• 한국결정성장학회지
• /
• 제7권3호
• /
• pp.377-383
• /
• 1997

이트리아 안정화 지르코니아(Y-TZP)에 5가 산화물$(Ta_2O_5,\;Nb_2O_5)$을 첨가하여 $1500^{\circ}C$온도에서 상압소결한 삼성분계중 quasi-binary system인 $ZrO_2-YTa(Nb)O_4$의 조성영역안에서 상 안정성을 관찰하기 위해 상태도를 작성하였으며, 결정립 크기나 annealing 온도에 상관없이 상 안정성을 유지하는 non-transformable $t-ZrO_2$ solid solution$(NT_{ss}$ )영역을 확인하고 안정화 mechanism을 조사하였다. $NT_{ss}$ 의 상 안정성은 정방정 fergusonite 구조를 갖는 $YTa(Nb)O_4$의 안정화로 상 변태를 억제하여 우수한 상 안정성을 유지하는 것으로 추정되었다. 기계적 특성을 향상시키기 위해 상 변태율이 가장 좋은 transformable-TZP $(T_{ss/})$ 를 에 첨가하여 조사한 결과 mixture의 조성이 $NT_{ss}$ 영역밖의 $NT_{ss}$영역에 위치하여도 상 안정성과 우수한 기계적 특성을 갖는다는 것이 발견되었다.

• 한국재료학회지
• /
• 제30권4호
• /
• pp.176-183
• /
• 2020

The high-temperature stability of YSZ specimens fabricated by die pressure and cold isostatic press (CIP) is investigated in CaCl₂-CaF₂-CaO molten salt at 1,150 ℃. The experimental results are as follows: green density 46.7 % and 50.9 %; sintering density 93.3 % and 99.3 % for die press and CIP, respectively. YSZ foremd by CIP exhibits higher stability than YSZ formed by die press due to denseness dependency after high-temperature stability test. YSZ shows peaks mainly attributed to CaZrO₃, with a small t-ZrO₂ peak, unlike the high-intensity tetragonal-ZrO₂ (t-ZrO₂) peak observed for the asreceived specimen. The t-ZrO₂ phase of YSZ is likely stabilized by Y₂O₃, and the leaching of Y₂O₃ results in phase transformation from t-ZrO₂ to m-ZrO₂. CaZrO₃ likely forms from the reaction between CaO and m-ZrO₂. As the exposure time increases, more CaZrO₃ is observed in the internal region of YSZ, which could be attributed to the inward diffusion of molten salt and outward diffusion of the stabilizer (Y₂O₃) through the pores. This results in greater susceptibility to phase transformation and CaZrO₃ formation. To use SOM anodes for the electroreduction of various metals, YSZ stability must be improved by adjusting the high-density in the forming process.

• 한국결정성장학회지
• /
• 제10권3호
• /
• pp.233-238
• /
• 2000

생체적합성과 상 안정성이 우수한 t-$ZrO_2/Al_2O_3$복합체에 $Eu_2O_3$을 0~4 mol%첨가한 복합체를 $1600^{\circ}C$ 온도에서 1 시간 소결하여 상 안정성, 색상변화, 기계적 특성을 조사하였다. $180^{\circ}C$, 3.5MPa의 수증기 압력 하에서 20시간 열처리 후 X-선 회절법으로 관찰한 결과 $Eu_2O_3$가 첨가된 (Y,Nb,Eu)-TZP/$Al_2O_3$복합체는 우수한 상 안정성이 유지되었다. $Eu_2O_3$의 양이 증가함에 따라 백색계통의 상아색에서 미색의 핑크색으로 서서히 변화하였다 $Eu_2O_3$가 3 mol%까지 첨가된 복합체의 경우 620MPa, 7.6MPa.$m^{1/2}$ 이상의 강도와 인성값이 관찰되었다.

• 한국세라믹학회지
• /
• 제37권4호
• /
• pp.354-358
• /
• 2000

Tetragonal (t)-ZrO2/Al2O3 composites doped with Y2O3, Nb2O5, and Fe2O3 ((Y, Nb, Fe)-TZP/Al2O3) were prepared over the range containing Fe2O3 from 0.1 to 0.5 mol% with 0.1 mol% intervals to evaluate the effect of Fe2O3 addition on chromaticity, hydrothermal stability, and mechanical property of the composites. After autoclaving for 20 h at 18$0^{\circ}C$ under 3.5 MPa water vapor pressure, no tlongrightarrowm phase transformation was observed probably due to the preferential solid solubility of Fe2O3 in Al2O3, the presence of the rigid Al2O3 particles, and the inherent phase stability of (Y, Nb)-TZP. The optimized strength and the fracture toughness of the composite were 700 MPa and 8.5 MPa.m1/2, respectively, when 0.1 mol% Fe2O3 was added. The composites have shown a gradual color change from a slightly white ivory to a pale yellowish brown with increasing the Fe2O3 concentration.

• 한국세라믹학회지
• /
• 제34권6호
• /
• pp.645-651
• /
• 1997

입성장 제어없이 정방정 니르코니아의 파괴인성과 상 안정성을 증진시키기 위해 $Y_{2}O_{3}$와 $Nb_{2}O_{5}$가 첨가된 정방정 지르코니아를 상압소결방법으로 제조하였다. 지르코니아 복합체는 상 안정성이 뛰어난 조성에 상변화가 우수한 조성을 중량비로 혼합 합성하였다. 상변화가 우수한 조성을 15 wt% 첨가한 복합체와 동일한 단일조성의 경우 공기중에 $1500^{\circ}C$ 10시간 소결후 9$MPam^{1/2}$의 파괴인성값과 $220^{\circ}C$에서 $1000^{\circ}C$/까지 100시간이상 agmg을 한 뒤에도 우수한 저온 및 고온 상 안정성이 관찰되었다. 복합체와 상응하는 단일조성은 90.24 mol% $ZrO_2$-5.31 mol% $Y_{2}O_{3}$ mol% $Nb_{2}O_{5}$이었다. 조직관찰 결과 결정립은 소결시간에 따라 증가하였으며 미세균열이나 twinning은 발견되지 않았다.

