• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.11a
• /
• pp.245-246
• /
• 2006

A propyl alcohol based sol-gel method was used as to replace the 2-methoxyethanol with 1,1,1 tris (hydroxymethyl) ethane for preparation of pzt piezoelectric ceramic. The powder obtained by this sol-gel process were calcined at $900^{\circ}C$ and followed by the sintering at $1100^{\circ}C$ for ca2 hrs as to reach a pyrochlore-free crystal phase. The characterization of synthesized material was carried out by the XRD analysis and the surface morphology were determined by high resolution scanning electronmicroscopy. Further, the prepared small sized pzt thin powders are likely to be used m various applications.

• Journal of the Korean Ceramic Society
• /
• v.44 no.6 s.301
• /
• pp.313-318
• /
• 2007

ITO (Indium-tin oxide) thin films have been prepared by a sol-gel spinning coating method and fired and annealed in the temperature range of $450-600^{\circ}C$. The XRD patterns of the films indicated the main peak of (222) plane and showed higher crystallinity with increasing an annealing temperature. The surface of the ITO thin films were treated with 0.1 N HCl 20% solution at room temperature. The effects of surface treatment on electrical properties and surface morphologies of the ITO films were investigated with the results of sheet resistance and FE-SEM, AFM images. The samples, subsequently treated with acidic solution for 40 sec showed the sheet resistance of $0.982\;k{\Omega}/square$. The surface treatment using acidic solution diminished the RMS (root mean square) value and the residual carbon content of the ITO films. It seemed that the acid-cleaning of the ITO thin films lead to the decrease of surface roughness and sheet resistance.

• Journal of Environmental Science International
• /
• v.11 no.6
• /
• pp.597-603
• /
• 2002

Photocatalytic degradation of phenol was carried out with UV-illuminated TiO$_2$-SiO$_2$ in aqueous suspension. TiO$_2$-SiO$_2$ catalysts were prepared by sol-gel method from the titanium isopropoxide and tetraethylorthosilicate at different Ti/Si ratio and some commercial TiO$_2$ catalysts were used as purchased. All catalysts were characterized by X-ray Diffraction(XRD) and BET surface area analyzer. The effect of reaction conditions, such as initial concentration of phenol, reaction temperature and catalyst weight on the photocatalytic activity was studied. In addition, TiO$_2$-SiO$_2$(49: 1) prepared by sol-gel method showed higher activity than commercial TiO$_2$catalysts on the photocatalytic degradation of phenol. The addition of SiO$_2$ into TiO$_2$hepled to increase the thermal stability of titania which suppressed the formation of anatase into rutile. The photocatalytic degradation of phenol showed pseudo-1st order reaction and the degradation rate increases with decreasing initial phenol concentration.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.5 no.2
• /
• pp.142-151
• /
• 1995

Complex alkoxides were synthesized using metal alkoxide method and were then hydrolyzed to prepare the precursors using sol - gel method. Then, the precursors were calcined in order to make barium hexaaluminate. Factors affecting the material properties of the barium hexaaluminate precursors were studied and they are the kinds and amount of alcohols, and reaction time. In addition, in the course of hydrolysis, the effects of the amount of water, reaction temperature and aging time were also studied in terms of the specific surface area and average particle size of the barium hexaaluminates.

• Journal of the Korean Ceramic Society
• /
• v.34 no.7
• /
• pp.774-780
• /
• 1997

Porous low reflective coating films of SiO2.ZrO2 system were prepared from the mixed alkoxide solutions of Zr(O-nC3H7)4 and partially prehydrolyzed TEOS by the sol-gel method using the dip-coating technique. In the case of 90SiO2.10ZrO2 porous coating films with HCl and H2O content was 0.3 mole and 4 mole, 378 m2/g of the specific surface area, 0.254 cm3/g of total pore volume, 30-50$\AA$ of average pore diameter. The transmittance of 90SiO2.10ZrO2 porous coated films was 95.38% at the wavelength of 550 nm, compared with the parent glass, the transmittance was increased with 4.38%.

• Journal of Ceramic Processing Research
• /
• v.13 no.spc2
• /
• pp.373-376
• /
• 2012

Thin films of Ag-SiO2-TiO2 composite oxides with SiO2/TiO2 of 20/80 molar compositions were prepared by the sol-gel method, using tetraethylorthosilicate (TEOS) and titanium isopropoxide (TIP) as precursors. Ag-SiO2-TiO2 films coated on commercial glass substrates have successfully been synthesized using sol-gel method. The Ag-SiO2-TiO2 film with 0.5% Ag-added concentration and 20 mol% SiO2-mixture gives optimal results on crystalline structure, optical property, surface area, and photochromic property. Absorption near the wavelength of the incident light decreased gradually. The reversibility of the two-photon writing process in Ag-SiO2-TiO2 film is clearly seen.

