Internal Friction Behavior in AZ31 Magnesium Alloy after Annealing Treatment (AZ31 마그네슘 합금의 어닐링 이후 내부마찰 거동)

  • Kwak, Juho;Kang, Changyong;Kim, Kwonhoo
    • Journal of Power System Engineering
    • /
    • v.22 no.1
    • /
    • pp.87-93
    • /
    • 2018
  • Specimens were machined out from hot-rolled AZ31 magnesium alloy, and deformed at 623K with rolling reduction of 30%. After hot rolling, specimens were annealed at various range of temperature and time. In this study, static recrystallization was occurred during heat treatment, however, variation of main component and intensity of texture was not revealed. The results of microstructure observation, damping capacity test and dislocation mechanism indicated that increasing of damping capacity was caused by grain growth. It means that grain size is effective factor to damping capacity.

Cold Roll Bonding of (Ag-10% Ni)/Cu Clad Metals ((Ag-10 % Ni)/Cu 접점재의 냉간압연접합)

  • 김종헌;김성일;박상용
    • Transactions of Materials Processing
    • /
    • v.6 no.2
    • /
    • pp.136-144
    • /
    • 1997
  • (Ag-10%Ni)/Cu clad metals for electric contact switch were fabricated by cold-roll bonding process. 2 or 3 passes of cold-rolling was carried out for each process to investigate the effect of the rolling passes on the bonding property. The effect of the annealing temperature of copper before the cold-roll bonding on the bond strength was also studied. The specimen bonded with copper annealed below 30$0^{\circ}C$ before roll bonding showed good bond strength. This is because high stored energy in copper promoted the short range diffusion and the grain refinement of copper by the static recrystallization increased the degree of the interfacial coherency. The maximum peel strength of clad metals bonded with Cu annealed below 30$0^{\circ}C$ was 120N.

  • PDF

Textural Implications of Fine-Grained Peridotite Xenoliths in Basaltic Rocks from Jeju Island (제주도 현무암에 포획된 세립질 맨틀 페리도타이트 포획암의 조직적 특성)

  • Yang, Kyoung-Hee;Nam, Bok-Hyun;Kim, Jin-Seop;Szabo, Csaba
    • Journal of the Mineralogical Society of Korea
    • /
    • v.22 no.1
    • /
    • pp.1-11
    • /
    • 2009
  • Fine-grained peridotite xenoliths are rarely trapped in the basaltic rocks from the southeastern part of Jeju Island. Based on textural characteristics of the constituent phases showing uniform-sized, fine-grained tabular to mosaic grains with rare porphyroclastic relics, the studied samples can be defined as fine-grained, foliated porphyroclastic peridotites (FPP). Almost no significant difference among the FPPs in textures and major element compositions implies that the FPPs were derived from a structural domain, experiencing similar deformation events and deformation patterns. Moreover, the bimodal distribution with kink-banded porphyroclasts ($2{\sim}3mm$) and stain-free neoblasts ($200{\sim}300{\mu}m$), straight to gently curved grain boundaries with triple junctions, interstitial melt pockets, and microstructures for migrating grain boundary suggest that the studied samples went through dynamic recrystallization (${\pm}$ static recrystallization) in the presence of melt/fluid movement along foliation planes. No notable difference between the FPP and common protogranular xenoliths in major element compositions and geochemical evolution also implies that the FPP and protogranular xenoliths were from a similar horizon. Thus, the textural and geochemical characteristics of the FPPs reflects deformation events occurred at a localized and narrow zone within the lithospheric mantle beneath the Jeju Island. Although further detailed studies are necessary to define deformation events, the most possible process which could trigger deformation in the FPP in the rigid upper mantle was the ascending basaltic magma forming high-stress deformation zones. The suggested high-stress deformation zones in the lithosphere beneath the Jeju Island may be produced by paleo-faulting events related to the ascent of basalt magma before Jeju Island was formed.

