• Tribology and Lubricants
• /
• v.30 no.4
• /
• pp.240-245
• /
• 2014

Low alloy heat resistant brake disk and sintered brake pad are applied to mechanical brake system for the speed-up of urban rapid transit. In this research, we analyzed how the frictional characteristics between brake disk and pad are influenced by the disk mass. At a high disk mass, the friction stability was the lower value as a result of the lack of tribofilm formation at the disk surface. Wear rates of friction materials showed the higher value at a low disk mass and wear rates of 10 mm and 15 mm showed the similar level. Average friction coefficient was the lower value at the 10 mm disk thickness and range of variation of average friction coefficient was also the smaller value at the 10 mm disk thickness. However, there were no significant changes in the friction coefficients under any of test conditions. Surface roughness of a disk showed the highest value at the 5 mm disk and surface roughnesses of 10 mm and 15 mm showed the similar level. As a result, friction characteristics of disk mass influenced the friction stability, as well as the wear rate of friction pad and disk, but not the friction coefficient.

• The Korean Journal of Ceramics
• /
• v.6 no.3
• /
• pp.193-200
• /
• 2000

Si$_3$N$_4$powder with 2 wt% $Al_2$O$_3$and 6 wt% $Y_2$O$_3$additives was sintered by the gas pressure sintering (GPS) technique. The unlubricated wear behavior depending on sintering conditions such as sintering temperature, pressure, and sintering time was investigated. When the sintering temperature and time increased, the larger elongated grains were formed and the microstructural heterogeneity increased. When sintering pressure increased, grain growth, however, was impeded. Also, the wear properties depended on microstructure and friction coefficient were related to grain size. Based on the experimental results, the wear properties were associated with initial friction coefficients as well as mechanical properties including fracture toughness and flexural strength.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2004.10a
• /
• pp.218-221
• /
• 2004

Dry sliding wear behavior of electro-pressure sintered Co, $Co-20\;wt.\%$ CuSn and $Co-20\;wt.\%$ WC composites were investigated. Wear tests of the materials were carried out using a pin-on-disk wear tester at various loads of 10N-100N under a constant sliding speed condition of 0.38m/s against glass ($83\%\;SiO_2$) beads. Sliding distances were varied with a range of $100m{\sim}600m$. A scanning electron microscopy was used to examine morphologies of worn surfaces, cross-sections, and wear debris. The $Co-20\;wt.\%$ WC composite had the highest and the $Co-20\;wt.\%$ CuSn composite showed the lowest wear resistance among the tested materials. All specimens exhibited low friction coefficients ranging from 0.12 to 0.4 at the applied load of 100N.

• Journal of Powder Materials
• /
• v.11 no.6 s.47
• /
• pp.451-461
• /
• 2004

Dry sliding wear behavior of electro-pressure sintered Co-Fe and Co-Ni compacts was investigated. Pin-on-disk wear tests were performed on the sintered Co-Fe, Co-Ni disks against alumina $(Al_2O_3)$ and silica $(SiO_2)$ balls at various loads ranging from 3N to 12N. A constant sliding speed of 0.1m/sec was employed. Wear rate was calculated by dividing the weight loss of a specimen by the measured specific gravity and sliding dis-tance. Worn surfaces and cross-sections of the specimens were examined using an SEM and EDS to investigate wear mechanism of the compacts. The wear behavior of the compacts were discussed as a function of their com-position. Effects of mechancial properties of the compact as well as oxide layers formed on wearing surface on the wear were also discussed.

• Journal of Advanced Marine Engineering and Technology
• /
• v.24 no.6
• /
• pp.139-146
• /
• 2000

The development of high performance materials is very important subject in order to enhance the properties of bearings whose role is to transfer energy harmoniously by reducing the problem of friction and wear down, etc. between the interacting solid surfaces in relative motion under high loads in comply with mechanical operating mechanism of engines. In this study, several (100-x)Al-xSn coating films (where x=85, 75, 65 atomic % at Al) on substrates which are abt. 2mm thickenss of Kelmet layer sintered back steel were prepared by using RF sputtering system. These coating films were observed the morphology by SEM(Scanning Electron Microscope) and investigated the crystal structure by XRD(X-ray Diffractor) for their properties. And friction coefficient of these films was measured by ball-on-disc tester for their tribological properties. From the experimental results, it was shown that high performance properties of bearing can be improved greatly by controlling the composition and morphology of material surface with effective use of the plasma-assisted sputtering process.

• The Korean Journal of Ceramics
• /
• v.3 no.1
• /
• pp.47-51
• /
• 1997

The dense sintered bodies of Si/SiC composite with various Si contents could be fabricated by changing the green density in the forming process. The Si/SiC/graphite composites with various graphite contents could be also fabricated by changing a graphite content in the starting composition. Their mechanical and tribological properties were characterized and wear mechanism was also studided. The hardness and strength of the Si/SiC and the Si/SiC/graphite were decreased with increasing the contents of free Si and graphite, respectively. However, the friction coefficient and specific wear rate had no specific relations to their hardness and strength. Adhesion of free Si was a main factor to determine a wear resistance of the Si/SiC composite. In the case of the Si/SiC/graphite, solid lubricationl and liquid reservoir of the graphite particles played the main role of the reduction of the friction force. In the torque test to estimate the possibility of practical of practical applications, the value of torque between the Al2O3 disk and Si/SiC/graphite disk was 1/6 lower compared with two $Al_2O_3$ disks on the basis of 100,000 cycles.

