• 한국재료학회지
• /
• 제26권10호
• /
• pp.549-555
• /
• 2016

We have investigated a glass-forming region of $V_2O_5-P_2O_5-ZnO$ glass and the effects of the addition of modifier oxides ($B_2O_3$) to the glass systems as a sealing material to improve the adhesion between the glass frits and a soda lime substrate. Thermal properties and coefficient of thermal expansion were measured using a differential scanning calorimetry, a dilatometer and a hot stage microscopy. Structural changes and interfacial reactions between the glass substrate and the glass frit after sintering (at $400^{\circ}C$ for 1 h) were measured by Fourier transform infrared spectroscopy, X-ray photoelectron spectroscopy and scanning electron microscope. The results showed that the adhesion strength increases as the content of $B_2O_3$ at 5 mol% increases because of changes in the structural properties. It seems that the glass structures change with $B_2O_3$, and the $Si^{4+}$ ions from the substrate are diffused to the sealing glass. From these results, we could understand the mechanism of strengthening of the adhesion of soda lime silica substrate by ion-diffusion from the substrate to the glass.

• 대한기계학회논문집A
• /
• 제20권7호
• /
• pp.2196-2204
• /
• 1996

The damage mechanism by the impact of steel ball on the soda-lime glass having a different surface roughness was investigated. An initiation and a propagation behavior of cracks formed by each impact velocity were quantitatively studied. A 4-point bending test was carried out to evaluate the remaining bending strength of a scratched soda-lime glass which impacted by the steel ball. As the surface roughness was increased, the shape of cracks became more irregular rather than those of the smooth specimens. The phenomenon of turning up in the wing of cone cracks occurred even at the lower velocity than the critical velocity caused the crushing. The threshold velocity of cracks initiation generally became lower than those of smooth specimen. An initiation and a propagation behavior of radial cracks had no relation with the direction of scratch on the surface. The remaning benidng strength of the scratched specimen according to impact velocity had no big difference compared with those of the smooth specimen.

• 한국해양공학회지
• /
• 제12권3호통권29호
• /
• pp.49-59
• /
• 1998

The damage mechanism of $Cr_2O_3$ plasma coated soda-lime glass and uncoated glass by steel ball particle impact was analyzed in this study. And the shape variation of the cracks was investigated by stereo-microscope according to the impact velocity and steel ball diameter. In order to improve the damage reduction effect by $Cr_2O_3$ coating layer, crack size was measured and surface erosion state was observed for both of two kinds of specimen after impact experiment. And the results were compared with each other. The 4-point bending test was performed according to ASTM D790 testing method to evaluate the effect of coating layer for bending strength variation. As a result, it was found that the crack size of $Cr_2O_3$ coated specimen was smaller than that of uncoated one, because of the impact absorption by interior pores in the coating layer and the load dispersion by the structural characteristic of the coating layer. For the specimens subjected to the steel ball impact, the bending strength of coated specimen was higher than that of uncoated specimen.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2000년도 하계학술대회 논문집 C
• /
• pp.1625-1627
• /
• 2000

Cu(InGa)$Se_2$(CIGS) thin film absorbers with various Cu/(In+Ga) atomic ratios were prepared by a three-stage process using a co-evaporation appartus. The effect of Na on the structural and electrical properties of CIGS films were studied and their effects on the CIGS/Mo thin film solar cells were investigated. Soda-lime glass and Corning glass were used as substrates to compare the effect of Na diffusion into CIGS film. The resistivity of CIGS films was not changed in the Cu-poor lesion due to diffusion of Na from soda-lime glass but was mainly determined by the surface resistivity controlled by excess Na.

• 한국세라믹학회지
• /
• 제12권1호
• /
• pp.16-22
• /
• 1975

The network structure of a glass is known to be cracked by a chemical reaction, diffusion, and ion exchange of alkali ion, formed at the crack tip of the glass surface, when water is present on the glass surface. Since the durability of glass is reduced, due to the fatigue phenomenon mentioned above, pollution problem of glass goods, especially bottle glass, is becoming acute gradually. A static fatigue phenomenon was studied thermodynamically in this paper, and a mechanism of static fatigue, a quality control, and a method of preventing pollution for the main local glass goods were also investigated. The PH of reacted solution and the quantity of extracted alkali were measured at different conditions such as temperature, reacting time, particle size of a crushed glass sample, and the nature of reacting solution. The enthalpy change was calculated from the Arrhenius equation. The results are given below; 1) The absolute value of enthalpy change for the bottle glass was found to be higher than the for the flat glass. 2) The fatigue phenomenon of a glass was more sensitive to the temperature than to the reacting time. 3) The durability of glass in acid solution is stronger than in alkaline solution. 4) The substance which cracks the network structure of glas is considered the hydroxyl ion.

