• 대한기계학회논문집A
• /
• 제24권12호
• /
• pp.2909-2916
• /
• 2000

6.5wt% Si steel is widely known as an excellent magnetic material because its magnetostriction is nearly zero. The AX magnetic properties as magnetostriction of 6.5% Si steel were evaluated and compared with those of conventional 3% Si steel sheet. In this paper, the fracture behavior of the poly crystals and single crystals of Fe-6.5wt%Si alloy has been observed. Single crystals were prepared by Floating Zone(FZ) method, which melts the alloy by the use of high temperature electron beam in pure argon gas condition. And the single crystals were annealed at 500$^{\circ}C$ and 700$^{\circ}C$ respectively and tensile tested at room temperature. According to the result, B2 phase has more good elongation than DO$_3$ phase. It was also found that the fracture surfaces of the single crystals have hairline facets in same direction, and the facets change the direction according to the single crystal phase.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 1999년도 특별강연 및 춘계학술발표대회 개요집
• /
• pp.96-97
• /
• 1999

• 동력기계공학회지
• /
• 제15권5호
• /
• pp.72-76
• /
• 2011

In this work, the parameter optimization for thermal-sprayed Al/SiC composites have been designed by $L_9(3^4)$ orthogonal array and analysis of variance(ANOVA). Al/SiC composites were fabricated by flame spray process on steel substrate. The hardness of composites were measured using micro-vickers hardness tester, and these results were analyzed by ANOVA. The ANOVA results showed that the oxygen gas flow, powder feed rate and spray distance affect on the hardness of the Al/SiC composites. From the ANOVA results, the optimal combination of the flame spray parameters could be extracted. It was considered that experimental design using orthogonal array and ANOVA was efficient to determine optimal parameter of thermal-sprayed Al/SiC composites.

• Journal of Welding and Joining
• /
• 제29권5호
• /
• pp.99-105
• /
• 2011

In this study, effect of Si content on nugget diameter in electric resistance spot welded dual-phase(DP) steel was investigated. The cold rolled DP steels with different Si content (0.5, 1.0, 1.5, 2.0 wt.%) were used and thickness of those sheet was 1.2mm. With increasing Si content, nugget diameter was increased at the same welding current. This is attributed to increase of heat input result from high resistivity. Also, nugget diameter was increased with an increase in Si content for the same heat input. For this reason, the melting point of DP steel is lowered with an increase in the Si content. And solid DP steel can easily be transformed to a liquid phase because the low melting point. Finally, a prediction formula for the nugget diameter(N.D.) could be obtained in terms of heat input(Q) and melting point(M.P) as follows: N.D.(mm) = 0.11Q(J) - 0.0031 M.P.($^{\circ}C$) + 0.32.

• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 1988년도 제7회 학술강연회초록집
• /
• pp.43-48
• /
• 1988

보호피막을 입히는 방법으로는 화학증착법과 물리증착법이 주로 사용되고 있다. 고온 분위기에서 기체 상태인 반응물의 화학반응을 통하여 원하는 물질을 증착시키는 화학증착법은 물리증착법에 비해 점착성(adhesion)이 우수하고, 보호피막층의 성분조절이 용이하며, 반응물이 기체상태이므로 대량생산이 용이하여 보호피막 증착법으로 많이 사용되고 있다. $Si_3N_4$-TiC ceramic 표면에 TiC, TiN 및 Ti(C, N) coating을 함으로써 얻을 수 잇는 장점들은 표면층의 경도를 증가시키며, steel과의 마찰계수의 감소 및 coating 층 자체가 고온에서 고체 윤활제로 작용하여 마찰열의 상당한 감소를 얻을 수 있으며, 또한 coating층 자체가 비교적 안정한 화합물로 피삭재내의 성분원소들에 대한 diffusion barrier로 작용되며, 내식성을 증가시킬 수 있다. 본 연구에서는 각 증착층의 미소경도, 열충격저항, steel과의 마찰계수를 측정하였으며, 최종적으로 절삭시험을 통하여 증착층들의 내마모성을 조사, 규명하였다.

