• 접착 및 계면
• /
• 제10권2호
• /
• pp.106-112
• /
• 2009

본 연구에서 처음으로 생분해성 라이오셀 직물과 poly(butylene succinate) (PBS)로 이루어진 바이오복합재료가 성공적으로 제조되었다. 0, 30, 40, 50 그리고 60 wt%의 서로 다른 함량의 라이오셀직물을 포함하는 라이오셀/poly(butylene succinate) 바이오복합재료는 sheet interleaving 방식으로 압축성형에 의해 제조되었다. 바이오복합재료의 층간전단강도, 인장 및 굴곡 특성, 열변형 온도, 열팽창 거동 및 열안정성에 미치는 라이오셀직물 함량의 영향을 조사하였다. 특성들은 직물함량에 크게 의존하였으며, 그 결과들은 서로 일치하였다. 라이오셀직물을 수지에 도입하는 것이 poly(butylene succinate)의 여러 가지 특성 향상에 두드러진 역할을 하는 것으로 확인되었다. 라이오셀직물이 중량비로 50%일 때, 바이오복합재료의 가장 우수한 층간전단강도, 인장, 굴곡 및 열적 특성이 얻어졌다.

• Advances in concrete construction
• /
• 제15권6호
• /
• pp.431-444
• /
• 2023

This study investigated the use of latex-modified sand concrete reinforced with sisal fibers (LMSC) as a repair material. Notably, no prior research has explored the application of LMSC for this purpose. This paper examines the interface bond strength and the type of failure between LMSC as a repair material and the normal concrete (NC) substrate utilising four different surfaces: without surface preparation as a reference (SR), hand hammer (HA), sandblasted (SB), and grooved (GR). The bond strength was measured by bi-surface shear, splitting tensile, and pull-off strength tests at 7, 28, and 90 days. Scanning electron microscopy analysis was also performed to study the microstructure of the interface between the normal concrete substrate and the latex-modified sand concrete reinforced with sisal fibers. The results of this study indicate that LMSC has bonding strength with NC, especially for HR and SB surfaces with high roughness. Therefore, substrate NC surface roughness is essential in increasing the bonding strength and adhesion. Eventually, The LMSC has the potential to repair and rehabilitate concrete structures.

• 한국가스학회지
• /
• 제12권3호
• /
• pp.38-42
• /
• 2008

본 연구에서는 폴리에스테르 폴리올의 구조와 이소시아네이트 인덱스의 변화에 따라 초저온($-190^{\circ}C$)과 상온($25^{\circ}C$)에서 폴리우레탄 접착제의 접착강도변화를 고찰하였다. 전단강도는 폴리우레탄 접착제를 plywood에 접착하여 측정하였으며, 접착제의 화학적, 기계적 물성 변화를 UTM, DSC, FT-IR로 비교 분석 하였다. 지방족 폴리에스테르 폴리올을 사용하여 합성한 폴리우레탄은 초저온에서의 전단강도가 상온에서의 전단강도보다 증가하였으나 방향족 폴리에스테르 폴리올을 사용하여 합성한 폴리우레탄의 경우는 초저온에서의 전단강도가 상온에서보다 작아지는 경향을 나타내었다. 또한 접착강도는 사용된 MDI의 양에 비례하여 증가하였으며, 지방족계 폴리올은 초저온에서 그리고 방향족계 폴리올은 상온에서 높은 접착 강도를 보임을 알 수 있었다.

• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 2001년도 추계학술발표대회 논문집
• /
• pp.153-157
• /
• 2001

Interfacial properties and microfailure modes of electrodeposition (ED) treated carbon fiber reinforced polyetherimide (PEI) toughened epoxy composite were investigated using microdroplet test and the measurement of surface wettability. As PEI content increased, Interfacial shear strength (IFSS) increased due to enhanced toughness and plastic deformation of PEI. In the untreated case, IFSS increased with adding PEI content, and IFSS of pure PEI matrix showed the highest. On the other hand, for ED-treated case IFSS increased with PEI content with rather low improvement rate. The work of adhesion between fiber and matrix was not directly proportional to IFSS for both the untreated and ED-treated cases. The matrix toughness might contribute to IFSS more likely than the surface wettability. Interfacial properties of epoxy-PEI composite can be affected efficiently by both the control of matrix toughness and ED treatment.

