• Korean Journal of Materials Research
• /
• v.14 no.5
• /
• pp.305-309
• /
• 2004

Mechanical alloying (MA) of Ti-25.0～37.5at%Si powders was carried out in a high-energy ball mill, and in situ thermal analysis was also made during MA. In order to classify the synthesis behavior of the powders with respect to at%Si, the synthesis behavior during MA was investigated by in situ thermal analysis and X-ray diffraction (XRD). In situ thermal analysis curves and XRD patterns of Ti-25.0～26.1at%Si powders showed that there were no peaks during MA, indicating $Ti_{5}$ $Si_3$ was synthesised by a slow reaction of solid state diffusion. Those of Ti-27.1～37.5at%Si powders, however, showed that there were exothermic peaks during MA, indicating $_Ti{5}$ $Si_3$ and$ Ti_3$Si phase formation by a rapid exothermic reaction of self-propagating high-temperature synthesis (SHS). For Ti-27.1～37.5at%Si powders, the critical milling times for SHS decreased from 38.1 to 18.5 min and the temperature rise, ΔT (= peak temperature - onset temperature) increased form $19.5^{\circ}C$ to $26.7^{\circ}C$ as at%Si increased. The critical composition of Si for SHS reaction was found to be 27.1at% and the critical value of the negative heat of formation of Ti-27.1at%Si to be -1.32 kJ/g.

• Korean Journal of Materials Research
• /
• v.14 no.5
• /
• pp.310-314
• /
• 2004

Mechanical alloying (MA) of Ti-50.0～66.7at%Si powders was carried out in a high-energy ball mill, and in situ thermal analysis was also made during MA. In order to classify the synthesis behavior of the powders with respect to at%Si, the synthesis behavior during MA was investigated by in situ thermal analysis and X-ray diffraction (XRD). In situ thermal analysis curves and XRD patterns of Ti-50.0～59.6at%Si powders showed that there were exothermic peaks during MA, indicating TiSi, $TiS_2$, and $Ti_{5}$ $Si_4$ phase formation by a rapid exothermic reaction of self-propagating high-temperature synthesis (SHS). Those of Ti-59.8～66.7 at%Si powders, however, showed that there were no peaks during MA, indicating any Ti silicide was not synthesised until MA 240 min. For Ti-50.0～59.6at%Si powders, the critical milling times for SHS increased from 34.5 min to 89.5 min and the temperature rise, $\Delta$T (=peak temperature-onset temperature) decreased form $26.2^{\circ}C$ to $17.1^{\circ}C$ as at%Si increased. The critical composition of Si for SHS reaction was found to be 59.6at% and the critical value of the negative heat of formation of Ti-59.6at%Si to be -1.48 kJ/g.

• Korean Journal of Materials Research
• /
• v.12 no.9
• /
• pp.696-700
• /
• 2002

The Ti-aluminide intermetallic compound was formed from high purity elemental Ti and Al foils by self-propagating, high-temperature synthesis(SHS) in hot press. formation of $TiAl_3$ at the interface between Ti and Al foils was controlled by temperature, pressure, heating rate, and so on. According to the thermal analysis, it is known in this study that the heating rate is the most important factor to form the intermetallic compound by this SHS reaction. The V layer addition between Al and Ti foils increased SHS reaction temperatures. The fully dense, well-boned inter-metallic composite($TiA1/Ti_3$Al) sheets of 700 m thickness were formed by heat treatment at $1000^{\circ}C$ for 10 hours after the SHS reaction of alternatively layered 10 Ti and 9 Al foils with the V coating layer. The phases and microstructures of intermetallic composite sheets were confirmed by EPMA and XRD.

• Journal of the Korean Ceramic Society
• /
• v.31 no.6
• /
• pp.637-642
• /
• 1994

Using SHS(Self-propagating High-temperature Synthesis) method, the optimum synthetic condition of titanium carbonitride was established by controlling the parameters such as relative density of mixture (Ti+C), nitrogen pressure, additive amounts of titanium hydride(TiH1.924) and protecting heat loss. Under 1 atm nitrogen pressure, nitridation ratio with changing relative density of the sample compacts has a maximum (87.2%) at about 55%, and in the case of enveloping the pellet with a quartz tube, the highest nitridation ratio of 90% was obtained at about 68%. At relative density of 55%, nitridation ratio with the nitrogen pressure has a miximum (87.3%) at 7 atm. As the amounts of additive titanium hydride increased, nitridation ratio decreased at below 7 atm nitrogen pressure and, increased at above this pressure until percent of addition percent reached 15 wt% and decreased abruptly upon futher increases in titanium hydride. In the synthesis of TiCxNy by combustion reaction, heat transfer from combustion zone to preheating zone and nitrogen gas penetration into the compact were found to be important factors affecting the TiCxNy formation. It was difficult to obtain high nitridation ratio when the conbustion temperature was either too high or too low, and it seems that the retention of high temperature after a combustion wave sweeped through the reactant mixture pellet is critical to obtain a satisfactory nitridation ratio.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.11a
• /
• pp.101-101
• /
• 2003

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2001.05a
• /
• pp.156-156
• /
• 2001

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2000.04a
• /
• pp.18-19
• /
• 2000

• Journal of the Korean Ceramic Society
• /
• v.41 no.7
• /
• pp.534-540
• /
• 2004

• Resources Recycling
• /
• v.12 no.6
• /
• pp.3-7
• /
• 2003

For the manufacture of iron oxide, the hydro-process and the pyre-process are conventionally used. Both processes use a huge amount of chemicals in reaction which affect the environment harmfully. This paper introduced the new environment friendly processes; the bio-chemical process and the self propagating high temperature synthesis process.

• Korean Journal of Materials Research
• /
• v.7 no.4
• /
• pp.295-302
• /
• 1997

금속분말 Fe와 Si에 KNO$_{3}$(Fe+Si)무게비=0.2로 점화촉매 KNO$_{3}$를 혼합하고 50MPa로 성형한 후 점화시키는 비기체연소합성(SHS; Self propagating High temperature Synthesis)법으로 출발 분말을 얻었다. 점화분위기를 공기 및 Ar으로 한 경우 XRD결과에서 특별한 차이가 없었고 두 경우 모두 SiO$_{2}$피크가 검출되었다. 합성된 분말을 성형한 후 119$0^{\circ}C$환원분위기에서 소결하고 포석온도이하에서 열처리하여 반도성 FeSi$_{2}$가 주상인 Fe-Si계 열전재료를 제조하였다. Fe/Si무게비=46/54,44/56 및 42/58시편의 제벡계수는 Si함량이 증가할수록 증가하였다. 점화후의 세척처리를 2단계로 하는 경우 제벡계수의 부호가 변화하여 p-type에서 n-type으로 변화하며 소결밀도가 크게 상승하였다. 조성에 관계없이 공통적으로 발견되는 SiO$_{2}$는 점화시의 분위기보다는 점화촉매에 포함된 K성분이 소결 및 열처리시 산화제로 작용하여 형성되는 것이 확인되었다.