• Korean Journal of Materials Research
• /
• v.29 no.2
• /
• pp.92-96
• /
• 2019

Transition metal oxide is widely used as a water electrolysis catalyst to substitute for a noble metal catalyst such as $IrO_2$ and $RuO_2$. In this study, the sol-gel method is used to synthesize the $Cu_xCo_{3-x}O_4$ catalyst for the oxygen evolution reaction (OER),. The CuxCo3-xO4 is synthesized at various calcination temperatures from $250^{\circ}C$ to $400^{\circ}C$ for 4 h. The $Cu_xCo_{3-x}O_4$ synthesized at $300^{\circ}C$ has a perfect spinel structure without residues of the precursor and secondary phases, such as CuO. The particle size of $Cu_xCo_{3-x}O_4$ increases with an increase in calcination temperature. Amongst all the samples studied, $Cu_xCo_{3-x}O_4$, which is synthesized at 300?, has the highest activity for the OER. Its onset potential for the OER is 370 mV and the overpotential at $10mA/cm^2$ is 438 mV. The tafel slope of $Cu_xCo_{3-x}O_4$ synthesized at $300^{\circ}C$ has a low value of 58 mV/dec. These results are mainly explained by the increase in the available active surface area of the $Cu_xCo_{3-x}O_4$ catalyst.

• Proceedings of the Korea Association of Crystal Growth Conference
• /
• 1997.10a
• /
• pp.13-19
• /
• 1997

From the formation of the monodispersed silica particle which is a valuable for the industry by Sol-Gel process, the effects of the parameters participated in the process, the growth mechanism and the characteristics of silica particles for each rection conditions are investigated. To investigate about the formation of final silica particles, the suspension which performs the polymerization is reacted with molybdic acid, and the evolutions of TEOS and silica particle size are investigated in the reaction time ？ 새 the characteristics of molybdic acid with the suspension. From the results, a constant number of silica particle is formed at early reaction stage. Silica particles grow through the aggregation of smaller particles and nucleation is rate-limiting step for the growth of particles. In the conditions of this study, spherical silica particles are formed, [NH$_3$] and [$H_2O$] concentration increase the particle size but particle size decrease with [$H_2O$] concentration which is a certain above region. Average particle sizes are 187.4~483.3 nm and standard deviations in the average particle size are 1.7~2.9% with each experimental condition. From the BET results, specific surface area is 5.5~23.4 $m^2$/g and these values decrease with increase size. The average pore size is 50~70$\AA$.

• Journal of the Korean Ceramic Society
• /
• v.51 no.5
• /
• pp.477-480
• /
• 2014

An $Al_2O_3$-CuO-ZnO (ACZ) precursor powder was synthesized by a facial sol-gel process using a nonionic surfactant span 80 as the chelating agent to improve the surface area and morphology. When creating a hydrogen membrane, several kinds of properties are required, such as easy dissociation of hydrogen molecules, fast hydrogen diffusion, high hydrogen solubility, and resistance to hydrogen embrittlement. ACZ-Ni composite membranes (cermet) were prepared with this precursor and pure Ni powder via the hot press sintering (HPS) method. The ACZ powder was characterized by XRD, BET, and FE-SEM. Hydrogen permeation experiments were performed by Sievert's type of hydrogen permeation membrane equipment. The hydrogen permeability of ACZ/Ni 10 wt% and ACZ/Ni 20 wt% was obtained as 7.2 and $10molm^{-2}s^{-1}$ at RT, respectively. These values of the corresponding membranes were slightly increased with increasing pressures.

• Journal of the Microelectronics and Packaging Society
• /
• v.22 no.4
• /
• pp.77-82
• /
• 2015

To increase the performance of solid oxide fuel cell operating at intermediate temperature ($600^{\circ}C{\sim}800^{\circ}C$), $Sm_{0.2}Ce_{0.8}O_2$ (SDC) thin layer was applied to the $La_{0.8}Sr_{0.2}Mn_{0.8}Cu_{0.2}O_3$ (LSMCu) cathode by sol-gel coating method. The SDC was employed as a diffusion barrier layer on the yttria-stabilized zirconia(YSZ) to prevent the interlayer by-product formation of $SrZrO_3$ or $La_2Zr_2O_7$. The by-products were hardly formed at the electrolyte-cathode interlayer resulting to reduce the cathode polarization resistance. Moreover, SDC thin film was coated on the cathode pore wall surface to extend the triple phase boundary (TPB) area.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.05b
• /
• pp.16-19
• /
• 2002

(Ba,Sr)TiO3(BST) thin film is an attractive material for the application in high-density dynamic random access memories (DRAMs) because of the high relative dielectric constant and small variation in dielectric properties with frequency. In this study, (Ba0.6,Sr0.4)TiO3 thin films on Pt/Ti/SiO2/Si substrates were deposited by a sol-gel method and the CF4/Ar inductively coupled plasma (ICP) etching behavior of BST thin films had been investigatedby varying the process parameters such as chamber pressure, ICP power, and substrate bias voltage. To analysis the composition of surface residue following etching BST films etched with different Ar/CF4 gas mixing ratio were investigated using x-ray photoelectron spectroscopy (XPS) and secondary ion mass spectrometer (SIMS).

