• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.13 no.5
• /
• pp.241-246
• /
• 2003

The transparent conducting thin film of ATO (antimony-doped tin oxide) was successfully fabricated on$SiO_2$/glass substrate by a sol-gel dip coating method. The crystalline phase of the ATO thin film was identified as SnO$_2$ major phase and the film thickness was about 100 nm/layer at the withdrawal speed of 50 mm/minute. Optical transmittance and electrical resistivity of the 400 nm-thick ATO thin film which was annealed under nitrogen atmosphere were 84% and $5.0\times 10^{-3}\Omega \textrm{cm}$, respectively. It was found that the $SiO_2$ layer inhibited Na ion diffusion and the formation of impurities like $Na_2SnO_3$ or SnO while increasing Sb ion concentration and higher ratio of $Sb^{5+}/Sb^{3+}$in the film. Annealing at nitrogen atmosphere leads to the reduction of $Sn^{4+}$ as well as $Sb^{5+}$ resulting in decrease of the electrical resistivity of the film.

• Journal of the Korean Chemical Society
• /
• v.24 no.3
• /
• pp.183-192
• /
• 1980

Oxidation reactions of carbon monoxide on $SnO_2$, Sb-doped $SnO_2$, and Pt catalyst were studied. The oxidation reaction was found to be first order with respect to both CO and O$_2$ on $SnO_2$ and Sb-doped $SnO_2$ catalysts, and to be of half order on Pt catalyst. A small addition of Sb to $SnO_2$ (depant composition: 0.05∼0.1 mol %) increased the rate of oxidation. On the contrary, a large addition decreased the rate. From the rate expression of oxidation on Pt catalyst, the inhibition effect of carbon monoxide on the rate of oxidation was deduced. The experimentally obtained activatio energies were 5.7 kcal for the Sb doped $SnO_2$ catalyst (dopant composion: 0.05 mole%), and 6.4 kcal for the Pt catalyst. A possible reaction mechanism was proposed from the experimentally obtained kinetic data.

• Journal of the Korean Ceramic Society
• /
• v.51 no.1
• /
• pp.43-50
• /
• 2014

We fabricated undoped and Sb-doped $SnO_2$ thin films on glass substrates by a pulsed laser deposition (PLD) process. Undoped and 2 - 8 wt% $Sb_2O_3$-doped $SnO_2$ targets with a high density level of ~90% were prepared by the spark plasma sintering (SPS) process. Initially, the effects of the deposition temperature on undoped $SnO_2$ thin films were investigated in the region of $100-600^{\circ}C$. While the undoped $SnO_2$ film exhibited the lowest resistivity of $1.20{\times}10^{-2}{\Omega}{\cdot}cm$ at $200^{\circ}C$ due to the highest carrier concentration generated by the oxygen vacancies, 2 wt% Sb-doped $SnO_2$ film exhibited the lowest resistivity value of $5.43{\times}10^{-3}{\Omega}{\cdot}cm$, the highest average transmittance of 85.8%, and the highest figure of merit of 1202 ${\Omega}^{-1}{\cdot}cm^{-1}$ at $400^{\circ}C$ among all of the doped films. These results imply that 2 wt% $Sb_2O_3$ is an optimum doping content close to the solubility limit of $Sb^{5+}$ substitution for the $Sb^{4+}$ sites of $SnO_2$.

