• 한국원자력학회:학술대회논문집
• /
• 한국원자력학회 1997년도 춘계학술발표회논문집(2)
• /
• pp.165-170
• /
• 1997

Samples of extruded dispersions of 24 vol.% spherical U-2wt%Mo and U-10wt.%Mo powders in an aluminum matrix were annealed for over 2,000 hours at 40$0^{\circ}C$. No significant dimensional changes occurred in the U-1025.%Mo/aluminum dispersions. The U-2wt.%Mo/aluminum dispersion, however, increased in volume by 26% after 2,000 hours at 40$0^{\circ}C$. This large volume change is mainly due to the formation of voids and cracks resulting from nearly complete interdiffusion of U-Mo and aluminum. Interdiffusion between U-10wt.%Mo and aluminum was found to be minimal. The different diffusion behavior is primarily due to the fact that U-2wt.%Mo decomposes from an as-atomized metastable r-phase(bcc) solid solution into the equilibrium r-U and U$_2$Mo two-phase structure during the experiment, whereas U-10wt.%Mo retains the metastable r-phase structure after the 2,000 hours anneal and thereby displays superior thermal compatibility with aluminum compared to U-2wt.%Mo. In addition, the molybdenium supersaturated in U-10wt.%Mo particles inhibits the diffusion of aluminum atoms along the grain boundary into the particle. Also, the dissolution of only a few Mo atoms in UAL$_3$ retards the formation of the intermediate phase, as Mo atoms need to migrate from new intermetallic compounds to unreacted islands.

• 대한금속재료학회지
• /
• 제49권12호
• /
• pp.995-1000
• /
• 2011

The microstructure of Cu-24 wt.%Ag filamentary nanocomposite fabricated by a thermo-mechanical process has been investigated by transmission electron microscopy (TEM) observations. This study is focused on the stability of Ag filaments formed by cold drawing; the effects of thermal treatment on the precipitation behavior and distribution of Ag-rich precipitates were also investigated. The Ag filaments elongated along the <111> orientation were observed in Cu-rich ${\alpha}$ phase of the as-drawn specimen and the copper matrix and the silver filament have a cube on cube orientation relationship. Annealing at temperatures lower than $200^{\circ}C$ for the as-drawn specimen caused insignificant change of the fibrous morphology but squiggly interfaces or local breaking of the elongated Ag filaments were easily observed with annealing at $300^{\circ}C$. When samples were annealed at $400^{\circ}C$, discontinuous precipitation was observed in supersaturated Cu solid solution. Ag precipitates with a thickness of 7-20 nm were observed along the <112> direction and the orientation relationship between the copper matrix and the Ag precipitates maintained the same orientation relationship in the as-drawn specimen. The interface between the copper matrix and the Ag precipitates is parallel to {111} and micro-twins were observed in the Ag precipitates.

• 한국재료학회지
• /
• 제4권8호
• /
• pp.847-854
• /
• 1994

Mg-Zn-Ce계 합금에서 비정질 단상 및 hcp-Mg입자분산형 비정질합금이 20-40%, Zn, 0-10%Ce과 5-20%Zn, 0-5%Ce 의 조성범위에서 각각 생성되었다. 초미세 hcp-Mg입자분산형 $Mg_{85}Zn_{12}Ce_{3}$비정질합금은 급속응고 또는 급속응고리본의 열처리에 의해 Mg입자의 입경을 4-20nm의 범위로 조절할 수 있었으며, 이 범위에서는 밀착굽힘이 가능할 만큼 충분한 인성을 가지고 있었다. 이 합금의 최대인장강도($\sigma_{B}$)와 파단 연신율($\varepsilon_{f}$)은 hcp-Mg입자의 체적분율에 따라서 670-930MPa, 5.2-2.0%의 범위였으며, 최대 비강도($\sigma_{B}$밀도 =$\sigma_{s}$)는 $3.6 \times 10^5N \cdot m/kg$에 달하였다. 이와 같이 Mg입자분산형 비정질 합금의($\sigma_{B}$), ($\sigma_{s}$)그리고 $\varepsilon_{f}$의 최대치가 Mg-Zn-Ce계 비정질합금(690MPa, $2.5 \times 10^5N \cdot m/kg$, 2.5%)보다 월등하게 높다는 것은 주목할 만 하다. 복합상 조직이 형성됨으로서 기계적 강도가 증가하는 것은 동일 조성의 비정질상보다 강한 hcp과포화 고용체의 분산강화에 기인하는 것이라고 고찰되었다.

