• Restorative Dentistry and Endodontics
• /
• v.30 no.4
• /
• pp.312-318
• /
• 2005

This study compared the microtensile bond strength $({\mu}TBS)$ of three single step adhesives to dentin. Occlusal superficial dentin was exposed in fifteen human molars. They were assigned to three groups by used adhesives: Xeno group (Xeno III). Prompt group (Adper Prompt L-Pop). AQ group (AQ Bond). Each adhesive was applied to dentin surface. and composite of same manufacturer was constructed. The bonded specimens were sectioned into sticks with an interface area approximately $1mm^2$, and subjected to $\mu$ TBS testing with a crosshead speed of 1mm/minute. The results of this study were as follows; 1. The ${\mu}TBS$ to dentin was $48.78\pm9.83MPa$ for Xeno III. $30.22\pm4.52MPa$ for Adper Prompt L-Pop. and $26.31\pm7.07MPa$ for AQ Bond. 2. The mean ${\mu}TBS$ of Xeno group was significantly higher than that of Prompt group and AQ group (p<0.05). 3. There was no significant difference between the ${\mu}TBS$ of Prompt group and AQ group.

• Restorative Dentistry and Endodontics
• /
• v.35 no.3
• /
• pp.164-172
• /
• 2010

During a composite resin restoration, an anticipating contraction gap is usually tried to seal with low-viscosity resin after successive polishing, etching, rinsing and drying steps, which as a whole is called rebonding procedure. However, the gap might already have been filled with water or debris before applying the sealing resin. We hypothesized that microleakage would decrease if the rebonding agent was applied before the polishing step, i.e., immediately after curing composite resin. On the buccal and lingual surfaces of 35 extracted human molar teeth, class V cavities were prepared with the occlusal margin in enamel and the gingival margin in dentin. They were restored with a hybrid composite resin Z250 (3M ESPE, USA) using an adhesive AdperTM Single Bond 2 (3M ESPE). As rebonding agents, BisCover LV (Bisco, USA), ScotchBond Multi-Purpose adhesive (3M ESPE) and an experimental adhesive were applied on the restoration margins before polishing step or after successive polishing and etching steps. The infiltration depth of 2% methylene blue into the margin was measured using an optical stereomicroscope. The correlation between viscosity of rebonding agents and mciroleakage was also evaluated. There were no statistically significant differences in the microleakage within the rebonding procedures, within the rebonding agents, and within the margins. However, when the restorations were not rebonded, the microleakage at gingival margin was significantly higher than those groups rebonded with 3 agents (p < 0.05). The difference was not observed at the occlusal margin. No significant correlation was found between viscosity of rebonding agents and microleakage, except very weak correlation in case of rebonding after polishing and etching at gingival margin.

• Restorative Dentistry and Endodontics
• /
• v.25 no.2
• /
• pp.299-308
• /
• 2000

The purpose of this in vitro study was to evaluate the microleakage of 5 curing methods in class V composite restorations which are composed of two-step light curing, pulse-delay cure, low curing-light intensity, moderate curing-light intensity and high curing-light intensity. In this study, class V cavities were prepared on buccal and lingual surfaces of 50 extracted human upper or lower molars on cementum margin. Single Bond adhesive and Z-100 shade A2 were applied for each group following the manufacture's instruction. The experimental teeth were randomly divided into 5 groups of 10 samples (20 surfaces) each. Group 1: two-step light curing; Group 2: pulse-delay cure; Group 3: low curing-light intensity; Group 4: moderate curing-light intensity; Group 5: high curing-light intensity. After 500 thermocycling between $5^{\circ}C$ and $55^{\circ}C$, the 60 teeth were placed in 2% methylene blue dye for 24 hours, then rinsed with tab water. The specimens were embedded in clear resin, then sectioned buccolingually through the center of restoration with a low speed diamond saw. The dye penetration on each of the specimen was then observed with a stereomicroscope at ${\times}20$. The composite resin/tooth interfaces were examined under Scanning Electron Microscopy. The results were statistically analyzed using the Kruskal-Wallis One Way ANOVA and Dunn's Method. The results of this study were as follows. 1. In all groups, the leakage values seen at the enamel margin were significantly lower than those seen at the dentin margin(P<0.05). 2. No group in this study showed significant differences in leakage values at both the enamel and the dentin margins(P<0.05). 3. In all groups, the gaps seen at the enamel margin were significantly lower than those seen at the dentin margin(P<0.05). 4. The gaps in this study showed significant differences and two-step light-curing and low curing-light intensity produced significant less gap than high curing-light intensity(P<0.05).

