_2$ particles are synthesized by the direct injection of TEOS(Tetraethyorthosilicate) using electro-hydrodynamic spray ins method. Electro-hydrodynamic spray can generate in the range of submicron-size TEOS particles with high electric charge by applying a high electric field between the liquid injection nozzle and the reaction tube. This TEOS particles are thermally decomposed or oxidized to produce nanometresized $SiO_2$ particles in the reaction tube. Spherical, nonagglomerated and ultrafine particle generated and examined at furnaced temperature, $800^{\circ}C$ and TEOS flowrate of 0.49 or $1.00cm^3/hr$ using SEM and SMPS. As the total gas flowrate changes from 1.51pm to 5.01pm, the mean diameter of $SiO_2$ particle decreases from 120 nm to 68nm.

• Applied Chemistry for Engineering
• /
• v.8 no.2
• /
• pp.301-307
• /
• 1997

Monodisperse, spherical $SiO_2/TiO_2$ composite fine powders were prepared by modified Sol-Gel process which $TiO_2$ fine Powders was used as a seed particles for condensation of TEOS (Tetraethyl Orthosilicate). The reaction was carried out under $N_2$ atmosphere at ambient temperature using $NH_3$ as a catalyst. Ethanol was used as a solvent. Drying process was carried out with vacuum trap which cooled by liquid $N_2$. The reaction variables were the concentration of TEOS, the concentration of ammonia, the size of $TiO_2$ seed and molar ratio of $SiO_2/TiO_2$. The optimum condition for the preparation of $SiO_2/TiO_2$ composite fine powders without agglomeration was [TEOS]=0.3M, [$NH_3$]=0.7M, size of $SiO_2/TiO_2$ seed = 200~300nm.

• Polymer(Korea)
• /
• v.38 no.5
• /
• pp.573-579
• /
• 2014

The effect of synthesis conditions such as carbon nanotube (CNT), 2,2,2-trifluoroethylmethacrylate (3FMA), and composition of organic-inorganic material in ozone resistance and surface characteristics of ultraviolet cured organic-inorganic hybrid coating film has been investigated. Coating solution was prepared using tetraethoxysilane (TEOS), silane coupling agent methacryloyloxypropyltrimethoxysilane (MPTMS), 3FMA, various organic materials with acrylate group, and CNT, then bar-coated on substrates using applicator, and densified by UV-curing. It was found that ozone resistance and adhesion of the coating film were strongly dependent upon contents of TEOS, 3FMA, and CNT. Especially, ozone resistance, adhesion, and surface hardness of coating film with CNT were improved, relatively. Ozone resistance of coating film with a high TEOS content was increased, but adhesion was decreased. In addition, it was also found that ozone resistance of coating film was increased with contents of 3FMA. On the other hand, surface hardness was decreased with increase of 3FMA.