• 대한화학회지
• /
• 제4권1호
• /
• pp.18-26
• /
• 1957

There are two problems to be solved by our efforts in the enamel frit. One is how we can cover the enamel frit thin with complete milk white as possible, and the other is how it can be, made resistant for chemicals than before one. The frit which can solved the two problems just mentioned above is titanium enamel frit. This frit has been developed in America after War Ⅱ, and now the research for concerning antimony frit into titanium frit is under development entirely. In order to develope the enamel industry in Korea, it is urgent problem to convert antimony frit into titanium frit. By the way the titanium frit is emulsified titanium oxide crystal which made through reheating the supersaturated solution of titanium oxide in the basis of glass. Unfortunately, there are many obscure points in active fact or which influence on its composition and characteristics yet. However, this task was tried for the first in Korea. As first step, the test was carried on the reference books, and we can be possible convert antimony frit into titanium frit as a result of this experiment. As a conclusion, for the purpose of developing the enamel industry in Korea, we studied that the research for converting antimony enamel frit which has been used popularly into titanium enamel frit which is more economic and resistant for chemicals. As a result of experiments, the following points concerning with titanium frit have become clearly. 1. It is better when the composition of titanium enamel frit has as following table.Man Duck San Silica 24 An Yang Feldspar 20 Borax 28 Sodium Nitrate 4 Cryolite 7 Calcium Carbonate 3.6∼1 Titanium Oxide 10 Calcium phosphate 0 ∼3.2 Calcium Fluoride 0∼1.8 Antimony Oxide 0∼0.5 2. The amount of $TiO_2$, to be added is $10%\;to\;12{%,\;CaF_2\;is\;under\;1.8%,\;P_2O_5\;is\;under\;1.6%,\;Sb_2O_3\;is\;under\;0.5%$. 3. In the titanium frit, the limit of iron oxide amount to be included is under 0. 5%. 4. Comparing the titanium enamel frit with antimony enamel frit not only the titanium frit can be savely 20.6% in the price of raw materials, but one time of glazing and heating process is omitted in each case, and it is known the titanium frit is more resistant for chemicals than antimony frit.

• Journal of Periodontal and Implant Science
• /
• 제30권1호
• /
• pp.145-157
• /
• 2000

Cytotoxic substances in dental calculus and root cementum of periodontally diseased teeth inhibit new attachment and regeneration. The purpose of scaling and root planing is to remove pathologic structures harboring these cytotoxic substances in order to create a biologically acceptable root surface. However, these procedures inevitably leave a non-biocompatible smear layer. Conventionally, the smear layer has been removed with low pH etching agents such as citric acid, phosphoric acid and tetracycline hydrochloride(TC). Lately, a supersaturated neutral pH etching solution of ethylene diamine tetraacetic acid(EDTA) has been found to be as effective as low pH etchants with respect to smear removal and to be superior in exposing root surfaceassociated collagen. The aim of the present study was to determine the effect of root surface treatment using EDTA on the initial attachment of human gingival fibroblasts. 27 human teeth, extracted due to severe periodontitis, were cut into dentin slices after root planing. The specimens were divided into TC group(treated with $50㎎/m{\ell}$ tetracycline-HCl, pH 1.52), EDTA group(treated with 17% EDTA, pH 7.4), and non-treated control group. After sterilization, 5th subcultured human gingival fibroblasts were seeded in each culture well containing a prepared root slice and incubated for 15 min., 60 min., and 4 hours in 5% $CO_2$ incubator at $37^{\circ}C$. At each incubation time, the number of attached fibroblasts were counted on the microphotographs taken at a magnification of x100. The difference of the number of attached cells between groups was statistically analyzed by the ANOVA followed by Duncan test in SPSS/PC＋programs. The results were as follows : 1. After incubation for 15 min, the attached cells were significantly more in EDTA group and TC group than non-treated control group(p<0.05), but there was no significance in the difference between EDTA group and TC group(p>0.1). 2. After incubation for 60 min and 4 hours, there was no significant difference in the number of attached cells between all groups(p>0.1). 3. In both EDTA group and TC group, there was no significant difference in the number of attached cells between different incubation(p>0.1). But in control group, the number of attached cells was significantly increased after incubation for 60 min, compared with incubation for 15 min(p<0.05). The above results suggest that root surface treatment using EDTA could enhance the initial attachment of gingival fibroblasts to root surface as effective as tetracycline-HCl.

