• Journal of Sensor Science and Technology
• /
• v.9 no.3
• /
• pp.242-247
• /
• 2000

$Pb_{0.99}[(Zr_{0.6}Sn_{0.4})_{0.9}Ti_{0.1}]_{0.98}Nb_{0.02}O_3(PNZST)$ thin films were deposited by RF magnetron sputtering on $(La_{0.5}Sr_{0.5})CoO_3(LSCO)/Pt/Ti/SiO_2/Si$ substrate using a PNZST target with excess PbO of 10 mole%. The thin films deposited at substrate temperature of $500^{\circ}C$, and at RF power of 80W were crystallized to a perovskite phase after rapid thermal annealing(RTA). The thin films annealed at $650^{\circ}C$ for 10 seconds in air exhibited the good structures and electrical properties. The fabricated PNZST capacitor had a remanent polarization value of about $20\;{\mu}C/cm^2$ and coercive field of about 50 kV/cm. The reduction of the polarization after $2.2{\times}10^9$ switching cycles was less than 10%.

• Journal of Sensor Science and Technology
• /
• v.11 no.1
• /
• pp.48-53
• /
• 2002

Ferroelectric $Pb_{0.99}[(Zr_{0.6}Sn_{0.4})_{1-x}Ti_x]_{0.98}Nb_{0.02}O_3$(PNZST) thin films were deposited by a RF magnetron sputtering on $(La_{0.5}Sr_{0.5})CoO_3$(LSCO)/Pt/Ti/$SiO_2$/Si substrate using a PNZST target with excess PbO of 10 mole%. The crystallinity and electrical properties of the thin films with various composition ratio were investigated. The thin films deposited at the substrate temperature of $500^{\circ}C$ and the power of 80 W were crystallized to a perovskite phase after rapid thermal annealing(RTA) at $650^{\circ}C$ for 10 seconds in air. A PNZST thin films with Ti of 10 mole% showed the good crystallinity and ferroelectric properties. The remanent polarization and coercive field of the PNZST capacitor were about $20\;{\mu}C/cm^2$ and 50 kV/cm, respectively. The reduction of the polarization after $2.2{\times}10^9$ switching cycles was less than 10%.

• Journal of the Korean institute of surface engineering
• /
• v.50 no.5
• /
• pp.411-420
• /
• 2017

In this paper, two methods of making the Pd-added $SnO_2$ ($Pd-SnO_2$) powder with pure tetragonal phase by the hydrazine method were suggested and compared in terms of crystal structure, surface morphology, and alcohol gas response. One of the addition methods is to use $PdCl_2$ as a Pd source, the other is to use Pd-based organic with oleylamine (OAM). When Pd concentration was increased from 0 to 5 wt%, the average grain size of $Pd-SnO_2$ made with Pd-OAM were decreased from 32 to 12 nm. In the case of using with $PdCl_2$, grain size of the $PdCl_2$ fell to less than 10 nm. However, agglomerated and extruded surface morphology was observed for the films with Pd addition over 4 wt%. The crack-free $Pd-SnO_2$ thick films were able to successfully fill the $30{\mu}m$ gap of patterned Pt electrodes by optimized ink dropping method. Also, the 2 wt% $Pd-SnO_2$ thick film made with PdCl2 showed gas responses ($R_{air}/R_{gas}$) of 3.7, 5.7 and 9.0 at alcohol concentrations of 10, 50 and 100 ppm, respectively. On the other hand, the prepared 3 wt% $Pd-SnO_2$ thick film with Pd-OAM exhibited very excellent responses of 3.4, 6.8 and 12.2 at the equivalent measurement conditions, respectively. The 3 wt% $Pd-SnO_2$ thick film with Pd-OAM has a specific surface area of $31.39m^2/g$.

• Journal of the Institute of Electronics and Information Engineers
• /
• v.54 no.1
• /
• pp.21-25
• /
• 2017

In this study, we have fabricated Schottky barrier diodes (SBD) on single-crystal ${\beta}-Ga_2O_3$ semiconductor that has received much attention for use in next-generation power devices. The SBD had a Pt/Ti/Au Schottky contact on a $2{\mu}m$ Sn-doped low concentration N-type epitaxial layer. The fabricated device exhibited a breakdown voltage of > 180 V, a specific on-resistance of $1.26m{\Omega}{\cdot}cm^2$, and forward current densities of $77A/cm^2$ at 1 V and $473A/cm^2$ at 1.5 V, which proved the potential for use in power device fabrication.

