• Journal of the Korean Society of Industry Convergence
• /
• v.23 no.1
• /
• pp.25-32
• /
• 2020

Generally, high-temperature, high-pressure, high-priced sintering equipment is used for diamond sintering, and conductivity is a problem for improving the surface modification of the sintered body. In this study, to improve the efficiency of diamond sintering, we identified a new process and material that can be sintered at low temperature, and attempted to develop a composite thin film that can be discharged by doping boron gas to improve the surface modification of the sintered body. Sintered bodies were sintered by mixing Si and two diamonds in different particle sizes based on CIP molding and HIP molding. In CVD deposition, CVD was performed using WC-Co cemented carbide using CH₄ and H₂ gas, and the specimen was made conductive using boron gas. According to the experimental results of the sintered body, as the Si content is increased, the Vickers hardness decreases drastically, and the values of tensile strength, Young's modulus and fracture toughness greatly increase. Conductive CVD deposited diamond was boron deposited and discharged. As the amount of boron added increased, the strength of diamond peaks decreased and crystallinity improved. In addition, considering the release processability, tool life and adhesion of the deposition surface according to the amount of boron added, the appropriate amount of boron can be confirmed. Therefore, by solving the method of low temperature sintering and conductivity problem, the possibility of solving the existing sintering and deposition problem is presented.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.02a
• /
• pp.161-161
• /
• 2012

질화티타늄(Titanium Nitride, TiN)은 화학적 안정성이 우수하고, N/Ti 원소 비율에 따라 열전도성 및 전기전도성이 변화하는 특성을 가지고 있어서 Metal Insulator Silicon (MIS) 나 Metal Insulator Metal (MIM) capacitor의 metal electrode 물질로 적용되고 있다. $TiCl_4$와 $NH_3$ gas를 이용하여 $500^{\circ}C$ 이상의 고온 조건에서 Chemical Vapor Deposition (CVD) 법으로 TiN 박막을 증착하는 방식이 가장 널리 사용되고 있으나, TiN 박막 내의 Chlorine (Cl) 원소가 SiO2 두께와 누설전류 밀도를 증가시키는 요인으로 작용하므로 Cl의 거동 및 함량 제어를 통한 전기적인 특성의 향상 평가가 요구되고 있다[1-3]. 본 실험에서는 $SiO_2$ 위에 TiN을 적층 한 구조에서 magnetic sector type의 Secondary Ion Mass Spectrometry (SIMS)를 이용하여 Cl 원소의 검출도 개선 방법을 연구하였다. 일반적인 $Cs^+$ 이온을 이용하여 $Cl^-$ 이온을 검출할 경우에는 TiN 하부에 $SiO_2$가 존재함에 따른 charging effect와 mass interference가 발생되는 문제점이 관찰되었다. 이를 개선하기 위해 Cl과 Cs 원소가 결합된 $ClCs^+$ cluster ion을 검출하는 방법을 시도하였으나, Cl- 이온 검출 방식에 비해 오히려 낮은 검출도를 나타내었으나 Cl 원소가 속하는 halogen 족 원소의 높은 전자 친화도 특성을 이용한 $ClCs_2^+$ cluster ion을 검출하는 방법[4]을 적용한 경우에는 $ClCs^+$ 방식에 비해 검출도가 3order 개선되는 결과를 확보하였으며, 이 결과를 토대로 Cl dose ($atoms/cm^2$) 와 Rs (ohm/sq) 간의 상관 관계에 대해 고찰하고자 한다.

• Journal of the Semiconductor & Display Technology
• /
• v.12 no.3
• /
• pp.41-46
• /
• 2013

Efficient and inexpensive solar cells are necessary for photo-voltaic to be widely adopted for mainstream electricity generation. For this to occur, the recombination losses of charge carriers (i.e. electrons or holes) must be minimized using a surface passivation technique suitable for manufacturing. Recently it has been shown that aluminum oxide thin films are negatively charged dielectrics that provide excellent surface passivation of silicon solar cells to attract positive-charged holes. Especially aluminum oxide thin film is a quite suitable passivation on the rear side of p-type silicon solar cells. This paper, it demonstrate the interfacial microstructure and electrical properties of mono-crystalline silicon surface passivated by $Al_2O_3$ films during firing process as applied for screen-printed solar cells. The first task is a comparison of the interfacial microstructure and chemical bonds of PECVD $Al_2O_3$ and of PEALD $Al_2O_3$ films for the surface passivation of silicon. The second is to study electrical properties of double-stacked layers of PEALD $Al_2O_3$/PECVD SiN films after firing process in the temperature range of $650{\sim}950^{\circ}C$.

