Amino Silane, Vinyl Silane, TESPD, ZS(TESPD/Zinc Complex) Effects on Carbon Black/Clay Filled Chlorobutyl Rubber(CIIR) Compounds Part I: Effects on Hard Clay/Carbon Black Filled Compounds

  • Kim, Kwang-Jea
    • Carbon letters
    • /
    • 제10권2호
    • /
    • pp.101-108
    • /
    • 2009
  • Various silanes, amino silane, vinyl silane, TESPD, and ZS (TESPD/zinc soap complex), are added into chlorinated isobutylene-isoprene copolymer (CIIR)/hard clay/carbon black (CB) compound and they are investigated with respect to the vulcanization characteristics, the processability, and the mechanical properties. In hard clay/CB filled system, only ZS silane added compound shows both lower Mooney viscosity and extrusion torque while vinyl silane added compound showed only a lower extrusion torque. All the ZS added compounds showed the lowest viscosity among them. The silane added compounds showed an increased modulus. In 'fatigue to failure' count test, the ZS added compound showed superior counts compared to other silane (amino, vinyl, TESPD) added compounds. The mechanical properties were significantly increased when the S2 and ZS were added into CIIR/hard clay/CB compound. The ZS added compounds showed a significant improvement on elongation modulus.

Amino Silane, Vinyl Silane, TESPD, ZS (TESPD/Zinc Complex) Effects on Carbon Black/Clay Filled Chlorobutyl Rubber (CIIR) Compounds Part III: Comparative Studies on Hard Clay and Soft Clay Filled Compounds

  • Kim, Kwang-Jea
    • Carbon letters
    • /
    • 제10권3호
    • /
    • pp.190-197
    • /
    • 2009
  • Various silanes, amino silane, vinyl silane, sulfur silane (TESPD), and ZS (TESPD/zinc soap complex), are added into chlorinated isobutylene-isoprene copolymer (CIIR)/soft clay/carbon black (CB) and CIIR/hard clay/CB compounds and they are investigated with respect to the vulcanization characteristics, the processability, and the mechanical properties. Comparing hard clay and soft clay filled compounds, hard clay (Suprex) filled system shows a higher die C tear than the soft clay (GK) filled one. The other properties (Mooney, extrusion torque/pressure, torque rise ($M_H-M_L$), modulus at 300%) are close to each other. Among various silanes, the ZS treated hard clay (Suprex) compound shows the highest mechanical property following hard clay(S)/vinyl silane(V) and soft clay(GK)/vinyl silane(V) compounds. The TESPD and the ZS effectively helps a formation of a strong 3-dimensional network structure between silica and CIIR via coupling reaction due to bifunctional nature of TESPD. In addition to that, the ZS added compounds show both a better processability and mechanical properties compared to the S2 ones at low concentration due to improved compatibility between zinc soap and CIIR matrix. Only the ZS added compound shows both improved processabilities (Mooney, Extrusion torque-& pressure) and improved mechanical properties (degree of crosslinking, elongation modulus, tear, and fatigue to failure counts) on both CIIR/hard clay/CB and CIIR/soft clay/CB compounds.

Preparation and Properties of Silicone Hydrogel Material Containing Silane Group with Cobalt Oxide Nanoparticles through Thermal Polymerization

  • Lee, Min-Jae;Kong, Ki-Oh;Sung, A-Young
    • 한국재료학회지
    • /
    • 제30권6호
    • /
    • pp.273-278
    • /
    • 2020
  • This research is conducted to analyze the compatibility of used monomers and produce the high functional hydrogel ophthalmic polymer containing silane and nanoparticles. VTMS (vinyltrimethoxysilane), TAVS [Triacetoxy(vinyl)silane] and cobalt oxide nanoparticles are used as additives for the basic combination of SilM (silicone monomer), MMA (methyl methacrylate) and MA (methyl acrylate). Also, the materials are copolymerized with EGDMA (ethylene glycol dimethacrylate) as cross-linking agent, AIBN (thermal polymerization initiator) as the initiator. It is judged that the lenses of all combinations are optically excellent and thus have good compatibility. Measurement of the optical and physical characteristics of the manufactured hydrophilic ophthalmic polymer are different in each case. Especially for TAVS, the addition of cobalt oxide nanoparticles increases the oxygen permeability. These materials are considered to create synergy, so they can be used in functional hydrogel ophthalmic lenses.

