• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2006년도 제37회 하계학술대회 논문집 C
• /
• pp.1432-1433
• /
• 2006

$Li_{2}CO_3$ doped $Ba_{0.5}Sr_{0.5}TiO_3$ ceramics were fabrication by sol-gel method. Sintering temperature must be suited to the LTCC technology. Structure and dielectric properties were investigated for effect of $Li_{2}CO_3$ dopants at BST. Structure of $Li_{2}CO_3$ doped $Ba_{0.5}Sr_{0.5}TiO_3$ ceramics were dense and homogeneous with almost no pore. Relative permittivity was decreased and dielectric loss was increased with increasing $Li_{2}CO_3$ doping rations. In the case of the 3wt% $Li_{2}CO_3$ doped $Ba_{0.5}Sr_{0.5}TiO_3$ ceramics sintered at $900^{\circ}C$, relative permittivity and dielectric loss were 907 and 0.003 at 100 kHz.

• 소성∙가공
• /
• 제12권5호
• /
• pp.493-497
• /
• 2003

The present investigation aims at visualizing the crack tip stress field using a mechanoluminescence material. The well known compound $SrAl_2O_4$:$Eu^{2+}$ was adopted as a mechanolurninescence material. Two more trivalent rare-earth elements such as Dy and Nd were taken into consideration as codopants to provide the appropriate trap levels. Samples of a variety of compositions were prepared by varing $Eu^{2+}$, $Dy^{3+}$, and $Nd^{3+}$ doping contents, for which the combinatorial chemistry method was used. In order to search for the optimum composition for the highest mechanoluminescence, the luminescence induced by a compressive device including a CCD camera. In parallel, a compact tension specimen was prepared by mixing the luminescence powders of optimum composition and epoxy resin. Crack initiation from the mechanically machined sharp note tip and its growth during loading were found to be associated with the extent of light emission from $SrAl_2O_4$.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2008년도 Techno-Fair 및 추계학술대회 논문집 전기물성,응용부문
• /
• pp.173-174
• /
• 2008

페로브스카이트 구조의 (Ba,Sr,Ca)$TiO_3$ 분말에 $Dy_2O_3$ 불순물을 첨가하여 첨가량에 따른 영향을 연구하였다. 시편의 제작은 Screen-printing을 이용하여 후막으로 제작하였으며, 구조적인 특성과 전기적인 특성을 관찰하였다. XRD 회절 분석을 통하여 $Dy_2O_3$가 첨가된 모든 시편에서 이차상이 없는 전형적인 페로브스카이트 구조를 나타내었다. 시편의 미세구조를 관찰한 결과 grain size는 $Dy_2O_3$ 첨가량이 증가 할수록 감소하였으며, 기공은 증가하는 것을 알 수 있었다. 후막의 두께는 $Dy_2O_3$ 첨가량에 영향을 받지 않았으며 평균 두께는 $69{\mu}m$이었다. 큐리 온도는 $Dy_2O_3$ 첨가량에 따라 감소하였으며, 유전 손실은 상온 이상에서 1%이하로 크게 감소하였다.

• 전기학회논문지
• /
• 제59권2호
• /
• pp.352-354
• /
• 2010

The effects of Au addition on the structure and the superconducting properties of Bi system bulk have been investigated. Au exists in the metalic form in above materials. It does not affect the formation and structure of the BiSrCaCuO(2223) phase. The superconducting transition temperature Tc does not change for $Bi_{1.7}Pb_{0.3}Sr_2Ca_2Cu_3O$ composite However Au doping can make the grains smaller. Metallic Au can make gathers on the grains boundary and lead to the increment of critical transport current density. The current density of $Bi_{1.7}Pb_{0.3}Sr_2Ca_2Cu_3Au_{0.5}O$ was 1000A/$cm^2$ at liquid nitrogen temperature.

• 한국초전도ㆍ저온공학회논문지
• /
• 제25권4호
• /
• pp.14-18
• /
• 2023

We have investigated the behavior induced by Ga substitution in B-1212 system and observed an anomalous superconductor-like resistivity drop with an onset near 260 K and an offset at 248 K in the nominal (B_0.65Ga_0.35)(Ba_1.25Sr_0.75)(Er_0.5Ca_0.5)Cu₂O_z compound. However, this property degraded with repeated cycling. Systematic studies of the superconducting properties of the (B_1-xGa_x)(Ba_1.25Sr_0.75)(Er_0.5Ca_0.5)Cu₂O_z compounds are reported and discussed in the context of the anomalous resistivity transition.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2002년도 춘계학술대회 논문집 유기절연재료 전자세라믹 방전플라즈마 일렉트렛트 및 응용기술
• /
• pp.79-82
• /
• 2002

$(Ba_{0.6-x}Sr_{0.4}Ca_x)TiO_3$ + ywt% MgO (x=0.10, 0.15, 0.20, y=0.0~3.0) ceramics were fabricated by the conventional solid-state reaction, and their structural and dielectric properties were investigated with variation of composition ratio and MgO doping content. A second phase, representative of MgO, appears in 3wt% MgO-doped BSCT specimens. Average grain sizes decreased with increasing amounts of MgO, and the BSCT(40/40/20) specimens doped with 3wt% MgO showed a value of $9.3{\mu}m$. The Curie temperature and relative dielectric constant at room temperature were decreased with increasing MgO doping content and Ca composition ratio. The relative dielectric constant was non-linearly decreased as the field strength is increased. The tunability was increased with decreasing a Ca content and the BSCT(50/40/10) specimen doped with 1.0wt% MgO content showed the highest value of 6.4% at 5kV/cm.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2002년도 추계학술대회 논문집 Vol.15
• /
• pp.43-46
• /
• 2002

