• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.08a
• /
• pp.281-281
• /
• 2010

Very low refractive index (<1.4) materials have been proved to be the key factor improving the performance of various optical components, such as reflectors, filters, photonic crystals, LEDs, and solar cell. Highly porous SiO2 are logically designed for ultralow refractive index materials because of the direct relation between porosity and index of refraction. Among them, ordered macroporous SiO2 is of potential material since their theoretically low refractive index ~1.10. However, in the conventional synthesis of ordered macroporous SiO2, the time required for the crystallization of organic nanoparticles, such as polystyrene (PS), from colloidal solution into well ordered template is typical long (several days for 1 cm substrate) due to the low interaction between particles and particle - substrate. In this study, polystyrene - polyacrylic acid (PS-AA) nanoparticles synthesized by miniemulsion polymerization method have hydrophilic polyacrylic acid tails on the surface of particles which increase the interaction between particle and with substrate giving rise to the formation of PS-AA film by simply spin - coating method. Less ordered with controlled thickness films of PS-AA on silicon wafer were successfully fabricated by changing the spinning speed or concentration of colloidal solution, as confirmed by FE-SEM. Based on these template films, a series of macroporous SiO2 films whose thicknesses varied from 300nm to ~1000nm were fabricated either by conventional sol - gel infiltration or gas phase deposition followed by thermal removal of organic template. Formations of SiO2 films consist of interconnected air balls with size ~100 nm were confirmed by FE-SEM and TEM. These highly porous SiO2 show very low refractive indices (<1.18) over a wide range of wavelength (from 200 to 1000nm) as shown by SE measurement. Refraction indices of SiO2 films at 633nm reported here are of ~1.10 which, to our best knowledge, are among the lowest values having been announced.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.48 no.9
• /
• pp.623-627
• /
• 1999

We report a new in-situ fluorine passivation method without in implantation by employing excimer laser annealing of $SiO_{x}F_{y}$/a-Si structure and its effects on p-channel poly-Si TFTs. The proposed method doesn't require any additional annealing step and is a low temperature process because fluorine passivation is simultaneous with excimer-laser-induced crystallization. A in-situ fluorine passivation by the proposed method was verified form XPS analysis and conductivity measurement. From experimental results, it has been shown that the proposed method is effective to improve the electrical characteristics, specially field-effect mobility, and the electrical stability of p-channel poly-Si TFTs. The improvement id due to fluorine passivation, which reduces the trap state density and forms the strong Si-F bonds in poly-Si channel and $SiO_2/poly-Si$ interface. From these results, the high performance poly-Si TFTs canbe obtained by employing the excimer-laser-induced fluorine passivation method.

• Korean Journal of Metals and Materials
• /
• v.48 no.2
• /
• pp.133-140
• /
• 2010

10 nm thick Ni layers were deposited on 200 nm $SiO_2/Si$ substrates using an e-beam evaporator. Then, 60 nm or 20 nm thick ${\alpha}$-Si:H layers were grown at low temperature (<$200^{\circ}C$) by a Catalytic-CVD. NiSi layers were already formed instantaneously during Cat-CVD process regardless of the thickness of the $\alpha$-Si. The resulting changes in sheet resistance, microstructure, phase, chemical composition, and surface roughness with the additional rapid thermal annealing up to $500^{\circ}C$ were examined using a four point probe, HRXRD, FE-SEM, TEM, AES, and SPM, respectively. The sheet resistance of the NiSi layer was 12${\Omega}$/□ regardless of the thickness of the ${\alpha}$-Si and kept stable even after the additional annealing process. The thickness of the NiSi layer was 30 nm with excellent uniformity and the surface roughness was maintained under 2 nm after the annealing. Accordingly, our result implies that the low temperature Cat-CVD process with proposed films stack sequence may have more advantages than the conventional CVD process for nano scale NiSi applications.

• Journal of Sensor Science and Technology
• /
• v.1 no.2
• /
• pp.173-181
• /
• 1992

Tantalum pentoxide($Ta_{2}O_{5}$) thin films on p-type (100) silicon wafer were fabricated by RF reactive sputtering. Physical properties and structure of the specimens were examined by XRD and AES. From the C-V analysis, the dielectric constant of $Ta_{2}O_{5}$ films was in the range of 10-12 in the reactive gas atmosphere in which 10% of oxygen gas is mixed. The ratio of Ta : 0 was 1 : 2 and 1 : 2.49 by AES and RBS examination, respectively. The heat-treatment at $700^{\circ}C$ in $O_{2}$ ambient led to induce crystallization. When the heat-treatment temperature was $1000^{\circ}C$, the dielectric constant was 20.5 in $O_{2}$ ambient and 23 in $N_{2}$ ambient, respectively. The crystal structure of $Ta_{2}O_{5}$ film was pseudo hexagonal of ${\delta}-Ta_{2}O_{5}$. The flat band voltage shift(${\Delta}V_{FB}$) of the specimens and the leakage current density were decreased for higher oxygen mixing ratio. The maximum breakdown field was 2.4MV/cm at the oxygen mixing ratio of 10%. The $Ta_{2}O_{5}$ films will be applicable to hydrogen ion sensitive film and gate oxide material for memory device.