AGS Distribution in Low-Speed Round-Oval Rolling of S20C Steel (S20C강 저속 라운드-모발 압연의 AGS 분포)

  • Kwon H. C.;Lee H. W.;Lee Y.;Im Y. T.
    • Proceedings of the Korean Society for Technology of Plasticity Conference
    • /
    • 2004.08a
    • /
    • pp.297-306
    • /
    • 2004
  • This study investigated Austenite Grain Size (AGS) distribution in Low-Speed Round-Oval Rolling. Rolling experiments were done along with the AGS numerical modeling to characterize the final AGS distribution and its kinetics behavior. For bar rolling experiment, we utilized the pilot rolling mill, operating at 34 fixed rpm, at POSCO Technical Research Laboratories. To investigate the microstructural observation, the rigid-viscoplastic finite element analysis was combined with Hodgson's AGS evolution model. To consider the transient thermal history in the integrative AGS modeling, additivity rule was introduced. The integrated analysis revealed that static or meta-dynamic recrystallization is responsible for the AGS difference in the inner or outer region of rolled bar. Comparative study showed that the current AGS modeling approach can be used to model the overall AGS distribution in bar rolling processes. For more accurate AGS prediction, the AGS modeling method should be verified under the various rolling conditions such as different rolling speeds and different deformations.

  • PDF

Change in Microstructure and Mechanical Properties of Deoxidized Low-Phosphorous Copper Processed by Accumulative Roll-Bonding with Annealing (ARB가공된 인탈산동의 어닐링에 따른 미세조직 및 기계적 특성 변화)

  • Lee, Seong-Hee;Kim, Chun-Su;Kim, Sang-Shik;Han, Seung-Zeon;Lim, Cha-Yong
    • Korean Journal of Materials Research
    • /
    • v.17 no.7
    • /
    • pp.361-365
    • /
    • 2007
  • A deoxidized low-phosphorous copper processed by eight cycles of accumulative roll-bonding (ARB) was annealed at various temperatures ranging from 100 to $400^{\circ}C$. The annealed copper was characterized by transmission electron microscopy (TEM) and tensile & hardness test. TEM observation revealed that the ultrafine grains developed by the ARB still remained up to $350^{\circ}C$, however above $400^{\circ}C$ they were replaced by equiaxed and coarse grains due to an occurrence of the static recrystallization. The hardness of the copper decreased slightly with the annealing temperature up to $350^{\circ}C$, however they dropped largely above $400^{\circ}C$. Annealing characteristics of the copper were compared with those of an oxygen free copper processed by ARB and subsequently annealed.

Annealing Characteristics of Oxygen Free Copper Severely Deformed by Accumulative Roll-Bonding Process (ARB법에 의해 강소성가공된 무산소동의 어닐링 특성)

  • Lee Seong-Hee;Cho Jun;Lee Chung-Hyo;Han Seung-Zun;Lim Cha-Yong
    • Korean Journal of Materials Research
    • /
    • v.15 no.9
    • /
    • pp.555-559
    • /
    • 2005
  • An oxygen free copper severely-deformed by eight cycles (an equivalent strain of $\~6.4$) of accumulative roll-bonding (ARB) was annealed at various temperatures ranging from 100 to $300^{\circ}C$. The annealed copper was characterized by transmission electron microscopy (TEM) and tensile & hardness test. TEM observation revealed that the ultrafine grains developed by the ARB still remained up to $150^{\circ}C$, however above $200^{\circ}C$ they were replaced by equiaxed and coarse grains due to an occurrence of the static recrystallization. Tensile strength and hardness of the copper decreased slightly with the annealing temperature up to $150^{\circ}C$, however they dropped largely above $200^{\circ}C$. Annealing characteristics of the copper were compared with those of a commercially pure aluminum processed by ARB and subsequently annealed.

