• Current Optics and Photonics
• /
• v.5 no.5
• /
• pp.576-582
• /
• 2021

Dichroic beam-splitter (DBS) with polarization-maintaining took an important role in the free space quantum telecommunication tests on the Micius satellite of China. In this presentation, we designed and prepared a 50 layer polarization-maintaining DBS coating by a dual ion beam sputtering deposition (Dual-IBS) method. In order to solve a stress problem, an 18 layer special anti-reflection (AR) coating with similar physical thickness ratio was deposited on the backside. By stress compensation, the surface flatness RMS value of the DBS sample decreased from 0.341 λ (@632.8 nm) to 0.103 λ while beam splitting and polarization maintaining properties were almost kept unchanged. Further, we discussed the mechanism of film stress and stress compensation by equation deduction and found that total stress had a strong relationship with the total physical thickness and the ratio of layer materials.

• Journal of Korean Vacuum Science & Technology
• /
• v.3 no.1
• /
• pp.74-78
• /
• 1999

For a high efficient field emission display (FED), the specific vacuum conditions below 10-7 Torr should be required. However, because the FED has the geometrical restriction due to its micro size, the thin film getters can be proposed for chemical pumping as a way to reduce impurity gases in the panel. The thin film getters, developed by employing the coating of new materials such as NI or Pt on getter surface, can be used without any activation process and show the enhanced sorption characteristics. Especially, using the Zr (1${\mu}{\textrm}{m}$) thin film getters with the Pt surface layer, the significant gettering for various active gases could be achieved from 9$\times$10-5 Torr to 1$\times$10-6 Torr or below. this good sorption properties is mainly contributed to the surface coating layer which shows the catalytic effect for gas dissociation and protects the getter materials against oxidation.

• Korean Journal of Crystallography
• /
• v.8 no.2
• /
• pp.154-159
• /
• 1997

Hydorthemal coating technique has been sucessfully applied to improve oxidation resistance of graphite by forming rutile-TiO2 layer. Hydrothermal treatment of graphite in 0.2M TiCl4 aquous solution at 35℃ resulted in improved water wettability due to the formation of surface-modifying TiO2. The amount of TiO2 increased with temperature. In the presence of surface TiO2 layer, weight loss was reduced by 30%, while the initiation temperature of oxidation was lowered by 30℃.

• Journal of the Korean Electrochemical Society
• /
• v.14 no.2
• /
• pp.77-82
• /
• 2011

The surface of $Li[Ni_{0.35}Co_{0.3}Mn_{0.35}]O_2$ cathode was modified by $[Li,La]TiO_3$ coating using pH controlled coating solution. At low pH values (acidic solution), cathode powders, which is oxides, have a positive surface charge, whereas, they have a negative surface charge at high pH values. As a result, their charge could affect the formation of the coating layer on the surface of cathode powder. To determine the optimal pH value, the surface coating of the pristine powder was carried out at various pH values of the coating solution. The surface morphology of coated samples was characterization by SEM and TEM analyses. Impedance analysis and cyclic voltammogram presented that internal resistance of the cell was dependent upon the pH of coating solution.

• Journal of the Korean institute of surface engineering
• /
• v.40 no.4
• /
• pp.170-174
• /
• 2007

High Velocity Oxygen Fuel (HVOF) thermal spray coating of nano size WC-Co powder (nWC-Co) has been studied as one of the most promising candidate for the possible replacement of the traditional hard plating in some area which causes environmental and health problems. nWC-Co powder was coated on Inconel 718 substrates by HVOF technique. The optimal coating process obtained from the best surface properties such as hardness and porosity is the process of oxygen flow rate (FR) 38 FMR, hydrogen FR 57 FMR and feed rate 35 g/min at spray distance 6 inch for both surface temperature $25^{\circ}C\;and\;500^{\circ}C$. In coating process a small portion of hard WC decomposes to less hard $W_2C$, W and C at the temperature higher than its decomposition temperature $1,250^{\circ}C$ resulting in hardness decrease and porosity increase. Friction coefficient increases with increasing coating surface temperature from 0.55-0.64 at $25^{\circ}C$ to 0.65-0.76 at $500^{\circ}C$ due to the increase of adhesion between coating and counter sliding surface. Hardness of nWC-Co is higher or comparable to those of other hard coatings, such as $Al_2O_3,\;Cr,\;Cr_2O_3$ and HVOF Tribaloy 400 (T400). This shows that nWC-Co is recommendable for durability improvement coating on machine components such as high speed spindle.