• Restorative Dentistry and Endodontics
• /
• v.36 no.5
• /
• pp.409-418
• /
• 2011

Objectives: The purpose of this study was to compare the microshear bond strength (${\mu}$SBS) and bonding interfaces of two-step total-etching and self-etching adhesive systems to three etch types of dentin either the acid etched, laser etched or laser and acid etched. Materials and Methods: The occlusal dentinal surfaces of thirty human molars were used. They were divided into six groups: group 1, 37% $H_3PO_4$ + Single Bond 2 (3M ESPE); group 2, Er:YAG laser (KEY Laser 3, KaVo) + Single Bond 2; group 3, Er:YAG laser + 37% $H_3PO_4$ + Single Bond 2; group 4, Clearfil SE Primer + Bond (Kuraray); group 5, Er:YAG laser + Clearfil SE Bond; group 6, Er:YAG laser + Clearfil SE Primer + Bond. The samples were subjected to ${\mu}$SBS testing 24 hr after bonding. Also scanning microscopic evaluations were made on the resin-dentin interfaces of six specimens. Results: The ${\mu}$SBS of group 2 was significantly lower than that of groups 1 and 3 in Single Bond 2 (p < 0.05). There were significant differences among the uSBS of groups 4, 5, and 6 in Clearfil SE Bond (p < 0.05). Very short and slender resin tags were observed in groups 2 and 5. Long and slender resin tags and lateral branches of tags were observed in groups 3 and 6. Conclusions: Treatment of dentin surface using phosphoric acid or self-etching primer improved the adhesion of Er:YAG lased dentin.

• Restorative Dentistry and Endodontics
• /
• v.30 no.4
• /
• pp.344-351
• /
• 2005

This study compared the microshear bond strength $({\mu}SBS)$ to end and side of enamel rod bonded by four adhesives including two total etch adhesives and two self-etch adhesives. Crown segments of extracted human molars were cut mesiodistally. The outer buccal or lingual surface was used as specimens cutting the ends of enamel rods, and inner slabs used as specimens cutting the sides of enamel rods. They were assigned to four groups by used adhesives: Group 1 (All-Bond 2), Group 2 (Single Bond), Group 3 (Tyrian SPE/One-Step Plus), Group 4 (Adper Prompt L-Pop). After each adhesive was applied to enamel surface, three composite cylinders were adhered to it of each specimen using Tygon tube. After storage in distilled water for 24 hours, the bonded specimens were subjected to ${\mu}SBS$ testing with a crosshead speed of 1 mm/minute. The results of this study were as follows: 1. The $({\mu}SBS)$ of Group 2 $(16.50\pm2.31 MPa)$ and Group 4 $(15.83\pm2.33 MPa)$ to the end of enamel prism was significantly higher than that of Group 1 $(11.93\pm2.25 MPa)$ and Group 3 $(11.97\pm2.05 MPa)$ (p<0.05). 2. The $({\mu}SBS)$ of Group 2 $(13.43\pm2.93 MPa)$ to the side of enamel prism was significantly higher than that of Group 1 $(8.64\pm1.53 MPa)$, Group 3 $(9.69\pm1.80 MPa)$, and Group 4 $(10.56 \pm1.75 MPa)$ (p<0.05), 3. The mean $({\mu}SBS)$ to the end of enamel rod was significantly higher than that to the side of enamel rod in all group (p<0.05).

• Restorative Dentistry and Endodontics
• /
• v.35 no.3
• /
• pp.211-221
• /
• 2010

Proteoglycan is highly hydrophilic and negatively charged which enable them attract the water. The objective of study was to investigate the effects of Proteoglycan on microtensile bond strength of dentin adhesives and on architecture of dentin collagen matrix of acid etched dentin by removing the chondroitin sulphate attached on Proteoglycan. A flat dentin surface in mid-coronal portion of tooth was prepared. After acid etching, half of the specimens were immersed in 0.1 U/mL chondroitinase ABC (C-ABC) for 48 h at $37^{\circ}C$, while the other half were stored in distilled water. Specimens were bonded with the dentin adhesive using three different bonding techniques (wet, dry and re-wet) followed by microtensile bond strength test. SEM examination was done with debonded specimen, resin-dentin interface and acid-etched dentin surface with/without C-ABC treatment. For the subgroups using wet-bonding or dry-bonding technique, microtensile bond strength showed no significant difference after C-ABC treatment (p > 0.05). Nevertheless, the subgroup using rewetting technique after air dry in the Single Bond 2 group demonstrated a significant decrease of microtensile bond strength after C-ABC treatment. Collagen architecture is loosely packed and some fibrils are aggregated together and relatively collapsed compared with normal acid-etched wet dentin after C-ABC treatment. Further studies are necessary for the contribution to the collagen architecture of noncollagenous protein under the various clinical situations and several dentin conditioners and are also needed about long-term effect on bond strength of dentin adhesive.

