• Corrosion Science and Technology
• /
• 제20권4호
• /
• pp.169-174
• /
• 2021

In this study, performance tests, a field evaluation, and a life cycle cost (LCC) analysis for high performance coating systems were conducted to prepare a plan to reduce the cost of maintenance coating and contribute to the service life extension of steel bridges by applying high performance coatings to steel bridges that will be constructed in the future. From the deterioration models based on the field evaluation for chlorinated rubber and urethane topcoat systems, which have been applied often, the mean service lives were derived as 20.8 and 26.6 years, respectively. For the other coating systems that have not been applied in practice, the coordination factors were differentially applied with evaluation items. The most durable coating system was predicted to be thermal spray coating (TSC) primer/epoxy intermediate coat/fluoride resin topcoat, with a predicted value as long as 42.2 years. The LCC analysis indicates that partial application of high performance coating, such as TSC and fluoride resin, to specific parts vulnerable to corrosion and ultraviolet ray (UV) is more advantageous than the use of general coating systems.

• 한국강구조학회 논문집
• /
• 제28권5호
• /
• pp.325-335
• /
• 2016

국내의 강교 도장 시방에 등재되어 있는 도장계에 대한 공용수명 예측을 위하여 현장 열화도 평가 및 촉진 내후성 시험을 수행하였고, 평가 결과에 대한 회귀분석을 통하여 열화모델을 도출하였다. 현장 적용 실적이 없는 도장계에 대해서는 국외 연구 결과 및 본 연구에서 수행한 촉진 내후성 시험 결과를 참고하여 염화고무계 및 우레탄 마감 도장계의 현장 열화도 평가 결과에 열화도 항목별 조정계수를 적용하여 가상의 평가 결과를 도출한 후에 회귀분석을 실시하였다. 공용수명 예측 결과는 금속용사를 적용하면 도장계의 수명을 일반 도장계 대비 2배 이상 연장시킬 수 있다는 것을 보여주었다.

• 한국철도학회:학술대회논문집
• /
• 한국철도학회 2007년도 추계학술대회 논문집
• /
• pp.345-351
• /
• 2007

The research which it sees will confront to the coating with paint material and a coating with paint public law application of the river bridge and it will present it will sleep and it will execute, it will reach and a comparison - an analysis from the research which it tries to respect middle of special environment the polyurethane system which is a method coating with paint system and fluorine resin system, against a ceramic system it executed more an objectivity and rational fundamental data. With research method against each coating with paint evening sunlight a research investigation material and structure, it separated with spatial-temporal characteristic and economic viewpoint it executed. When considering overview from material viewpoint, fluorine resin system ceramic system polyurethane system pure with it is judged with the fact that it is excellent. There is a possibility of saying that the coefficient of friction of the fluorine resin system which uses the weapon quality zinc end coating compound ever so hard and polyurethane system is excellent ceramic system than from structure viewpoint. That fluorine resin system = polyurethane system ceramic system pure with it is excellent, it is judged from spatial-temporal characteristic viewpoint. It measures but it considered an internal troubles year grudge in the standard which becomes disturbance the place where it executes the market the expectation life person of the general bridge against 100 years the result fluorine resin system polyurethane system ceramic system which compares a materials unit cost pure with it appeared.

• 한국구조물진단유지관리공학회 논문집
• /
• 제23권2호
• /
• pp.75-83
• /
• 2019

본 연구에서는 국내에서 사용되고 있는 우레탄계, 세라믹계, 폴리실록산계 및 불소수지계 강교량용 도장계를 대상으로 실내 부식실험을 실시하여 도장계별 노화모델을 도출하였다. 상도를 구분하여 각 도장계별로 시험편을 제작하였으며, 직경 0.5, 1, 3, 5 mm의 원형 결함을 도입하였다. ISO 20340를 이용하여 극한환경을 모사한 부식촉진실험을 실시하였다. 도장계별 노화곡선은 원형결함의 노화면적을 기준으로 평가되었다. 노화곡선을 사용하여 공용중인 강교의 도장 사용수명을 평가하기 위하여 촉진배율을 산출하였으며, 촉진배율은 ISO 20340과 ISO 9223의 대기환경 부식속도를 기준으로 산출되었다. 실험결과, 노화진전속도는 원형결함의 크기와 상관없이 증가하였으며, 노화면적이 3%일 때 우레탄 도장계의 노화수명은 C2, C3, C4 및 C5 등급에서 약 31.8, 15.8, 9.9 및 3.9년으로 평가되었다.