• 한국세라믹학회지
• /
• 제33권10호
• /
• pp.1177-1185
• /
• 1996

Y-TZP/Ce-TZP ceramics having relative sintered densities of>95% average grain sizes of 0.36$\mu\textrm{m}$ microhar-dness of 1150 kg/mm2 fracture strength of 390-830 MPa and toughness of 6.4-10.2 MPa$.$mm1/2 were prepared by conventional sintering of 3 mol% Y2O3-ZrO2 and 12 mol% CeO2-ZrO2 powders at 1400 and 1500$^{\circ}C$ The average grain sizes of Y-TZP/Ce-TZP ceramics were mainly governed by those of Ce-TZP. White increasing Ce-TZP content toughness increased while microhardness and fracture strength decreased. With comparing microhardness and toughness fracture strength was more sensitive on not only grain size but also other factors such as microstructural and compositional variations. The densification of Y-TZP/Ce-TZP cermaics was not greatly affected by composition and soaking time at temperature over 1400$^{\circ}C$ With increasing CE-TZP content the stability of t-ZrO2 decreased under thermal aging in air whereas increased in hydrothermal atmosphere and aqueous solution.

• 한국세라믹학회지
• /
• 제32권10호
• /
• pp.1147-1161
• /
• 1995

When ceramic membrance was made from metal salt solution in place of metal akoxide solution, crack free and good adhesion to supporter was optimized for sol stability and good adhesion force. A starting sol was prepared from aluminum oxychloride aqueous solutjion in order to inhibit the grain growthof Al2O3 during heat treatment. The crack free dip coating can't be achieved in 1mol/ι zirconium oxychloride solution because of the high viscosity which interferes with the hydration copolymerization between Al3+ ion and Zr4+ ion. Thus Al2O3-ZrO2 sol stability and viscosity for dip coating was effective when 0.01 mol/ι zirconium oxychloride was added. The minimizing of crack and achieving better adhesion to the supporter wa obtained by microwave drying, surfactant addition and ultrasonic dip coating in wet atmosphere. The result seems to minimize the capillary force and improve the adhesive ability to supporter during the process. Where the average pore size of Al2O3-ZrO2 ultrafilter ceramic membrane measured 17 Å by the BET method and observed γ-Al2O3 phase with tetragonal zirconia after firing at 700℃.

• 한국결정성장학회지
• /
• 제11권4호
• /
• pp.170-175
• /
• 2001

It was possible to grow the $Al_{2}O_{3}$ based $Y_{3}A_{5}O_{12}(YAG),ZrO_{2}$ binary and ternary eutectic fibers using micro-pulling down method with a growing rate of 0.1~15 mm/min. While $Al_{2}O_{3}/ZrO_{2}$ showed cellular-lamellar structure, $Al_{2}O_{3}$/YAG and $Al_{2}O_{3}$/YAG/$ZrO_{2}$ternary eutectic fibers showed homogeneous Chinese script lamellar structures. The microstructures of $Al_{2}O_{3}/ZrO_{2}$ binary eutectic fibers changed with solidification rate from lamellar pattern to cellular structure. The interlamellar spacing agreed with the inverse-square-root dependance on pulling rate according to $\lambda$=$kv_p\;{-1/2}$. $Al_{2}O_{3}/ZrO_{2}$ binary eutectic fibers recorded the highest tensile strength of about 1560MPa at room temperature. $Al_2O_3/YAG/ZrO_2$ternary eutectic fiber showed excellent thermal stability to $1200^{\circ}C$ without significant decrease. The maximum strength of ternary eutectic fibers recorded were 1100MPa at $25^{\circ}C$ and 970MPa at $1200^{\circ}C$, respectively.

• 한국재료학회지
• /
• 제23권9호
• /
• pp.531-536
• /
• 2013

This paper investigates the effect of prolonged high temperature exposure on concentric laminated $Al_2O_3-ZrO_2$ composites. An ultrafine scale microstructure with a cellular 7 layer concentric lamination with unidirectional alignment was fabricated by a multi-pass extrusion method. Each laminate in the microstructure was $2-3{\mu}m$ thick. An alternate lamina was composed of 75%$Al_2O_3$-(25%m-$ZrO_2$) and t-$ZrO_2$ ceramics. The composite was sintered at $1500^{\circ}C$ and subjected to $1450^{\circ}C$ temperature for 24 hours to 72 hours. We investigated the effect of long time high temperature exposure on the generation of residual stress and grain growth and their effect on the overall stability of the composites. The residual stress development and its subsequent effect on the microstructure with the edge cracking behavior mechanism were investigated. The residual stress in the concentric laminated microstructure causes extensive micro cracks in the t-$ZrO_2$ layer, despite the very thin laminate thickness. The material properties like Vickers hardness and fracture toughness were measured and evaluated along with the microstructure of the composites with prolonged high temperature exposure.

• 한국세라믹학회:학술대회논문집
• /
• 한국세라믹학회 2000년도 춘계총회,특별강연,심포지움,연구발표회
• /
• pp.48.1-48.1
• /
• 2000