• Journal of the Korean Ceramic Society
• /
• v.44 no.8
• /
• pp.445-450
• /
• 2007

A conversion layer of SiC was fabricated on the graphite substrate by a chemical vapor reaction method in order to enhance the oxidation resistance of graphite. The effect of boron carbide containing powder bed on the morphology of SiC conversion layer was investigated during the chemical vapor reaction of graphite with the reactive silicon-source at $1650^{\circ}C\;and\;1700^{\circ}C$ for 1 h. The presence of boron species enhanced the conversion of graphite into SiC, and altered the morphology of the conversion layer significantly as well. A continuous and thick SiC conversion layer was formed only when the boron source was used with the other silicon compounds. The boron is deemed to increase the diffusion of SiOx in SiC/C system.

• Journal of Power System Engineering
• /
• v.17 no.1
• /
• pp.110-115
• /
• 2013

The electrochemical performance and microstructure of Al-Si, Al-Si/C was investigated as anode for lithium ion battery. The Al-Si nano composite with 5 : 1 at% ratio was prepared by arc-discharge nano powder process. However, some of problem is occurred, when Al nano composite was synthesized by this manufacturing. The oxidation film is generated around Al-Si particles for passivating processing in the manufacture. The oxidation film interrupts electrical chemistry reaction during lithium ion insertion/extraction for charge and discharge. Because of the existence the oxidation film, Al-Si first cycle capacity is very lower than other examples. Therefore, carbon synthsized by glucose ($C_6H_{12}O_6$) was conducted to remove the oxidation film covered on the composite. The results showed that the first discharge cycle capacity of Al-Si/C is improved to 113mAh/g comparing with Al-Si (18.6mAh/g). Furthermore, XRD data and TEM images indicate that $Al_4C_3$ crystalline exist in Al-Si/C composite. In addition the Si-Al anode material, in which silicon is more contained was tested by same method as above, it was investigated to check the anode capacity and morphology properties in accordance with changing content of silicon, Si-Al anode has much higher initial discharge capacity(about 500mAh/g) than anode materials based on Aluminum as well as the morphology properties is also very different with the anode based Aluminum.

• Bulletin of the Korean Chemical Society
• /
• v.27 no.8
• /
• pp.1175-1180
• /
• 2006

Si-C composites were prepared by the carbonization of polyaniline (PAn) coated on silicone powder. The physical and electrochemical properties of the Si-C composites were characterized by particle-size analysis, X-ray diffraction, scanning electron microscopy, and battery electrochemical tests. The average particle size of Si was increased by the coating of Pan but somewhat reduced by the carbonization to give silicone-carbon composites. The co-existence of crystalline silicone and amorphous-like carbon was confirmed by XRD analyses. SEM photos showed that the silicone particles were well covered with carbonaceous materials, depending on the PAn content. Si-C$\mid$Li cells were fabricated using the Si-C composites and tested using galvanostatic charge-discharge. Si-C$\mid$Li cells gave better electrochemical properties than Si|Li cells. Si-C$\mid$Li cells using Si-C from HCl-undoped precursor PAn showed better electrochemical properties than precursor PAn doped in HCl. The addition of an electrolyte containing 4-fluoroethylene carbonate (FEC) increased the initial discharge capacity. Also, another electrochemical test, the galvanostatic charge-discharge test with GISOC (gradual increasing of the state of charge) was carried out. Si-C(Si:PAn = 50:50 wt. ratio)|Li cell showed 414 mAh/g of reversible specific capacity, 75.7% of IIE (initial intercalation efficiency), 35.4 mAh/g of IICs (surface irreversible specific capacity).

• Applied Chemistry for Engineering
• /
• v.24 no.3
• /
• pp.231-238
• /
• 2013

In this study, the $TiO_2$ nano spheres were synthesized by Sol-gel method to give an excellent UV-blocking effect and increase waste adsorption. The pH value was adjusted to obtain a superb UV-blocking effect and adsorption capacity due to the high surface area which is the characteristics of porosity. Base treated $TiO_2$ showed outstanding characteristics. The adsorption of gycerine onto the $TiO_2$ sample using TGA resulted in a high surface area of 1.16 mg/mg. This also showed a high reflectance in the UV-A region. In order to find the optimum dispersion, inorganic powder particles were maintained their sizes as 180 nm for about 6 months. The size of particles were measured using ester oil and silicon oil. Overall, the results reveal that $TiO_2$ has an excellent capability sunscreen in the UV-A region and skin waste adsorption.

• Proceedings of the Korea Committee for Ocean Resources and Engineering Conference
• /
• 2006.11a
• /
• pp.181-184
• /
• 2006

Nano Infiltration Transient Eutectic Phase - Silicon Carbide (NITE-SiC) and $SiC_f/SiC$ composite have been fabricated by a Hot Pressing (HP) process, using SiC powder with an average size of about 30nm. Alumina ($Al_2O_3$) and Yttria ($Y_2O_3$) were used for additives materials. These mixed powders were sintered at the temperature a of $1300^{\circ}C$, $1650^{\circ}C$, $1800^{\circ}C$ and $1900^{\circ}C$ under an applied pressure of 20MPa. And unidirection and two dimension woven structures of $SiC_f/SiC$ composites were prepared starting from Tyranno SA fiber. Densification of microstructure gives an effect to density. Specially, Densification Mechanism basically is important from the sintering which use the HP. In this study, the densification of NITE-SiC and $SiC_f/SiC$ composite mechanism by a press displacement appears investigated. The mechanism on the densification of each sintering temperature was investigated. The each step is shows a with each other different mechanism quality.