• Proceedings of the Korea Association of Crystal Growth Conference
• /
• 1997.06a
• /
• pp.19-22
• /
• 1997

The surface modificaion of alumina by $Al_2$O$_3$/SiC nanocomposite coating was studied in terms of processing and microstructure. A powder slurry of 5 vol% SiC composition was dipcoated onto presintered alumina bodies and pressurelessly sintered at 1$700^{\circ}C$ for 2 h in $N_2$. The used of organic binder and plasticizer in the slurry preparation, and the control of the density of presintered alumina body were found to be necessary to avoid cracking and warping during processing. The nanocomposite coating well bonded to the alumina body with thickness about 110 ${\mu}{\textrm}{m}$. The average grain size of coating (2 ${\mu}{\textrm}{m}$) was much finer than that of alumina body (13 ${\mu}{\textrm}{m}$). Fracture surface observations revealed mostly transgranular fracture for the coating, whereas intergranular fracture for the alumina body. Some pores (about 6%) were observed in the coating layer, although the alumina body showed fully dense microstructure.

• Journal of the Korean institute of surface engineering
• /
• v.35 no.1
• /
• pp.53-63
• /
• 2002

Ni coating was carried out by pulse plating at room temperature. So, experimental conditions for Ni-coating were based on Watt's bath, and new additives(propionic acid) were introduced in the Watt's bath electrolyte as $H_3$$BO_3$ alternatives. By adding propionic acid, coating layer demonstrated a good adhesion and uniformity without special pre-treatment of the 316L stainless steel at room temperature. With a decrease of amount of propionic acid and applied average current density, cathode current efficiency increased. Also, edge effect was decreased with decreasing a peak current and increasing a pulse frequency in the same bath condition. It was found that the optimum condition for Ni coating was a current density of 10~20mA/$\textrm{cm}^2$ at below 500 mA peak current in the $5m\ell/\ell$ propionic acid solution.

• Journal of the Korean institute of surface engineering
• /
• v.27 no.1
• /
• pp.29-35
• /
• 1994

The effects of coating of 3$\mu\textrm{m}$ thickness on the mechanical property of alumina after heat treatment at 100$0^{\circ}C$ for 30minutes under $10^{-6}$torr vacuum was quantified in terms of modulus of rupture(MOR) using Weibull plot. While the copper coating did not change MOR of alumina due to the nonwetting behavior of Cu on $Al_2O_3$, the reactive titanium metal coating caused a noticeable 29% reduction in averaged MOr strength. This was related with the combined effects of microcracks in coating formed during heat treatment and good bonding character between Ti and $Al_2O_3$. The effect of cosputtering of Ti and Cu, bilayer coatings of Cu/Ti and Ti/Cu were also investigated. It was found that Ti, cosputtered, Cu/ti and Ti/Cu coatings reduced MOR strength of alumina in the order listed. This was correlated with the amount of Ti at coating/alumina inter-face associated with a coated layer or segregation of Ti during heat treatment.

• Journal of the Korean institute of surface engineering
• /
• v.32 no.1
• /
• pp.31-42
• /
• 1999

The effect was investigated that aluminium in the zinc bath has on the coating adhesion of Hot-rolled Galvanized Iron(HGI) manufactured without pickling process. It is thought that the coating adhesion of HGI manufactured without pickling process is good due to the fact that increasing aluminium content in the zinc bath makes zinc and aluminium diffuse to the cracks or pores in the scale formed through the reduction heat treatment, and Fe-Zn-Al compound with good ductility is formed in the scale layer and plays a role of anchor between zinc coating and substrate. It is possible that HGI with the good coating adhesion was produced without pickling treatment in the zinc bath with more that 3wt% of Al content even at the $550^{\circ}C$ of conventional reduction heating temperature. In creasing the temperature of heating section and aluminium content in the zinc bath prevents the Zn-Fe alloy. The corrosion resistance of HGI manufactured without pickling process is excellent because of the mixed reaction of zinc sacrifice and aluminium passivity film.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2008.11a
• /
• pp.55-55
• /
• 2008

반사방지막은 태양전지 셀 제작에 적용되고 있으며, 효율을 향상시키기 위하여 $SiO_2$, $TiO_2$를 이용한 Multi-layer 반사방지막을 적용하였다. Multi-layer의 효과가 기존의 SiN 반사방지막에 비하여 광수집의 향상에 영향을 주었음을 알 수 있었다.