• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.7 no.5
• /
• pp.771-777
• /
• 2006

Recently regulations which make it mandatory to use the environment-friendly goods are increaing in automobiles. In this study the TIG autogenous welding process was developed by solving the problem of previous spot welding of side part and the ceramic protection Jig was developed for the welding of fragile glass ball. And the optimal process parameter was selected by complementing the demerit of the previous filler material welding to fill up the bottom part. Finally the lamp aging test and earthquake resistant test was done to check the reliability of welded brake lamp.

• Journal of Welding and Joining
• /
• v.30 no.2
• /
• pp.59-64
• /
• 2012

Welding is an essential process in the automotive industry. Most welding processes that are used for auto body are spot welding and $CO_2$ welding are used in a small part. In production field, $CO_2$ welding process is decreased and spot welding process is increased due to welding quality is poor and defects are occurred in $CO_2$ welding process frequently. But $CO_2$ welding process should be used at robot interference parts and closed parts where spot welding couldn't. Because of the 0.65mm ~ 2.0mm thickness steel sheet were used in the automotive industry, poor quality of welding area such as burn through and under fill were happened frequently in $CO_2$ process. In this paper, we will study about the penetration depth which gives a huge impact on burn through changing a degree of base metal, welding position and torch angle. Voltage, current and welding speed were fixed but degree of base metal, welding position and torch angle were changed. And Cold- Rolled(CR) steel sheet was used. Penetration depth was analysed by multiple regression analysis to derive approximate calculations. And reliability of approximate calculations were confirmed through additional experiments. As the results of this research, we confirmed the effect of torch and plate angle to bead shape. And we present a possibility that can simulate more accurate to weld geometry, as deduced the verification equations that has tolerance of less than 21.69%.

• Journal of Mechanical Science and Technology
• /
• v.17 no.8
• /
• pp.1113-1119
• /
• 2003

Experimental and numerical analyses were performed to characterize the fatigue behavior of spot welded joints in suspension mounting of a passenger car body. Static and fatigue tests were carried out for the tensile-shear and cross-tension specimens. S-N curve and fatigue strengths were obtained from the fatigue test of various specimens. Nonlinear finite element analysis showed that fatigue behavior of spot welded joints could be well estimated in terms of Von Mises stress at the nugget edge. Fatigue behavior of spot welded joint was represented by Von Mises stress better than the fatigue load.

• Laser Solutions
• /
• v.13 no.4
• /
• pp.14-20
• /
• 2010

Robot path generation and laser welding technology for manufacturing automotive body are studied. Laser welding and industrial robot systems are used with the robot based laser welding system. The laser system used in this study is 1.6kW Fiber laser, while the robot system is 6 axes Industrial robot (payload: 130kg). The robot based laser welding system is equipped with laser scanner system for remote laser welding. The laser source, robot and laser scanner system are used to increase the processing speed and to improve the process efficiency. The welding joints of steel plate are butt and lapped joints. The quality test of the laser welding are through the observation the shape of bead on plate and cross-section of welding part. The 3 dimensional laser welding for non-linear pipe welding line is performed. This paper introduces the robot based laser welding system to resolve the limited welding speed and accuracy of the conventional spot welding system.

• Journal of the Korean institute of surface engineering
• /
• v.30 no.1
• /
• pp.13-22
• /
• 1997

In order to investigate the effects of microstructure Oil film on the welding spatter in Zn electroplated steel, Zn electroplated surface and layer structure with USS-Paddition was observed using XRD, XPS and optical microscopy. Wettability of water drop on the Zn electroplated steel surface was measured using Z.Mei model. Oil absorption test was carried out using Oil pen. Morphology of spot welding and spatter with USS-P addition, applied current, and oil-spray or oil-without was observed using SEM and optical microscopy. Surface morphology of Zn electroplated steel showed finer structure as USS-P content increased. Wettabiliy on the Zn electroplated surface decreased with increasing USS-P content. Size of welding trace increased and spatter occured arround the welding part as applied current increased, whereas spatter disappeared as USS-P content increased and disappeared in case of oil spraying on the Zn electroplated surface.