• 자원리싸이클링
• /
• 제21권6호
• /
• pp.12-22
• /
• 2012

본 연구는 제강용도로 사용하기 위해 돌로마이트를 하소후 남은 2 mm 이하의 경소백운석 부산물을 건축용 바닥 몰탈의 기존 팽창재로서 활용 가능성을 검토하고자 하였다. 경소백운석은 $600{\sim}800^{\circ}C$ 정도에서 하소하였을 때 반응성이 높은 준결정상태의 활성 마그네시아로 존재하게 되며, 이 활성화된 마그네시아는 수화초기 Brucite gel을 형성하여 수화물 비율을 상대적으로 줄여 치밀한 조직을 형성하는 원인으로 작용하고, 수화후기에는 결정질의 Brucite가 형성되어 수축 현상을 억제하며 부피가 2배 이상 팽창하여 화학적 수축균열 방지 역할을 하게 되는 것이다. 실험결과 경소백운석은 기존 사용 중인 팽창재 대비 동일량 적용시 압축강도는 우수하게 확인되었으나, 반응성은 기존 팽창재(생석회+무수석고)에 비해 다소 낮게 측정되었다. 하지만 팽창재로서의 역할은 충분한 것으로 확인되었으며, 공사기간 단축 등 부가적인 효과를 나타내었다.

• 한국광물학회지
• /
• 제17권1호
• /
• pp.11-21
• /
• 2004

자발적 침전법에 의하여 다양한 과포화 용액에서 탄산염광물을 합성하였다. 합성용액의 온도는 $25^{\circ}C$에서 유지 시켰고 pH범위는 6.9에서 8.8 이였다. 용액의 과포화도 조절 시 2가지 변수를 두어 농도를 변화 시켰다. (1) total carbonate의 농도와 total calcium의 농도비가 다음 세 가지 조건을 만족시키도록 변화시켰다: [C $O_3$]$_{Τ}$/[Ca]$_{Τ}$ >1. [C $O_3$]$_{Τ}$/[Ca]$_{Τ}$=1, and [C $O_3$]$_{Τ}$/[Ca]$_{Τ}$<1. (2) 앞서 언급한 조건에 total calcium의 농도를 0.02 mol/d $m^3$, 0.2 mol/d $m^3$, 그리고 0.4 mo1/d $m^3$이 되도록 변화 시켰다. [C $O_3$]$_{Τ}$/[Ca]$_{Τ}$$\geq$ 1의 조건 하에서 형성된 미립의 탄산염 광물은 대부분 거의 순수한 방해석으로 바테라이트가 1% 이하로 존재하였으며 이와는 달리 [C $O_3$]$_{Τ}$/[Ca]$_{Τ}$ < 1 조건하에서는 거의 순수한 바테라이트가 합성되었다. 본 연구 결과 탄산염광물의 상은 합성 용액상의 [C $O_3$]$_{Τ}$ 농도보다는 [C $O_3$]$_{Τ}$의 농도에 의하여 좌우되는 것으로 나타났다. 또한 바테라이트의 합성 결과는 [C $O_3$]$_{Τ}$/[Ca]$_{Τ}$의 비가 0.8 에서 0.5로 낮아짐에 따라 roughness가 증가하고 결과적으로 광물표면적이 5.64∼7.34 $\mu\textrm{m}$에서 8.39∼10.3 $\mu\textrm{m}$로 증가한다.