• The Korean Journal of Ceramics
• /
• v.5 no.4
• /
• pp.363-367
• /
• 1999

New glass ceramics were investigated for the application as substrates to be used in hard disk devices. The glass system to precipitate lithium di-silicate was studied so as to optimize the composition to realize very high surface flatness. The addition of small amount of several metal oxides with high valences had very drastic effects on the microstructure, because they played a role of crystallization agents, and consequently it determined surface flatness even after the polishing process. The possible mechanism changes of crystal growth due to the addition of metal oxides were discussed in relation to the final micro-texture development. The glass ceramics with very high surface flatness(Ra=7.1 $\AA$) was obtained by the addition of the mixture of $P-2O_5 \;and \;MoO_3$ as crystallization agents.

• Journal of the Korean Ceramic Society
• /
• v.51 no.4
• /
• pp.312-316
• /
• 2014

The joining behavior of forsterite ceramics to SUS304 alloy using $8PbO-78Bi_2O_3-8B_2O_3-4ZnO-2SiO_2$ (wt%) system glass frit was investigated. The contact angle was smaller than $90^{\circ}$ at a temperature of $460^{\circ}C$. Redox reaction at the interface between forsterite and SUS304 was found to appear when the electrons in the metal part moved toward the glass part and the oxygen ions in glass moved to the metal side. The decrease of the surface tension due to the PbO solubility on the forsterite side contributed to the better wetting behavior at low temperature.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.26 no.8
• /
• pp.624-628
• /
• 2013

With the recent development of less-costly uncooled detector technology, expensive optics are among the remaining significant cost drivers in the thermography camera. As a potential solution to this problem, the fabrication of IR lenses using chalcogenide glass has been studied in recent years. We report on the molding and evaluation of a ultra-precision chalcogenide-glass lens for the thermography camera for body-temperature monitoring. In addition, we fabricated prototype thermography camera using the chalcogenide-glass lens and obtained the thermal image from the camera. In this work, it was found out that thermography camera discerned body-temperature between 20 and $50^{\circ}C$ through the analysis of thermal image. It is confirmed that thermography camera using the chalcogenide-glass lens is applicable to the body-temperature monitoring system.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.07a
• /
• pp.552-556
• /
• 2000

The crystallization behavior and dc Conductivities of CuO-Nb$_2$O$_{5}$ -V$_2$O$_{5}$ glasses prepared by quenching on the copper plate were investigated. The conductivities of the glasses were range from 10$^{-4}$ s.$cm^{-1}$ / at room temperature, but the conductivities of the glass-ceramics were 10$^{-3}$ s.$cm^{-1}$ / increased by 10$^1$ order. The linear relationship between In($\sigma$T) and T$^{-1}$ suggested that the electrical conduction in the present glass system would be due to a small polaron hopping mechanism. The value of activation energy of glass-ceramics heat-treated at 30$0^{\circ}C$ for 12hrs was found to be 0.leV

• 제어로봇시스템학회:학술대회논문집
• /
• 2004.08a
• /
• pp.1102-1105
• /
• 2004

In this paper, the problem of a viewer's head tracking in a desktop-based interactive stereoscopic display system is considered. A fast and low-cost approach to the problem is important for such a computing environment. The system under consideration utilizes a shuttle glass for stereoscopic display. The proposed method makes use of an image taken from a single low-cost video camera. By using a simple feature extraction algorithm, the obtained points corresponding to the image of the user-worn shuttle glass are used to estimate the glass center, its local 'yaw' angle, as measured with respect to the glass center, and its global 'yaw' angle as measured with respect to the camera location. With these estimations, the stereoscopic image synthetic program utilizes those values to interactively adjust the two-view stereoscopic image pair as displayed on a computer screen. The adjustment is carried out such that the so-obtained stereoscopic picture, when viewed from a current user position, provides a close-to-real perspective and depth perception. However, because the algorithm and device used are designed for fast computation, the estimation is typically not precise enough to provide a flicker-free interactive viewing. An error concealment method is thus proposed to alleviate the problem. This concealment method should be sufficient for applications that do not require a high degree of visual realism and interaction.

