• Journal of the Microelectronics and Packaging Society
• /
• v.21 no.2
• /
• pp.91-97
• /
• 2014

With Pb-free solder joints containing Sn-Ag-Cu-based ternary alloys (Sn-1.0 wt.%Ag-0.5Cu and Sn-4.0Ag-0.5Cu) and Sn-Ag-Cu-In-based quaternary alloys (Sn-1.0Ag-0.5Cu-1.0In, Sn-1.2Ag-0.5Cu-0.4In, Sn-1.2Ag-0.5Cu-0.6In, and Sn-1.2Ag-0.7Cu-0.4In), fracture-mode change, shear strengths, and fracture energies were observed and measured under a high-speed shear test of 500 mm/s. The samples in each composition were prepared with as-reflowed ones or solid-aged ones at $125^{\circ}C$ to 500 h. As a result, it was observed that ductile or quasi-ductile fracture modes occurs in the most of Sn-Ag-Cu-In samples. The happening frequency of a quasi-ductile fracture mode showed that the Sn-Ag-Cu-In joints possessed ductile fracture properties more than that of Sn-3.0Ag-0.5Cu in the high-speed shear condition. Moreover, the Sn-Ag-Cu-In joints presented averagely fracture energies similar to those of Sn-Ag-Cu joints. While maximum values in the fracture energies were measured after the solid aging for 100 h, clear decreases in the fracture energies were observed after the solid aging for 500 h. This result indicated that reliability degradation of the Sn-Ag-Cu-In solder joints might accelerate from about that time.

• Journal of the Microelectronics and Packaging Society
• /
• v.8 no.3
• /
• pp.43-47
• /
• 2001

Sn-3Ag-8Bi-5In was developed for the intermediate melting point solder. Although In-contained solder is expensive, its melting point is lower than these of Sn-Ag-Cu alloys. Sn-3Ag-8Bi-5In solder used for this research has a melting range of 188~$204^{\circ}C$. On this study wetting characteristics of Sn-3Ag-8Bi-5In were evaluated in order to investigate its availability as a Pb-free solder. Wettabilities of Sn-37Pb and Sn-3.5Ag solders were also studied to compare these of the Sn-3Ag-8Bi-5In. Experimental results showed that the zero-cross-time and wetting time at $240^{\circ}C$ for the Sn-3Ag-8Bi-5In were 1.1 and 2.2 second respectively. These values are a little better than these of Sn-37Pb and Sn-3.5Ag solders. The equilibrium wetting farce of the Sn-3Ag-8Bi-5In was 5.8 mN at $240^{\circ}C$, and it was tuned out to be a little higher than that of Sn-3.5Ag and lower than that of Sn-37Pb.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2003.11a
• /
• pp.114-117
• /
• 2003

본 연구에서는 계산을 통해 나온 Sn-Ag-Cu 삼원계 공정점(Sn-3.7Ag-0.9Cu)을 바탕으로 그 근처의 응고경로가 다른 6가지 조성(Sn-4.6Ag-0.4Cu, Sn-4.9Ag-1.0Cu, Sn-3.9Ag-1.3Cu, Sn-2.2Ag-1.2Cu, Sn-2Ag-0.7Cu, Sn-2.7Ag-0.3Cu)에 대한 솔더합금의 미세조직을 관찰하였다. 응고경로는 $L\;\rightarrow\;L+Primary\;\rightarrow\;L+Primary+Secondary\;\rightarrow\;Ternary\;Eutectic+Primary+Secondary$로 되며 6가지 경우를 예상할 수 있다 솔더합금의 미세조직은 느린 냉각으로 인하여 빠른 냉각, 보통 냉각에 비해 상대적으로 커다란 $\beta-Sn$ dendrite를 보였고 $Ag_3Sn,\;Cu_6Sn_5$과는 다르게 $\beta-Sn$는 약 $30^{\circ}C$의 과냉(DSC분석)이 존재하게 되어 Sn-4.6Ag-0.4Cu의 경우에는 $Ag_3Sn$상이, Sn-2.2Ag-1.2Cu의 경우에는 $Cu_6Sn_5$가 과대성장을 하였다. 솔더의 기계적 특성을 살펴보고자 Cu 기판위에서 각 조성의 솔더볼을 솔더링한 후 다양한 냉각 속도를 적용하여 reflow 솔더링을 하고 솔더/기판 접합에 대한 전단 강도 시험을 실시했다. 냉각 속도가 빠를수록 $\beta-Sn$의 dendrite가 미세해져서 높은 전단 강도를 보였고 6가지 조성의 솔더볼중 공정조직 분율이 낮은 Sn-2Ag-0.7Cu 조성의 경우에서 낮은 전단 강도가 나타났다.

