• The Journal of Advanced Prosthodontics
• /
• v.14 no.6
• /
• pp.335-345
• /
• 2022

PURPOSE. This in vitro study aimed to evaluate the surface characteristics of a full veneer crown fabricated chairside (CS) from a (Y, Nb)-TZP zirconia block in response to conventional zirconia grinding and polishing. MATERIALS AND METHODS. Zirconia crowns (n = 40) were first prepared and divided into two groups of materials: Labside (LS) and CS, after which each specimen went through a five-step grinding and polishing procedure. Following each surface treatment, surface characteristics were analyzed using confocal laser microscopy (CLSM), average surface roughness (Ra) values were processed from the profile data through Gaussian filtering, and X-ray diffraction pattern analysis was performed to evaluate the monoclinic (M) phase content. Then, a representative specimen was selected for field-emission scanning electron microscopy (FE-SEM), followed by a final analysis of the roughness and X-ray diffraction of the specimens using the independent t-test and repeated measures analysis of variance (RM-ANOVA). RESULTS. In every group, polishing significantly reduced the Ra values (P < .001). There was no significant difference in Ra between the polished state CS and LS. Furthermore, CLSM and FE-SEM investigations revealed that even though grain exposure was visible in CS specimens throughout the as-delivered and ground states, the exposure was reduced after polishing. Moreover, while no phase transformation was visible in the LS, phase transformation was visible in CS after every surface treatment, with the M phase content of the CS group showing a significant reduction after polishing (P < .001). CONCLUSION. Within the limits of this study, clinically acceptable level of surface finishing of (Y, Nb)-TZP can be achieved after conventional zirconia polishing sequence.

• The Journal of Korean Academy of Prosthodontics
• /
• v.43 no.5
• /
• pp.599-610
• /
• 2005

Purpose: The success of the bonding between electroformed gold and ceramic is dependent on the surface treatment of the pure gold coping. The purpose of this study was to evaluate the bonding strength between the electroformed gold and ceramic with varying surface treatment. Materials and methods: A total of 32 disks,8 were using conventional ceramometal alloy, 24 were using electroforming technique as recommended by manufacturer, were prepared. 24 electroformed disks were divided 3 groups according to surface treatment, i.e. 50 microns aluminium oxide sandblasting(GES-Sand), gold bonder treatment(GES-Bond) and $Rocatec^{TM}$ system(GES-Rocatec). For control group of conventional alloy 50 microns aluminium oxide treatment was done(V-Supragold). Energy dispersive x-ray analysis and scanning electron microscope image were observed. Using universal testing machine, shear bond strength and bonding failure mode at metal-porcelain interface were measured. Results and Conclusion: The following conclusions were drawn: 1. In the energy dispersive x-ray analysis, the Au was main component in electroformed gold(99.9wt%). After surface treatment, a little amount of $Al_2O_3(2.4wt%)$ were found in GES-Sand, and $SiO_2(4wt%)$ in GES-Bond. In GES-Rocatec, however, a large amount of $SiO_2(17.4wt%)$ were found. 2. In the scanning electron microscopy, similar pattern of surface irregu larities were observed in V-Supragold and GES-Sand. In GES-Bond, surface irregularities were increased and globular ceramic particles were observed. In GES-Rocatec, a large amount of silica particles attached to metal surface with increased surface irregularities were observed. 3. The mean shear bond strength values(MPa) in order were $22.9{\pm}3.7(V-Supragold),\;22.1{\pm}3.8(GES-Bond),\;20.1{\pm}2.8(GES-Rocatec)\;and\;13.0{\pm}1.4(GES-Sand)$. There was no significant difference between V-Supragold, GES-Bond, and GES-Rocatec. (P>0.05) 4. Most bonding failures modes were adhesive type in GES-Sand. However, in V-Supragold, GES-Bond and GES-Rocatec, cohesive and combination failures were commonly observed. From the result, with proper surface treatment method electroformed gold may have enough strength compare to conventional ceramometal alloy.

• Elastomers and Composites
• /
• v.37 no.1
• /
• pp.49-56
• /
• 2002

Polypropylene is oxidized with UV/ozone as a function of UV treatment time and ozone flow rate and its surface characteristics are investigated using contart angle measurements and XPS. The aging behavior of oxidized surface is investigated under air, water and ethylene glycol as the aging media. Adhesion strength is also investigated using a lap shear test. Polar surface energy increases with increasing UV/ozone treatment time as well as ozone flow rate. No polar surface energy change is observed under water aging, while under air aging it decreases significantly within 2-3 days and reaches the close value as that of the untreated PP. Adhesion strength increases with increasing UV/ozone treatment time as well as ozone flow rate.

