• Design & Manufacturing
• /
• v.6 no.1
• /
• pp.24-28
• /
• 2012

Friction and wear affect all processes involved in the extraction of materials and their conversion into finished products in the die applications such as drawing, extrusion etc. Originating phenomenon from the contact surface between the tool and workpiece, they are usually a hindrance to materials process operations which usually result in damaging the tools, increasing energy consumption, the contamination of processed material by wear particles and also some problems associated with technologies to control friction and wear. The most well established method to control friction and wear is by the application of lubricant such as fluorocarbon. Besides, a surface technique so-called surface modification can be applied to solve the tribology problems of the die applications for both the economical and ecological reasons. In this article, we applied DLC(diamond-like carbon) thin film on alumina ceramic for HT test using the PIID(plasma ion immersion deposition), 4 groups of test specimens were tested up to $200^{\circ}C$ which is a little higher than the normal working temperature of die application. Pin-on-disc tribo-tester was used to test the friction and surfaces were characterized by SEM and EDS and else, the morphology changes of DLC coatings were studied. The present work indicated that the DLC had a great potential to reduce the friction and wear in the alumina die application without lubricants.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.21 no.7
• /
• pp.660-664
• /
• 2008

Titanium nitride (TiN) thin films are widely used for hard coatings due to their superior hardness, chemical stability, low friction and good adhesion properties. In this study, we investigated the effect of DC power on the characteristics of TiN thin films deposited on Si and glass substrates by DC magnetron sputtering using TiN target. We made TiN films of 300 nm thickness with various DC powers. The structural properties of films are investigated by x-ray diffractions (XRD) and tribological properties are measured by nano-indentation, nano-scratch tester. The rms roughness was measured by atomic forced microscopy (AFM). In the result, TiN films had the smooth surface and exhibited (111) directions with the increase of DC Power. Also, especially in case of 175 W DC power, TiN film exhibited the maximum hardness about 8 GPa, and the critical load near 25.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.19 no.3
• /
• pp.705-712
• /
• 1995

The wear characteristics and wear mechanisms in TiN coating deposited on high speed steel and alloy tool steel by ion plating were investigated. Pin on V-block wear tester was used for a wear test method. The specimen was composed of three kinds of high speed steel and alloy tool steel which had different hardness by changing the heat treating condition. Three kinds of coating thickness were also applied to each specimen. Microscopic observation of worn surfaces was made by SEM. The scratch test of coating surface by the ion plating showed that critical load to break the coating interface was greater than 50N. The critical load increased with both substrate hardness and coating thickness. The wear resistance of TiN coated high speed steel became 10 times greater than that of non-coated ones. SEM observation showed that leading edge of contact was compressive and trailing edge was under maximum tensile stress and then surface cracking broke out perpendicular to sliding direction.

• Proceedings of the Korean Vacuum Society Conference
• /
• 1999.07a
• /
• pp.47-47
• /
• 1999

2.45 GHz 마이크로웨이브를 이용하는 electron cyclotron resonance plasma enhanced chemical vapor deposition(ECR-PECVD)방법으로 다이아몬드성 탄소박막(diamond-like carbon, DLC)을 증착하였다. DLC 박막의 산업 응용을 위해서는 높은 경도와 밀착력이 필요하다. 그래서 본 실험에서는 DLC 박막의 산업 응용을 위하여 ECR-PECVD 방법으로 증착된 DLC 박막의 분석결과로부터 DLC 박막의 물성과 증착조건의 관계를 조사하였다. 기판으로는 실리콘 웨이퍼와 실험용 SUS 판을 사용하였다. 아르곤 가스를 주입하여 ECR 마이크로 웨이브 플라즈마와 negative DC bias로 기판을 플라즈마 세척한 후, 수소와 메탄가스를 반응기체로 하여 DLC 박막을 증착하였다. 박막 증착시에 13.56MHz RF 전원 공급장치로 기판에 전원을 공급하였다. DLC 박막 증착의 변수는 반응기체의 호합율, 마이크로웨이브 파워, 프로세스 압력 및 RF 전원공급장치에서 유도되는 negative self DC bias 등이다. 이때 사용된 반응기체의 혼합율(메탄/수소)은 10~50%이고, 수소 가스 흐름율은 100sccm, 메탄은 10~50sccm이다. 마이크로웨이브의 크기는 360~900W, negative self DC bias는 -500~-10 V였다. 그리고 본 실험에서는 높은 증착율을 고려하여 프로세스 압력을 10~30mTorr까지 조절하였다. ER-PECVD 방법으로 증착된 DLC 박막은 SEM으로 단면, $\alpha$-Step으로 두께, Raman 분광계로 탄소 결합구조, FTIR 분광계로 탄소와 수소 결합구조, Micro-Hardness로 경도 그리고 Scratch Tester로 밀착력 등을 분석하였다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 1999.07a
• /
• pp.132-132
• /
• 1999