• Restorative Dentistry and Endodontics
• /
• v.24 no.2
• /
• pp.310-321
• /
• 1999

In this in vitro study, confocal laser scanning microscopic morphology of dentin-resin interface and its relationship to shear bond strength were investigated after the exposed dentin surfaces were treated with 3 different kinds of dentin adhesive systems[three-step; Scotchbond Multi-Purpose Plus(SMPP), self-priming bonding resin; Single Bond(SB), self-etching primer; Clearfil Liner Bond 2(LB2)]. 52 extracted human molar teeth without caries and/or restorations. The experimental teeth were randomly divided into three groups of seventeen teeth each. In five teeth of each group, class V cavities(depth: 1.5mm) with 900 cavosurface angles were prepared at the cementoenamel junction on buccal and lingual surfaces. Bonding resins of each dentin adhesive system were mixed with rhodamine B. Primer of SMPP was mixed with fluorescein. In group 1. the exposed dentin was conditioned with etchant, applied with above primer and bonding resin of SMPP. In group 2, with etchant and self-priming bonding agent of SB. In group 3, with self-etching primer and bonding agent of LB2. After treatment with dentin adhesive systems, composite resin were applied and photocured. The experimental teeth were cut longitudinally through the center line of restoration and grounded so that about $90{\mu}m$-thick wafers of buccolingually orientated dentin were obtained. And, $70{\sim}80{\mu}m$-thick wafers sectioned horizontally, thus presenting a dentinal tubules at 900 to the cut surface of a remaining tooth, were obtained. Primer of SMPP mixed with rhodamine B was applied to these wafers. Confocal laser scanning microscopic investigations of these wafers were done within of 24 hours after treatment. To measure shear bond strength, the remaining twelve teeth of each group were grounded horizontally below the dentinoenamel junction, so that no enamel remained. After applying dentin adhesive systems on the dentin surface, composite was applied in the shape of cylinder. The cylinder was 5mm in diameter, and 2mm in thickness. Shear bond strength was measured using Instron with a cross-head speed of 0.5mm/min. It was concluded as follows ; 1. Hybrid layer of SMPP(mean: $4.56{\mu}m$) was thicker than that of any other groups. This value was not statistically significant thicker than that of SB(mean: $3.41{\mu}m$, p>0.05), and significant thicker than that of LB2(mean: $1.56{\mu}m$, p<0.05). There was a statistical difference between SB and LB2(p<0.05). 2. Although there were variations in the length of resin tag even in a sample, and in a group, most samples in SMPP and SB showed resin tags extending above $20{\mu}m$. But samples in LB2 showed resin tags of $10{\mu}m$ at best. 3. Besides primer's infiltration into demineralized peritubular dentin and dentinal tubules, fluorophore of primer was detected in the lateral branches of dentinal tubules. 4. All groups demonstrated statistically significant differences from one another(p<0.05), with shear bond strengths given in descending order as follows: SMPP(18.3MPa), SB(16.0MPa) and LB2(12.4MPa). 5. LB2 having thinnest hybrid layer($1.56{\mu}m$) showed the lowest shear bond strength(12.4MPa).

• Restorative Dentistry and Endodontics
• /
• v.34 no.2
• /
• pp.87-94
• /
• 2009

The purpose of this study was to assess the current materials, methods and difficulties according to the year of licence and educational background of Korean dentists in Class II direct composite resin restorations. Total 17 questions were included in the questionnaire. Questions were broadly divided into two parts: first. operator's information. and second. the materials and methods used in Class II posterior composite restoration. The questionnaire was sent to dentists enrolled in Korean Dental Association via e-mail. Total 12,193 e-mails were distributed to dentists. 2,612 e-mails were opened, and 840 mails (32.2%) were received from respondents. The data was statically analyzed by chi-square test using SPSS(v. 12.0.1, SPSS Inc. Chicago, IL, USA). Male dentists among respondents was 79%. 60.3% of the respondents acquired their licences recently (1998-2007), and 77% practiced in private offices. 83.4% have acquired their knowledge through school lectures, conferences and seminars. For the Class II restorations, gold inlays were preferred by 65.7% of respondents, while direct composite resin restorations were used by 12.1 % amalgam users were only 4.4% of respondents. For the restorative technique, 74.4% of respondents didn't use rubber dam as needed. For the matrix. mylar strip (53.4%), metal matrix (33.8%) and Palodent system (6.5%) were used. 99.6% of respondents restored the Class II cavity by incremental layering. Obtaining of the tight interproximal contact was considered as the most difficult procedure (57.2%) followed by field isolation (21 %). Among various bonding systems, 22.6% of respondents preferred SE Bond and 20.2% used Single Bond. Z-250 was used most frequently among a variety of composite resins.