• 한국결정성장학회지
• /
• 제17권3호
• /
• pp.102-107
• /
• 2007

인산염계 유리를 사용하여 PDP 소자의 하판유전체 후막을 제작하였다. 유전체 후막의 제조는 soda-lime glass위에 silk screen printing 법을 사용하였다. 기판과 유전체후막의 열팽창계수를 맞추기 위하여 $TiO_2$와 $Al_2O_3$를 충진제로 사용하였다. 유전체의 결정화 거동은 DTA, XRD를 사용하였으며 광학적 열적 전기적인 특성을 알아보기 위하여 UV-spectrometer, Dilatometer, Impedance Analyser를 사용하였다. 실험결과 주 결정상은 메타인산아연과 피로인산아연으로 나타났다. $TiO_2$의 첨가로 인하여 반사율은 높아졌으나 상대적으로 유전상수는 높아졌다. 또한 $Al_2O_3$를 첨가한 경우 반사율은 크게 변화가 없었으나 유전상수 값은 낮아졌다. 또한 열팽창 계수는 약 $62{\times}10^{-7}/^{\circ}C$ 정도였다.

• 공업화학
• /
• 제20권5호
• /
• pp.557-560
• /
• 2009

본 연구에서는 글라스를 $100{\mu}m$ 이하의 두께로 박판화하기 위한 새로운 습식 에칭방법 및 에칭 용액을 검토하였다. $NH_4F$ 또는 $NH_4HF_2$를 주성분으로 황산 또는 질산을 첨가한 경우 에칭 용액의 불산 함유량을 저감하는 데에 효과가 있었다. 혼산 용액의 조성과 온도의 영향을 검토하였으며, 음이온계 계면활성제의 첨가는 에칭반응에 의해 생성되는 슬러지의 부착을 억제해주는 효과가 있었다. 수류 발생부를 가지는 새로운 파일럿 장비를 사용하여 상용 무알칼리 글라스와 소다라임 글라스의 에칭 실험을 실시하였다. $640{\mu}m$ 두께의 무알칼리 글라스를 $45{\mu}m$ 두께로 $500{\mu}m$ 두께의 소다라임 글라스를 $100{\mu}m$ 두께로 박판화하였으며, 에칭 후의 표면 조도는 $0.01{\sim}0.02{\mu}m$를 유지하였다.

• 태양에너지
• /
• 제20권2호
• /
• pp.43-54
• /
• 2000

동시 진공증발법을 이용하여 coming glass, soda-lime glass, Mo가 증착된 soda-lime glass 위에 $Cu(In_{1-x}Ga_x)Se_2$ 박막을 증착하였다. Soda-lime glass 위에서 제조된 $Cu(In_{0.5}Ga_{0.5})Se_2$ 박막의 전기비저항값과 정공농도는Cu/(In+Ga)비에 큰 영향을 받지 않았다. Soda-lime glass위에서의 $Cu(In_{1-x}Ga_x)Se_2$ 박막내부와 표면에는 Na이 검출되었고, 표면의 Na는 산소와 결합하고 있었으며, Cu가 부족한 조성에서 이차상이 형성되었다. Ga/(In+Ga)비가 증가할수록 $Cu(In_{1-x}Ga_x)Se_2$ 박막은 회절 peak들의 큰 회절각으로 이동, 초격자 peak등의 분리, 결정립 크기의 감소가 관찰되었다. $Cu_{0.91}(In_{1-x}Ga_x)Se_2$ 박막은 Ga/(In+Ga)비에 무관하게 전기적으로 p-type을 나타내었다. Ag/n-ZnO /i-Zno/CdS/$Cu_{0.91}(In_{0.7}Ga_{0.3})Se_2$/Mo/glass구조의 태양전지를 제조하였으며, 태양전지변환효율(Eff.) = 14.48%, 단락전류밀도(Jsc) = $34.88mA/cm^2$, 개방전압(Voc) =581.5 mV, 충실도(F.F) = 0.714을 나타내었다.

• 한국진공학회지
• /
• 제16권3호
• /
• pp.205-209
• /
• 2007

Atomic layer deposition(ALD)를 이용하여 Si와 soda lime glass 기판 위에 ZnO 박막을 증착하였다. 기판의 온도는 비교적 저온인 $130^{\circ}C{\sim}150^{\circ}C$를 채택하였다. 증착결과 단위 cycle 당 $2.72{\AA}$이 증착되어 균일한 박막이 증착되었음이 확인되었다. 증착된 박막의 결정성을 X-ray diffraction(XRD)으로 조사해본 결과 비교적 저온에서도 (100)과 (101)방향의 성장이 우세하였다. 또 Auger electron spectroscopy(AES)로 분석해본 결과 불순물이 없는 순도 높은 박막이 성장되었음을 알 수 있었다.

• 한국정밀공학회지
• /
• 제20권5호
• /
• pp.156-163
• /
• 2003

In order to investigate the possibility of punching process of brittle material by ball impact, the effects of sealing materials about impact damage of soda-lime glass by small spheres were evaluated experimentally. The using of sealing materials in the development of perfect cone crack was more effective than no using of sealing materials. At the sealing materials condition, in the case of 5mm-thick specimen, Copper and PMMA sealing were more effective in producing a perfect cone formation than the other sealing materials. And in the case of 8mm-thick specimen, Aluminum sealing was most effective in producing a perfect cone formation. The impact velocity range over which perfect cones were formed was influenced by both the thickness of specimen and sealing materials. By a proper selection of sealing materials, the application fur industrial technology for hole (or nozzle) punching process of brittle materials is expected.