Surface Modification of Ag Coated Cu Conductive Metal Powder for Conductive Silicone Sealant Gasket Paste

  • Park, Seong-Yong;Yoon, Tae-Won;Lee, Chung-Ho;Jeong, In-Bum;Hyun, Sang-Hoon
    • 한국분말야금학회:학술대회논문집
    • /
    • 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
    • /
    • pp.1076-1077
    • /
    • 2006
  • Conductive pastes consist of conductive fillers( Au, Ag, Ni, Cu etc.), organic binders, solvents and additives. Meanwhile, there are some metal powders such as copper, nickel etc that are used for pastes which have serious surface corrosion problems. This problem leads to change of the color and decrease in conductivity and affect storage stability of conductive pastes. By using silane coupling agent and dispersion agent, we can ensure both the corrosion stability and long term storage stability, and enhance the high performance electrical and mechanical properties of EMI shielding silicone sealant.

  • PDF

실란 및 분산제가 Epoxy와 연자성 금속 파우더 복합체의 Packing에 미치는 영향 (The Effect of Silane and Dispersant on the Packing in the Composite of Epoxy and Soft Magnetic Metal Powder)

  • 이창현;신효순;여동훈;남산
    • 한국전기전자재료학회논문지
    • /
    • 제30권12호
    • /
    • pp.751-756
    • /
    • 2017
  • A molding-type power inductor is an inductor that uses a hybrid material that is prepared by mixing a ferrite metal powder coated with an insulating layer and an epoxy resin, which is injected into a coil-embedded mold and heated and cured. The fabrication of molding-type inductors requires various techniques such as for coil formation and insertion, improving the magnetic properties of soft magnetic metal powder, coating an insulating film on the magnetic powder surface, and increasing the packing density by well dispersing the powder in the epoxy resin. Among these aspects, researches on additives that can disperse the metal soft magnetic powder having the greatest performance in the epoxy resin with high charge have not been reported yet. In this study, we investigated the effect of silanes, KBM-303 and KBM-403, and a commercial dispersant on the dispersion of metal soft magnetic powders in epoxy resin. The sedimentation height and viscosity were measured, and it was confirmed that the silane KBM-303 was suitable for dispersion. For this silane, the packing density was as high as about 72.49%. Moreover, when 1.2 wt% of dispersant BYK-103 was added, the packing density was about 80.5%.

Study on the Waterproofing Performance of FGD Gypsum Building Products from Inorganic-Organic Composite Additives

  • Ding, Yi;Fang, Youchun;Ren, Qifang;Fang, Hui;Zhang, Qicai;Oh, Won-Chun
    • 한국재료학회지
    • /
    • 제25권11호
    • /
    • pp.590-597
    • /
    • 2015
  • In this article, poly methyl triethoxy silane was compounded with an inorganic waterproof admixture at a certain ratio to improve the performance of gypsum products; a new type of high-efficiency compound water-proofing additive was also investigated. Furthermore, the waterproof mechanism and the various properties on the hardened gypsum plaster were investigated in detail by XRD and SEM. The results show that the intenerate coefficient of gypsum plaster increased to more than 0.9; the water absorbing rate decreased to less than 10 %. Both the bending strength and the compressive strength of gypsum plaster increased by various degrees. The intenerate coefficient reached a maximum value of 0.73 and the strength of the samples showed almost no change when 5% cement alone was added. In this new type of the high-efficiency compound with waterproof additive, the optimal technological parameters for formulas were obtained to be: 5% cement, 18 % mineral powder, and 0.8% poly methyl triethoxy silane, to compound gypsum plaster. Meanwhile, the production of high performance gypsum as a building material has become possible.

분말사출성형체에서 Sr-페라이트 자성분말의 배향도에 미치는 첨가제의 영향 (Effect of Additives on the Orientation of Magnetic Sr-Ferrite Powders in Powder Injection Molded Compacts)