• Journal of the Korean Magnetics Society
• /
• v.11 no.4
• /
• pp.168-172
• /
• 2001

Co-Zn ferrite thin films grown on thermally oxidized silicon wafers were fabricated by a sol-gel method. Magnetic and structural properties of Co-Zn thin films were investigated by using x-ray diffractometer (XRD), atomic force microscopy (AFM), auger electron spectroscopy (AES) and a vibrating sample magnetometer (VSM). Co-Zn ferrite thin films annealed at 400 $^{\circ}C$ presented have only a single phase spinel structure without any preferred crystallite orientation. Their surface roughness of Co-Zn ferrite thin films was shown as less than 3 nm and the grain size was about 40 nm for annealing temperatures over 600 $^{\circ}C$. A moderate saturation magnetization of Co-Zn ferrite thin films for recording media was obtained in this study and there is no significant difference of their magnetic property with those external fields of parallel and perpendicular to planes of the films. The maximum value of the coercivity was obtained as 1,900 Oe for Co-Zn ferrite thin film annealed at 600 $^{\circ}C$.

• Korean Journal of Materials Research
• /
• v.4 no.5
• /
• pp.510-515
• /
• 1994

Yttria-stabilized zirconia(YSZ) films were prepared onto p-type (100) silicon wafer by a plasma-enhanced metallorganic chemical vapor deposition(PE MO CVD) processing involving the application of vapor mixture of tri(2.2.6.6-tetramethyl-3, 5-heptanate) yttrium$[Y(DPM)_3]$, zirconiumtriflouracethyla cetonate$(Zr(tfacac)_4$ and oxygen gas. The x-ray diffraction(XRD) and fourier transform infrared spectra(FT1R) results showed that the deposited YSZ films had a single cubic phase. $Y_2O_3$ content of YSZ film was analyzed by PIXE(partic1e induced x-ray emission). The experimental results by PIXE revealed that 12.lmol%, 20.4mol% and 31.6mol% $Y_2O_3$ could be obtained as the $Y(DPM)_3$ bubbling temperature varied at $160^{\circ}C, 165^{\circ}C$ and $170^{\circ}C$ respectively. The increase of $Y(DPM)_3$ bubbling temperature caused shifting flat band voltage to have a negative value.

• Journal of the Korean Vacuum Society
• /
• v.15 no.1
• /
• pp.97-102
• /
• 2006

Anodic alumina with self-organized and ordered nano hole arrays can be a good candidate of an irradiation mask to modify the properties of nano-scale region. In order to try using porous anodic alumina as a mask for ion-beam patterning, ion beam transmittance of anodic alumina was tested. 4 Um thick self-standing AAO templates anodized from Al bulk foil with two different aspect ratio, 200:1 and 100:1, were aligned about incident ion beam with finely controllable goniometer. At the best alignment, the transmittance of the AAO with aspect ratio of 200:1 and 100:1 were $10^{-8}\;and\;10^{-4}$, respectively. However transmittance of the thin film AAO with low aspect ratio, 5:1, were remarkably improved to 0.67. The ion beam transmittance of self-standing porous alumina with a thickness larger than $4{\mu}m$ is extremely low owing to high aspect ratio of nano hole and charging effect, even at a precise beam alignment to the direction of nano hole. $SiO_2$ nano dot array was formed by ion irradiation into thin film AAO on $SiO_2$ film. This was confirmed by scanning electron microscopy that the $SiO_2$ nano dot array is similar to AAO hole array.

• Journal of the Korean Solar Energy Society
• /
• v.39 no.5
• /
• pp.1-10
• /
• 2019

Recently, the installation capacity of PV (photovoltaic) systems has been increasing not only field installation but also floating PV, farm land, BIPV/BAPV. For this reason, the new design and materials of PV module are needed. In particular, in order to apply a PV system to a building, lightweight of the PV module is essential. PV modules made of generally used texturing glass are excellent in output and reliability, but there is a limit to the weight that can be reduced. For the lightweight of the PV module, it necessary to use a film instead of a glass. However, the application of film rather than a glass may cause various problems such as decrease in photocurrent by decrease in transmittance and a increase of CTM (cell to module) loss, a degradation of the reliability, and so on. In this paper, PV modules using Ultra barrier film, which is recently a lot of interest as a substitute for a glass, its characteristic analysis and reliability test were conducted. The transmittance and UV characteristics of each material were verified, and the output of the fabricated 1 cell PV module was measured. In addition, 24 cell PV modules were fabricated at the lab-scale and its reliability tests were conducted. As a result of the experiment, the reliability characteristics of the ultra barrier film PV module were excellent, and it was confirmed that it could be used as the front material of the PV module instead of glass