• International Journal of Korean Welding Society
• /
• v.1 no.1
• /
• pp.58-62
• /
• 2001

The surface of AC8A Ah alloy was modified by adding the Cu powder using a Plasma Transferred Arc (PTA) welding process. Under the optimum fabricating conditions, the modified surface of AC8A Ah alloy was observed to possess the sound microstructure with a minimum porosity. Hardness and wear resistance properties of the as-fabricated alloy were compared with those of the 76 heat-treated one. In case of the as-fabricated alloy, the hardness of the modified layer was twice that of the matrix region. Although significant increase in the hardness of the matrix region was observed after T6 heat treatment, the hardness of the modified layer was not observed to change. The wear resistance of the modified layer was significantly increased compared to that of the matrix region. The microstructure of a weld zone and the matrix region were investigated using the optical microscope, scanning electron microscope (SEM), electron probe microanalysis (EPMA), and transmission electron microscope (TEM). The primary and eutectic silicon in the weld zone were finer and more curved than in the matrix region, while some precipitates has had been found therein. According to the TEM observation, the predominant precipitate present in the weld zone was the $\theta$'phase, which is precipitated during cooling by rapid solidification in PTA welding process. Improvement of hardness and wear properties in the weld zone in the as-fabricated condition can be explained based on the presence of $\theta$’precipitates and fine primary and eutectic silicon distribution.

• Journal of the Korean Ceramic Society
• /
• v.36 no.12
• /
• pp.1356-1363
• /
• 1999

Self-reinforced silicon carbide was prepared by hot pressing and the control of starting phases of raw materials and its microstructural characteristics was investigated. The specimens with self-reinforced microstructure were obtained from the compacts with mixed compositions of ${\alpha}$-and ${\beta}$-SiC powders. Self-reinforced microstructure which is composed of large dispersed grains with rod-like shape and matrix with small equiaxed grains was formed by the transformation to the ${\alpha}$-SiC with 4H polytype for ${\beta}$-SiC and anisotropic grain growth during the heat treatment. Of all speimens the values of volume fraction maximum length and aspect ratio for large grains with rode-like types were the highest at the specimen with 50 vol% ${\beta}$-SiC in the starting SiC powder and therefore this specimen showed the highest fracture toughness due to the crack deflection by rod-like grains during crack propagation.

• Journal of the Korean Ceramic Society
• /
• v.38 no.5
• /
• pp.405-411
• /
• 2001

Compacts of a mixture of fine $\alpha$-Si$_3$N$_4$powders, 6% $Y_2$O$_3$and 1% $Al_2$O$_3$were attrition milled time on phase and microstructural development in silicon nitride ceramics. The sintered surface and the interior showed different behaviors in phase and microstructral developments. Increased oxygen content with increased milling time of powder mixture leads to the formation of Si$_2$$N_2$O phase at temperatures as low as 155$0^{\circ}C$. Si$_2$$N_2$O is stable in the interior of the samples but unstable in the surface region of the specimen sintered at higher temperature. This results in a duplex structure where the interior consists of Si$_2$$N_2$O grains dispersed in $\beta$-Si$_3$N$_4$matrix and a surface which contains only $\beta$-Si$_3$N$_4$. The alpha to beta phase transformation and the microstructural development are shown to be influenced by the formation and decomposition of the Si$_2$$N_2$O.

• Journal of the Korean Ceramic Society
• /
• v.50 no.6
• /
• pp.402-409
• /
• 2013

The objective of this study was to develop a synthesis process for ${\beta}$-SiC powders to reduce the synthesis temperature and to control the particle size and to prevent particle agglomeration of the synthesized ${\beta}$-SiC powders. A phenol resin and TEOS were used as the starting materials for the carbon and Si sources, respectively. $SiO_2$-C hybrid precursors with various C/Si mole ratios were fabricated using a conventional sol-gel process. ${\beta}$-SiC powders were synthesized by a carbothermal reduction process using $SiO_2$-C hybrid precursors with various C/Si mole ratios (1.6 ~ 2.5) fabricated using a sol-gel process. In this study, the effects of excess carbon and the addition of Si powders to the $SiO_2$-C hybrid precursor on the synthesis temperature and particle size of ${\beta}$-SiC were examined. It was found that the addition of metallic Si powders to the $SiO_2$/C hybrid precursor with excess carbon reduced the synthesis temperature of the ${\beta}$-SiC powders to as low as $1300^{\circ}C$. The synthesis temperature for ${\beta}$-SiC appeared to be reduced with an increase of the C/Si mole ratio in the $SiO_2$-C hybrid precursor by a direct carburization reaction between Si and excess carbon.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.30 no.6
• /
• pp.271-276
• /
• 2020

In this study, an amorphous SiC block was manufactured using polycarbosilane (PCS), an organosilicon polymer. The dense SiC blocks were easily fabricated in various shapes via pyrolysis at 1100℃, 1200℃, 1300℃, 1400℃ after manufacturing a PCS molded body using cured PCS powder. Physical and chemical properties were analyzed using a thermogravimetric analyzer (TGA), scanning electron microscope (SEM), energy dispersive spectroscopy (EDS), and universal testing machine (UTM). The prepared SiC block was decomposed into SiO and CO gas as the temperature increased, and β-SiC crystal grains were grown in an amorphous structure. In addition, the density and flexural strength were the highest at 1.9038 g/㎤ and 6.189 MPa of SiC prepared at 1100℃. The manufactured amorphous silicon carbide block is expected to be applicable to other fields, such as the previously reported microwave assisted heating element.