• Journal of the Korea institute for structural maintenance and inspection
• /
• v.18 no.2
• /
• pp.117-125
• /
• 2014

This paper examines the fundamental properties of alkali-activated slag cement (AASC) activated by sodium hydroxide (NaOH). The water to binder (W/B) ratio was 0.4 and 0.5. And concentration of activator were 2M and 4M. Five mix design of each W/B ratios was considered. The N0 mixture was KS L 5109 method and N1~N4 were varied in different mixing time, mix step and entering points of fine aggregate. Test results clearly showed that the flow value, strength and drying shrinkage development of AASC were significantly dependent on the entering point of fine aggregate. The flow value tended to decreases with delaying entering point of fine aggregate. The compressive strength and flexural strength increases with delaying entering point. Moreover, the XRD analysis confirmed that there were sustain these results. The drying shrinkage increases with delaying entering point of fine aggregate. Futhermore, a modified mixing method incorporating all hereby experimentally derived parameters, is proposed to improvement the physical properties of AASC.

• KOREAN JOURNAL OF CROP SCIENCE
• /
• v.58 no.1
• /
• pp.71-77
• /
• 2013

The world demand of renewable bioenergy as an alternative transportation fuel is greatly increasing. Research for bioethanol production is currently being progressed intensively throughout the world. Therefore it will be necessary to develop bioethanol production with cellulosic materials. In this study, the yield of ethanol production was evaluated by simultaneous saccharification and fermentation (SSF) using sodium hydroxide pretreated sorghum ${\times}$ sudangrass hybrids. Composition analysis of 11 varieties of sorghum ${\times}$ sudangrass hybrids was performed for selection of excellent variety to efficiently produce bioethanol. The content of cellulose, hemicellulose, lignin and ash of these varieties were 32~39%, 19~24%, 17~22% and 6~11%, respectively. Among these varieties, 4 varieties of sorghum ${\times}$ sudangrass hybrids were selected for the evaluation of ethanol yield and those were pretreated with 1 M NaOH solution at $150^{\circ}C$ for 30 min using high temperature explosion system. After pretreatment, samples were neutralized with tap water. It contained 52~57% of cellulose. Simultaneous saccharification and fermentation (SSF) was carried out for 48 h at $33^{\circ}C$ by Saccharomyces cerevisiae CHY1011 using Green star variety. The yield of ethanol was 92.4% and the amount of ethanol production was estimated at 6206 L/ha.

• Analytical Science and Technology
• /
• v.12 no.4
• /
• pp.290-298
• /
• 1999

A study on the application of impedance phase angle for redox titration, acid-base titration, chelate titration and precipitation titration has been carried out. A constant alternating current was passed between two platinum electrodes. One of them was a polarizable micro-electrode of $0.1cm^2$ or $0.026cm^2$ surface area and the other a non-polarizable large electrode of $1cm^2$ surface area dipped in the solution to be titrated. The impedance and the phase angle of the titration cell were measured with lock-in amplifier to obtain well behaved titration curve respectively. In titration of oxalic acid vs. potassium permanganate, the end-point was obtained successfully from the phase angle titration curve. In this experiment, the concentration of 0.0005 M to 0.05 M, the current of $50{\mu}A$ and the frequency of near 50 Hz were used. In titration of phosphoric acid vs. sodium hydroxide, the first end-point was obtained successfully on the optimum experimental condition of 0.001 M concentration, $50{\mu}A$ current and 25~97 Hz frequency. However, the end-point in titration of cupric sulfate vs. disodium-EDTA couldn't be obtained clearly. The end-point was obtained with the out-of-phase impedance curve on the experimental condition of 0.01 M concentration, $100{\mu}A$ current, 5~35 Hz frequency range. In titration of sodium chloride vs. silver nitrate, the end-point was obtained successfully on the experimental condition of 0.1 M concentration, $100{\mu}A$ current and 5~47 Hz frequency range. This study showed that the impedance phase angle was applicable for the detection of the end-points in redox titration curve, acid-base titration curve, chelate titration curve and precipitation titration curve.