• Resources Recycling
• /
• v.28 no.6
• /
• pp.64-72
• /
• 2019

Fly ash has different chemical composition depending on the type and quality of flaming coal. Fly ash is classified according to carbon content and particle size. Waste glass powder is manufactured by crushing glass. Exterior Insulation Finish System (EIFS) is generally applied by using poly-styrene foam which is economical and has excellent thermal insulation performance. However, poly-styrene foam has excellent insulation performance, but it is vulnerable to fire, which is becoming a serious problem. In this study, using a fly ash and waste glass powder to produce a finishing mortar at high temperatures. Also, High temperature strength and flame retardant properties were tested according to the cover thickness. From the test result, finishing mortar prepared using fly ash and waste glass powder is due to the improved heat resistance by alkali-activated bonding. However, since the strength decreases at high temperatures, it is necessary to select an appropriate mixing proportion.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2012.05a
• /
• pp.341-342
• /
• 2012

• Journal of the Korean Ceramic Society
• /
• v.20 no.2
• /
• pp.147-152
• /
• 1983

For $Na_2O-BaO-SiO_2$ system glass the pelletizing conditions of the disk type equipment were investigated. The effects of the pelletized batch on melting were also examined. Through the experiment the optimum conditions for pelletizing the batch were found as follows. Revolving speed of the pan 30rpm pan angle 40-35 degree Water content 12-13% Drying temperature $200^{\circ}C$ Preheating temperature $650^{\circ}C$ The molten glass of the pelletized batch was refined better than that of the loose batch.

• The Journal of Korean Academy of Prosthodontics
• /
• v.50 no.4
• /
• pp.235-242
• /
• 2012

Purpose: The purpose of this study was to compare the fracture behavior of Zironia, glass infiltrated Alumina and PFM full crown system. Materials and methods: Fifteen crowns for each of 3 experimental groups (Zironia, glass infiltrated Alumina and PFM full crown) were made by the conventional method. The crowns mounted on the testing jig were inclined in 30 degrees to the long axis of the tooth and the universal testing machine was used to measure the fracture strength. Results: 1. The mean fracture strengths were $588.3{\pm}49.6MPa$ for zirconia system, $569.1{\pm}61.8MPa$ for PFM system and $551.0{\pm}76.5MPa$ for glass-infiltrated alumina system (P>.05). 2. The mean shear bond strengths were $25.5{\pm}5.6MPa$ for zirconia system, $38.9{\pm}5.0MPa$ for Ni-Cr alloy system and $39.4{\pm}5.1MPa$ for glass-infiltrated alumina system. 3. The chemical bonding was observed at interfaces between PFM or glass-infiltrated alumina and veneering porcelain, however, no chemical bonding was observed at interface between zirconia and veneering porcelain. Conclusion: With the study, the fracture strengths of PFM crown system had a higher fracture strength than conventional zirconia system crown and glass-infiltrated alumina crowns. and than the shear bond strengths glass-infiltrated alumina system had a higher shear bond strength than conventional PFM system and zirconia system.

• Progress in Medical Physics
• /
• v.19 no.1
• /
• pp.9-13
• /
• 2008

The purpose of this study was to measure the skin dose using the glass dosimeter and diode and to compare those measurements to the planned skin dose from the treatment planning system. For the reproducibility of the glass dosimeter (ASAHI TECHNO GLASS CIRPORATION, Japan), the same dose was irradiated to 40 glass dosimeters three times, among which 28 with the reproducibility within 3% were selected for the use of this study. For each of 27 breast cancer patients, the glass dosimeters and diodes were attached to 4 different locations on the skin to measure the dose during treatment. All the patients received one fraction of 180 cGy each. The maximum difference of measurements between the glass dosimeter and diode at the same location was 3.2%. Comparing with the planned skin dose from the treatment planning system (Eclipse v6.5, Varian, USA), the dose measured by the glass dosimeter and the diodeshowed on an average 3.4% and 2.3% difference, respectively. The measured doses were always less than the planned skin dose. This may be due to the specific errors of both detectors. Also, the difference may be caused by the fact that since the skin where the detectors were attached is pretty moveable, it was not fix the detectors on the skin.