• Corrosion Science and Technology
• /
• v.6 no.4
• /
• pp.177-185
• /
• 2007

The purpose of this study is to evaluate freezing-thawing and surface scaling resistance in order to examine the frost durability of concrete in a chloride-inherent environment. The mixing design for this study is as follows: 3 water binder ratios of 0.37, 0.42, and 0.47; 2-ingredient type concrete (50% OPC concrete and 50% ground granulated blast-furnace slag), and 3-ingredient type concrete (50% OPC concrete, 15% fly ash, and 35% ground granulated blast-furnace slag). As found in this study, the decrease of durability was much more noticeable in combined deterioration through both salt damage and frost damage than in a single deterioration through either ofthese; when using blast-furnace slag in freezing-thawing seawater, the frost durability and surface deterioration resistance was evaluated as higher than when using OPC concrete. BF 50% concrete, especially, rather than BFS35%+FA15%, had a notable effect on resistance to chloride penetration and freezing/expansion. It has been confirmed that surface deterioration can be evaluated through a quantitative analysis of scaling, calculated from concrete's underwater weight and surface-dry weight as affected by the freezing-thawing of seawater.

• 한국방재학회:학술대회논문집
• /
• 2011.02a
• /
• pp.91-91
• /
• 2011

The quality of the surface layer in concrete structures plays an important role in the durability of the concrete. The concrete factory products are made as they improve the appearance of the surface and compressive strength in need. A common criterion to judge the quality of concrete products frequently seen in our daily life appears to be "beauty" in terms of consistent shaping. However, as for most concrete curb in such areas where a large amount of anti-freezing agents(NaCl) and ice and snow melting agents(CaCl2) are spread over roads to ensure road safety during the winter season, since deterioration advances from the surface, scaling is seen on the surface concrete due to deterioration which combined freezing damage and salt damage. Especially, In cold northern districts, the spreading amount of deicing salts increases by regulation of studded tire use, and the scaling of the concrete products, the various parts of concrete structures for roads is increasing in recent years. In this study, L-shape concrete curb were targeted, the permeable form method with the commercial permeable sheet was applied to it and the improvements of the quality were examined. By the permeable form method, surface layers got strengthened, which prevented permeation of the deterioration factor from the outside, and the scaling resistance of the upper surface where the permeable sheet was applied improved exceedingly. It will be expected by applying the permeable form method to various concrete products that frost resistance improves and scaling damage decreases.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2004.11a
• /
• pp.221-224
• /
• 2004

Several factors of concrete durability decline factor are acted as complex deterioration and is happened not that happen by simplicity deterioration. Specially, in case of sea construction, as complex salt damage, carbonation and freezing & thawing, concrete surface and pore structure is deteriorated. Therefore, analyzing concrete carbonation and pore structure after freezing and thawing test by fresh water and sea water in this research, we wish to study about acceleration of decline of durability and complex deterioration by concrete surface deterioration in sea environment.

• International Journal of Highway Engineering
• /
• v.19 no.2
• /
• pp.7-15
• /
• 2017

PURPOSES : Infiltration of moisture, polluted material, and deicer into concrete, accompanied by freeze and thaw can cause significant deterioration of concrete pavement. In order to protect concrete from deterioration, it is necessary to prevent the infiltration of these concrete external materials. The moisture-repellent agent, which is a surface treatment and maintenance material added to concrete structures to render them water resistant, has advantages such as prevention of water infiltration and security against air permeation. Nano-coat, which is referred to as silicon hydride, is typically used as a moisture-repellent agent. Therefore, in this study, an attempt is made to use penetration-type Nano-coat as an alternative in order to evaluate its applicability through environmental resistance tests. METHODS : This study aimed to evaluate the applicability of penetration-type Nano-coat, which can provide water repellency to concrete, in concrete pavements, through various environmental resistance tests such as freezing and thawing resistance, chloride ion penetration resistance, and surface scaling resistance tests. The applicability of penetration-type Nano-coat was demonstrated based on the specification of KS F 2711, KS F 2456, and ASTM C 672. RESULTS :In the case of penetration-type Nano-coat applied on sound concrete, an increase in concrete durability was demonstrated by the negligible chloride ion penetrability and the absence of scaling, as revealed by visual observation of the surface, after 50 cycles of scaling resistance test. In addition, test result of the application of penetration-type Nano-coat on deteriorated concrete established that concrete surface pretreated by grinding provided improved durability than non-treated concrete. CONCLUSIONS :This study indicates that penetration-type Nano-coat is applicable as an effective alternative, to increase the durability of concrete structures. In addition, it was known that pretreatment of deteriorated concrete surface, such as grinding, is required to improve the long-term performance of concrete pavement.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.5 no.1
• /
• pp.131-140
• /
• 2001