• Journal of Sensor Science and Technology
• /
• v.27 no.4
• /
• pp.221-226
• /
• 2018

Misfueling accidents significantly damage the engines of both gasoline and diesel vehicles, and should be avoided by rapid and accurate fuel discrimination. Gasoline fuel contains bioethanol. Thus, the detection of ethanol vapor produced by gasoline can be used to distinguish between gasoline and diesel. In the present study, Pt-doped $SnO_2$ hollow nanospheres, Mg-doped $In_2O_3$ hollow microspheres, and Pt-doped ZnO nanostructures have been used as gas sensors to discriminate between gasoline and diesel fuels. All three sensors are able to detect and discriminate between gases evaporating from gasoline and diesel. Among the sensors, the Mg-doped $In_2O_3$ hollow microspheres show a significant gas response (resistance ratio = 4.97) quickly (~3 s) after exposure to gasoline-evaporated gas at $225^{\circ}C$, but did not show any substantial response to diesel-evaporated gas. This demonstrates that gasoline and diesel fuels can be discriminated using small and cost-effective oxide semiconductor gas sensors.

• Proceedings of the IEEK Conference
• /
• 2000.06b
• /
• pp.24-27
• /
• 2000

Ferroelectric P $b_{0.99}$〔(Z $r_{0.6}$S $n_{0.4}$)$_{0.9}$ $Ti_{0.1}$〕$_{0.98}$N $b_{0.02}$ $O_3$(PNZST) thin films were deposited by a RF magnetron sputtering on (L $a_{0.5}$S $r_{0.5}$)Co $O_3$(LSCO)/Pt/Ti/ $SiO_2$/Si substrate using a PNZST target with excess PbO of 10 mole％. The thin films deposited at the substrate temperature of 500 $^{\circ}C$ were crystallized to a perovskite phase after rapid thermal annealing(RTA) The thin films annealed at 650 $^{\circ}C$ for 10 seconds in air exhibited the good crystal structures and ferroelectric properties. The remanent polarization and coercive field of the PNZST capacitor were about 20 $\mu$C/$\textrm{cm}^2$ and 50 kV/cm, respectively. The reduction of the polarization after 2.2$\times$10$^{9}$ switching cycles was less than 10 ％.0 ％.％.0 ％.0 ％.

• Bulletin of the Korean Chemical Society
• /
• v.32 no.6
• /
• pp.1865-1872
• /
• 2011

This study investigates the sensitivity of a gas sensor to volatile organic compounds (VOCs) at various operating temperatures and catalysts. Nano-sized powdered $WO_3$ prepared by sol-gel and chemical precipitation methods was mixed with various metal oxides. Next, transition metals (Pt, Ru, Pd, and In) were doped on the surface of the mixture. Metal-$WO_3$ thick films were prepared using the screen-printing method. The physical and chemical properties of the films were studied by SEM/EDS, XRD, and BET techniques. The measured sensitivity to VOCs is defined as the ratio ($R_a/R_g$) of resistance ($R_{air}$) of $WO_3$ film in the air to resistance ($R_{gas}$) of $WO_3$ film in a VOCs test gas. The sensitivity and selectivity of the films were tested with various VOCs such as acetaldehyde, formaldehyde, methyl alcohol, and BTEX. The thick $WO_3$ film containing 1 wt % of Ru and 5 wt % of $SnO_2$ showed the best sensitivity and selectivity to acetaldehyde gas at an operating temperature of 300 $^{\circ}C$.