• Journal of Information Display
• /
• 제13권2호
• /
• pp.61-66
• /
• 2012

The double-layered Ti/Si barrier metal is demonstrated for the source/drain Cu interconnections in oxide semiconductor thin-film transistors (TFTs). The transmission electromicroscopy and ion mass spectroscopy analyses revealed that the double-layered barrier structure suppresses the interfacial reaction and the interdiffusion at the interface after thermal annealing at $350^{\circ}C$. The underlying Si layer was found to be very useful for the etch stopper during wet etching for the Cu/Ti layers. The oxide TFTs with a double-layered Ti/Si barrier metal possess excellent TFT characteristics. It is concluded that the present barrier structure facilitates the back-channel-etch-type TFT process in the mass production line, where the four- or five-mask process is used.

• 한국결정성장학회:학술대회논문집
• /
• 한국결정성장학회 1997년도 Proceedings of the 12th KACG Technical Meeting and the 4th Korea-Japan EMGS (Electronic Materials Growth Symposium)
• /
• pp.215-218
• /
• 1997

• 한국표면공학회지
• /
• 제40권6호
• /
• pp.279-282
• /
• 2007

Cr-Mo-Si-C-N coatings were deposited on steel and Si wafer by a hybrid system of AIP and sputtering techniques using Cr, Mo and Si target in $Ar/N_2/CH_4$ gaseous mixture. Instrumental analyses of XRD and XPS revealed that the Cr-Mo-Si-C-N coatings must be a composite consisting of fine(Cr, Mo and Si)(C and N) crystallites and amorphous $Si_3N_4$ and SiC. The hardness value of Cr-Mo-Si-C-N coatings significantly increased from 41 GPa of Cr-Mo-C-N coatings to about 53 GPa with Si content of 9.3 at.% due to the refinement of (Cr, Mo and Si)(C and N) crystallites and the composite microstructure characteristics. A systematic investigation of the microstructures and mechanical properties of Cr-Mo-Si-C-N coatings prepared with various Si contents is reported in this paper.

• 한국주조공학회지
• /
• 제27권5호
• /
• pp.221-223
• /
• 2007

공구강은 C, Cr, V, Mo, W, Co 및 Si 과 같은 첨가원소를 함유한 복잡한 철계 합금으로 주요 특성인 경도, 부식저항성, 열 연화저항성 그리고 인성의 요구수준에 따라 화학성분이 결정된다. 본 연구에서는 1.0C, 0.2Mn, 3.8Cr, 1.5W, 8.5Co, 9.2Mo, 1.0V 조성의 M42 공구강의 미세조직과 열간가공성에 미치는 Si 함량의 효과를 체계적으로 조사하였다. 진공유도용해를 이용하여 Si 함량을 중량비로 0.33 에서 1.7% 까지 변화시켜 $140{\times}140{\times}330\;mm^{3}$ 크기의 잉곳으로 제조하였다. 이렇게 제조한 잉곳들은 $1150^{\circ}C$에서 1.5시간 동안 용체화처리한 후 노냉하였고, 이어 $1180^{\circ}C$에서 15mm 두께의 판재로 열간압연하였다. 공정 탄화물의 형상 및 분해 거동을 중심으로 미세조직을 관찰한 결과 Si 함량이 증가함에 따라 분해속도가 느려지는 것을 알 수 있었고 이로 인해 열간성형성이 급격히 저하되는 것으로 나타났다.

• 한국주조공학회지
• /
• 제25권3호
• /
• pp.123-127
• /
• 2005

0.8wt.% C과 $0.75{\sim}3.2$(0.75, 1, 1.26, 1.44, 1.89, 2.1, 2.46, 2.94, 3.22)wt.% Si을 함유한 고탄소 고실리콘 강에서 Si의 함량이 미세조직과 processing window에 미치는 영향에 대해 조사하였다. 열처리는 $940^{\circ}C$에서 1시간 동안 오스테나이징을 실시한 후, $320^{\circ}C$에서 $0.2{\sim}300$분 동안 오스템퍼링을 하였다. 미세조직에서, 0.75 wt.% Si을 함유한 강에서 국부적으로 오스페라이트(ausferrite)가 존재하는 것을 확인하였다. Processing window는 경도 및 XRD 측정으로 결정하였다. $t_{1}$은 Si의 함량이 2.5 wt.% 이하에서는 거의 변화가 없다가,2.5 wt.% 이상에서는 감소하는 결과를 보였다. 반면, $t_{2}$는 Si의 함량이 증가함에 따라 연속적으로 증가하였다. 즉, 0.8 wt.% C을 함유한 강에서 processing window는 Si의 함량이 약 2.5 wt.%일 때 열렸다.