• Journal of the Korean Ceramic Society
• /
• v.35 no.7
• /
• pp.721-725
• /
• 1998

In this study solid-phase sintered silicon caribide samples composed of SiC powder having boron and car-bon black as additives were prepared by pressureless sintering at $1950^{\circ}C$. The bending strength the frac-ture toughness and the specific werar rate of the samples were examined and the micro structures of the broken and the worn surface were observed by SEM to understand the relationship between the tri-bological charcteristics and the micro structure. Additionally the relationship between the micro struc-tures and the tribological characteristics of the samples for the frictional opponents SiC and $Al_{2}O_{3}$ pins were investigated Conclusions are as follows ; 1. The specific were rate of the samples for the SiC pin was larger than that for the $Al_{2}O_{3}$ pin. HOwever the specific wear rate for the $Al_{2}O_{3}$ pin was increased about 6,45 times as that for the SiC pin under the load increasing. 2. The specific wear rate of the SiC pin was larger than that of the $Al_{2}O_{3}$ pin. owever the specific wear rate of the $Al_{2}O_{3}$ pin was increased about 4 times as that of the SiC pin under the load increasing 3. The micro stucture of the worn surface showed a flat face without cracks in the case that the frictional opponents has the low friction coefficient but in the case of without cracks in the case that the frictional opponents has the low friction coefficient but in the case of the high friction coefficient the micro structure of the worn surface showed an uneven face having spread-ed cracks. 4. The tribological characteristics of thesolid-phase sintered SiC samples was similar to that of li-quid-phase sintered ones when the pin having the high friction coefficient was used.

• Journal of Surface Science and Engineering
• /
• v.47 no.5
• /
• pp.263-268
• /
• 2014

Nanocrystalline diamond(NCD) coated SiC balls were applied in a ball-on-disk tribometer. After seeding in an ultrasonic bath containing nanometer diamond powders, $2.2{\mu}m$ thick NCD films were deposited on sintered 3 mm diameter SiC balls at $600^{\circ}C$ in a 2.45 GHz microwave plasma CVD system. Bare $ZrO_2$ and SiC balls were prepared for comparison as test balls. Tribology tests were performed in air with pairs of three different balls and mirror polished steel(SKH51) disk. The wear tracks on balls and disks were examined by optical microscope and alpha step profiler. Under the load of 3 N, the friction coefficients of steel against $ZrO_2$, SiC and NCD-coated balls were between 0.4 and 0.8. After a few thousands sliding laps, the friction coefficient of NCD-coated balls dropped from 0.45 to below 0.1 and maintained thereafter. Under a higher load of 10 N or 20 N with a long sliding distance of 2 km, $ZrO_2$ and SiC balls exhibited the similar friction coefficients as above. The friction coefficient of NCD-coated balls was less than 0.1 from the beginning and increased to above 0.1 steadily or with some fluctuations as sliding distance increased. NCD coating layers were found worn out after long duration and/or high load sliding test, which resulted in the friction coefficient higher than 0.1.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.32 no.11
• /
• pp.1003-1009
• /
• 2008

In this study, liquid phase sintered SiC (LPS-SiC) materials were made by hot pressing method. The particle size of nano-SiC powder was 30nm. Alumina ($Al_2O_3$), yttria ($Y_2O_3$) and silica ($SiO_2$) were used for sintering additives. To investigate effects of $SiO_2$, ratios of $SiO_2$ contents were changed by five kinds. Materials have been sintered for 1 hour at $1760^{\circ}C$, $1780^{\circ}C$ and $1800^{\circ}C$ under the pressure of 20MPa. The system of sintering additives which affects a property of sintering as well as the influence depending on compositions of sintering additives were investigated by measurement of density, mechanical properties such as flexural strength, vickers hardness and sliding wear resistance were investigated to make sure of the optimum condition which is about matrix of $SiC_f$/SiC composites. The abrasion test condition apply to load of 20N at 100RPM for 20min. Sintered density, flexural strength of fabricated LPS-SiC increased with increasing the sintering temperature. And in case of LPS-SiC with low $SiO_2$, sliding wear resistance has very excellent. Monolithic SiC $1800^{\circ}C$ sintering temperatures and 3wt% have excellent wear resistance.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.177-178
• /
• 2006

The results of monotonic and cyclic uniaxial compression tests, in which the deviatoric component of the stress is predominant, carried out on green and recrystallized iron compacts with different levels of density are presented and discussed in order to analyse the macro and micro-mechanisms governing the mechanical behaviour of non-sintered PM materials. The plastic deformation of the particles, especially at the contact areas between neighbouring grains, produces an internal friction responsible for the main features observed in the behaviour of green metallic compacts. These results show important discrepancies with the plasticity models, Cam-Clay and Drucker-Prager Cap.