• 한국주조공학회지
• /
• 제18권6호
• /
• pp.593-603
• /
• 1998

Commercial ductile iron was coated with titanium and aluminum powders by low pressure plasma spraying and then irradiated with a $CO_2$ laser to produce anti-corrosive TiC composite layer. TiC carbides were precipitated homogeneously in a laser alloyed layer by in-situ reaction between carbon existed in the base metal and titanium with thermal sprayed coating. The formation of gas pores and brittle limited mixing zone with ledeburite microstructure in TiC composite layer were surpressed by the complementary alloying of aluminum. The hardness of TiC composite layer obtained by addition of titanium and aluminum was between 600 and 660 Hv, which was three times as high as the hardness of ferritic ductile iron. From the results of isothermal oxidation at 1123k for 24 hours in air, high temperature oxidation resistance of the TiC composite layer with aluminum was improved and doubled when compared with the TiC composite layer without aluminum.

• 한국수소및신에너지학회논문집
• /
• 제9권2호
• /
• pp.47-52
• /
• 1998

A mixture with a composition $Mg_2Ni$ is mechanically alloyed. Its hydriding and dehydriding properties are compared with those of the intermetallic compound $Mg_2Ni$ prepared by partial melting and sintering. The principal effects of mechanical alloying in a planetary mill and hydriding-dehydriding cycling are considered the enlargement in the specific surface area and the augmentation in the density of defects.

• Progress in Superconductivity
• /
• 제1권1호
• /
• pp.51-55
• /
• 1999

A Ni/Ag/Stainless steel 310S(SS310S) multi-layer sheet has been fabricated by a combination of vacuum brazing, cold rolling and texture annealing processes. After heat-treating the thin Ni/Ag/SS310S multi-layer sheet at $900^{\circ}C$ for 2h, development of (100)<001>cube texture on Ni surface was revealed by (111) pole figure. Quantitative chemical analysis was made by EPMA for the cross-section of the Ni/Ag/SS310S multi-layer sheet. EPMA results showed that Ag diffusion into the Ni layer, which may suppress the cube texture development, was negligible. A small amount of Cr atoms were detected in the Ni layer. It showed that Ag can be used as a chemical barrier of alloying element atoms in Ni layer for the Ni/Ag/SS310S multi-layer sheet and a strong cube texture was developed for the Ni layer in the Ni/Ag/SS310S multi-layer sheet.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 1996년도 특별강연 및 춘계학술발표 개요집
• /
• pp.6-9
• /
• 1996

The Joining of copper rod and zirconia tube was carried out in Ar gas atmosphere. There are two type of the joining. The one is the reaction bond consisting of Cu and zirconia was dominated by surface reaction wi th a undetctable very thin layer. It was found that copper elements were diffused to zirconia side, but that most of Z $r^{4+}$ ions were not diffused to copper side. This result means application of a DC voltage to migrate oxygen to the copper/zirconia interface can oxidize metal at the copper /zirconia interface, and the bonding reaction between zirconia and copper oxide may occur. The other is the reaction bonding was dominated by interdiffusion with a very thick interface layer. This result means application of a DC voltage can reduce zirconia at the interface. The bonding reaction is to be an alloying between Zr and Cr.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part 1
• /
• pp.306-307
• /
• 2006

The sinter-bonding behavior of iron based powder mixtures was investigated. To produce the green compacts to be joined the following powders based on $H{\ddot{o}}gan{\ddot{a}}s$ AB grade NC 100.24 plain iron powder were used: NC 100.24 as delivered, PNC 30, PNC 60 and NC 100.24 + 4%Cu powder mixtures. Dimensional behaviour of all those materials during the sintering cycle was monitored by dilatometry. Simple ring shaped specimens as the outer parts and cylindrical as the inner parts were pressed. The influence of parts' composition on joining strength was established. Diffusion of alloying elements: copper and phosphorous, across the bonding surface was controlled by metallography, SEM and microanalysis.

• 한국원자력학회:학술대회논문집
• /
• 한국원자력학회 1997년도 춘계학술발표회논문집(2)
• /
• pp.98-103
• /
• 1997

원전 증기 발생기 재료로 사용되는 Alloy 600의 내부식성 향상을 위하여 레이저 범을 이용한 레이저 표면합금화(Laser Surface Alloying, LSA) 방법을 이용, 표면에 약 200$\mu\textrm{m}$ 두께의 합금층을 형성시켰다. 첨가한 원소는 크롬 또는 크롬과 니켈의 혼합체를 사용하였으며 첨가법으로는 도금과 용사를 이용하였다. 용사법으로 만든 LSA 시편의 특성과 문제점에 대해 고찰하고 이러한 문제점을 해결하는 방법으로 크롬 도금법을 택하였다. 이들 결과를 레이저 처리를 하지 않은 시편들과 비교하여 부식 거동을 분석하였다. 분석 결과 LSA 시편의 경우 As-received 시편, 레이저 표면 용융(LSM) 들과 비교해 아주 우수한 내부식성을 가졌으며 입계 내부식성도 크게 증가하였다. 이는 크롬 첨가로 인해 크롬의 농도가 많아져 부동태 피막의 형성이 쉬워졌기 때문으로 해석되었다.