• Journal of Food Hygiene and Safety
• /
• v.31 no.3
• /
• pp.186-193
• /
• 2016

An analytical method was developed for the determination of oxathiapiprolin in agricultural commodities. Oxathiapiprolin is a new oomycide (fungicide of piperidinyl thiazole isoxazoline class) which controls downy mildew in cucurbits caused by Pseudoperonospora cubensis (oomycete plant pathogen). Agricultural commodities were extracted with acetonitrile and partitioned with dichloromethane to remove the interference, adjusting pH between 9 and 10 by 1 N sodium hydroxide. After purification by silica SPE cartridge to clean up the interference of organic compounds, they were finally quantified by HPLC-UVD (high performance liquid chromatograph ultraviolet detector) using a wavelength at 260 nm and confirmed by LC-MS (liquid chromatograph mass spectrometer) in electro-spray ionization positive ion mode. The standard calibration curve was linear with coefficients of determination ($r^2$) 1.00 over the calibration ranges (0.025-2.5 mg/L). Recoveries were ranged between 86.7 to 112.7%, with relative standard deviations less than 10% at three concentration levels (LOQ, 10LOQ, and 50LOQ) performing five replicates. The overall results were determined and estimated according to the CODEX guidelines (CAC/GL40). The proposed method for determination of oxathiapiprolin residues in agricultural commodities can be used as an official method.

• Journal of the Korean Geotechnical Society
• /
• v.30 no.1
• /
• pp.65-74
• /
• 2014

Cemented soils have been widely used in road and dam construction, and recently ground improvement of soft soils. The strength of such cemented soils can be tested by using cored sample or laboratory-prepared specimen through unconfined compression or triaxial tests. It takes time to core a sample or prepare a testing specimen in the laboratory. In a certain situation, it is necessary to determine the in-situ strength of cemented soils very quickly and on time. In this study, the relation between unconfined compressive strength and shear wave velocity was investigated for predicting the in-situ strength of cemented soils. A small cemented specimen with 5 cm in diameter and 10 cm in height was prepared by Nakdong river sand and ordinary Portland cement. Its cement ratios were 4, 8, 12, and 16% and air cured for 7, 14, and 28 days. For recycling of resources, a blast furnace slag was also used with sodium hydroxide as an alkaline activator. The shear wave velocity for cemented soils was measured and then unconfined compressive strength test was carried out. As a cement ratio increased, the shear wave velocity and unconfined compressive strength increased due to increased density and denser structure. The relation between unconfined compressive strength and shear wave velocity increased nonlinearly for cemented soils with less than 16% of cement ratio.

• Journal of Korean society of Dental Hygiene
• /
• v.13 no.4
• /
• pp.701-711
• /
• 2013

Objectives : The aim of this study was to evaluate the pH and buffering capacity in some commercial fermented milks in Korea. Methods : The study was carried ouf from June to August, 2012. In 35 liquid type, 79 condense-stirred type and 71 condense-drink type fermented milks, available on the market, pH and buffering capacity were measured. Titration(with NaOH) was used to determine the buffering effect of each fermented milk. They were titrated with 1 M sodium hydroxide, added in 0.1 milliliters increments, until the pH reached about 5.5 and 7.0. Results : The average pH of tested fermented milks was $4.08{\pm}0.27$. The average pH values of fermented milks were $3.64{\pm}0.22$ in liquid type, $4.14{\pm}0.12$ in condense-stirred type, and $4.22{\pm}0.17$ condense-drink type. The average buffering capacity (pH 5.5) of tested fermented milk was $2.40{\pm}0.54$. The average buffering capacity (pH 5.5) of liquid type fermented milk was $2.37{\pm}0.33$, condense-stirred type fermented milk was $2.77{\pm}0.46$ and condense-drink type fermented milk was $2.01{\pm}0.42$. The average buffering capacity (pH 7.0) of tested fermented milks was $4.00{\pm}0.87$. The average buffering capacity (pH 7.0) of liquid type fermented milk was $3.11{\pm}0.36$, condense-stirred type fermented milk was $4.78{\pm}0.55$ and condense-drink type fermented milk was $3.58{\pm}0.59$. Conclusions : The average pH of tested fermented milks in this study was lower than pH 4.5. The type of fermented milks was an important factor for selection of fermented milk which is related with enamel erosion.

