• Steel and Composite Structures
• /
• 제21권2호
• /
• pp.443-460
• /
• 2016

In this paper, the efficiency and effectiveness of two strengthening methods for upgrading behavior of the two external weak reinforced concrete (RC) beam-column joints were experimentally investigated under cyclic loading. Since two deficient external RC joints with reduced beam height and low strength concrete were strengthened using one-way steel prop and curbs with and without steel revival sheets on the beam. The cyclic performance of these strengthened specimens were compared with two another control external RC beam-column joints, one the standard RC joint that had not two mentioned deficiencies and another had both. Therefore, four half-scale RC joints were tested under cyclic loading.The experimental results showed that these innovative strengthening methods (RC joint with revival sheet specially) surmounted the deficiencies of weak RC joints and upgraded their performance and bearing capacity, stiffness degradation, energy absorption, up to those of standard RC joint. Also, results exhibited that the prop at joint acted as a fuse element due to adding steel revival sheets on the RC beam and showed better behavior than that of the specimen without steel revival sheets. In other words by stiffening of beam, the prop collected all damages due to cyclic loading at itself and acted as the first line of defense and prevented from sever damages at RC joint.

• 콘크리트학회논문집
• /
• 제12권1호
• /
• pp.61-67
• /
• 2000

The strengthening method with CFS(Carbon Fiber Sheet) has some fatal defects that the beams strengthened with CFS is always failed far below its ultimated strenth due to rapid progress of horizontal delamination. The crack between beam and CFS are always started from the center of the beam and propagated to the end of the beam. The moment of the beam is always the largest in the middle of the beam, so is the tensile force of the CFS. The bumped surface of the CFS causes debonding force depending on the tensile force of CFS. In this study, two methods which delay early delamination are suggested and proved its validity, experimentally. The first method is using anchor bolt at the end of CFS, and the second method is using CFS wrap aroud at the center and the end of beam. The maximum load and ductility of the two methods are increased significantly. However, the maximum load is still far below the ultimate load. That's because the tensile strength of CFS is so large that its tensile strength can not be reached under normal loading condition. The ductility of the strengthened beam is improved more that twice before modiffication.

• Design & Manufacturing
• /
• 제14권1호
• /
• pp.56-62
• /
• 2020

An electron beam was used to mainly utilize for polishing, finishing, welding, a lithography process, etc. Due to the high technical level of difficulty of high-power density electron beam, it is difficult to secure related technologies. In this study, research was carried out to improve the machinability by developing the vaporized amplification sheets to realize the electron beam drilling technology. Their vaporized amplification sheets were analyzed by using the measurement of chemical and composition, which is such as TGA, SEM. We analyzed micro-hole processing using a microscope. Also, the thermal characteristics of vaporized amplification sheets are highly significant for applying to high-power density electron beam technique. So, we finished the vaporized amplification sheets according to the process conditions and analyzed it according to the machining conditions of the electron beam. It was confirmed that the effect on the experimental results differs depending on the influence of the metal powder contained in the developed material.

• 한국기계가공학회지
• /
• 제11권6호
• /
• pp.82-87
• /
• 2012

The purpose of this study is to produce a side impact beam with high tensile steel using a roll forming process. The door side impact beam plays an important roll in a car because it protects passengers from external crash. The roll forming process is a continuous bending process wherein a long metal sheet is bended as it continuously passes several rolls. The characteristic of this study is that an impact beam is produced by a continuous process using a ultra high strength steel without a hardening heat treatment. A model was determined by analysing plasticity of a cross section shape considering high strength. Design parameters of the impact beam was determined by crash-analysing the model. Workpiece products were manufactured by designing dies for roll forming and setting them up in a following process line. Results of a bending test and a FEM analysis was considered and reviewed.