• 한국주조공학회지
• /
• 제43권6호
• /
• pp.294-301
• /
• 2023

The effects of Cu on feeding and macro-porosity characteristics were investigated in hypo- (A356 and 319) and hypereutectic (391) aluminum-silicon alloys. T-section and Tatur tests showed that the feeding and macro-porosity characteristics were significantly different between the hypo- and hypereutectic alloys. The hole and the pipe in the T-section and the Tatur casting in hypereutectic alloy showed a rough and irregular shape due to the faceted growth of the primary silicon, while the results of the hypoeutectic alloys exhibited a rather smooth surface. However, the addition of Cu did not strongly affect the macro-feeding behavior. It is known that copper segregates and interferes the feeding process in the last stage of solidification, possibly leading to form more amount of micro shrinkage porosity by the addition of Cu. The macro porosity formation mechanism and feeding properties were discussed upon T-section and Tatur tests together with an alloying addition.

• Corrosion Science and Technology
• /
• 제7권2호
• /
• pp.119-124
• /
• 2008

Steel is generally not corrosion resistant to water with formation of non protective rusts on its surface. Rusts are composed of iron oxides such as $Fe_3O_4$, $\alpha-$, $\beta-$, $\gamma-$and ${\delta}-FeOOH$. However, steel, particularly weathering steel containing small amounts of Cu, Ni and Cr etc., shows good corrosion resistance against rural, industrial or marine environment. Its corrosion rate is exceedingly small as compared with that of carbon steel. According to the exposure test results undertaken in outdoor environments, the atmospheric corrosion rate for weathering steel is only 1 mm for a century. Atmospheric corrosion for steels proceeds under alternate dry and wet conditions. Dry condition is encountered on steel surface on fine or cloudy days, and wet condition is on rainy or snowy days. The reason why weathering steel shows superior atmospheric corrosion resistance is due to formation of corrosion protective rusts on its surface under very thin water layer. The protective rusts are usually composed of two layer rusts; the upper layer is ${\gamma}-FeOOH$ termed as lepidocrocite, and inner layer is nano-particle ${\alpha}-FeOOH$ termed as goethite. This paper is aimed at elucidating the atmospheric corrosion mechanism for steel in comparison with corrosion in bulky water environment by use of empirical data.The summary is as follows: 1. No corrosion protective rusts are formed on steel in bulky water. 2. Atmospheric corrosion for steel is the corrosion under wetting and drying conditions. Corrosion and passivation occur alternately on steel surface. Steel, particularly weathering steel with small amounts of alloying elements such as Cu, Ni and Cr etc. enhances forming corrosion protective rusts by passivation.

• Journal of Welding and Joining
• /
• 제15권5호
• /
• pp.134-143
• /
• 1997

The formation of thick alloyed layer with high Si content have been investigated on the surface of Al alloy (A5083) plate by PTA process with Si powder. Hardening characteristics and wear resistance of alloyed layer was examined in relation to the microstructure of alloyed layer. Thick hardened layer in mm-order thickness on the surface of A5083 plate can be formed by PTA process with wide range of process condition by using Si powder as alloying element because of eutectic reaction of Al-Si binary alloy. High temperature and rapid solidification rate of molten pool, which are features of PTA process, enable the formation of high Si content alloyed layer with uniform distribution of fine primary Si paticle. High plasma arc current was beneficial to make the alloyed layer with smooth surface appearance in wide range of powder feeding rate, because enough volume of molten pool was necessary make alloyed layer. Uniform dispersion of fine primary Si particle with about 30${\mu}{\textrm}{m}$ in particle size can be obtained in layer with Si content ranging from 30 to 50 mass %. Hardness of alloyed layer increased with increasing Si content, but increasing rate of hardness differed with macrostructure of alloyed layer. Wear resistance of alloyed layer depended on $V_{si}$(volume fraction of primary Si) and was remarkably improved to two times of base metal at 20-30% $V_{si}$ without cracking, but no more improvement was obtained at larger $V_{si}$.

• 대한금속재료학회지
• /
• 제46권7호
• /
• pp.427-436
• /
• 2008

The effect of dewpoints on annealing behavior and coating characteristics such as wettability and galvannealing kinetics was studied by annealing 0.3wt%Si - 0.1~0.4wt% Mn added interstitial-free high strength steels(IF-HSS). The 0.3wt%Si-0.1wt%Mn steel exhibited good wettability with molten zinc and galvannealing kinetics after annealing when the dewpoint of $H_2-N_2$ mixed gas was above $-20^{\circ}C$. It is shown that the wettability and galvannealing kinetics are directly related to the coverage of the external(surface) oxide formed by selective oxidation during annealing. At $N_2-15%H_2$ annealing atmosphere, the increase of dewpoint results in a gradual transition from external to internal selective oxidation. The decrease of external oxidation of alloying elements with a concurrent increase of their subsurface enrichment in the substrate, showing a larger surface area that was free of oxide particles, contributed to the improved wettability and galvannealing kinetics. On the other hand, the corresponding wettability and galvannealing kinetics were deteriorated with the dewpoints below $-20^{\circ}C$. The continuous oxide layer of network and/or film type was formed on the steel surface, leading to the poor wettability and galvannealing kinetics. It causes a high contact angle between annealed surface and molten zinc and plays an interrupting role in interdiffusion of Zn and Fe during galvannealing process.