• International Journal of Concrete Structures and Materials
• /
• v.5 no.2
• /
• pp.119-123
• /
• 2011

Presented in the paper are findings of a project that examined the effect of slag grade and cement source on the performance of concrete mixtures. Slag cement contents were 20, 40, and 60 percent of the total cementitious material content. Two grades of slag cement were examined (Gr. 100 and Gr. 120) along with two sources of Type I cement. Compressive strength, durability, and permeability were measured. The results showed that the cement source affected the early age strength of the mixtures. At 28 days of age, mixtures containing Gr. 120 slag cement had higher compressive strengths than mixtures containing Gr. 100 slag cement, but by 90 days of age, the trend reversed. As for the chloride ion penetrability, mixtures cast with Gr. 100 slag cement passed fewer coulombs at 28 and 90 days of age than similar mixtures containing Gr. 120 slag. Mixtures containing Gr. 120 slag had the greatest durability factors.

• Advances in concrete construction
• /
• v.8 no.3
• /
• pp.217-223
• /
• 2019

This paper presents the mechanical and microstructural properties of the geopolymer paste which was developed by utilizing the industrial by-products, rice husk ash (RHA) and ultra-fine slag. Ultra-fine slag particles with average particle size in the range of 4 to 5 microns. RHA is partially replaced with ultra-fine slag at different levels of 0 to 50%. Sodium silicate to sodium hydroxide ratio of 1.0 and alkaline liquid to binder (AL/B) ratio of 0.60 is taken. Setting time, compressive, flexural strengths were studied up to the age of 90 days with different concentrations of NaOH. The microstructure of the hybrid geopolymer paste was studied by performing the SEM, EDS, and XRD on the broken samples. RHA based geopolymer paste blended with ultrafine slag resulted in high compressive and flexural strengths and increased setting times of the paste. Strength increased with the increase in NaOH concentration at all ages. The ultra-small particles of the slag acted as a micro-filler into the paste and enhanced the properties by improving the CASH, NASH, and CSH. The maximum compressive strength of 70MPa was achieved at 30% slag content with 16M NaOH. The results of XRD, SEM, and EDS at 30% replacement of RHA with ultra-fine slag densified the paste microstructure.

• Journal of Advanced Engineering and Technology
• /
• v.11 no.4
• /
• pp.295-301
• /
• 2018

In this study, freezing-thawing resistance of concrete using steel slag as coarse aggregate(steel slag concrete) from Gwangyang Iron Co. was estimated to offer basic data for utilization of much more steel slag. Freezing-thawing test of concrete using crushed stone as coarse aggregate(crushed stone concrete) whose compressive strength and air contents are as close as possible to those of the steel slag concrete was performed. Because they are main two factors that affect of freezing-thawing resistance. The test was carried out up to 400 cycles according to KS F 2456. The compressive strength and weight of two concretes were measured and compared. As a result, the freezing-thawing resistance of steel slag concrete curing in water was almost the same with that of crushed stone concrete. But the resistance of steel slag concrete curing in air dry condition was weaker than that of crushed stone concrete. Also, the steel slag concrete which has more than 60% of W/C ratio showed much more surface degradation when compared to crushed stone concrete.

• Advances in concrete construction
• /
• v.12 no.6
• /
• pp.507-515
• /
• 2021

To evaluate the influence of slag on the alkalinity of pore solution and microstructure of concrete, this paper performs a leaching experiment on hardened cement-slag pastes (HCSP) slice specimens with different slag content in purified water. The pH value of pore solution, average porosity, morphology, phase composition and Ca/Si of HCSP specimens in the leaching process are measured by solid-liquid extraction, saturated-dried weighing, scanning electron microscopy-energy dispersive spectrometry (SEM-EDS) and X-ray diffraction (XRD). Results shows that the addition of slag can mitigate an increase in porosity and a decrease in Ca/Si of HCSP in the leaching process. Besides, an appropriate slag content can improve the microstructure so as to obtain the optimum leaching resistance of HCSP, which can guarantee the suitable alkalinity of pore solution to prevent a premature corrosion of reinforced bar. The optimum slag content is 40% in HCSP with a water-binder ratio of 0.45, and an excessive slag causes a significant decrease in the alkalinity of pore solution, resulting in a loss of protection on reinforced bar in HCSP.

• Progress in Superconductivity and Cryogenics
• /
• v.19 no.1
• /
• pp.22-25
• /
• 2017

Steel slag has been considered as an industrial waste. A huge amount of slag is produced as a byproduct and the steel slag usually has been dumped in a landfill site. However the steel slag contains valuable resources such as iron, copper, manganese, and magnesium. Superconducting magnetic separation has been applied on recovery of the valuable resources from the steel slag and this process also has intended to reduce the waste to be dumped. Cryo-cooled Nb-Ti superconducting magnet with 100 mm bore and 600 mm of height was used as the magnetic separator. The separating efficiency was evaluated in the function of magnetic field. A steel slag was ground and analyzed for the composition. Iron containing minerals were successfully concentrated from less iron containing portion. The separation efficiency was highly dependent on the particle size giving higher separating efficiency with finer particle. The magnetic field also effects on the separation ratio. Current study showed that an appropriate grinding of slag and magnetic separation lead to the recovery of metal resources from steel slag waste rather than dumping all of the volume.