• Journal of the Korean Wood Science and Technology
• /
• v.37 no.3
• /
• pp.255-264
• /
• 2009

To evaluate the effects of chemical pretreatments of lignocellulosic biomass on enzymatic hydrolysis process, Populus euramericana was pretreated for 1 hr with 1% sulfuric acid ($H_2SO_4$) at $150^{\circ}C$ and 1% sodium hydroxide (NaOH) at $160^{\circ}C$, respectively. Before the enzymatic hydrolysis, each pretreated sample was subjected to drying process and thus finally divided into four subgroups; dried or non-dried acid pretreated samples and dried or non-dried alkali pretreated samples and chemical and physical properties of them were analyzed. Biomass degradation by acid pretreatment was determined to 6% higher compared to alkali pretreatment. By the action of acid ca. 24.5% of biomass was dissolved into solution, while alkali degraded ca. 18.6% of biomass. However, reverse results were observed in delignification rates, in which alkali pretreatment released 2% more lignin fragment from biomass to the solution than acid pretreatment. Unexpectedly, samples after both pretreatments were determined to somewhat higher crystallinity than untreated samples. This result may be explained by selective disrupture of amorphous region in cellulose during pretreatments, thus the cellulose crystallinity seems to be accumulated in the pretreated samples. SEM images revealed that pretreated samples showed relative rough and partly cracked surfaces due to the decomposition of components, but the image of acid pretreated samples which were dried was similar to that of the control. In pore size distribution, dried acid pretreated samples were similar to the control, while that in alkali pretreated samples was gradually increased as pore diameter increased. The pore volume which increased by acid pretreatment rapidly decreased by drying process. Alkali pretreatment was much more effective on enzymatic digestibility than acid pretreatment. The sample after alkali pretreatment was enzymatically hydrolyzed up to 45.8%, while only 26.9% of acid pretreated sample was digested at the same condition. The high digestibility of the sample was also influenced to the yields of monomeric sugars during enzymatic hydrolysis. In addition, drying process of pretreated samples affected detrimentally not only to digestibility but also to the yields of monomeric sugars.

• Journal of Korean Society of Forest Science
• /
• v.29 no.1
• /
• pp.1-19
• /
• 1976

This study has been made to make an observation regarding present status of the coal mine props which is desperately needed for coal production, despite of great shortage of the timber resources in this country, and investigate the effects of diffusion process on the decay resistances of the mine props as applied preservatives of Malenit and chromated zinc chloride. The results are as follows. 1. Present status of the coal mine props Total demand of coal mine props in the year of 1975 was approximately 456 thousand cubic meters. The main species used for mine props are conifer (mainly Pinus densiflora) and hardwood (mainly Quercus). Portions between them are half and half. With non fixed specification, wide varieties of timber in size and form are used. And volume of wood used per ton-of coal production shows also wide range from 0.017 cubic meter to 0.03 cubic meter. 2. Decay resistance test a) The oven dry weight decreased between untreated specimen and treated specimen has not shown any significantly, although it has shown some differences in average values between them. It may be caused by the shorter length of the test. b) The strength of compression test between untreated specimen and treated specimen has also shown the same results as shown in case of weight decrease. Reasons assumed are the same. c) The amounts of the extractives in one percent of sodium hydroxide (NaOH) between untreated and treated specimen have shown the large value in case of untreated specimen than that of treated. 3. The economical benifit between untreated and treated wood when applied in field has seen better in long term base in case of treated wood, although the primary cost of treated wood add a little bit more cost than that of the untreated wood.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.31 no.4
• /
• pp.555-563
• /
• 2004

The pH of beverages is known to be low and have, therefore, been implicated in the increasing incidence of erosion. Erosion is believed to be the predominant cause of teeth wear in children and young adults, although there will always be a contribution from attrition and abrasion. The aim of the present study was to evaluate the effect of yogurt on the progression of erosive demineralization in human enamel using demineralization model in vitro. In 4 yogurts, available on the market, pH, buffering capacity and the concentrations of calcium, phosphate and fluoride were determined. The buffering effect was determined by titration with NaOH. 50 milliliters of each drink was then titrated with 1M sodium hydroxide, added in 0.5 milliliters increments, until the pH reached about 7. Human deciduous enamel(n=40) samples were divided into four groups and exposed to 80ml of the yogurt for 30,60, 90 and 120min. Enamel surface microhardness(VHN) was examined before and after each exposure. 1. The average PH of fermented milk was 3.77 and this pH value was acidic enough to cause tooth erosion. 2. All of the fermented milks were found to be erosive(p<0.05) 3. The teeth exposed to the fermented milk all showed erosion like lesions and microhardness measurements showed that enamel surface hardness decreased proportionately with increased time of immersion in all tooth specimen groups. 4. After immersion for 30 and 60 minutes, reduction rate of microhardness values was not significantly different between the groups(p>0.05). However, after 90 and 120 minutes, reduction rate of each group was significantly different(p<0.05).