• Journal of the Korean Ceramic Society
• /
• v.33 no.7
• /
• pp.793-801
• /
• 1996

The effect of catalysts which was catalyzed by acid($HNO_3$) and base ($NH_4OH$) or not on the surface microst-ructures and consequent dielectric characteristics of the $PbTiO_3$ thin films prepared by sol-gel method were investigated. The result indicated that bse catalyst promoted the phase transformation of perovskite phase while acid catalyst was found to produce most uniform surface microstructure and improved dielectric properties However degradation of properties due to secondary phase formation and non-uniform microstructure at high annealing temperature (>75$0^{\circ}C$) by rapid diffusion of lead was unavoidable in any case as long as $Si_{(100)}$ \ $SiO_2$ \Pt substrate used.

• The Journal of Korea Institute of Information, Electronics, and Communication Technology
• /
• v.1 no.2
• /
• pp.27-32
• /
• 2008

A current research basically diverted towards an increase in the operational output with the minimization of the materials used, which ultimately scaled down the dimensions of ceramic electronic components. In this direction the nano-technology pave the revolutionary changes in particular the electronic industries. The applications of nano-sized particles or nano-sized materials are hence, playing a significant role for various purposes. The PZT(lead, zirconium, titanium) based ceramics which, are reported to be ferroelectric materials have their important applications in the areas of surface acoustic waves (SAW), filters, infrared detectors, actuators, ferroelectric random access memory, speakers, electronic switches etc. Moreover, these PZT materials possess the large electro mechanical coupling factor, large spontaneous polarization, low dielectric loss and low internal stress etc. Hence, keeping in view the unique properties of PZT piezoelectric ceramics we also tried to synthesize indigenously the small sized PZT ceramic powder in the laboratory by using the modified sol-gel approach. In this paper, propyl alcohol based sol-gel method was used for preparation of PZT piezoelectric ceramic. The powder obtained by this sol-gel process was calcined and sintering to reach a pyrochlore-free crystal phase. The characterization of synthesized material was carried out by the XRD analysis and the surface morphology was determined by high resolution scanning electron microscopy.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.15 no.6
• /
• pp.504-510
• /
• 2002

Recently, thin film capacitors of high dielectric constant and low leakage current are applied to integrated devices. In this study, (Ba, Sr)$TiO_3$ (BST) thin films for low cost were prepared by Sol-Gel method. BST solution was spin-coated on Pt/$SiO_2$/Si substrate at 4,000 rpm for 10 seconds. Coating process was repeated 3 times and then sintered at $700^{\circ}C$ for 30 minutes. Structural and electrical characteristics of each specimen were analyzed by TG-DTA, SEM, fractal phenomenon, voltage-current and dielectric factor. Thickness of BST ceramics thin films are about 2,600~2,800 ${\AA}$ at depositing 3 times. Dielectric constant of thin films was decreased in 1 kHz~1 MHz. Dielectric constant and loss to frequency were 250 and 0.02 in $(Ba_{0.7}Sr_{0.3})TiO_3$ (BST3). Leakage current of BST3 was $10^{-9}\sim10^{-11}$/ A under 3 V.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.11 no.9
• /
• pp.711-717
• /
• 1998

BST(70/30) and BST(50/50) thin films were prepared by Sol-Gel method and studied about the microstructural and dielectric properties with Pt and ITO bottom electrodes. The stock solution was synthesized and spin coated on the Pt/Ti$SiO_2$/Si and Indium Tin Oxide(ITO)/ glass substrate. the coated films were dries at 350$^{\circ}C$ for 10 minutes and annealed at $750^{\circ}C$ for 1 hour for the crystallization. The thin films coated on ITO substrate were crystallized easily and the packing density and roughness of surface were better that those of films coated on Pt substrates. In the BST(50/50) composition the structural properties were similar to the BST(70/30) composition and grain size were decreased with increasing the contents of Sr. The dielectric constant was higher in the BST(50/50) composition compared with the BST(70/30) composition. Using the ITO substrate, the dielectric constant was higher than the Pt substrate while the dielectric loss was showed a reverse trend. The dielectric constant with and increase of temperature was decreased slowly.