Microstructure and High-Cycle Fatigue Properties of High-Speed-Extruded Mg-5Bi-3Al Alloy (Mg-5Bi-3Al 마그네슘 고속 압출재의 미세조직과 고주기피로 특성)

  • Cha, J.W.;Jin, S.C.;Park, S.H.
    • Transactions of Materials Processing
    • /
    • v.31 no.5
    • /
    • pp.253-260
    • /
    • 2022
  • In this study, the microstructural characteristics of a high-speed-extruded Mg-5Bi-3Al (BA53) alloy and its tensile, compressive, and high-cycle fatigue properties are investigated. The BA53 alloy is successfully extruded at a die-exit speed of 16.6 m/min without any hot cracking using a large-scale extruder for mass production. The homogenized BA53 billet has a large grain size of ~900 ㎛ and it contains fine and coarse Mg3Bi2 particles. The extruded BA53 alloy has a fully recrystallized microstructure with an average grain size of 33.8 ㎛ owing to the occurrence of complete dynamic recrystallization during high-speed extrusion. In addition, the extruded BA53 alloy contains numerous fine lath-type Mg3Bi2 particles, which are formed through static precipitation during air cooling after exiting the extrusion die. The extruded BA53 alloy has a high tensile yield strength of 175.1 MPa and ultimate tensile strength of 244.4 MPa, which are mainly attributed to the relative fine grain size and numerous fine particles. The compressive yield strength (93.4 MPa) of the extruded BA53 alloy is lower than its tensile yield strength, resulting in a tension-compression yield asymmetry of 0.53. High-cycle fatigue test results reveal that the extruded BA53 alloy has a fatigue strength of 110 MPa and fatigue cracks initiate at the surface of fatigue test specimens, indicating that the Mg3Bi2 particles do not act as fatigue crack initiation sites. Furthermore, the extruded BA53 alloy exhibits a higher fatigue ratio of 0.45 than other commercial extruded Mg-Al-Zn-based alloys.

Application of Automated Microscopy Equipment for Rock Analog Material Experiments: Static Grain Growth and Simple Shear Deformation Experiments Using Norcamphor (유사물질 실험을 위한 자동화 현미경 실험 기기의 적용과 노캠퍼를 이용한 입자 성장 및 단순 전단 변형 실험의 예)

  • Ha, Changsu;Kim, Sungshil
    • Economic and Environmental Geology
    • /
    • v.54 no.2
    • /
    • pp.233-245
    • /
    • 2021
  • Many studies on the microstructures in rocks have been conducted using experimental methods with various equipment as well as natural rock studies to see the development of microstructures and understand their mechanisms. Grain boundary migration of mineral aggregates in rocks could cause grain growth or grain size changes during metamorphism or deformation as one of the main recrystallization mechanisms. This study suggests improved ways regarding the analog material experiments with reformed equipment to see sequential observations of these grain boundary migration. It can be more efficient than the existing techniques and carry out an appropriate microstructure analysis. This reformed equipment was implemented to enable optical manipulation by mounting polarizing plates capable of rotating operation on a stereoscopic microscope and a deformation rig capable of experimenting with analog materials. The equipment can automatically control the temperature and strain rate of the deformation rig by microcontrollers and programming and can take digital photomicrographs with constant time intervals during the experiment to observe any microstructure changes. The composite images synthesized using images by rotated polarizing plates enable us to see more accurate grain boundaries. As a rock analog material, norcamphor(C7H10O) was used, which has similar birefringence to quartz. Static grain growth and simple shear deformation experiments were performed using the norcamphor to verify the effectiveness of the equipment. The static grain growth experiments showed the characteristics of typical grain growth behavior. The number of grains decreases and the average grain size increases over time. These case experiments also showed a clear difference between the growth curves with three temperature conditions. The result of the simple shear deformation experiment under the medium temperature-low strain rate showed no significant change in the average grain size but presented the increased elongation of grain shapes in the direction of about 53° regarding the direction perpendicular to the shearing direction as the shear strain increases over time. These microstructures are interpreted as both the plastic deformation and the internal recovery process in grains are balanced by the deformation under the given experimental conditions. These experiments using the reformed equipment represent the ability to sequentially observe changing the microstructure during experiments as desired in the tests with the analog material during the entire process.