• 한국신재생에너지학회:학술대회논문집
• /
• 2006.11a
• /
• pp.463-466
• /
• 2006

직접 알콜 연료전지는 액체인 알콜을 직접 연료전지에 공급하여 연소시킴으로써 높은 효율을 갖는 휴대용전원으로 주목받는 장치이다. 직접 알콜 연료전지에 담지체로 사용되는 탄소 소재는 넓은 표면적과 우수한 전기전도도를 가지고 있다는 장점 있으나 금속 촉매와의 상호작용이 약하여 촉매 활성에 영향을 주지 못한다. 산화물을 담지체로 사용할 경우 이러한 금속-담지체 간의 상호작용으로 인한 촉매활성 증가 및 입자성장 억제의 효과를 기대할 수 있다. 본 연구에서는, 안티몬 도핑된 주석산화물 (Sb-doped SnO2 : ATO nanoparticle)을 직접 메탄올 연료전지용 담지체어 적용하였으며 합성 과정은 다음과 같다. SnC14 5H2O SbC13, NaOH, HCl 수용액 혼합물을 삼구 플라스크에 넣고 $100^{\circ}C$ 온도에서 환류(reflux) 시킨 후 세척 및 건조하여 Air 분위기에서 열처리하였다. 합성된 산화물 수용액에 폴리올 방법으로 합성된 백금 콜로이드를 담지하였으며, 세척과 건조를 통하여 산화물에 담지된 백금 촉매를 촉매를 합성하였다. 촉매의 구조분석을 위해 XRD, TEM을 사용하였으며, 전극촉매로서의 활성을 평가하기 위해 cyclic voltammetry을 평가하였다. 본 연구에서는 백금의 담지량에 따른 Costripping voltammetry특성과 메탄올 및 에탄올 산화 반응 특성에 대하여, 탄소를 담지체로 사용한 Pt/C 촉매와 비교 평가하였다. 알콜 산화반응 평가결과, 주석산화물에 담지한 촉매가 탄소를 담지체로 사용한 촉매보다 우수한 활성을 나타내었으며 활성증가는 메탄올에 비해 에탄올 산화 반응의 경우 크게 증가하였다. 막과 비교해 보았다. $ZrO_2$ 입자는 전도성이며 동시에 친수성을 나타내기 때문에 상용 막에 비하여 함수율 및 수소이온 전도도가 우수하게 나타났다. 복합막의 이러한 물성은 $100^{\circ}C$이상의 고온에서 전해질 막 내의 물 관리를 용이하게 한다. 단위 전지 운전 온도 $130^{\circ}C$, 상대습도 37%의 운전 조건에서도 상당히 우수한 전지 성능을 보임에 따라 고온/저가습 조건에서 상용 Nafion 112 막보다 우수한 막 특성을 나타냄을 확인하였다.소/배후방사능비는 각각 $2.18{\pm}0.03,\;2.56{\pm}0.11,\;3.08{\pm}0.18,\;3.77{\pm}0.17,\;4.70{\pm}0.45$ 그리고 $5.59{\pm}0.40$이었고, $^{67}Ga$-citrate의 경우 2시간, 24시간, 48시간에 $3.06{\pm}0.84,\;4.12{\pm}0.54\;4.55{\pm}0.74 $이었다. 결론 : Transferrin에 $^{99m}Tc$을 이용한 방사성표지가 성공적으로 이루어졌고, $^{99m}Tc$-transferrin의 표지효율은 8시간까지 95% 이상의 안정된 방사성표지효율을 보였다. $^{99m}Tc$-transferrin을 이용한 감염영상을 성공적으로 얻을 수 있었으며, $^{67}Ga$-citrate 영상과 비교하여 더 빠른 시간 안에 우수한 영상을 얻을 수 있었다. 그러므로 $^{99m}Tc$<

• Journal of the Institute of Electronics Engineers of Korea SD
• /
• v.38 no.7
• /
• pp.473-478
• /
• 2001

Ferroelectric P $b_{0.99}$［(Z $r_{0}$ 6S $n_{0.4}$)/0.9/ $Ti_{0.1}$］0.98/N $b_{0.02}$ $O_3$(PNZST) thin films were deposited by a RF magnetron sputtering on L $a_{0.5}$S $r_{0.5}$Co $O_3$(LSCO)/Pt/Ti/ $SiO_2$/Si substrate using a PNZST target with excess PbO of 10 mole%. The crystallinity and electrical properties of the thin films annealed at various temperature and time were investigated. The thin films deposited at the substrate temperature of 500 $^{\circ}C$ and the power of 80 W were crystallized to a perovskite phase after rapid thermal annealing(RTA). The thin films annealed at 650 $^{\circ}C$ for 10 seconds in air exhibited the good crystal structures. The remanent polarization and coercive field of the PNZST capacitor were about 20 $\mu$C/$\textrm{cm}^2$ and 50 kV/cm, respectively. The reduction of the polarization after 2.2$\times$10$^{9}$ switching cycles was less than 10 %..10 %......

• Journal of Korean Society for Atmospheric Environment
• /
• v.20 no.6
• /
• pp.783-792
• /
• 2004

In this study, a thick-film semiconductor odor gas sensor for the detection of $CH_3$SH was developed using SnO$_2$ as the main substrate and was investigated in terms of its sensitivity and reaction time. In the process of manufacturing the sensor, Taguchi's design of experiment (DOE) was applied to analyze the effects of a variety of parameters, including the substrate, the additives and the fabrication conditions, systematically and effectively. Eight trials of experiments could be possible using the 27 orthogonal array for the seven factors and two levels of condition, which originally demands 128 trials of experiments without DOE. The additives of Sb$_2$O$_{5}$ and PdCl$_2$ with the H$_2$PtCl$_{6}$ ㆍ6$H_2O$ catalyst were appeared to be important factors to improve the sensitivity, and CuO, TiO$_2$, V$_2$O$_{5}$ and PdO were less important. In addition, TiO$_2$, V$_2$O$_{5}$ and PdO would improve the reaction time of a sensor, and CuO, Sb$_2$O$_{5}$, PdCl$_2$ and H$_2$PtCl$_{6}$ㆍ6$H_2O$ were negligible. Being evaluated simultaneously in terms of both sensitivity and reaction time, the sensor showed the higher performance with the addition of TiO$_2$ and PdO, but the opposite results with the addition of CuO, V$_2$O$_{5}$, Sb$_2$O$_{5}$ and PdCl$_2$. The amount of additives were superior in the case of 1% than 4%. H$_2$PtCl$_{6}$ㆍ6$H_2O$ would play an important role for the increase of sensor performance as a catalyst.nce as a catalyst.