• 대한전기학회논문지
• /
• 제44권7호
• /
• pp.914-918
• /
• 1995

In this study, Pb(Zr$_{x}$ Ti$_{1-x}$ )O$_{3}$ (x=0.65, 0.52, 0.35) thin films were fabricated by Sol-Gel method. A stock solution with excess Pb 10[mol%] of Pb(Zr$_{x}$ Ti$_{1-x}$ )O$_{3}$ was made and spin-coated on the Pt/SiO$_{2}$/Si substrate at 4000[rpm] for 30[sec.]. Coated specimens were dried on the hot-plate at 400[.deg. C] for 10[min.]. Sintering temperature and time were 500~800[.deg. C] and 1~60[min.]. The coating process was repeated 6 times and the final thickness of the thin films were about 4800[A]. To investigate crystallization condition, PZT thin films were analyzed with sintering temperature, time and composition by the XRD. The microstructure of thin fulms were investigated by SEM. The ferroelectric perovskite phases precipitated under the sintering of 700[.deg. C] for 1 hours. In the PZT(52/48) composition, dielectric constant and dielectric loss were 2133, 2.2[%] at room temperature, respectively.ively.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2003년도 춘계학술대회 논문집 디스플레이 광소자분야
• /
• pp.155-159
• /
• 2003

The preparation and luminescence characterization of yttrium oxide doped with trivalent europium phosphors by sol-gel method have been investigated. Aqueous metal nitrate solution was mixed with EDTA which was chosen by the most suitable material of sol-gel formation one of appled various chelating agents. we noticed that the samples when are heated with EDTA at a temperature of $100^{\circ}C$ for 1hrs, produced brownish and crisp powders due to condensation reaction on decomposition, dehydration and formation of sol-gel. Hence, when the powder pre-heated was then heated at $1200^{\circ}C$ for 3hrs in atmosphere, the luminescence characterization of resultant $Y_{2}O_{3}:Eu^{3+}$ phosphor was enhanced upto maximum 30% significantly than conventional method through increasing porous region and decreasing particle sizes.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2003년도 춘계학술대회 논문집 디스플레이 광소자분야
• /
• pp.151-154
• /
• 2003

The synthesis and luminescent properties of trivalent europium activated gadolinium oxide red phosphors by sol-gel process have been investigated. Aqueous metal nitrate solution was mixed with EDTA which was chosen by the most suitable material of sol-gel formation as chelating agents. We noticed that the samples when are heated with EDTA at a temperature of $100^{\circ}C$ for lhrs, produced brownish and crisp powders due to condensation reaction on decomposition, dehydration and formation of sol-gel. Hence, when the powder pre-heated at about $100^{\circ}C$ was then heated at $1200^{\circ}C$ for 3hrs in atmosphere, the luminescence properties of resultant $Gd_{2}O_{3}:Eu^{3+}$ phosphor was measured by SEM, FT-IT and brightness intensity was shown 20% higher than those prepared by conventional method and by other chelating agent.

• 한국전기전자재료학회논문지
• /
• 제28권12호
• /
• pp.821-825
• /
• 2015

Anti-reflective (AR) thin film was fabricated on a glass substrate by sol-gel method. The coating solution was synthesized with TEOS (tetraethlyorthosilicate) and poly ethylene glycol (PEG, 4.0 wt%). As the withdrawal speed of coating was changed from 0.1 mm/sec to 0.3 mm/sec, the thickness and refractive index of prepared thin films were changed. The reflectance and transmittance of coating glass fabricated by the withdrawal speed of 0.1 mm/sec were 0.62% and 95.0% in visible light range. The refractive index and thickness of single layer thin film were n= 1.29 and ca. 99.0 nm.

• Current Photovoltaic Research
• /
• 제2권3호
• /
• pp.110-114
• /
• 2014

We propose a low temperature sol-gel ZnO/Ag nanowire composite thin film to fulfill low temperature and low cost requirements, which are essential criteria in future flexible electronic devices. In this proposed thin film, Ag nanowire plays the role of electrical conduction, and sol-gel ZnO provides a structural medium with a high visible transmittance. Low temperature restriction in the sol-gel fabrication process prevents sufficient oxidation of Zn acetate precursors, which were solved by a post-coating treatment with ultraviolet light irradiation. Composite thin film formation was performed by spin coating methods with a mixed precursor solution or in a sequential manner. We obtained an average visible transmittance larger than 85% and a sheet resistance smaller than $50{\Omega}/sq$. After optimization in a fabricated composite transparent conductive thin film with the thickness around 100 nm. Similar experimental demonstration in a flexible substrate (polyethyleneterephthalate) was successful, which implies a promising application opportunity of this technology.