Development of jigs for planar measurement with DIC and determination of magnesium material properties using jigs (마그네슘 합금 판재의 평면 DIC 측정을 위한 지그 개발과 이를 활용한 단축 변형 특성 분석)

  • Kang, Jeong-Eun;Yoo, Ji-Yoon;Choi, In-Kyu;YU, Jae Hyeong;Lee, Chang-Whan
    • Design & Manufacturing
    • /
    • v.15 no.2
    • /
    • pp.23-29
    • /
    • 2021
  • The specific strength of magnesium alloy is four times that of iron and 1.5 times that of aluminum. For this reason, its use is increasing in the transportation industry which is promoting weight reduction. At room temperature, magnesium alloy has low formability due to Hexagonal closed packed (HCP) structure with relatively little slip plane. However, as the molding temperature increases, the formability of the magnesium alloy is greatly improved due to the activation of other additional slip systems, and the flow stress and elongation vary greatly depending on the temperature. In addition, magnesium alloys exhibit asymmetrical behavior, which is different from tensile and compression behavior. In this study, a jig was developed that can measure the plane deformation behavior on the surface of a material in tensile and compression tests of magnesium alloys in warm temperature. A jig was designed to prevent buckling occurring in the compression test by applying a certain pressure to apply it to the tensile and compression tests. And the tensile and compressive behavior of magnesium at each temperature was investigated with the developed jig and DIC equipment. In each experiment, the strain rate condition was set to a quasi-static strain rate of 0.01/s. The transformation temperature is room temperature, 100℃. 150℃, 200℃, 250℃. As a result of the experiment, the flow stress tended to decrease as the temperature increased. The maximum stress decreased by 60% at 250 degrees compared to room temperature. Particularly, work softening occurred above 150 degrees, which is the recrystallization temperature of the magnesium alloy. The elongation also tended to increase as the deformation temperature increased and increased by 60% at 250 degrees compared to room temperature. In the compression experiment, it was confirmed that the maximum stress decreased as the temperature increased.

Textural and Geochemical Characteristics and their Relation of Spinel Peridotite Xenoliths from Jeju Island (제주도 첨정석 페리도타이트 포획암의 조직 및 지화학적 특성과 그 관련성)

  • Yu, Jae-Eun;Yang, Kyoung-Hee;Kim, Jin-Seop
    • The Journal of the Petrological Society of Korea
    • /
    • v.19 no.3
    • /
    • pp.227-244
    • /
    • 2010
  • Abundant spinel lherzolite xenoliths showing distinctively different textural types such as protogranular, porphyroclastic, and mylonitic texture are trapped in the basaltic rocks from southeastern part of Jeju Island. These xenoliths show the textural spectrum from coarse-grained protogranular through porphyroclastic with bimodal grain size to fine-grained and foliated mylonitic texture. They tend to decrease in grain sizes and show more linear grain boundaries and more frequent triple junctions from protogranular through porphyroclastic to mylonitic. Spinel has different occurrence mode according the textural type. Spinel is always associated with orthopyroxene in protogranular texture, whereas it is scattered and independent of orthopyroxene in mylonitic texture. Additionally, porphyroblast from porphyroclastic and mylonitic textures has internal deformation features such as kink band, undulatory extinction and curved lamella, whereas neoblast is strain-free. These textural features indicate increasing degree of static/dynamic recrystallization from protogranular through porphyroclastic to mylonitic texture. The mg#[$=100{\times}Mg/(Mg+Fe_t)$] of olivine, orthopyroxene and clinopyroxene is relatively constant (ol: 88-91; opx: 89-92; cpx: 89-92) regardless of textural differences. The mg# of constituent minerals, NiO content (0.3~0.4 wt%) and MnO content (0.1~0.2 wt%) of olivine are similar to those of mantle xenoliths worldwide, also indicating that studied spinel lherzolite xenoliths were mantle residues having experienced 20~25% partial melting. The geochemical and textural characteristics have close relations showing that LREE and incompatible trace elements content of orthopyroxene and clinopyroxene increases from protogranular through porphyroclastic to mylonitic. These observations suggest that the studied mantle xenoliths experienced metasomatism by LREE enriched melt or fluid after partial melting, indicating a close relation between deformation and metasomatism. The metasomatism was possibly confined to narrow shear zones from where porphyroclastic and mylonitic textured xenoliths originated. These shear zones might favorably drive the percolation of LREE-enriched melts/fluids responsible for the metasomatism in the lithospheric mantle below the Jeju Island.