카본 박막은 내마모성, 내산성, 윤활성 및 높은 경도를 가지고 있어, 경질 박막 및 기능성 박막으로 주목을 받고 있으며 그 응용 분야가 매우 크다. 본 연구는 전자빔(Electron Beam)을 카본 grain을 증발시킴과 동시에 아르곤 보조 이온빔을 조사시켜 이온에너지에 따른 박막의 물성변화를 관찰하였다. 특히 본 연구에서 이용한 이온빔 증착 장치의 장점은 이온 충돌 에너지의 조절이 가능하다는 것이다. 카본 박막의 제조는 이온빔이 증착된 고진공 증착 장치를 이용하였고 이원빔원으로는 Oxford Applied Research 사의 RF 방전형 이온빔을 이용하였다. 배기장치는 유회전펌프와 터보펌프를 사용하였다. 기판은 홀더에 장착하기 전에 전처리를 거친 후 용기 내에서 이온빔에 의해 2차 청정을 하였다. 빔전압이 500V, 빔 전류는 4mA/cm2 및 RF power를 400W로 하여 기판 청정을 거친 후 전자빔을 이용하여 흑연을 증발시켜 박막을 제조하였다. 이때 이온빔 전압을 100~500V, RF power를 400~550W 으로 조절하였다. 카본 grain을 Si 및 Slide Glass 기판위에 1$\AA$/sec의 증착율을 유지하면서 증착하였다. 카본 박막의 박막은 평균두께는 0.3~0.4$\mu\textrm{m}$이며 SEM을 이용하여 단면을 관찰하였다. 라만 분광분석을 통하여 비정질 카본 박막의 결합특성을 조사하였고 scratch tester를 이용하여 박막의 밀착력을 관찰하였다. 그리고 카본 박막의 전도도 특성을 알고자 비저항을 측정하였으며, 박막의 성분 분석을 위한 AES 분석을 하였다. 1)AES 결과:표면에서와 박막 내부에서는 불순물인 산소나 질소의 함량이 거의 존재하지 않음을 관찰하였다. 2)경도:1,000~1,400kg/mm2 3)라만 분광 분석:300V의 이온 에너지를 분기로 박막 구조의 변화에 의한 스팩트럼의 변화를 보였다. 4)비저항:10-2~10-1$\Omega$.cm

• Journal of the Korean institute of surface engineering
• /
• v.28 no.6
• /
• pp.368-375
• /
• 1995

Thermal CVD method is in general used for the fabrication of TiC/$Al_2O_3$-coated carbide tools. The growth of TiC layer and the coating morphology depended on the chemical composition of the hard metal substrate on which the tool properties were strongly influenced. TiC-coated layer was grown by the diffusion of carbon from the substrate, whereas the growth of $Al_2O_3$ layer was unrelated to the composition of substrate. In the nitride hard coatings of Zr, Nb and Mo metals deposited on high speed steel substrate by magnetron sputtering, the reactivity of the metal elements was decreased with increasing group number in one period of the periodic system. The hard material films exhibited the highest adhesion with the chemical composition of stoichiometry or substoichiometry. The critical load as a measure of adhesion was evaluated using scratch tester. The CVD tools indicated the values of 80 and 40N in the coated layers with proper bonding to the substrate and with $\eta$ phase of 1$\mu\textrm{m}$ in the interface respectively, but the nitride films prepared by sputtering of PVD showed only the values between 10 and 20N.

