• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2004년도 학술.기술논문발표회
• /
• pp.97-100
• /
• 2004

In-place curing box for specimens is used to cure the compressive strength specimens for control in place concrete. The box if composed of insulating chamber maintaining 20$\pm$3$^{\circ}C$ of temperature, in this paper, strength and temperature history of specimens cured at in plate curing box are investigated to verify field applicability. According to test results, air temperature at measured time shows large temperature variation and below zero, whereas, inside temperature of in place curing box maintains within 20$\pm$3$^{\circ}C$ due to temperature control function. For curing condition. temperature of specimens cured at outside shows large temperature deviation. specimens lured at in-place curing box is not affected by outer temperature.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2002년도 학술.기술논문발표회
• /
• pp.11-15
• /
• 2002

This study is intended to analyze the relationship between the rebound value of P type schmidt hammer and the compressive strength for a quality control of concrete. According to the results, the compressive strength of standard curing specimen increases in proportion to age, but that of air curing specimen hardly increases after 28 days. The rebound value of P type schmidt hammer, however, increases due to carbonation of concrete in air curing specimen. The correlativity between the rebound value and the compressive strength is very favorable in the case of standard curing specimen, but drops remarkably in the case of air curing specimen. Thus, as application of age coefficient is required for exact estimation of the compressive strength, the age coefficient is derived from this study. The age coefficient of P type schmidt hammer is higher at the age of 3 and 7days, and drops significantly, compared with the age of 28days. And it is lower before 28days than that of N type schmidt hammer suggested in Japan, and shows the similar tendency after 28days.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2002년도 봄 학술발표회 논문집
• /
• pp.157-162
• /
• 2002

This study is intended to present a reference data for effective quality control of concrete through comparing the rebound value of P type schmidt hammer with the compressive strength with variation of mix proportion and curing condition. According to the results, the air-curing specimen shows the higher rebound value than standard specimen except high strength in the whole. Also the vertical stroke shows higher rebound value than horizontal stroke in standard specimen, however, the rebound value of the two does not show prominent difference in air-curing specimen. The estimation equation of compressive strength derived from this experiment estimates the compressive strength more largely than the estimation equation in P type schmidt hammer manual. Therefore it is thought that the new estimation equation that fits our condition will have to be presented.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2003년도 학술.기술논문발표회
• /
• pp.35-38
• /
• 2003

The purpose of this study is to investigate the manufacture of light weight concrete panel using the artificial light-weight aggregate as a part of the substitution of foamed styrene and polyurethane because of narrow allocable temperature Bone in use. The experimental parameter of this study is 40, 60 and 8$0^{\circ}C$ of curing temperature at 100% relative humidity and the type of admixture such as cement, 6mm glass fiber and St/BA emulsion. Testing item is compressive and flexural strength and strength of specimen cured at standard condition is compared to that of specimen cured at 40, 60 and 8$0^{\circ}C$ of curing temperature at 100% relative humidity. As a result or this, it was revealed that the maximum or strength is developed in 6$0^{\circ}C$ or cure temperature at 100% relative humidity in case of the most of the specimen. Specimens modified by St/BA emulsion show the highest development of strength dependent on the curing tmeperature. So, it seems to be effective that evaporation curing method shoud be considered to curing the specimen as the panel core.

• 한국건축시공학회지
• /
• 제2권4호
• /
• pp.169-176
• /
• 2002

To study of binder and fine aggregate a lot of replacement fly-ash concrete, initial characteristics, standard environment of curing temperature $20^{\circ}C$, hot-weather environment, cold weather environment of curing temperature $5^{\circ}C$. Flash concrete tested slump, air contest, setting and Hardening concrete valuated setting period of form, day of age 3, 7, 28 compression strength in sealing curing. Underwater curing specimen compression strength of age 3. 7, 28day used strength change accordingly fly-ash concrete curing temperature. Purpose of study is consultation materials in field that variety of fly-ash replacement concrete mix proportion comparison and valuation. (1) Setting test result, fly-ash ratio of replacement higher delay totting time. Same volume of fly-ash ratio of replacement is lower fly-ash ratio of replacement fine aggregate delay setting time. Setting test in curing temperature $35^{\circ}C$ over twice fast setting in curing temperature $20^{\circ}C$ and all specimen setting delay in curing temperature $5^{\circ}C$. F40 specimen end of setting about 30 time. (2) Experiment result age 28day compression strength more fisher plan concrete then standard environment in curing temperature $20^{\circ}C$, cold weather environment in curing temperature $5^{\circ}C$, most strength F43 is hot-weather environment in curing temperature $35^{\circ}C$ replacement binder 25%, fine aggregate 15%. (3) Hot-weather environment replacement a mount of fly-ash is a same of plan concrete setting period of form. Age 28day compression strength replacement a mount of fly-ash more hot-weather concrete then plan concrete.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2000년도 가을 학술발표회 논문집(II)
• /
• pp.1057-1062
• /
• 2000