• The Journal of Advanced Prosthodontics
• /
• v.6 no.6
• /
• pp.462-467
• /
• 2014

PURPOSE. This study investigated the influence of surface conditioning procedures and repeated firings on monoclinic content and strength of zirconia before cementation. MATERIALS AND METHODS. Sintered bar-shaped zirconia specimens were subjected to no surface treatment (control), air abrasion, or grinding (n=21). Their roughness was evaluated using a profilometer, and microscope analysis was performed on one specimen of each group. Then, 2 or 10 repeated firings (n=10) were executed, the monoclinic content of specimens was analyzed by X-ray diffraction, and a three-point flexural strength test was performed. Surface roughness values were compared using one-way analysis of variance (ANOVA) and Tukey honestly significant difference (HSD) tests, the monoclinic content values were tested using Kruskal-Wallis and Mann-Whitney U tests, and the flexural strength values were tested using two-way ANOVA and Tukey HSD tests (P=.05). Spearman's correlation test was performed to define relationships among measured parameters. RESULTS. Surface-treated specimens were rougher than untreated specimens and had a higher monoclinic content (P<.005), and the relationship between roughness and monoclinic content was significant (P<.000). Neither surface treatment nor firing significantly affected the flexural strength, but Weibull analysis showed that for the air-abraded samples the characteristic strength was significantly lower after the $10^{th}$ firing than after the $2^{nd}$ firing. CONCLUSION. After firing, a negligible amount of monoclinic content remained on the zirconia surfaces, and rougher surfaces had higher monoclinic contents than untreated surfaces. Multiple firings could be performed if necessary, but the fracture probability could increase after multiple firings for rougher surfaces.

• Asian Journal of Atmospheric Environment
• /
• v.7 no.1
• /
• pp.1-7
• /
• 2013

To establish the method for investigating the behavior of aerosol particles deposited on the leaf surface against fog water under natural conditions, scanning electron microscopy with energy-dispersive X-ray (SEM-EDX) analysis and wash water analysis by ion chromatography after the washing treatment were performed using leaves of white birch collected from low part of the tree crown and the top of the tree in Sapporo City, Hokkaido, northern Japan. Each of collected leaves was divided into two parts according to the treatment performed: leaf surface (adaxial side) was 1) untreated, and 2) washed with deionized water with a pipette. In untreated samples, many particles of various shapes, including soil particles and organic debris, were deposited on the surface. Particles containing S were found on the surface of samples collected from only low part of the tree crown. After the washing treatment, SEM-EDX analysis revealed that soil particles and particles containing S had been washed off with water, although some particles such as soil particles and organic debris still remained on the leaf surface. The major anion such as $SO{_4}^{2-}$ was detected in wash water of all samples, although the peak of S in X-ray spectra was not detected from samples collected at top of the tree. The combination of SEM-EDX analysis with wash water analysis indicated that $SO{_4}^{2-}$ was deposited on the leaf surface in dissolved state and/or in state of submicron particles. These results suggested that fog water could remove soil particles and particles containing S and $SO{_4}^{2-}$ from the leaf surfaces, but not all particles. There was no difference in sampling position in the tree crown. Our study suggested that combination with SEM-EDX analysis and wash water analysis would be effective for investigation of the behavior of particles on the leaf surface against fog water.

• Proceedings of the IEEK Conference
• /
• 2000.06b
• /
• pp.115-118
• /
• 2000

Uncooled pyroelectric infrared detectors based on BST(B $a_{-x}$S $r_{x}$Ti $O_3$) thin films have been fabricated by RF magnetron sputtering and surface Micromachining technology. The detectors form BST thin film ferroelectric capacitors grown by RF magnetron sputtering on N/O/N(S $i_3$ $N_4$/ $SiO_2$/S $i_3$ $N_4$) membrane. The sputtered BST thin film exhibits highly c-axis oriented crystal structure that no poling treatment for sensing applications is required. This is an essential factor to increase the yield for realization of an infrared image sensor. surface-Micromachining technology is used to lower the thermal mass of the detector by giving maximum sensor efficiency Gold-black is evaporated on top of the sensing elements used the thermal evaporator. fabricated uncooled pyroelectric infrared detectors is highly output voltage at the low temperature(1$^{\circ}C$).).).