• Journal of the Microelectronics and Packaging Society
• /
• v.9 no.2
• /
• pp.39-43
• /
• 2002

The eutectic solder Sn-37Pb and the lead free solder alloys with the compositions of Sn-0.7Cu, Sn-3.5Ag, Sn-3.5Ag-0.75Cu, Sn-2.0Ag-0.7Cu-3.0Bi were applied to the 48 BGA packages, and then it was discussed for the shear strength at the solder joints as the hardness and the composition of the small solder ball. As a result of experiments, the high degree of hardness with the displacement of 0.043 mm was obtained in Sn-2.0Ag-0.7Cu-3.0Bi. The shear strength of the lead free solder was higher than that of Sn-37Pb solder, and it can be obtained the maximum value of about 52% in Sn-2.0Ag-0.7Cu-3.0Bi.

• Journal of the Microelectronics and Packaging Society
• /
• v.20 no.3
• /
• pp.53-57
• /
• 2013

Although the lowering of Ag content in Sn-3.0Ag-0.5Cu is known to improve the mechanical shock reliability of the solder joint, it is also known to be detrimental to the solderbility. In this study, the quaternary alloying effect of In and the minor alloying effects of Mn and Pd on the solderability, thermal cycling and mechanical shock reliabilities of the low Ag content Sn-1.2Ag-0.7Cu solder were investigated using board-level BGA packages. The solderability of Sn-1.2Ag-0.7Cu-0.4In was proved to be comparable to that of Sn-3.0Ag-0.5Cu but its thermal cycling reliability was inferior to that of Sn-3.0Ag-0.5Cu. While the 0.03 wt% Pd addition to the Sn-1.2Ag-0.7Cu-0.4In decreased the solderability and reliabilities of solder joint, the 0.1 wt% Mn addition was proved to be beneficial especially for the mechanical shock reliability compared to those of Sn-3.0Ag-0.5Cu and Sn-1.0Ag-0.5Cu compositions. It was considered to be due that the Mn addition decreased the Young's modulus of low Ag content Pb-free solders.

• Proceedings of the KWS Conference
• /
• 2006.10a
• /
• pp.169-171
• /
• 2006

Solderability and reaction properties were investigated for four Pb-free alloys as a function of Ag contents; Sn-4.0Ag-0.5Cu, Sn-3.0Ag-0.5Cu, Sn-2.5Ag-0.5Cu, and Sn-1.0Ag-0.5Cu. The alloy of the lowest Ag content, i.e., Sn-1.0Ag-0.5Cu, showed poor wetting properties as the reaction temperature decreased to 230oC. Variation of Ag concentration in the Sn-xAg-0.5Cu alloy shifted exothermic peaks indicating the undercooling temperature in DSC curve. For the aging process at 170oC, the thickness of IMCs at the board-side solder/Cu interface increased with the Ag concentration.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.07a
• /
• pp.640-644
• /
• 2000