• 동력기계공학회지
• /
• 제19권5호
• /
• pp.38-44
• /
• 2015

The cold-rolled steel sheet for automobile is liable to corrosion, and will be painting in a variety of ways for the anticorrosive. This paper was coated on cold rolled steel (SPCC and SPFC590) for automobiles using five kinds of organic/inorganic hybrid solution. This was evaluated corrosion resistance and so on by the salt spray. Corrosion area was less according to increasing of curing time in 2 types of steel plate with 5 types of the coating solution. No.1 solution was showed the best corrosion resistance regardless of the kinds of the steel sheet. It is judged that the melamin hardner had the role of bridge between $SiO_2$ polysilicate and urethan resin. Other properties were excellent in all solution.

• 한국강구조학회 논문집
• /
• 제28권5호
• /
• pp.373-382
• /
• 2016

도장 또는 금속용사는 강구조물의 방식에 널리 사용되고 있으며, 금속용사와 도장의 복합방식법은 혹독한 부식환경하에 놓인 강구조물에 고내후성 피복방식법으로 적용되고 있다. 본 연구에서는 아연(Zn), 아연-알루미늄(ZnAl)합금, 알루미늄(Al), 알루미늄-마그네슘(AlMg)합금의 4종류 금속용사 후 실링 처리한 시편, 4종류 금속용사 후 중방식 도장한 시편과 도장만 실시한 시편을 대상으로 175일간의 ISO 20340 부식촉진실험을 실시하여, 각 방식법의 상대적인 내후성능을 비교, 검토하였다. 강재표면까지 도달하는 원형 및 선형 초기결함으로부터의 표면상태 변화 및 도막의 노화면적에 근거한 내후성능의 평가 결과, 금속용사 후 실링 처리한 시편의 경우에는 알루미늄(Al) 및 알루미늄-마그네슘(AlMg)금속용사 후 실링 처리한 시편이 가장 우수한 내후성능을 보였으며, 금속용사 후 도장을 실시한 금속용사와 도장의 복합방식법의 경우에는 아연(Zn)용사에 도장을 실시한 복합방식 시편이 가장 우수한 내후성능을 나타내었다.

• Corrosion Science and Technology
• /
• 제8권2호
• /
• pp.53-61
• /
• 2009

본 연구에서는 강교 도장재료로 사용될 수 있는 에폭시 하도 도료를 도포한 시험편을 촉진시험을 통해 열화시킨 후 도막의 외관 평가 및 EIS에 의한 평가를 실시하고, 그 2가지 방법에 대한 비교 분석을 실시하였다. 화상처리 기법에 의해 구한 총 열화 면적율과 열화도 평점 산정 결과를 상호 비교해 본 결과 녹이 발생한 경우가 그렇지 않은 경우보다 열화도 평점이 높게 나타났다. 이는 강교 도장의 열화도 평가 기준에서 단위 열화 면적율당 부여하는 열화도 평점이 박리의 경우보다 녹의 경우가 더 크기 때문이다. 열화 면적율과 EIS 측정 데이터를 비교해 본 결과 녹의 면적율 약 0.1% 이상, 블리스터링의 면적율 약 3% 이상만 되어도 도막의 임피던스는 약 $10^4{\Omega}{\cdot}cm^2$ 혹은 그 이하로 크게 저하되었다. 2개의 시험편을 제외한 모든 시험편에 대해 전하전달저항(charge transfer resistance, $R_{ct}$)과 이중층 정전용량(double layer capacitance, $C_{dl}$) 값이 나타났으며, 이 결과로부터 이들 시험편들은 도막과 강재 계면에 수분이 축적되어 부식이 진행되고 있음을 알 수 있었다. 열화도 평점과 EIS 측정결과를 상호 비교해 본 결과 저주파수(10 mHz)에서의 임피던스 값이 $10^6{\Omega}{\cdot}cm^2$ 이하로 떨어진 경우는 모두 열화도 평점이 10점 이상으로 나타났으며, NORSOK cyclic test 과정에 의해 열화시킨 경우 열화도 평점이 높지 않음에도 불구하고 임피던스는 가장 낮게 나타났다. 이것은 도장계와 열화조건이 주 시험편과 다르기 때문인 것으로 판단되며, 열화조건이 더 가혹하거나 복합적일 경우 외관 상태에 비해 도막의 저항이 더 크게 저하될 가능성이 있다고 생각된다.

