• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2002.05a
• /
• pp.47-50
• /
• 2002

This paper presents the results of fire resistance properties of high performance concrete varying with fiber kinds and the size of metal lath in order to verify the validities of fiber on the spatting resistance by fire. Metal lath, glass fiber and carbon fiber are used to confine the concrete. According to test results, plain concrete without lateral confinement and confined concrete with glass fiber and carbon fiber show entire failure after exposed to fire, while confined concrete with metal lath take place in the form of slight surface spatting by fire, which has favorable spatting resistance of concrete. As for the effect of the size of metal lath, when the size of metal lath is more than 1.2mm of thickness, the residual strength of concrete exposed to fire maintains more than 80% of its original strength. However, glass fiber and carbon fiber does not perform desirable spatting resistance by fire due to loss of lateral confinement of fiber exposed to fire caused by melting of fiber and reducing bond strength between concrete and fiber.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2005.11a
• /
• pp.7-10
• /
• 2005

This paper is about manufacture of spalling resistance concrete and also investigates the spalling mechanism and spalling resistance method with diverse materials, mixture proportion and lateral confinement. The present work with the basic experiment achieved successful method for spatting resistance using both proper amounts of fiber contents and lateral confinement using metal lath. Moreover, the developed spatting resistance method was applied for full sized column construction in the Doosan We've Poseidon I field, located in Busan city. The author investigated the physical properties examining workability, placeability and pumpability. These studies are continuously processing to develop new technology expecting remarkable impact on the spatting resistance and fire resistance performance of high-raise building construction in the future.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2005.05a
• /
• pp.37-40
• /
• 2005

High Performance Concrete(HPC) has been widely used in high-rise building. The HPC has several benefits including high strength, high fluidity and high durability. However. spatting is susceptible to occur in HPC and HPC also tends to be deteriorated in the side of fire resistance performance at fire. This paper focuses on the analysis of the temperature history and residual compressive strength with finishing material, in order to protect HPC from sudden-high-temperature, which is one of the main reason spatting occurs. Test results show that spalling occurs in all specimens. The most serious spalling took placed in HPC covering fire enduring spray-on material, whose covering thickness is 20mm but temperature history indicates that fire enduring spray effectively protected HPC from fire for more than 2hours. In addition, residual compressive strength ratio of HPC using fire enduring paint was more than $90\%$ of original strength, thus minimizing spatting and indicating significant fire resistance performance.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2001.05a
• /
• pp.463-468
• /
• 2001

A lot of considerations on the spatting by fire of high performance concrete should be taken into for fire resistance of the concrete structures. In this paper, fire resistance of high performance concrete is described using polypropylene fiber, which is known to be contributed to fire resistance. Strength level and member size are varied with. According to test results, spatting by fire takes place more easily, as W/C increases and member size decreases. It shows that concrete containing polypropylene fiber has good effects on preventing spatting by fire. In case high performance concrete does not contain polypropylene fiber, residual strength shows to be decreased remarkably compared :o that of normal concrete. Whereas, in case 0.1% of polypropylene fiber contents, high performance concrete shows higher residual strength than that of normal concrete. As member size is smaller, residual strength shows to be decreased.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2002.05a
• /
• pp.557-562
• /
• 2002

This paper describes the results of spalling by fire prevention of high performance concrete confining with metal-lath and containing PP fiber. According to test results, all the specimens without PP fiber shows entire failure after exposed to fire, while the other specimens confined with metal-lath has somewhat better spatting prevention performance than plain concrete specimens, which only show surface scale spatting combination of PP fiber with confinement of metal-lath leads to favorable spatting resistance. As PP fiber contents and thickness of metal-lath which is confined at concrete specimens increase, residual strength after exposed to fire shows to be increased.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2006.05a
• /
• pp.5-8
• /
• 2006

