• 한국생산제조학회지
• /
• 제18권5호
• /
• pp.449-454
• /
• 2009

This paper presents an experimental study on the failure characteristics of SnAgCu lead-free solder balls. To estimate the effect of Ag, three types of SnAgCu balls are first prepared by varying the weight percent of Ag(1.0, 3.0, 4.0 wt%) and then analyzed by reliability tests such as thermal shock, high speed ball shear, and drop tests. Thermal shock test reveals that the higher the weight percent of Ag is, the longer the fatigue lift becomes. To the contrary, high speed ball-shear test and drop test show that the shear strength and the fracture toughness of solder balls are inversely proportional to the weight percent of Ag, respectively, Reasons for these observations will be further investigated In the future work.

• 마이크로전자및패키징학회지
• /
• 제18권2호
• /
• pp.49-55
• /
• 2011

전자기기에서의 고장 중 대부분은 작동 중 발생하는 열과 충격에 기인한다. 이 열과 충격은 PCB(Printed Board) 부품의 접합부 계면에 균열을 야기 시키고, 이 균열은 금속간 화합물(Intermetallic Compound: IMC)의 형성과 밀접한 관계를 가진다. 본 연구에서는 Sn-Ag-Cu계의 Ag함량을 변화한 Sn-1.0Ag-0.5Cu와 Sn-1.2Ag-0.5Cu 및 Sn-3.0Ag-0.5Cu의 3가지 조성의 솔더로 접합한 소재를 대상으로 1000시간 까지 등온시효(Isothermal Aging) 하였다. 등온시효 동 안 솔더(Solder)의 계면에 발생하는 IMC(Intermetallic Compound) 성장이 관찰되었으며, solder 접합부의 기계적 특성은 굽힘충격 시험법을 이용하여 평가되었다. 그 결과 시효처리 전에는 Ag 함량이 낮은 solder의 굽힘충격 특성이 우수하게 나타났으나, 시효처리 후에는 반대의 결과를 나타내었다. 이 결과는 IMC layer 주변에 생성된 미세한 $Ag_3Sn$ 및 조대한 $Cu_6Sn_5$와 관련되어, 미세한 $Ag_3Sn$이 충격을 완화한 것으로 나타나 이에 따라 굽힘충격 특성에 차이가 나타남을 알 수 있었다.

• Journal of Welding and Joining
• /
• 제32권3호
• /
• pp.60-67
• /
• 2014

The ability of electronic packages and assemblies to resist solder joint failure is becoming a growing concern. This paper reports on a study of high speed shear energy of Sn-4.0wt%Ag-0.5wt%Cu (SAC405) solder with different electroless Ni-P thickness, with $HNO_3$ vapor's status, and with various pre-conditions. A high speed shear testing of solder joints was conducted to find a relationship between the thickness of Ni-P deposit and the brittle fracture in electroless Ni-P deposit/SAC405 solder interconnection. A focused ion beam (FIB) was used to polish the cross sections to reveal details of the microstructure of the fractured pad surface with and without $HNO_3$ vapor treatment. A scanning electron microscopy (SEM) and an energy dispersive x-ray analysis (EDS) confirmed that there were three intermetallic compound (IMC) layers at the SAC405 solder joint interface: $(Ni,Cu)_3Sn_4$ layer, $(Ni,Cu)_2SnP$ layer, and $(Ni,Sn)_3P$ layer. The high speed shear energy of SAC405 solder joint with $3{\mu}m$ Ni-P deposit was found to be lower in pre-condition level#2, compared to that of $6{\mu}m$ Ni-P deposit. Results of focused ion beam and energy dispersive x-ray analysis of the fractured pad surfaces support the suggestion that the brittle fracture of $3{\mu}m$ Ni-P deposit is the result of Ni corrosion in the pre-condition level#2 and the $HNO_3$ vapor treatment.