• Restorative Dentistry and Endodontics
• /
• 제28권3호
• /
• pp.209-221
• /
• 2003

The objectiveness of this study was to evaluate whether low-viscosity composite can bond effectively to dentin surface without bonding resin. The low-viscosity composites being 50wt% filler content were made by the inclusion of bonding resin of two self-etching systems(Cleafil SE Bond, Unifil Bond) varied with contents as 0, 10, 20, 30, 40, 50wt%. Exposed dentin surfaces of extracted 3rd molars are used. Dentin bond strengths were measured. The tests were carried out with a micro-shear device placed testing machine at a CHS of 1mm/min after a low-viscosity composite was filled into an iris cut from micro tygon tubing with internal diameter approximately 0.8mm and height of 1.0mm. 1 Flexural strength and modulus was increased with the addition of bonding resin. 2. Micro-shear bond strength to dentin was improved according to content of bonding resin irrespective of applying or not bonding resin in bonding procedure, and that of Clearfil SE Bond groups was higher than Unifil Bond. 3. There were no significant difference whether use of each bonding resin in bonding procedure for S-40, S-50, U-50(p＞0.05). 4. In SEM examination, resin was well infiltrated into dentin after primed with self-etching primer only for S-50 and U-50 in spite of the formation of thinner hybrid layer. Low viscosity composite including some functional monomer may be used as dentin bonding resin without an intermediary bonding agent. It makes a simplified bonding procedure and foresees the possibility of self-adhesive restorative material.

• 대한소아치과학회지
• /
• 제50권4호
• /
• pp.443-451
• /
• 2023

The purpose of this study was to evaluate whether the newly introduced calcium silicate-based materials with fast-setting properties could be appropriately used as basement materials in indirect pulp treatment (IPT). This was performed by quantifying the durability of adhesion between the material and composite resin, measured by the shear bond strength (SBS). Five calcium silicate-based materials, TheraCal LC^® (TLC), TheraCal PT^® (TPT), TheraBase^® (TB), Well-Root^TM PT (WPT), and Endocem^® MTA (EMTA), as well as two glass ionomer-based materials, Fuji II and Fuji II LC, were included. Specimens containing these materials were manufactured and bonded to composite resin with a universal adhesive applied in self-etch mode. The SBS values and failure modes were recorded, and the mean SBSs of the materials were compared. Both TPT and TB exhibited SBS values that were similar to TLC, while both WPT and EMTA appeared to have statistically lower SBS values. Mixed failure was commonly observed in TLC and TPT, while all WPT and EMTA samples showed cohesive failure. In comparison with TLC and TPT, more samples with cohesive failure were observed in TB, implying that this material forms a stronger bond with composite resin. Together with the ability of TB to chemically bind to dentin due to its 10-methacryloyloxydecyl dihydrogen phosphate component, TB seems to be a promising material for IPT within the limitations of this in vitro study.

• Journal of the Korean Wood Science and Technology
• /
• 제30권2호
• /
• pp.165-171
• /
• 2002

본 연구는 마루판의 천연무늬단판 접착에 이용되고 있는 요소-멜라민 접착제의 수지조성에 따른 접착성능 및 포름알데히드 방출량의 변화를 알아보고자 하였다. 요소에 멜라민에 대한 포름알데히드의 몰비 1.0, 1.1, 1.2, 1.4를 기준으로 제조된 접착제로 마루판용 합판과 섬유판에 천연무늬단판을 접착한 목질마루판에 의해 시험을 실시하였다. 그 결과는 화학양론적으로 멜라민-요소와 포름알데히드간의 비율이 적정한 조건에서 반응이 충분히 일어난 경우에 상태접착력, 준내수접착력, 포름알데히드 방출량 등이 가장 양호하게 나타났다. 복합마루판의 평면인장강도는 각 몰비에서 14 kgf/cm²를 상회하였으며, 포름알데히드 방출량은 1.0몰비에서 9.53 mg/L로 가장 낮게 나타났다. 합판마루판의 평면인장 접착력 시험에서는 1.4몰비에서 14.02 kgf/cm²로 가장 높은 값을 보였다. 합판마루판의 포름알데히드 방출량 조사에서도 1.0목비에서 0.26 mg/L로 가장 낮게 나타났다.