High strength concrete has been increasingly used in high rue building and it is very obvious re consider fire resistance performance of that. Unlike the normal strength concrete, high strength concrete in sudden elevating temperature at fire is susceptible to spalling with severe explosion and surface split, due to high density of concrete. In order to endure the spalling, inner space temperature of concrete should be control less than certain point. Therefore this study investigated the influence of covering materials on high strength concrete finishing spray-on materials of fiber composite spray mortar(FCSM). Both polypropylene(PP) and polyvinyl alcohol(PVA) fiber were used in this test. Test showed that concrete, covering 18mm mortar containing PVA fiber and confining metal lath 2.3mm thickness, decreased 50% of main bar ambient temperature. compared with control concrete. In addition, concrete covering 18mm mortar without fiber caused falling of covering materials and then it was exposed in elevating temperature. As a result, spatting of the concrete occurred same as control concrete. However, concrete covering spray-on mortar containing PVA or PP fiber resisted spatting occurrence.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2007.04a
• /
• pp.63-66
• /
• 2007

This study investigates the fire resistance properties of high strength concrete, around 60MPa class, designed with various admixture types and fiber content. Test showed that the increase of fiber content decreased the fluidity and slightly inclined the air content of fresh concrete. However, the fiber content in concrete did not affect the compressive strength. For the addition of admixture, specimens adding the shrinkage-reducing-agent (SR) indicated the strength value at 70MPa, which is followed by incorporating silica fume (SF) at 66MPa, the combination of expansive admixture (EA) and SR at 63MPa, only EA at 59MPa, blast furnace slag (BS) at 58MPa and fly ash (FA) at 50MPa in an order. After completing the fire test, all specimens adding 0.05vol.% of polypropylene fiber exhibited protection of spatting, except for the specimens incorporating loft of SF and incorporating 20% of SF with only SR and the combination of EP and SRA, respectively. Therefore the most effective result of this study was shown in the specimens incorporating love of FA and 30% of BS and incorporating 20% of SF with 5 % of EA. It is expected that this test results will be crucial references in near future to develope the spatting resistance method of high strength concrete.

• Proceedings of the Korea Institute of Fire Science and Engineering Conference
• /
• 2006.04a
• /
• pp.172-175
• /
• 2006

Recently, fire resistance of high performance concrete for explosive spatting was issued as high performance concrete was vulnerable to the explosive spatting in initial fire. Therefore, This study is willing to propose fundamental data for quick and accurate diagnosis of deteriorated concrete structure by fire damage with making variable concrete test specimen, exposing high temperature environment, observing the explosive spatting and examining engineering property.

• Fire Science and Engineering
• /
• v.21 no.2 s.66
• /
• pp.54-63
• /
• 2007

Concrete is generally accepted to have good inherent fire resistance. It mainly relies on the assumption that concrete has low heat-transfer characteristic and spatting does not occur during the course of a fire. However, the significant numbers of fire accidents have shown in recent years that incidence of spatting has caused sever damages to many structures. This review has systematically investigated the behaviour of concrete in fire, including phenomenon of spatting, with respect to the theorical consideration and experimental results. Explosive spatting is caused by the build-up of water vapor pressure in concrete subjected to increasing temperatures. When this pressure exceeds the tensile strength of the concrete over a fire-exposed area, explosive spatting can result in a typical temperature range between $200^{\circ}C\;and\;400^{\circ}C$. The major functions are known to be moisture content, pore pressure, load ratio, and heating regime.

• Journal of the Korea Institute of Building Construction
• /
• v.8 no.5
• /
• pp.101-107
• /
• 2008

This study investigated fundamental characters of the concrete according to various fiber types and contents and their properties of spatting resistance and residual compressive strength after fire test corresponding to ISO and RABT heating corves. The results were summarized as following. The Flowability was gradually declined as the increase of fiber contents, and it was the most favorable with nylon(NY) fibers. The decrease of air contents due to increasing fiber contents was in order by polypropylene(PP), polyvinyl alcohol(PVA) and NY fibers. The compressive strengths were over 40 MPa at 7 days and 50 MPa at 28 days. It was in order by PVA, PP and NY fibers. For the spatting properties, all specimens were prevented at ISO heating curve. In the other hand, the partial spatting at the surface occurred on the plain without fibers, but it was prevented over 0.10 % of PVA and 0.05 % of PP and NY fibers at the RABT heating curve.