• Proceedings of the KIEE Conference
• /
• 1999.07d
• /
• pp.1710-1712
• /
• 1999

암모니아가스에 민감한 In이 도핑된 ZnO(ZnO:In) 박막을 In 박막$(100{\AA})$ 및 ZnO박막$(3000{\AA})$의 연속적인 증착과 열처리공정을 통하여 제조하고, 이와 같은 방법으로 Al과 In이 도핑된 ZnO (ZnO:Al, In) 박막을 In 박막과 ZnO:Al 박막의 연속적인 증착과 같은 조건에서의 열처리를 통하여 제조하였다. 기판은 $1000{\AA}$의 산화막이 열적으로 성장되어 있는 Si 기판을 사용하였다. In/ZnO 및 In/ZnO:Al 박막 이중층의 열처리온도에 따른 구조적 및 전기적 특성을 x-선회절기, 주사전자현미경, 오제전자분광법 및 4점측정시스템을 통하여 조사하였다. 이들 막에 대하여 열처리온도에 따른 암모니아가스에 대한 감도, 선택성 및 시간응답특성을 구하였다. 열처리온도 $400^{\circ}C$, 동작온도 $300^{\circ}C$에서 100 ppm의 암모니아가스를 주입한 결과 140 %의 최대감도를 나타내었으며 CO, $NO_x$ 가스에 대한 감도는 아주 낮은 것으로 나타났다.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1999.11a
• /
• pp.76-76
• /
• 1999

Low resistance ohmic contacts to the Si-doped InGaN(~$\times$10$^{19}$ ㎤) were obtained using the W metallization schemes. Specific contact resistance decreased with increasing annealing temperature. The lowest resistance is obtained after a nitrogen ambient annealing at 95$0^{\circ}C$ for 90s, which results in a specific contact resistance of 2.75$\times$10$^{-8}$ Ω$\textrm{cm}^2$. Interfacial reactions and surface are analyzed using x-ray diffraction, transmission electron microscopy (TEM) and scanning electron microscopy (SEM). The X-ray diffraction results show that the reactions between the W film and the InGaN produce a $\beta$-W$_2$N phase at the interface. TEM results also show that the $\beta$-W$_2$N has a rough interface, which increase contact area. It shows that the morphology of the contacts is stable up to a temperature as high as 95$0^{\circ}C$. Possible mechanisms are proposed to describe the annealing temperature dependence of the specific contact resistance.

• Proceedings of the KIEE Conference
• /
• 1995.07c
• /
• pp.1133-1136
• /
• 1995

RF-magnetron sputtering 방법으로 형성한 $BaTa_2O_6$의 공정변수에 따른 전기, 광학적 특성변화를 관찰하여 $BaTa_2O_6$ 박막의 TFELD(thin film electroluminescent display) 절연막으로서 응용 가능성을 연구하였다. $BaTa_2O_6$ 박막의 유전특성은 증착시의 $O_2$ 함량과 sputtering 압력의 변화에는 큰 영향을 받지 않으나 기판온도에는 영향을 받는 것으로 확인되었다. 이들 공정변수를 가변하여 실험한 결과, $BaTa_2O_6$ 박막 형성의 최적조건으로 플라즈마 압력을 6 mtorr, sputtering gas 내의 $O_2$ 혼합비율은 40%, 기판온도는 $100^{\circ}C$로 결정하였다. 이상의 조건에서 제조된 $BaTa_2O_6$ 박막은 10.2 ${\mu}C/cm^2$의 매우 우수한 성능지수를 보였다. 이상의 $BaTa_2O_6$ 박막을 하부절연층으로, 절연파괴강도가 높은 $SiO_xN_y$를 상부 절연층으로 사용하여 제조된 EL 소자는 1 kHz, 삼각파 구동시 발광 임계전압은 약 32 volts, 최대휘도는 54 $cd/m^2$으로 측정되었다.