  • 조태식;정원용
    • 폴리머
    • /
    • 제25권2호
    • /
    • pp.240-245
    • /
    • 2001
  • 다극 이방성 Sr-페라이트 소결자석을 제조하기 위한 자장중 분말사출성형공정에서 Sr-페라이트 자성분말의 배향도에 미치는 결합제의 첨가제 영향이 연구되었다 외부자기장의 방향에 대한 Sr-페라이트 자성분말의 배향도는 첨가제의 종류, 사출성형온도와 관련한 사출성형체의 유동성과 외부자기장의 세기에 크게 의존하였다. Paraffin wax/carnauba wax/HDPE 3성분계 결합제에 stearic acid를 첨가하면 분말사출성형체의 유동성이 향상되어 Sr-페라이트 자성분말의 배향도가 증가되었으나, silane계 커플링제를 첨가하면 성형체의 유동성이 오히려 감소되어 Sr-페라이트의 배향도가 감소되었다. 80% 이상의 Sr-페라이트 자성분말의 배향도는 사출성형체의 겉보기점도가 2500 poise (1000sec$^{-1}$)이하이고 외부자기장의 세기가 4kOe 이상인 유용한 조건에서 얻어졌다.

  • PDF

전선피복용 컴파운드의 제조에서 난연제의 첨가량에 따른 물성 변화 연구 (Study on Property Modification with Fire Retardant Content in the Manufacture of Compounds for Cable Sheath)

  • 리시앙수;이상봉;조을룡
    • 반도체디스플레이기술학회지
    • /
    • 제18권3호
    • /
    • pp.47-51
    • /
    • 2019
  • The three different polymer compounds were manufactured with the three different fire retardant (silane coated magnesium dihydroxide) contents, 180, 200, 220 phr, for making cable sheath for ship industry. In the research, ethylene-vinylacetate, polyethylene as matrix polymers and ethylene-vinylacetate grafted maleic anhydride as coupling agent were selected for compounding with fire retardant, closslinking agent, plasticizer, and other additives. In the evaluation. ΔT, Mooney viscosity, and tensile strength increased with the content of fire retardant. But it was found that too much fire retardant damaged aging resistance and cold resistance of the polymer compound.

전선피복용 고분자 컴파운드의 제조 및 물성 연구 (Study on Manufacture and Properties of Polymer Compounds for Cable Sheath)

  • 리시앙수;이상봉;조을룡
    • 반도체디스플레이기술학회지
    • /
    • 제18권1호
    • /
    • pp.42-47
    • /
    • 2019
  • The four different polymer compounds were manufactured to make cable sheath for ship industry. Two kinds of ethylene-vinyl acetate (EVA) were selected as main matrix polymers for compounding with fire retardant, crosslinking agent, filler, plasticizer, and other additives. The properties of the four compounded materials were investigated with the contents of fire retardant, silane coated aluminum hydroxide (S-ATH). Rheology, Mooney viscosity, and tensile strength increased with S-ATH contents by reinforcing effect. With increasing fire retardant amount, fire resistance increased, but cold resistance didn't show an obvious enhancement due to polar effect of vinyl acetate in EVA.

나일론66/실리케이트 복합체의 충격특성 개선 연구 (Improvement research for impact strength of nylon66/silicate composites)

  • 이봄이;김연철
    • 한국산학기술학회논문지
    • /
    • 제15권7호
    • /
    • pp.4653-4658
    • /
    • 2014
  • 나일론66/실리케이트 복합체를 자동차 부품 소재로 적용하기 위해서 충격특성 개선에 대한 연구가 요구된다. 이축압출기(twin screw extruder)를 이용하여 나일론66/실리케이트 복합체를 실란계열의 ${\gamma}$-APS로 처리한 실리케이트 사용과 MAH가 그라프트된 옥텐계 ${\alpha}$ 올레핀을 첨가한 경우로 하여 제조하였다. 실란처리된 실리케이트의 화학구조는 적외선 분광기(FT-IR)을 이용하여 측정하였고, 나일론66/실리케이트 복합체의 열적특성, 실리케이트 삽입여부 및 아이조드 충격강도를 DSC, TGA, XRD, 그리고 Izod 시험기를 이용하여 분석하였다. 실란계열로 처리된 실리케이트의 화학반응여부는 표면 수산기 피이크의 감소로부터 확인하였다. 복합체의 분해온도에는 큰 차이를 보이지 않았지만 결정화온도와 결정화도는 약간 증가하였다. 이는 사용한 첨가제들이 나일론 66에 불균일 핵제로의 역할을 했기 때문으로 추측된다. 나일론66/실리케이트 복합체의 아이조드 충격특성 측정결과 실란으로 처리된 실리케이트를 사용한 경우 약 24% 정도의 충격강도 개선효과를 보여주었다.