• Journal of the korean academy of Pediatric Dentistry
• /
• v.31 no.3
• /
• pp.421-430
• /
• 2004

The purpose of this study was to measure and compare the amount of unreacted TEGDMA from pit and fissure sealants cured with three different light sources; conventional halogen light curing unit, plasma arc light curing unit and argon laser. The specimens were eluted in distilled water for different time intervals. The time-related release of TEGDMA were analyzed by reverse-phase high performance liquid chromatography(HPLC). The result of present study can be summarized as follows: 1. The time-related release of TEGDMA decreased with increasing curing time in conventional halogen light, however, that not statistically significant difference(p>0.05). 2. The elution from the specimens cured for 6 and 9 seconds with plasma arc light was similar results corresponding with the time-related TEGBMA release, and was significantly lower than that cured for 3 seconds(p<0.05). 3. The elution of TEGDMA from the specimens cured with argon laser was significantly higher than that cured with halogen and plasma arc light(p<0.05). 4. The elution of TEGDMA from under recommended time of three different light sources were showed to be no statistically significant difference(p>0.05). 5. In time-related release of TEGDMA from recommended time of each light sources, the results correspond to 40 seconds of halogen light and 6 seconds of plasma arc light were similar(p>0.05). 6. The elution of TEGDMA, from over recommended time of three different light sources were showed to be no statistically significant difference(p>0.05). In this study, I suggest that curing time of plasma arc light is 6 and/or 9 seconds in the field of clinical pediatric dentistry claiming its effectiveness in optimal polymerization and reduced chair time.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.33 no.3
• /
• pp.365-376
• /
• 2006

The purpose of this study was to evaluate the efficacy of blocking the oxygen in the air during the polymerization of sealant. All curing were performed with various light curing units under the application of oxygen gel barrier, stream of nitrogen and carbon dioxide gas for inhibition of oxygen diffusion into sealant surface. The results of present study can be summarized as follows : 1. The amount of eluted TEGDMA form the specimens cured with all the three different light units in the stream of $N_2$ and $CO_2$ gas and application of Oxygen gel barrier($DeOx^{(R)}$) were significantly lower than in the room-air atmosphere (Control) (p<0.05). 2. In the $DeOx^{(R)}$ application, the amount of eluted TEGDMA the specimen cured with PAC light for 10seconds was less than that cured in the stream of $N_2$ and $CO_2$ atmospheric conditions (p<0.05) 3. In the LED using 10 or 20sec irradiation times under the stream of $N_2$ and $CO_2$, the eluted TEGDMA showed to be no statistically significant difference (p>0.05). 4. The microhardness from the specimens cured with all the three different light units under each treated conditions were significantly higher than in the room-air atmosphere (p<0.05). 5. The surface treatment by $DeOx^{(R)}$, $N_2$ and $CO_2$ reduces the thickness of oxygen inhibited layer by sp proximately 49% of the untreated control value.

• Restorative Dentistry and Endodontics
• /
• v.34 no.1
• /
• pp.42-50
• /
• 2009

Deterioration of long-term dentin adhesion durability is thought to occur by hydrolytic degradation within hydrophilic domains of the adhesive and hybrid layers. This study investigated the hypothesis that priming the collagen network with an organic solvent displace water without collapse and thereby obtain good bond strength with an adhesive made of hydrophobic monomers and organic solvents. Three experimental adhesives were prepared by dissolving two hydrophobic monomers, bisphenol-A-glycidylmethacrylate (Bis-GMA) and triethyleneglycol dimethacrylate (TEGDMA), into acetone, ethanol or methanol. After an etching and rinsing procedure, the adhesives were applied onto either wet dentin surfaces (wet bonding) or dentin surfaces primed with the same solvent (solvent-primed bonding). Microtensile bond strength (MTBS) was measured at 48 hrs, 1 month and after 10,000 times of thermocycles. The bonded interfaces were evaluated using a scanning electron microscope (SEM). Regardless of bonding protocols, well-developed hybrid layers were observed at the bonded interface in most specimens. The highest mean MTBS was observed in the adhesive containing ethanol at 48 hrs. With solvent-primed bonding, increased MTBS tendencies were seen with thermo cycling in the adhesives containing ethanol or methanol. However, in the case of wet bonding, no increase in MTBS was observed with aging.