The purpose of this study is to practice the method which can estimate 28-days strength of concrete in advance. This method is made for reliant quality control. Based on existing experiment, concrete that flyash added and normal concrete are placed into wall structure, and it is examined the difference between experiment use concrete and field use concrete. The result of this study are as follows : 1) Core test specimen have 10% lower strength to standard curing specimen. 2) At 28-days accelerated strength by microwave, average 35% in normal concrete, average 23% in flyash added concrete. 3) At coefficient of determination between compressive strength and accelerated strength, 0.84 in normal concrete core, 0.86 in standard curing normal concrete, 0.86 in flyash added concrete, 0.90 in standard curing flyash added concrete.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2023년도 가을학술발표대회논문집
• /
• pp.143-144
• /
• 2023

The compressive strength of concrete varies depending on various factors. Among them, based on the curing temperature, the KCS 14 20 10 Standard Specification for General Concrete calculates the nominal strength by applying the temperature correction value (Tn) based on the compressive strength of the standard cured concrete at 20±2℃ when designing the formulation strength. However, Tn is a correction value that considers only the temperature, and the correction of strength difference due to heat of hydration is not applied. Therefore, in this study, one-component and two-component concrete are mixed in the summer, structural concrete are manufactured, standard concrete specimen are manufactured, and coring is performed on the central and boundary parts of the structural concrete to calculate the correction value applied to the nominal strength by comparing the compressive strength of standard cured concrete on the 28th day of curing and the compressive strength of structural concrete on the 91st day of curing.

• 한국도로학회논문집
• /
• 제19권2호
• /
• pp.67-74
• /
• 2017

PURPOSES : The objective of this study is to ascertain the curing period of cementless cold central plant recycled asphalt base-layer, using mechanical analyses and specimen quality tests on the field. METHODS : Cold central plant recycled asphalt base-layer mixture was produced in the plant from reclaimed asphalt, natural aggregate, filler for the cold mix, and the modified emulsion AP using asphalt mix design and plant mix design. In order to examine the applicability of the curing period during the field test, the international standards for the possibility of core extraction and the degree of compaction and LFWD deflection were analyzed. Moreover, Marshall stability test, porosity test, and indirect tensile strength test were performed on the specimens of asphalt mix and plant mix design. RESULTS : The plant production process and compaction method of cementless cold central plant recycled asphalt base-layer were established, and the applicability of the optical moisture content for producing the mixture was verified through the field test. In addition, it was determined that the core extraction method of the conventional international curing standard was insufficient to ensure performance, and the LFWD test demonstrated that the deflection converges after a two-day curing. However, the back-calculation analysis reveals that a three-day curing is satisfactory, resulting in a general level of performance of dense asphalt base-layer. Moreover, from the result of the specimen quality test of the asphalt mix design and plant mix design according to the curing period, it was determined that the qualities satisfied both domestic and international standards, after a two-day curing. However, it was determined that the strength and stiffness after three-day curing are higher than those after a two-day curing by approximately 3.5 % and 20 %, respectively. CONCLUSIONS:A three-day curing period is proposed for the cementless cold central plant recycled asphalt base-layer; this curing period can be demonstrated to retain the modulus of asphalt-base layer in the field and ensure stable quality characteristics.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1994년도 가을 학술발표회 논문집
• /
• pp.127-132
• /
• 1994

This study attemps to investigate the influence of heat of hydration occured during hardening on the strength development of high strength concrete. The concrete design strengths of 500kg/$\textrm{cm}^2$ and 700kg/$\textrm{cm}^2$ were considered to simulated the square columns having $80\times80cm$ and $100\times100cm$, respectively. Both standard curing and field curing specimen were prepared at the specified ages, and the cores were drilled out from the structure. The thermal sensors were installed into the specimen to measure the heat of hydration process occurred during the hardening. This paper tries to uncover the relationship between the temperature history of the concrete and strength development. The correlation of core strength and specimen strength with curing condition is also discussed. Further research is desired to enlight the relationship between strength and heat of hydration of high strength concrete.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1997년도 봄 학술발표회 논문집
• /
• pp.136-145
• /
• 1997

The purpose of this study is to develope of alternative adimixture for manufacture of PHC pile(compressive strength above 800kg/$\textrm{cm}^2$). For the investigation, properties of alternative admixture admixed with II-anhydrite and pozollanic fine powders(e.q., Fly-ash, Silica-Fume), the fluidity and viscosity in the cement pastes, the fluidity and compressive strength in mortars at steam curing condition, were respectively examined. Also, properties of compressive strength of concretes with exiting admixture(specimen name SM) and alterantive admixture(specimen name AP) for PHC pile, at steam and standard curing condition, were compared each other. As a result of this experimental study, it was found that specimens admixed with II-anhydrite and pozollanic fine powders had an increase on the fluidity of cement paste and mortar, and compressive strength of mortar and concrete was as good as concrete with SM.