• Journal of the Korean institute of surface engineering
• /
• v.44 no.5
• /
• pp.190-195
• /
• 2011

Diamond-like carbon (DLC) has many outstanding properties such as low friction, high wear resistance and corrosion resistance. However, it is difficult to achieve enough adhesion on the metal substrates because of weak bonding between DLC film and the metal substrate. The purpose of this study is to enhance an adhesion of DLC film. For improving adhesion, the substrate was treated by active screen plasma nitriding before DLC film deposing. Nitrided substrates were investigated by Glow Discharge Spectrometer (GDS), Micro-Vickers Hardness. DLC films were deposited on several metals by linear ion source, and characteristics of the films were investigated using nano-indentation, Field Emission Scanning Electron Microscope (FESEM). The adhesion was measured by scratch tester. The adhesion of DLC films was increased when nitriding layer was formed before DLC deposition. Therefore, the adhesion of DLC film can be enhanced as increasing the hardness of materials.

• Corrosion Science and Technology
• /
• v.9 no.6
• /
• pp.289-293
• /
• 2010

To investigate the corrosion behavior of tools steel surface in various coating film, the surface of hard coated Ti-Zr-N film on the tool steel by using magnetron-sputtering methods was researched using various experimental methods. STD 61 steels were manufactured by using vacuum furnace and solutionized for 1hr at $1050^{\circ}C$. Steel surface was coated with Ti-Zr-N film at $150^{\circ}C$ and 100W for 1h by using DC-sputtering equipment. Surface characteristics of Ti-Zr-N film coated specimens were investigated by OM, XRD, FE-SEM and nano-scratch tester. And corrosion behaviors of the coated specimen were investigated by polarization test and electrochemical impedance spectroscopy(EG&G Co, PARSTAT 2273. USA). It was found that Ti-Zr-N film coated sample had a thick coated layer and showed a good wear resistance and corrosion resistance of surface compared with ZrN and TiN coated sample. The corrosion resistance and mechanical property of Ti-Zr-N film coated STD 61 alloy increased as sputtering time increased.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.02a
• /
• pp.247-247
• /
• 2010

DLC(diamond-like carbon)는 비정질 고상 탄소의 하나로 다이아몬드의 유사한 높은 경도, 내마모성, 윤활성, 전기절연성, 화학적 안정성을 가지고 있는 재료이다. 이러한 우수한 특성 때문에 DLC는 박막의 형태로 여러 종류의 보호코팅에 많이 응용되고 있다. DLC의 광범위한 응용에 있어 가장 큰 문제점은 박막이 갖는 높은 잔류응력과 이에 따른 기판과의 낮은 접착성으로 알려져 있다. 최근 연구에 의하면, plasma pre-treatment를 통해 PTFE기판에 DLC박막의 adhesion strength를 증진 시킬 수 있다고 보고하였다. 또한 ion beam technique를 이용하여 잔류응력을 줄이고 기판과의 접착력을 높일 수 있다는 것도 보고 되었다. 이에 기인하여 pre-treatment가 DLC합성에 잔류응력을 낮추고 기판과의 접착성을 높이는 효과를 보일 것이라고 가정하고 연구하였다. 본 연구에서 pre-treatment가 Diamond-like Carbon의 stainless steel 합성시 stress와 adhesion에 어떤 효과가 있는지 알아보기 위해, pre-treatment시와 synthesis of DLC film시에 13.56MHz 150W RF플라즈마 화학기상 증착 (RF-PECVD) 법을 통해 합성되었다. pre-treatment시에 H2(80 sccm), O2(10 sccm), N2(20 sccm)의 가스 종류를 다르게 하였고, synthesis of DLC film시에는 CH4 (20 sccm), H2 (80 sccm)가스의 유량을 고정하였다. 합성된 DLC 박막은 Contact Angle Analyze, Raman spectroscopy, Scratch tester를 이용하여 접촉각, D peak Position, G peak Position, ID/IG ratio, 접착력을 측정하였다.

• Journal of Adhesion and Interface
• /
• v.22 no.2
• /
• pp.47-56
• /
• 2021

Steel plates coated by self-healable polymer still can be rusted since it takes time to be healed. In this study, dual self-healing coating material is developed using corrosion inhibitor (DTBEDA) which can form hindered urea (HUB) as reversible cross-linking bond at the same time. Developed dual self-healing polymer is coated on steel plate, and scratch healing property was investigated by surgical blades and nano/micro indentation tester. The anticorrosion effect of DTBEDA was investigated by electrochemical impedance spectroscopy (EIS).