• Proceedings of the KWS Conference
• /
• 2006.05a
• /
• pp.13-15
• /
• 2006

The effects of plasma treatment on the surfaces of the FR-4 (Flame Resistant-4) and copper substrates are investigated in terms of X-ray photoelectron spectroscopy (XPS), contact angle, and atomic force microscopy (AFM). The adhesion strengths of the underfills/FR-4 substrate and underfills/copper substrate are also studied. As experimental results, the plasma treatments of FR-4 and copper substrate surfaces yield several oxygen complexes in hydrophilic surfaces, which can play an important role in increasing the surface polarity, wettability, and adhesion characteristics of the underfills/substrates.

• Proceedings of the KIEE Conference
• /
• 2000.07c
• /
• pp.1748-1750
• /
• 2000

There are currently considerable interests in the applications of conjugated polymers, oligomers. and small molecules for thin-film electronic devices. Organic materials have potential advantages to be utilized as semiconductors in field-effect transistors and light-emitting diodes. In this study we fabricated the devices based on pentacene as active layer. Octadecyltrichlorosilane (OTS) is used as buffer layer between $SiO_2$ and pentacene. Atomic force microscopy (AFM), X-ray diffraction (XRD), and electrical conductivity were used with OTS on $SiO_2$ 10nm which the pentacene layer was thermally evaporated in vacuum at a pressure of about $2.0\times10^{-6}$ Torr. In the result of AFM, the grain length is grown by using OTS for surface treatment. Electrical conductivity is changed from $3.19{\times}10^{-6}$ S/cm to $2.12{\times}10^{-7}$ S/cm. We observed that electrical conductivity is also increased by surface treatment. According to these results, the surface treated devices exhibited the increase to compared no treatment.

• The Journal of Korean Academy of Prosthodontics
• /
• v.54 no.3
• /
• pp.218-225
• /
• 2016

Purpose: The purpose of this study was to evaluate the push-out bond strength of glass-fiber post cemented with different adhesive systems and surface treatments. Materials and methods: 160 tooth samples made from 48 human maxillary single-rooted teeth with similar root length were divided into 4 groups according to the adhesive system (no adhesive, Adper Single Bond 2, Clearfil SE Bond, Clearfil S3). Each group had 4 subgroups according to the post surface treatment methods (no treatment, sandblast, silane, sandblast and silane). Posts (Parapost Fiber White) were cemented with Rely X Unicem. The teeth were sectioned perpendicular to their long axis into 1-mm thick sections. The push-out tests was performed at a speed of 0.5 mm/min. The results were evaluated by 2-way ANOVA, 1-way ANOVA and multiple comparison procedures (Tukey test) (${\alpha}=0.05$). Results: Tukey test showed that the adhesive system significantly influenced the push-out strength. The Clearfil SE Bond group showed the highest value. Post surface treatments showed no significant effect. Conclusion: Bond strength of glass-fiber post cemented with self-adhesive resin cement using Clearfil SE Bond showed significantly higher values compared to other adhesive systems.

• The Journal of Advanced Prosthodontics
• /
• v.16 no.3
• /
• pp.189-199
• /
• 2024

PURPOSE. This study was conducted to evaluate the effects of plasma treatment of sandblasted and acid-etched (SLA) titanium implants on surface cleansing and osseointegration in a beagle model. MATERIALS AND METHODS. For morphological analysis and XPS analysis, scanning electron microscope and x-ray photoelectron spectroscopy were used to analyze the surface topography and chemical compositions of implant before and after plasma treatment. For this animal experiment, twelve SLA titanium implants were divided into two groups: a control group (untreated implants) and a plasma group (implants treated with plasma). Each group was randomly located in the mandibular bone of the beagle dog (n = 6). After 8 weeks, the beagle dogs were sacrificed, and volumetric analysis and histometric analysis were performed within the region of interest. RESULTS. In morphological analysis, plasma treatment did not alter the implant surface topography or cause any physical damage. In XPS analysis, the atomic percentage of carbon at the inspection point before the plasma treatment was 34.09%. After the plasma treatment, it was reduced to 18.74%, indicating a 45% reduction in carbon. In volumetric analysis and histometric analysis, the plasma group exhibited relatively higher mean values for new bone volume (NBV), bone to implant contact (BIC), and inter-thread bone density (ITBD) compared to the control group. However, there was no significant difference between the two groups (P > .05). CONCLUSION. Within the limits of this study, plasma treatment effectively eliminated hydrocarbons without changing the implant surface.