• 한국레이저가공학회:학술대회논문집
• /
• 한국레이저가공학회 1998년도 춘계학술발표대회 초록개요집
• /
• pp.29-30
• /
• 1998

• 한국레이저가공학회:학술대회논문집
• /
• 한국레이저가공학회 2000년도 춘계학술발표대회 논문개요집
• /
• pp.11-14
• /
• 2000

• 한국가시화정보학회:학술대회논문집
• /
• 한국가시화정보학회 2004년도 Proceedings of 2004 Korea-Japan Joint Seminar on Particle Image Velocimetry
• /
• pp.1-13
• /
• 2004

A scanning stereo-PIV system was developed to measure the three-dimensional distribution of three-component velocity in a turbulent round jet. A laser light beam produced by a high repetition rate YLF pulse laser was expanded vertically by a cylindrical lens to form a laser light sheet. The light sheet is scanned in a direction normal to the sheet by a flat mirror mounted on an optical scanner, which is controlled by a programmable scanner controller. Two high-speed mega-pixel resolution C-MOS cameras captured the particle images illuminated by the light sheet, and stereoscopic PIV method was adopted to acquire the 3D-3C-velocity distribution of turbulent round jet in an octagonal tank filled with water. The jet Reynolds number was set at Re=1000 and the streamwise location of the measurement was fixed at approximately x = 40D. Time evolution of three-dimensional vortical structure, which is identified by vorticity, is visualized. It revealed that the existence of a group of hairpin-like vortex structures was quite evident around the rim of the shear layer of the jet. Turbulence statistics shows good agreement with the previous data, and divergence of a filtered (unfiltered) velocity vector field was $7\%\;(22\%)$ of root-me an-squared vorticity value.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2004년도 추계 학술발표회 제16권2호
• /
• pp.781-784
• /
• 2004

Method of Steel plate reinforced by fiber sheet is advantageous in the secure loading facility. For this method are a light weight and a high strength, the thickness of steel can be reduced Effects of composite system are depreciated when the thickness of steel is thin. This is the result of the difference of ductility ratio with steel plate. Steel plate reinforced by fiber sheets confirms the ability of transformation. This is the result of the property of steel materials Steel plate reinforced by fiber sheet didn't display an enough performance when theadhesives are epoxy rosin. This is the result of the slide of the surface of stee1. The adhesive ability is varied by the number and span of anchor bolts. There wasn't happening the separation between steel and epoxy. Thus the method used in combination with anchor and epoxy is best excellent. This is the result of the upward of accumulation effects Shearing force is in proportion to the number of bolts. But the ability of shearing force per one bolt is reducing. Thickness of steel plate reinforced by fiber sheet must be designed so that steel is endure before concrete is wreck.

• Journal of Welding and Joining
• /
• 제16권1호
• /
• pp.52-62
• /
• 1998

Laser beam welding of zinc-coated steel, especially lap joints, has a problem of zinc vapor produced during welding which has a low vaporization temperature of 906.deg. C. It is lower than the melting temperature of steel (1500.deg. C). The high pressure formed by vaporization of zinc during laser welding splatters the molten pool and creates porosities in weld. During laser lap welds of zinc-coated steel sheets with CW CO$_{2}$ laser the gap size has been analyzed and simulated using a FEM. The simulation has been carried out in the range of gap aetween 0 and 0.16 mm. The vaporized zinc gas has effected to prevent heat from conducting toward the bottom of sheets. In vaporized zinc gas has effected to prevent heat from conducting toward the bottom of sheets. In the case of too small gap size, zinc gas has not ejected and existed between two sheets. Therefore heat was difficult to conduct from the upper sheet to lower sheet and the upper sheet could over-melted. In the case of large gap size the zinc gas has been prefectly ejected but only a part of lower sheet has melted. The optimum range of gap size in the lap welds of zinc-coated steel sheets has been calculated to be between 0.08 and 0.12 mm. According to the comparison of experiment, the simulation is proved to be acceptable and applicable to laser lap welds.

• Design & Manufacturing
• /
• 제16권1호
• /
• pp.43-49
• /
• 2022

As technologies in various industrial fields develop, high-quality parts are required. In the past, precision parts were produced by the contact machining method, but the contact machining method has clear limitations. In order to solve this problem, research on a non-contact processing method has been conducted, and laser processing and electric discharge processing are representative. However, the non-contact method has a problem in that productivity is insufficient, and there is a problem that it takes a lot of time to continuously process microholes. Researchers have developed an electron beam drilling equipment for continuous processing of fine holes, and a vaporization amplification sheet to increase the processing efficiency of the equipment. In this study, a cylindrical vaporization amplification sheet using room temperature curing type silicon was fabricated, and the metal distribution and thickness uniformity of the produced sheet were analyzed. In order to manufacture a cylindrical vaporization amplification sheet, an equipment capable of using centrifugal force was developed, and a sample in which metal powder was evenly distributed and a constant thickness was produced.