• Journal of the Korean Wood Science and Technology
• /
• v.7 no.2
• /
• pp.3-30
• /
• 1979

Larch ($\underline{Larix}$ $\underline{leptolepis}$ GORDON), one of the major afforestation species in Korea in view of its growing stock and rate of growth, is not favored as a raw material for pulp due to its low yield of pulp and difficulties with bleaching arising from the high content of extractives in wood, and the high heartwood ratio and the active phenolics, respectively. The purpose of this study is to investigate the characteristics of firstly pulping with various additives of cellulose protector for the yield of pulp, and secondly bleaching with oxygen for chlotination-alkali extraction of five stage-sequence to reduce chlorine compounds in bleaching effluents. The kraft cooking liquor for five age groups of larchwood was 18 percent active alkali with 25 percent sulfidity and 5 : 1 liquor-to-wood ratio, and each soda liquor for sap-and heart-wood of the 15-year-old larchwood was 18 percent alkali having one of the following cellulose protectors as the additive; magnesium sulfate ($MgSO_4$, 2.5%), zinc sulfate ($ZnSO_4$, 2.5%), aluminium sulfate ($Al_2(SO_4)_3$, 2.5%), potasium iodide (KI, 2.5%), hydroquinone (HQ, 2.5%), anthraquinone (AQ, 0.1%) and ethylene diamine (EDA, 2.5%). Then each anthraquinone-soda liquor for the determination of suitable cooking condition was the active alkali level of 15, 17 and 19 percent with 1.0, 0.5 and 0.1 percent anthraquinone, respectively. The cooking procedure for the pulps was scheduled to heat to 170$^{\circ}C$ in 90 minutes and to cook 90 minutes at the maximum temperature. The anthraquinone-soda pulps from both heartwood and sapwood of 15-year-old larchwood prepared with 0.5 percent anthraquinone and 18 percent active alkali were bleached in a four-stage sequency of OCED. (O: oxygen bleaching, D: chlorine dioxide bleaching and E: alkali extraction). In the first stage oxygen in atmospheric pressure was applied to a 30 percent consistency of pulp with 0.1 percent magnesium oxide (MgO) and 3, 6, and 9 percent sodium hydroxide on oven dry base, and the bleached results were compared pulps bleached under the conventional CEDED (C: chlorination). The results in the study were summarized as follows: 1. The screened yield of larch kraft pulp did not differ from particular ages to age group, but heartwood ratio, basic density, fiber length and water-extractives contents of wood and the tear factor of the pulp increased with increasing the tree age. The total yield of the pulp decreased. 2. The yield of soda pulp with various chemicals for cellulose protection of the 15-year-old larchwood increased slightly more than that of pure soda pulp and was slightly lower than that of kraft pulp. The influence of cellulose protectors was similar to the yield of pulps from both sapwood and heartwood. The effective protectors among seven additives were KI, $MgSO_4$ and AQ, for which the yields of screened pulp was as high as that of kraft pulp. Considering the additive level of protector, the AQ was the most effective in improving the yield and the quality of pulp. 3. When the amount of AQ increased in soda cooking, the yield and the quality of the pulp increased but rejects in total yield increased with decreasing the amount of active alkali from 19 to 15 percent. The best proportion of the AQ seemed to be 0.5 percent at 17 percent active alkali in anthraquinone-soda pulping. 4. On the bleaching of the AQ-soda pulp at 30 percent consistency with oxygen of atomospheric pressure in the first stage of the ODED sequence, the more caustic soda added, the brighter bleached pulp was obtained, but more lignin-selective bleaching reagent in proportion to the oxygen was necessary to maintain the increased yield with the addition of anthraquinone. 5. In conclusion, the suitable pulping condition for larchwood to improve the yield and quality of the chemical pulp to the level for kraft pulp from conventional process seemed to be. A) the selection of young larchwood to prevent decreasing in yield and quality due to the accumulation extractives in old wood, B) the application of 0.5 percent anthraquinone to the conventional soda cooking of 18 percent active alkali, and followed, C) the bleaching of oxygen in atmospheric pressure on high consistency (30%) with 0.1 percent magnesium oxide in the first stage of the ODED sequence to reduce the content of chlorine compounds in effluent.