• 한국건설관리학회논문집
• /
• 제17권4호
• /
• pp.57-65
• /
• 2016

본 연구에서는 신뢰성 개념을 도입하여 최근 10년간의 한국도로공사 관할의 교량부재별의 유지보수 이력 데이터를 기반으로 적합한 모수적 수명 분포를 찾고 최대우도법으로 구해진 모수를 이용하여 교량 부재별 평균수명 및 신뢰도를 산정하는 방안을 제안하였다. 교량 부재별의 수명 데이터를 가장 잘 설명하는 모수적 수명 분포형태를 찾기 위해 많이 활용되는 지수분포, 와이블분포, 대수정규분포를 대상으로 분석한 결과 대수정규분포와 와이블분포가 해당 수명 데이터의 특성을 가장 잘 설명하는 것으로 나타났다. 이 때 모수 추정을 위해서 최대우도법을 사용하였으며, 적합성 검정을 위해서는 AD통계량을 이용하였다. 추정된 모수를 기반으로 교량 부재별 평균수명을 산정한 결과, 강교도장이 18.51년으로 가장 길었으며, 바닥판이 17.56년으로 그 다음 순이었다. 배수시설과 교량받침의 경우 평균수명이 각각 12.27년, 12.57년으로 가장 짧았다. 또한 교량의 평균수명일 때 추정된 신뢰도 지표는 현재 교량 부재별 유지보수 시점이라고 할 수 있다. 교량받침, 바닥판, 하부구조, 배수시설의 경우 다른 부재보다 빠른 시기에 유지보수를 하는 것으로 분석되었다.

• 한국구조물진단유지관리공학회 논문집
• /
• 제23권2호
• /
• pp.130-134
• /
• 2019

본 논문에서는 레이저기반 응력측정을 위한 비접촉식 로드셀을 개발을 위하여, 실내실험을 통하여 기술을 검증하고, 실규모 실험을 통하여 문제점을 파악하였으며, 최종적으로 현장적용에 적합한 응력측정용 비접촉식 로드셀 프로토타입을 개발하였다. 이를 위하여, 중심공 압축타입의 로드셀 제작에 사용되는 로드셀 몸체 표면에 용사코팅기술을 이용하여 알루미나를 도포하고, 레이저를 기반으로한 압분광법을 이용하여, 비접촉식으로 응력을 계측하였다. 이때, 인가되는 응력과 스펙트럼 이동간의 관계가 선형임을 확인하였다. 해당 기술의 현장 적용성 확인을 위하여, 실규모 프리스트레스 콘크리트 시편을 제작하고, 레이저를 조사하여 인가된 응력을 확인하는 과정에서, 반복적인 상황 하에서 레이저 조사 위치가 동일해야 함을 확인하였다. 이를 보완하기 위하여 프로브를 고정할 수 있는 케이싱이 포함된 로드셀 프로토타입을 제작하였고, 실내일축압축시험을 통하여 압축력과 스펙트럼 이동간의 선형성을 확인하였다. 따라서, 본 연구를 통하여 개발된 비접촉식 로드셀을 이용하여, 압축력을 효과적으로 측정할 수 있을 것으로 기대된다.