• Bulletin of the Korean Chemical Society
• /
• v.32 no.6
• /
• pp.1865-1872
• /
• 2011

This study investigates the sensitivity of a gas sensor to volatile organic compounds (VOCs) at various operating temperatures and catalysts. Nano-sized powdered $WO_3$ prepared by sol-gel and chemical precipitation methods was mixed with various metal oxides. Next, transition metals (Pt, Ru, Pd, and In) were doped on the surface of the mixture. Metal-$WO_3$ thick films were prepared using the screen-printing method. The physical and chemical properties of the films were studied by SEM/EDS, XRD, and BET techniques. The measured sensitivity to VOCs is defined as the ratio ($R_a/R_g$) of resistance ($R_{air}$) of $WO_3$ film in the air to resistance ($R_{gas}$) of $WO_3$ film in a VOCs test gas. The sensitivity and selectivity of the films were tested with various VOCs such as acetaldehyde, formaldehyde, methyl alcohol, and BTEX. The thick $WO_3$ film containing 1 wt % of Ru and 5 wt % of $SnO_2$ showed the best sensitivity and selectivity to acetaldehyde gas at an operating temperature of 300 $^{\circ}C$.

• Journal of the Korean Chemical Society
• /
• v.62 no.1
• /
• pp.7-13
• /
• 2018

The potential of zinc fluorides with different molar ratios of Zn/F was applied as a solid catalyst in the simultaneous reaction of transesterification and esterification of crude palm oil (CPO) for biodiesel production. These materials were prepared by the fluorolytic sol-gel technique with different fluorine contents. The resulting samples were investigated using elemental analysis, XRD, FT-IR, TG/DTG, $N_2$ physisorption measurements and SEM. The results exhibited that the presence of fluorine strongly affected the catalytic activity in the biodiesel production. The catalysts with smaller fluorine contents (${\leq}1$) showed the best performance in all of the observed samples, yields from 92.94 to 89.95, 87.38 and 85.21% with increasing fluorine contents, respectively. The yield toward the formation of biodiesel depended on the phase and particle sizes of catalysts, but it was not influenced by surface area, pore size, and volume of the samples. The recovered catalyst showed a gradual decrease in activity over three cycles of same reactions.

• Carbon letters
• /
• v.13 no.2
• /
• pp.99-108
• /
• 2012

The sol-gel technique has been studied to fabricate a homogeneous Fe-Mo/MgO catalyst. Ambient effects (air, Ar, and $H_2$) on thermal decomposition of the citrate precursor have been systematically investigated to fabricate an Fe-Mo/MgO catalyst. Severe agglomeration of metal catalyst was observed under thermal decomposition of citrate precursor in air atmosphere. Ar/$H_2$ atmosphere effectively restricted agglomeration of bimetallic catalyst and formation of highly-dispersed Fe-Mo/MgO catalyst with high specific surface-area due to the formation of Fe-Mo nanoclusters within MgO support. High-quality thin-multiwalled carbon nanotubes (t-MWCNTs) with uniform diameters were achieved on a large scale by catalytic decomposition of methane over Fe-Mo/MgO catalyst prepared under Ar-atmosphere. The produced t-MWCNTs had outer diameters in the range of 4-8 nm (average diameter ~6.6 nm) and wall numbers in the range of 4-7 graphenes. The as-synthesized t-MWCNTs showed product yields over 450% relative to the utilized Fe-Mo/MgO catalyst, and indicated a purity of about 85%.

• Journal of the Korean Chemical Society
• /
• v.37 no.1
• /
• pp.92-97
• /
• 1993

Sol-Gel Process is a new method of synthesis of high-quality of glass and glass-ceramics. Ferroeletric material, $BaTiO_3$ powder was made by reacting $Ba(OH)_2$ and $Ti[OCH(CH_3)_2]_4$ in alcohol. There was about 16.5% weight loss in thermogravimetric analysis. It was crystallized to tetragonal structure by heat treatment at $700^{\circ}C$ for 2 hours and had a specific surface area, 16.0 $m^2/g.$ Shrinkage curve by sintering was began around $1100^{\circ}C$ in dilatometer analysis.

• Korean Chemical Engineering Research
• /
• v.45 no.3
• /
• pp.209-214
• /
• 2007

Sr hexaaluminate($Sr_{1-x}La_xMnAl_{11}O_{19-\alpha}$) were prepared by sol-gel method of metal alkoxide with 1-butanol or ethylene glycol as a solvent. The physical properties of prepared hexaaluminates were examined by TG/DTA, XRD and $N_2$ adsorption. When ethylene glycol was used as a solvent, the decomposition reaction and dehydroxylation reaction was observed above $400^{\circ}C$ and the temperature of the formation of a crystal structure of hexaaluminate was also increased resulting in small specific surface area and low catalytic activity of methane compared to Sr-hexaaluminate with 1-butanol.