• 한국안전학회지
• /
• 제16권3호
• /
• pp.76-82
• /
• 2001

An aqueous solution of a commercial liquid synthetic detergent for kitchen use was photodecomposed in the presence of titanium dioxides ponder under an atmosphere of air at room temperature. Titanium dioxides were prepared by sol-gel method from titanium iso-propoxide at different R R ratio($H_2O$/titanium iso-propoxide) and calcined at $500^{\circ}C$. All titanium dioxides m characterized by XRD, BET surface area analyzer and UV-VIS spectrometer. The surface mea of titanium dioxides prepared at R ratio=6 appeared higher volume about 20% than commercial $TiO_2$ catalyses. XRD patterns of titania particles were observed mixing phase together with rutile and anatase type. Titanium dioxides prepared by sol-gel method show higher activity about 6% than commercial $TiO_2$ catalysts on the Photocatalytic foundation of a commercial liquid synthetic detergent for kitchen. The concentration of the detergent decreased to about 90%, of its initial value at illumination times of 2 hour. illumination for 30 minutes decreased the concentration of oxygen to about one-fifth of the initial value.

• 한국전기전자재료학회논문지
• /
• 제11권9호
• /
• pp.711-717
• /
• 1998

BST(70/30) and BST(50/50) thin films were prepared by Sol-Gel method and studied about the microstructural and dielectric properties with Pt and ITO bottom electrodes. The stock solution was synthesized and spin coated on the Pt/Ti$SiO_2$/Si and Indium Tin Oxide(ITO)/ glass substrate. the coated films were dries at 350$^{\circ}C$ for 10 minutes and annealed at $750^{\circ}C$ for 1 hour for the crystallization. The thin films coated on ITO substrate were crystallized easily and the packing density and roughness of surface were better that those of films coated on Pt substrates. In the BST(50/50) composition the structural properties were similar to the BST(70/30) composition and grain size were decreased with increasing the contents of Sr. The dielectric constant was higher in the BST(50/50) composition compared with the BST(70/30) composition. Using the ITO substrate, the dielectric constant was higher than the Pt substrate while the dielectric loss was showed a reverse trend. The dielectric constant with and increase of temperature was decreased slowly.

• E2M - 전기 전자와 첨단 소재
• /
• 제10권6호
• /
• pp.541-547
• /
• 1997

(Pb$_{1-x}$ La$_{x}$)Ti$_{1-x}$ $_4$O$_3$(x=0, 0.02, 0.04, 0.08) ceramic thin films were fabricated by Sol-Gel method. A stock solution of (Pb, La)TiO$_3$ with excess Pb 10 mol% was made and spin-coated on the Pt/Ti/SiO$_2$/Si substrate at 400rpm for 30 seconds. Coated specimens were dried on the hot-plate at 35$0^{\circ}C$ for 10 min and sintered at 500~75$0^{\circ}C$ for 1 hour. The dielectric constant, remanent polarization and coercive field of the PLT(6at.%) thin films sintered at $650^{\circ}C$ were 884, 13.95$\mu$C/$\textrm{cm}^2$ and 8.7kV/cm, respectively. Pyroelectric coefficient, figure of merit of pyroelectric current, voltage responsivity and detectivity of PLT(6at.%) thin films were 3.2$\times$10$^{-8}$ C/$\textrm{cm}^2$K, 1.02$\times$10$^{-8}$ C.cm/J, 2.9 $\times$10$^{-11}$ C.cm/J, 0.29$\times$10$^{-8}$ C.cm/J, respectively.ely.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2004년도 하계학술대회 논문집 Vol.5 No.2
• /
• pp.809-812
• /
• 2004

(Pb,Sr)TiO3 (PST) thin films were fabricated by using the alkoxide-based sol-gel method. The PST stock solution was made and then spin-coated onto a PUTi/SiO2/Si substrate. The coating and drying procedures were repeated several times, and the PST thin films were sintered at 450-650 C for 1 h. All PST thin films showed dense and homogeneous structures without the presence of any rosette structure. The thicknesses of the PST thin films were approximately 200 nm. The dielectric constant and the dielectric loss of the PST thin films sintered at 550 C were about 404 and 0.0023, respectively. The leakage current density of the PST thin film sintered at 550 C was 3.13 x 10-8 A/cm2 at 1 V.

• 한국환경과학회지
• /
• 제12권4호
• /
• pp.481-485
• /
• 2003

Two types of polyimide/silica composite films were prepared using sol-gel method through hydrolysis and polycondensation of tetraethoxysilane (TEOS) with the polyamic acid (PAA) and end-capped PAA solution. Samples were characterized by the means of differential thermogravimetry, X-ray diffractometry, scanning electron microscopy, universal test, impedance analyzer, chemical resistance test, etc. All of the PAA/silanol solutions heat-treated at 300$^{\circ}C$ for 6h were transformed to polyimide/silica composites. It has been demonstrated that the properties of polyimide/silica composites were affected by the amount of silica addition and the bend type existed between polyimide and silica.