In general, the deterioration induced by the freezing and thawing cyclic in concrete structures often leads to the reduction in concrete durability by the cracking or surface spalling. If it can prediction of concrete deterioration subjected to cyclic freezing and thawing, we can rationally do the design of mix proportion in view of concrete durability and the maintenance management of concrete structures. Therefore in this study a prediction method of deterioration for concrete structures subjected to the irregular freezing and thawing is proposed from the results of accelerated laboratory freezing and thawing test using the constant temperature condition and the in-situ weathering data. Furthermore, to accurately predict the concrete deterioration, a method of modification for the effect of hydration increasing during rapid freezing and thawing test is investigated.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1991.10a
• /
• pp.158-161
• /
• 1991

By applying the newly developed techniques of polymer impregnated concrete (PIC) severely deteriorated and low quality concrete can be restored to an adequate structural material. Early deterioration of concrete causes severe problems for bridge deck concrete, pavement concrete for highways and airports, hydraulic structures and buiilding structures. Deterioration has its orgin in cracks on concrete surface, scaling of spalling due to freezing and thawing, neutralization of concrete, penetrations of water, salt, and calcium chloride. The objective of this study is to develope the new surface impregnants and strengthening techniques for them. It is found that the new impregnants and strengthening techniques developed in this study can retian the charecteristics of the existing concrete and decrease deterioration, and also increase durability, chemical resistance, strength, stiffness and ductility of the existing concrete.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.9 no.4
• /
• pp.177-186
• /
• 2005

The latest concrete structure has showed that the deterioration of durability has been increased by the damage from salt, carbonization, freezing & thawing and the others. Therefore, the measures for the concrete which has deteriorated durability have been taken. Among them, it has been often used that surface treatment which cuts off the deterioration factors of durability by protecting the surface of concrete. However, troubles such as fracture and rupture in the repair layer have been reported as time goes by due to the difference between the organic repair material like epoxy and concrete properties. Researchers have been developing the repair material which can cut off the deterioration factors of durability such as $CO_2$ gas, chloride ion and water by making the formation of concrete elaborate through the reaction with calcium ion when the surface improving agent is coated on the concrete. The main ingredient of that is inorganic substance which is the same as the concrete property. This study was evaluated the surface improving agent for permeability, watertightness, air-permeability, chemical resistance and elution resistance. As a result, it has been reported that the surface improving agent improves watertightness and air-permeability by penetration more than 10mm within concrete. Therefore, it is concluded that the surface improving agent developed in this research prevents deterioration of concrete durability when it is coated on the concrete structure.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2004.05a
• /
• pp.372-375
• /
• 2004

Scaling deterioration and resistance to freezing of port concrete structures due to the combined effects of chemical actions by containning chlorides and the freeze-thaw action is also a problem which has not yet been fundamentally solved. Furthermore, deterioration of concrete surface was considered as accelerate factor of concrete durability tended to decrease. Therefore, we considered the scaling measuring method and decreasing influence of durability of concrete according to kind of binders, such as OPC, Slag, Slag+Fa, due to freeze and thaw of concrete by containing chlorides. As a results of this study, it was effective method of scaling deterioration and resistance freewing of concrete, and confirmed the salt deterioration resistance effect to use slag binder against to containing chlorides.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2006.05b
• /
• pp.321-324
• /
• 2006

The latest concrete has showed that the deterioration of durability has been increased by the damage from salt, carbonation, freezing & thawing and the others. Therefore, it is needed to protect durability and performance according to the appropriate materials and methods in the concrete structures. In general, several types of polymer and silicate are used as protecting deterioration agents of concrete structures, but these agents have many problems because of low durability and properties. In this study, It developed the deterioration restraining agent using polycondensed silicate and monomer that can block a deterioration cause such as CO2 gas, salt and water from the outside and enhance waterproofing ability by reinforcing the concrete surface when applying it to concrete structures. Also, it evaluated improving concrete performance using a deterioration restraining agent.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1999.10a
• /
• pp.795-798
• /
• 1999

Deterioration induced by the freezing and thawing in concrete often leads to the reduction in concrete durability by the cracking or surface spalling. In this paper, the deterioration prediction model for concrete structures subjected to the irregular freeze-thaw was proposed from the results of accelerated laboratory test using the constant temperature condition and acceleration factor from the in-situ weather data.