• 한국강구조학회 논문집
• /
• 제16권4호통권71호
• /
• pp.397-406
• /
• 2004

본 논문은 경량형강으로 제작한 프레임에 경량기포모르터를 채운 경량합성벽체의 전단 거동에 대한 실험 결과와 전단 강도 및 강성 평가를 제시한 것이다. 경량기포모르터는 스틸하우스 벽체의 구조 성능 및 단열 성능의 향상과 마감에 대한 시공성 개선을 위해 도입되었다. 연구 결과 단열 성능에 대한 기여도는 낮으나, 경량기포모르터의 슬러리 비중이 0.8 이상인 경우 구조 성능의 향상과 마감성이 좋은 것으로 나타났다. 본 연구에서는 전단 거동에 미치는 경량기포모르터의 영향을 알아보기 위해 경량기포모르터의 비중(0.6, 0.8, 1.0, 1.2) 벽체의 스터드 배치간격(450mm, 600mm, 900mm), 마감재(경량기포모르터, OSB, 석고보드) 및 브레이싱 등을 변수로 한 14개의 경량합성벽체를 제작하였고 비교를 위해 대표적인 스틸하우스 벽체 3개를 제작하였다. 면내전단 실험결과, 경량기포모르터를 타설한 경량합성벽체가 기존의 스틸스터드 벽체에 비해 최대 내력은 1.15~5.38배, 초기강성은 1.45~13.7배 증가한 것으로 나타났다. 또한 벽체 내부의 스터드를 900mm까지 확장하여도 무리가 없는 것으로 나타났다. 그러나 이와 같은 결과는 건조수축 균열이 억제되지 않은 상태에서 나온 것으로 경량합성벽체의 내력을 향상시키기 위해서는 경량기포모르터의 초기 건조수축균열을 억제하고 스터드와 경량기포모르터 사이의 부착력을 확보하는 것이 무엇보다도 중요한 것으로 나타났다.

• The Journal of Advanced Prosthodontics
• /
• 제6권4호
• /
• pp.272-277
• /
• 2014

PURPOSE. The purpose of this study was to investigate the impact of different surface treatment methods and thermal ageing on the bond strength of autopolymerizing acrylic resin to Co-Cr. MATERIALS AND METHODS. Co-Cr alloy specimens were divided into five groups according to the surface conditioning methods. C: No treatment; SP: flamed with the Silano-Pen device; K: airborne particle abrasion with $Al_2O_3$; Co: airborne particle abrasion with silica-coated $Al_2O_3$; KSP: flamed with the Silano-Pen device after the group K experimental protocol. Then, autopolymerized acrylic resin was applied to the treated specimen surfaces. All the groups were divided into two subgroups with the thermal cycle and water storage to determine the durability of the bond. The bond strength test was applied in an universal test machine and treated Co-Cr alloys were analyzed by scanning electron microscope (SEM). Two-way analysis of variance (ANOVA) was used to determine the significant differences among surface treatments and thermocycling. Their interactons were followed by a multiple comparison' test performed uing a post hoc Tukey HSD test (${\alpha}=.05$). RESULTS. Surface treatments significantly increased repair strengths of repair resin to Co-Cr alloy. The repair strengths of Group K, and Co significantly decreased after 6,000 cycles (P<.001). CONCLUSION. Thermocycling lead to a significant decrease in shear bond strength for air abrasion with silica-coated aluminum oxide particles. On the contrary, flaming with Silano-Pen did not cause a significant reduction in adhesion after thermocycling.

• 접착 및 계면
• /
• 제16권2호
• /
• pp.69-75
• /
• 2015

돌침대에 사용되는 석재의 무게를 줄여 경량화를 추구하려면 석재의 두께를 줄이고 보강재료로 석재의 강도를 유지해야 한다. 본 연구에서는 돌침대용 석재/목재 보드 개발에 대한 연구를 진행하였다. 돌침대에 삽입될 돌의 무게를 줄이기 위해 석재와 목재를 접합하였다. 목재의 강도 향상과 표면개질을 위하여 열처리 조건에 따른 목재의 물성변화를 관찰하였다. 대기 조건에서 열처리한 목재의 경우 고온의 온도에 따라 목재의 강성이 높아졌다. 열처리 최적조건은 표면에너지와 인장, 굴곡 강도변화 경향을 바탕으로 $100^{\circ}C$ 조건임을 확인하였다. 석재와 목재간 높은 접착력을 확보하기 위해 최적의 접착제 조성을 연구하였다. 아민계 에폭시 접착제, 폴리우레탄(PU)계 접착제, 염화고무계(CR) 접착제 마지막으로 염화비닐초산계 접착제에 따른 석재와 목재간 랩 전단실험을 진행하였다. 랩 전단 실험 후 파단면을 관찰해볼 때 에폭시 접착제를 이용할 때 목재 기지의 인열 파괴가 발생되었다. 접착면에서의 전단력이 목재 자체의 파괴 강도보다 높다는 결과를 바탕으로 최적의 접착제 조건이 에폭시계 접착제임을 확인할 수 있었다.