• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.02a
• /
• pp.95-95
• /
• 2010

나노 크기에서 존재하는 Grain Boundary나 Dislocation과 같은 결함들은 거시적인 물성을 크게 좌우하는 요인들이 되기도 한다. 또한 다결정을 이루고 있는 입도(Grain Size)에 따라 기계적인 강도 특성도 달라지는데, 금속의 경우에 입도가 비교적 큰 영역(d > $d_c$)에서는 입도가 작고 균일해지면서 강도가 증가하는 'Hall-Petch 효과'를 보인다. 반면 입도가 작은 영역(d < $d_c$)에서는 입도가 줄어들 때 강도가 감소하는 경향을 보이는데 이를 '역 Hall-Petch 효과'라고 한다. 본 연구에서는 분자 동역학을 이용한 단결정과 다결정의 Si에 대한 기계적 성질에 대해 조사한다. 입도와 온도 변화에 따른 단결정 Si와 다결정 Si의 Strain-Stress Curve와 Young's Modulus, Yield Point에 대해 관찰하고 특이점을 제시한다. 이를 통해 나노 영역에서의 기계적 성질의 예측과 거시적 영역에서의 성질의 연관성을 추구한다.

• Journal of the Korean Vacuum Society
• /
• v.17 no.2
• /
• pp.130-137
• /
• 2008

$La_{0.7}Sr_{0.3}MnO_3$ films were deposited on $SiO_2$/Si and Si substrates annealed at $350^{\circ}C$ by rf magnetron sputtering. The oxygen gas flow rates were varied as 0, 40, and 80 sccm. Without post annealing process, $La_{0.7}Sr_{0.3}MnO_3$ thin films on $SiO_2$/Si and Si substrates were polycrystalline with (100), (110), and (200) growth planes. The grain size of $La_{0.7}Sr_{0.3}MnO_3$ thin films was increased with increasing oxygen gas flow rate. The sheet resistance of $La_{0.7}Sr_{0.3}MnO_3$ thin films was decreased with oxygen flow rate due to the increased grain size which induced a reduction of grain boundary. TCR (temperature coefficient of resistance) values of $La_{0.7}Sr_{0.3}MnO_3$ thin films were obtained from -2.0% to -2.2%.

• 한국연소학회:학술대회논문집
• /
• 2012.04a
• /
• pp.25-27
• /
• 2012

In this paper, combustion process in the perforated silicon carbide(SiC) tube using a two dimensional approaches with GRI Mechanism 1.2 was investigated. The computational mesh structure which is divided into $60{\times}15$ and boundary conditions are set to constant mass flow rate at the inlet and constant pressure condition at the outlet respectively. Its result shows that the temperature on this peak was roughly 100K higher than the adiabatic flame temperature of 2223K for a free laminar flame at these conditions.

• Korean Journal of Materials Research
• /
• v.2 no.6
• /
• pp.408-416
• /
• 1992

Stable TiS$i_2$was formed by RTA on single-Si and on poly-Si. Subsequently, an Al-1% Si layer with 600-nm thick was deposited on top of the TiS$i_2$, Finally, the specimens were annealed for 30min at 400-60$0^{\circ}C$in $N_2$ambient. The thermal stability of Al-1% Si/TiS$i_2$bilayer and interfacial reaction were investigated by measuring sheet resistance, Auger electron spectroscopy (AES), and scanning electron microscopy (SEM). The composition and phase of precipitates formed by the reaction of Al-1% Si with Ti-silicide were studied by energy dispersive spectroscopy (EDS), X-ray diffraction (XRD). In the case of single-Si substrate the reaction of Al-1% Si layer with TiS$i_2$layer resulted in precipitates, consuming all TiS$i_2$layer at 55$0^{\circ}C$. On the other hand, the disappearance of TiS$i_2$on poly-Si occurred at 50$0^{\circ}C$ and more precipitates were formed by the reaction of Al-1% Si/TiS$i_2$on potty-Si substrate than those of the reaction on single-Si substrate. This phenomenon resulted from the fact that Ti-silicide formed on poly-Si was more unstable than on single-Si by the effect of grain boundary. By EDS analysis the precipitates were found tobe composed of Ti, Al, and Si. X-ray diffraction showed the phase of precipitates to be theT$i_7$A$l_5$S$i_12$ternary compound.

• Korean Journal of Materials Research
• /
• v.12 no.5
• /
• pp.407-413
• /
• 2002

Eutectic high chromium cast irons containing 17%Cr and 26%Cr were produced for this research by making each of them solidify unidirectionally. Abrasion wear test against SiC or $Al_2$O$_3$bonded paper was carried out using test pieces cut cross-sectionally at several distances from the chill face of castings. The wear resistance was evaluated in connection with the parameters such as eutectic colony size($E_w$), area fraction of boundary region of the colony($S_B$) where comparatively large massive chromium carbides are crystallized and, average diameter of chromium carbides in the boundary region($D_c$). The wear rate($R_w$), which is a gradient of straight line of wear loss versus testing time, was influenced by the type and the particle size of the abrasives. The $R_w$ value against SiC was found to be larger than that against A1$_2$O$_3$under the similar abrasive particle size. In the case of SiC, the $R_w$ value increased with an increase in the particle size. The $R_w$ value also increased as the eutectic colony size decreased, and that of the 17%Cr iron was larger than that of the 26%Cr iron at the same $E_w$ value. Both of the $S_B$ and $D_c$ values were closely related to the $R_w$ value regardless of chromium content of the specimens. The $R_w$ values of the annealed specimens were greater than those of the as-cast specimens because of softened matrix structures. As for the relationship between wear rate and macro-hardness of the specimens, the hardness resulting in the minimum wear rate was found to be at 550 HV30.