The microstructure, wettability, shear strength and aging effect of Sn-3.5Ag/Cu and Alloy42 lead-frame solder joints were measured for comparison. In the case of Sn-3.5Ag/Cu, Ag$_3$Sn and Cu$\sub$6/Sn$\sub$5/ phases in the matrix Sn and 1∼2$\mu\textrm{m}$ thick Cu$\sub$6/Sn$\sub$5/ Phase at the interface of solder/lead-frame were formed. In the case of Sn-3.5AAg/A11oy42, only Ag$_3$Sn Phase of low density in the matrix Sn and 0.5∼1.5$\mu\textrm{m}$ thick FeSn$_2$phase at the interface of solder/lead-frame were formed. Comparing to Cu, Alloy42 shear strength of Alloy 42 solder joints was smaller than that of Cu and all declined after aging. After aging at 180$^{\circ}C$ for 1 week, η-Cu$\sub$6/Sn$\sub$5/ layer was formed on Cu lead-frame, while AgSn$_3$ phase in the matrix and thickened FeSn$_2$at the interface were formed on Alloy42 lead-frame.

• Journal of Welding and Joining
• /
• v.16 no.3
• /
• pp.148-156
• /
• 1998

The purpose of this study is to investigate the characteristics of Pb-Free Sn-2%Ag-Bi solder alloys. The solder alloys used in this study is Sn-2%Ag-(3,5,7,9%) Bi It is examined that their properties such as melting range, wettability, microstructure, microhardness, and tensile property. The addition of Bi(3,5,7,9%) lowered the melting point of the solder and the melting range was 196~203$^{\circ}C$. The wettability of the solder as equal to that of Sn-37% Pb solder. The morphology of structure did not change largely by addition of Bi. But the structure of cellular dendrite of linear type displayed. The tensile strength of the solder was superior to that of Sn-37%Pb solder. But the elongation was inferior to that of Sn-37%Pb solder. The hardness of Sn-2%Ag solder was tow times and that of Sn-2%Ag-Bi solder was three times of that in Sn-37%Pb solder. But the effect of increment of Bi content did not change largely.

• Korean Journal of Materials Research
• /
• v.9 no.7
• /
• pp.747-752
• /
• 1999

The interfacial reaction and joint properties of Sn-3.5Ag/Cu and Sn-3.5Ag-1Zn/Cu joint were studied. Modified double lap shear solder joints of Sn-3.5Ag and Sn-3.5Ag- lZn solder were aged for 60days at $100^{\circ}C$ and $150^{\circ}C$ and then loaded to failure in shear. The Sn-3.5Ag/Cu had a fast growth rate of the reaction layer in comparison with the Sn-3.5Ag-lZn at the aging temperature of $150^{\circ}C$ Through the SEM/EDS analysis of solder joint, it was proved that intermatallic layer was $Cu_{6}Sn_5$ phase and aged specimens showed that intermatallic layer grew in proportion to $t_{1/2}$, and the precipitate of $Ag_3Sn$ occur to both inner layer and interface of layer and solder. In case of Zn-containing composite solder, $Cu_{6}Sn_{5}$ phase formed at the side of substrate and $Cu_{5}Zn_{8}$ phase formed at the other side in double layer. The shear strength of the Sn-3.5Ag/Cu joint improved by addition of IZn. The strength of the joint increases with strain rate and decreases with aging temperature

• Journal of the Microelectronics and Packaging Society
• /
• v.10 no.4
• /
• pp.81-86
• /
• 2003

Electromigration of Sn-3.5Ag solder bump was investigated using flip chip specimens which consisted of upper Si chip and lower Si substrate. While the resistance of the flip chip sample did not almost change until the time right before the failure, the resistivity increased abruptly at the moment when complete failure of the solder joint occurred in the flip chip sample. At current densities of $3\times 10^4$∼$4\times 10^4$A/$\textrm{cm}^2$, the activation energy for electromigration of the Sn-3.5Ag solder bump was characterized as ∼0.7 eV. Failure of the Sn-3.5Ag solder bump occurred at the solder/UBM interface due to the formation and propagation of voids at cathode side of the solder bump.