Ferroelectric Mg-doped SBT and Ti-doped SBT were successfully deposited on Pt/Ti/$SiO_2/Si$ substrate by using a sol-gel solution coating method. The solutions were prepared through out adding the metal alkoxide solutions to SBT solution. The typical hysteresis loop of the films was obtained at 5V. The measured $2P_r$ value were $16.50{\mu}C/cm^2$ for SBT, $18.98{\mu}C/cm^2$ and for Mg-doped SBT, and $17.10{\mu}C/cm^2$ for Ti-doped SBT at an applied voltage of 5V, respectively. And it is found that the leakage current densities are less than $10^{-7}A/cm^2$ when applied voltage is less than 10.8MV/cm, which indicates the excellent insulating characteristics.

• 한국재료학회지
• /
• 제23권12호
• /
• pp.727-731
• /
• 2013

In this study, green barium strontium silicate phosphor ($BaSrSiO_4:Eu^{3+}$, $Eu^{2+}$) was synthesized using a solid-state reaction method in air and reducing atmosphere. Investigation of the firing temperature indicates that a single phase of $BaSrSiO_4$ is formed when the firing temperature is higher than $1400^{\circ}C$. The effect of firing temperature and doping concentration on luminescent properties are investigated. The light-emitting property was the best when the molar content of $Eu_2O_3$ was 0.025 mol. Also, the luminescent brightness of the $BaSrSiO_4$ fluorescent substance was the best when the particle size of the barium was $0.5{\mu}m$. $BaSrSiO_4$ phosphors exhibit the typical green luminescent properties of $Eu^{3+}$ and $Eu^{2+}$. The characteristics of the synthesized $BaSrSiO_4:Eu^{3+}$, $Eu^{2+}$ phosphor were investigated using X-ray diffraction (XRD) and scanning electron microscopy. The maximum emission band of the $BaSrSiO_4:Eu^{3+}$, $Eu^{2+}$ was 520 nm.

• 한국세라믹학회지
• /
• 제34권8호
• /
• pp.803-810
• /
• 1997

Ba0.5Sr0.5TiO3박막을 RF 마그네트론 스퍼터링법을 이용하여 Pt/Ti/SiO2/Si(100) 기판에 증착하였다 .누설전류에 영향을 주는 것으로 알려진 열처리 조건, dopant 효과 등을 평가하고자 이온반경이Ti와 유사하고 대부분이 Ti 자리를 치환하는 것으로 알려진 Nb와 Al을 각각 danor와 acceptor로 선택하여 BST 박막에 첨가한 후 누설전류를 측정하였다. 고온에서 in-situ 증착된 BST 박막은 거친 표면 형상을 보이며 낮은 전압에서 파괴가 발생하고, Nb 첨가로 누설전류가 증가하였다. 삼온 증착후 후열처리된 박막은 표면 형상도 평할도가 증가하였으며 in-situ로 제조된 박막에 비해 높은 파괴전압과 낮은 누설전류를 나타내었다. 특히 Al이 첨가된 BST 박막의 누설전류밀도는 ~10A/cm2로 도핑을 하지 않은 박막이나 Nb가 첨가된 박막에 비해 매우 낮은 누설전류밀도를 나타내었으며, 이는 산화로 인한 산소공공의 감소, 이동 가능한 hole의 감소와 후열처리과정중 계면 및 입계의 산화로 Schottky 장벽에 높아진 결과로 판단된다.

• Journal of Magnetics
• /
• 제18권4호
• /
• pp.386-390
• /
• 2013

This paper studies the effects of A-site substitution by barium on the magnetic and magnetocaloric properties of $Pr_{0.5}Sr_{0.5-x}Ba_{x}MnO_{3}$ (x = 0, 0.04, 0.08 and 0.1). The tetragonal crystal structures of the samples are confirmed by room temperature X-ray diffraction. The dependence of the Curie temperature ($T_C$) and the magnetic entropy change (${\Delta}S_M$) on the Ba doping content has been investigated. The samples of all doping contents undergo the second order phase transition. As the concentration of Ba increased, the maximum entropy change ($|{\Delta}S_M|_{max}$) increased gradually, from 1.15 J $kg^{-1}$ $K^{-1}$ (x = 0) to 1.36 J $kg^{-1}$ $K^{-1}$ (x = 0.1), in a magnetic field change of 1.5 T. The measured value of $T_C$ is 265 K, 275 K, 260 K and 250 K for x = 0, 0.04, 0.08 and 0.1, respectively. If combining these samples for magnetic refrigeration, the temperature range of ~220 K and 290 K, where |${\Delta}S_M$|max is stable at ~1.27 J $kg^{-1}$ $K^{-1}$ and RCP = 88.9 $J{\cdot}kg^{-1}$ for ${\Delta}H$ = 1.5 T. $Pr_{0.5}Sr_{0.5-x}Ba_{x}MnO_{3}$ compounds, are expected to be suitable for magnetic-refrigeration application due to these magnetic properties.