• Journal of Magnetics
• /
• v.14 no.2
• /
• pp.71-74
• /
• 2009

The magnetic and structural properties of FINEMET (the Hitachi product name of the Fe-Si-B-Nb-Cu alloy) nanopowder with a composition of $Fe_{73.5}Si_{13.5}B_9Nb_3Cu_1$ atomic percent were investigated after annealing, chemical etching, and mechanical milling. The primary and secondary crystallization temperatures were 523 and $550^{\circ}C$, respectively. The grain size of the particles was adjusted by annealing time. Optimally annealed particles exhibited a homogenous microstructure composed of nanometer-sized crystalline grains. The grain boundary of the annealed particles was etched preferentially by chemical etching. Chemically etched particles were broken at the grain boundary by high-energy ball milling. As a result, a nanometer-sized FINEMET powder with a uniform size of crystalline grains was fabricated.

• Journal of the Microelectronics and Packaging Society
• /
• v.13 no.4
• /
• pp.27-36
• /
• 2006

We fabricated thermally evaporated 10 nm-Ni/(poly)Si, 10 nm-Ni/l nm-Ir/(poly)Si and 10 nm-Ni/l nm-Pt/(poly)Si films to investigate the thermal stability of nickel monosilicides at the elevated temperatures by rapid annealing them at the temperatures of $300{\sim}1200^{\circ}C$ for 40 seconds. Silicides of 50 nm-thick were formed on top of both the single crystal silicon actives and the polycrystalline silicon gates. A four-point tester was used to examine sheet resistance. A scanning electron microscope and field ion beam were employed for thickness and microstructure evolution characterization. An X-ray diffractometer and an Auger depth profiler were used for phase and composition analysis, respectively. Nickel silicides with platinum have no effect on widening the NiSi stabilization temperature region. Nickel silicides with iridium farmed on single crystal silicon showed a low resistance up to $1200^{\circ}C$ while the ones formed on polycrystalline silicon substrate showed low resistance up to $850^{\circ}C$. The grain boundary diffusion and agglomeration of silicides lowered the NiSi stable temperature with polycrystalline silicon substrates. Our result implies that our newly proposed Ir added NiSi process may widen the thermal process window for nano CMOS process.

• Journal of the Korean Ceramic Society
• /
• v.31 no.7
• /
• pp.777-783
• /
• 1994

Oxidation behavior of hot-pressed silicon nitride ceramics with various sintering additives has been investigated. The weight gain of each specimens has shown in the range of 0.11 mg/$\textrm{cm}^2$ ~3.4 mg/$\textrm{cm}^2$ at 140$0^{\circ}C$ for 192 h and eleven compositions have shown good oxidation resistance with the weight gain below 0.5 mg/$\textrm{cm}^2$. The oxidation rate has been shown to obey the parabolic rate law and the oxidized surface has consisted of $\alpha$-cristobalite and M2Si2O7 or MSiO3 (M=rare earth or transition metals) phase. The oxidation rate of each specimens has related to the eutectic temperature between additive oxide and SiO2, and ionic radius of additive oxides, respectively. From the above results, it could be concluded that the oxidation behavior of hot pressed silicon nitride is dominated by the high temperature properties of grain boundary glassy phase and the high temperature properties of grain boundary glassy phase are affected by the ionic radius of additive oxides.

• Journal of Magnetics
• /
• v.8 no.4
• /
• pp.157-159
• /
• 2003

The strengths of the inter-grain exchange interaction were evaluated for nanocrystalline $Nd_{2.33}Fe_{14}B_{1.06}Si_{0.21}$ magnets of different grain size by comparing the $_{i}H_{c}$ calculated by micromagnetics with the experiments. With increase of the grain boundary thickness to that of the magnet of grain diameter 12.4, 24.8, 37.2 and 49.6 nm, the strengh of the interaction in reference to that without the grain boundary phase decreases to 83％, 69％, 54％ and 42％.

• Journal of the Korean Magnetics Society
• /
• v.26 no.3
• /
• pp.76-80
• /
• 2016

CoSiB is the amorphous ferromagnetic material and multilayer consisting of CoSiB and Pd has perpendicular magnetic anisotropic property. PMA has strong advantages for STT-MRAM. Moreover, amorphous materials have two advantages more than crystalline materials: no grain boundary and good thermal stability. Therefore, we studied the magnetic properties of multilayers consisting of the $Co_{75}Si_{15}B_{10}$ with PMA. In this study, we investigated the magnetic property of the [CoSiB (3, 4, 5, and 6) ${\AA}$/Pd(11, 13, 15, 17, 19,and $24{\AA})]_5$ multilayers and found the annealing temperature dependence of the magnetic property. The annealing temperature range is from room temperature to $500^{\circ}C$. The coercivity and the saturation magnetization of the CoSiB/Pd multilayer system have a close association with the annealing temperature. Moreover, the coercivity especially shows a sudden increasing at the specific annealing temperature.