• Journal of Welding and Joining
• /
• v.27 no.4
• /
• pp.73-78
• /
• 2009

Characterization of the microweld CCFL electrode for the TFT-LCD backlight unit was carried out in terms of the glass beading heat treatment conditions. We evaluate the weld zone and parent metal of the microweld CCFL electrodes that were exposed to simulated glass beading heat treatment. The CCFL electrode was composed of the cup made with pure Ni, the pin made with pure Mo and the lead wire made with Ni-Mn alloy. Each part of the electrode was assembled together by micro spot welding process and then the assembled electrodes were exposed to simulated glass beading temperatures of $700^{\circ}C,\;750^{\circ}C$ and $800^{\circ}C$. The microstructures of the microweld CCFL electrode were observed by using optical microscope, scanning electron microscope and EDS. Micro-tensile and microhardness test were also carried out. The results indicated that the grain coarsening in the HAZs(heat affected zones) for both the cup-pin weld and pin-lead wire were exhibited and the grain coarsening of the HAZ for the cup and the lead wire was more obvious than the HAZ of the pin. The micro-tensile test revealed that the fracture occurred at the cup-pin weld zone for all test conditions. The fracture surface could be classified into two parts such as pin portion and cup portion including weld nugget. The failure was seemed to be initiated from the boundary between nugget and pin through the weld joint. The result of the microhardness measurement exhibited that the relatively low hardness value, about 105HV was recorded at the HAZ of the cup. This value was about 50% less than that of the original value of the cup. The reduction of the microhardness was considered as the cause of the grain coarsening due to welding process. It was also appeared that there was no change in electric resistance for the standard electrodes and heat treated electrodes.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.15 no.11
• /
• pp.6432-6439
• /
• 2014

The NAUT (Non-contact Air coupled Ultrasonic Testing) technique is one of the ultrasonic testing methods that enables non-contact ultrasonic testing by compensating for the energy loss caused by the difference in acoustic impedance of air with an ultrasonic pulser receiver, PRE-AMP and high-sensitivity transducer. As the NAUT is performed in a state of steady ultrasonic transmission and reception, testing can be performed on materials of high or low temperatures or specimens with a rough surface or narrow part, which could not have been tested using the conventional contact-type testing technique. For this study, the internal defects of spot weld, which are often applied to auto parts, and CFRP parts, were tested to determine if it is practical to make the NAUT technique commercial. As the spot welded part had a high ultrasonic transmissivity, the result was shown as red. On the other hand, the part with an internal defect had a layer of air and low transmissivity, which was shown as blue. In addition, depending on the PRF (Pulse Repetition Frequency), an important factor that determines the measurement speed, the color sharpness showed differences. With the images obtained from CFRP specimens or an imaging device, it was possible to identify the shape, size and position of the internal defect within a short period of time. In this paper, it was confirmed in the above-described experiment that both internal defect detection and image processing of the defect could be possible using the NAUT technique. Moreover, it was possible to apply NAUT to the detection of internal defects in the spot welded parts or in CFRP parts, and commercialize its practical application to various fields.

• Korean Journal of Metals and Materials
• /
• v.46 no.10
• /
• pp.672-682
• /
• 2008

The resistance spot welding of TRIP590 steels was investigated to enhance understanding of weld fracture during tensile-shear strength (TSS) test. The main failure modes for spot welds of TRIP590 steels were nugget pullout and interfacial fracture. The peak load to cause a weld interfacial failure was found to be related to fracture toughness of the weld and the weld diameter. Although interfacial fracture occurred in the samples, the load carrying capacity of the weld was high and not significantly affected by the fracture mode. Substantial part of the weld exhibits the characteristic dimple (or elongated dimple) fractures on interfacial fractured surface, in spite of the high hardness values associated with the martensite microstructures. The high load-bearing ability of the weld is directly associated with the area of ductile fracture occurred in weld. Therefore, the judgment of the quality of resistance spot welds in TRIP590 steels, the load carrying capacity of the weld should be considered as an important factor than fracture mode.

• Journal of Ocean Engineering and Technology
• /
• v.35 no.2
• /
• pp.161-171
• /
• 2021

For the fatigue design of offshore structures, it is essential to understand and use the S-N curves specified in various industry standards and codes. This study compared the characteristics of the S-N curves for five major codes. The codes reviewed in this paper were DNV Classification Rules (DNV GL, 2016), ABS Classification Rules (ABS, 2003), British Standards (BSI, 2015), International Welding Association Standards (IIW, 2008), and European Standards (BSI, 2005). Types of stress, such as nominal stress, hot-spot stress, and effective notch stress, were analyzed according to the code. The basic shape of the S-N curve for each code was analyzed. A review of the survival probability of the basic design S-N curve for each code was performed. Finally, the impact on the conservatism of the design was analyzed by comparing the S-N curves of three grades D, E, and F by the five codes. The results presented in this paper are considered to be a good guideline for the fatigue design of offshore structures because the S-N curves of the five most-used codes were analyzed in depth.

• Journal of Welding and Joining
• /
• v.30 no.6
• /
• pp.113-119
• /
• 2012

Ultrasonic bonding is the novel packaging method for flip-chip with high yield and low-temperature bonding. The bonding module is a core part of the bonding machine, which can transfer the ultrasonic energy into the bonding spot. In this paper, we propose topology optimization technique which can make new design of boding modules due to the constraints on resonance frequency and mode shapes. The designed bonding module using topology optimization was fabricated in order to evaluate the bonding performance and reliable operation during the continuous bonding process. The actual production models based on the proposed design satisfied the target frequency range and ultrasonic power. The bonding test was performed using flip-chip with lead-free Sn-based bumps, the results confirmed that the bonding strength was sufficient with the designed bonding modules. Also the performance degradation of the bonding module was not observed after the 300-hour continuous process with bonding conditions.