• Korean Journal of Metals and Materials
• /
• v.50 no.10
• /
• pp.753-761
• /
• 2012

The reduction behavior of low level oxides such as (T.Fe), (MnO) and ($P_2O_5$) in molten EAF slag was investigated using commercial reductants. In an air atmosphere, the slag volume increased and the reduction rate of the slag was very low due to the oxidation loss of reductants by oxygen in the air. The reduction rate of the slag was also low when a commercial reductant was used alone in an Ar gas atmosphere. The reason is probably because the material transfer through the interface between the slag and reductant is difficult due to the formation of high melting point oxide. When reductants were mixed with burnt lime in order to form low melting point reaction products, the reduction rate of the slag increased up to the range of 45-70%. By using the mixtures of reductants and burnt lime so as to form a low melting point slag at the reaction end, the reduction rate of the slag was improved up to 60-85%.

• Journal of the Korean Society of Safety
• /
• v.30 no.4
• /
• pp.120-127
• /
• 2015

The aim of the present study is to investigate some characteristics of concrete according to addition of blast furnace slag and alkali-activator dosages. Blast furnace slag was used at 30%, 50% replacement by weight of cement, and liquid sulfur having NaOH additives was chosen as the alkaline activator. In order to evaluate characteristics of blast furnace slag concrete with sulfur alkali activators, compressive strength test, total porosity, chloride ions diffusion coefficient test were performed. The early-compressive strength characteristics of blast furnace slag concrete using a sulufr-alkali activators was compared with those of reference concrete and added 30, 50% blast furnace slag concrete. Also, Blast furnace slag concrete using sulfur-alkali activators enhanced the total porosity, chloride ions diffusion coefficient than two standard concrete. Alkali-activated blast furnace slag concrete was related to total porosity, compressive strength and chloride ions diffusion coefficient each others. As a result, it should be noted that the sulfur-alkali activators can not only solve the demerit of blast furnace slag concrete but also offer the chloride resistance of blast furnace slag concrete using sulfur alkali activators to normal concrete.

• Journal of the Korea Institute of Building Construction
• /
• v.18 no.6
• /
• pp.551-558
• /
• 2018

This study evaluate the fluidity and hardening properties of mortar by replacement ratio of ferronickel slag powder to estimate the applicability of ferronickel slag powder for cement replacement materials. Ferronickel slag powder was replaced by 0, 5, 10, 15 and 20% of the cement weight. In addition, blast furnace slag powder and fly ash were also used for comparing with the mixtures using ferronickel slag powder. As the test results, the micro-hydration heat of the mixture containing the ferronickel slag powder was lower than that of the mixtures containing the same amount of blast furnace slag powder and fly ash. The flow of the sample with ferronickel slag powder was relatively higher than the other mixtures. In all ages, the compressive strength of the mixture with ferronickel slag powder and fly ash was similar to that of the mix containing only fly ash. In case of drying shrinkage, the mixture containing ferronickel slag powder exhibited lower drying shrinkage than the mixture using blast furnace slag powder, and similar to the mixture containing fly ash.

• Advances in environmental research
• /
• v.8 no.1
• /
• pp.55-69
• /
• 2019

The generation of ferrous slag, an industrial by-product from the iron ore industry, results in serious environmental problems. The chemical compositions indicate 30-34% SiO₂, 30-34% CaO, 18-22% Al₂O₃ and 0.5-0.6% Fe₂O₃. The specific gravity, moisture content and pH are in the range of 1.3-1.65, 9.1-10% and 8.5-9.0 respectively. The major part of the slag is composed of sand-size particles. The problems of disposal of slag could be minimized by considering its use in various environmental engineering applications providing additional value to the by-product. This paper mainly focuses on the potential utilization and valorisation of ferrous slag in both water and wastewater treatments. It is effective for the treatment of water and wastewater containing nutrients, heavy metals and polluted river/stormwater.

• Journal of Ceramic Processing Research
• /
• v.19 no.5
• /
• pp.378-382
• /
• 2018

It is a known fact that the cement production is responsible for almost 5% of total worldwide $CO_2$ emission, the primary factor affecting global warming. Geopolymers are valuable as ordinary Portland cement (OPC) substitutes because geopolymers release 80% less $CO_2$ than OPC and have mechanical properties sufficiently similar to those of OPC. Therefore, geopolymers have proven attractive to eco-friendly construction industries. Geopolymers can be fabricated from aluminum silicate materials with alkali activators such as fly ash, blast furnace slag, and so on. Integrated gasification combined cycle (IGCC) slag has been used for fabricating geopolymers. In general, IGCC slag geopolymers are fabricated with finely ground and sieved (<128 mesh) IGCC slag. The grinding process of as-received IGCC slag is one of the main costs in geopolymer production. Therefore, the idea of using as-received IGCC slag (before grinding the IGCC slag) as aggregates in the geopolymer matrix was introduced to reduce production cost as well as to enhance compressive strength. As-received IGCC slag (0, 10, 20, 30, 40 wt%) was added in the geopolymer mixing process and the mixtures were compared. The compressive strength of geopolymers with an addition of 10 wt% as-received IGCC slag increased by 19.84% compared to that with no additional as-received IGCC slag and reached up to 41.20 MPa. The enhancement of compressive strength is caused by as-received IGCC slag acting as aggregates in the geopolymer matrix like aggregates in concrete. The density of geopolymers slightly increased to $2.1-2.2g/cm^3$ with increasing slag addition. Therefore, it is concluded that a small addition of as-received IGCC slag into the geopolymer can increase compressive strength and decrease the total cost of the product. Moreover, the direct use of as-received IGCC slag may contribute to environment protection by reducing process time and $CO_2$ emission.