• Journal of the Korean Ceramic Society
• /
• v.29 no.4
• /
• pp.319-327
• /
• 1992

Sb-doped SnO2 films were formed on Corning glass 7059 substrate by chemical vapor deposition using simulataneous hydrolysis of SnCl4 and SbCl5. Fairly good transparent conducting film with a low resistivity of ~6$\times$10-4{{{{ OMEGA }}cm and high average optical transparency above ~85% in the range of visible light was obtained at the deposition condition of 50$0^{\circ}C$ and input-gas ratio, [Psbcl5/Psncl4] of 0.05. Film conductivity was improved without loosing optical transparency at light doping of Sb and found to be due to the increase of electron concentration. However, high doping of Sb into SnO2 film largely deteriorated conductivity, optical transparency and crystallinity of the film.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.13 no.5
• /
• pp.254-259
• /
• 2003

In the fabrication process of transparent conducting thin films of the ATO (antimony-doped tin oxide) on a soda lime glass substrate by a sol-gel dip coating method, the effects of the $SiO_2$ buffer layer formed on the substrate and $N_2$ annealing treatment were investigated by XPS (X-ray photoelectron spectroscopy) analysis. Optical transmittance and electrical resistivity of the 400 nm-thick ATO thin films which were deposited on $SiO_2$ buffer layer/soda lime glass and then annealed under nitrogen atmosphere were 84 % and $5.0\times 10^{-3}\Omega \textrm{cm}$ respectively. The XPS analysis confirmed that a $SiO_2$ buffer layer inhibited Na ion diffusion from the substrate, resulting in prohibiting the formation of a secondary phase such as $Na_2SnO_3$ and SnO and increasing Sb ion concentration and ratio of $Sb^{5+}/Sb^{3+}$ in the film. And it was also found that $N_2$ annealing treatment leads to the reduction of $Sn^{4+}$as well as $Sb^{5+}$ however the reduction of $Sn^{4+}$ is more effective and therefore consequently results in decrease in the electrical resistivity to produce an excellent electrical properties of the film.

• Journal of Sensor Science and Technology
• /
• v.22 no.4
• /
• pp.302-307
• /
• 2013

The Sb-doped $SnO_2$ nanowire network sensors were prepared by thermal evaporation of the mixtures between tin and antimony powders. Pure $SnO_2$ nanowire networks showed high sensor resistance in air ($99M{\Omega}$), similar gas responses to 4 diffferent gases (5 ppm $C_2H_5OH$, CO, $H_2$, and trimethylamine), and very sluggish recovery speed (90% recovery time > 800 s). In contrast, 2 wt% Sb-doped $SnO_2$ showed the selective detection toward $C_2H_5OH$ and trimethylamine, relatively low resistance ($176k{\Omega}$) for facile measurement, and ultrafast recovery speed (90% recovery times: 6 - 18 s). The change of gas sensing charactersitics by Sb doping was discussed in relation to gas sensing mechanism.

• Journal of the Korean Ceramic Society
• /
• v.37 no.2
• /
• pp.194-200
• /
• 2000

Sb-doped tin oxide films were deposited on Corning glass 1737 substrate by plasma enhanced chemical vapor deposition(PECVD) technique using a gas mixture of SnCl4/SbCl5/O2/Ar. The deposition behaviors of tin oxide films by PECVD were compared with those by thermal CVD, and effects of deposition temperature, r.f. power and Sb doping on the electrical properties of tin oxide films were investigated. PECVD technique largely increased the deposition rate and smoothed the surface of tin oxide films compared with thermal CVD. Electrical resistivity decreased with doping of Sb due to the increase of carrier concentration. However, large doping of Sb diminished carrier concentration and mobility due to the decrease of crystallinity, which resulted in the increase of electrical resistivity. As the deposition temperature and r.f. power increased, Cl content in the film decreased.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.22 no.3
• /
• pp.269-276
• /
• 2009

Antimony doped tin oxide ($SnO_2:Sb$) films, which are used as the front contact and back reflector of thin film solar cells, have been deposited by d,c, magnetron sputtering. The dependence of electrical and optical properties of the films on the preparation conditions, such as $O_2$ gas ratio, substrate temperature, annealing temperature was investigated. The sputter gas composition was found to affect the properties of the films. With incorporating $O_2$ gas, the electrical and optical properties of films significantly were improved. The minimum resistivity and optical transmittance over 80 % in visible region were obtained at the oxygen concentration of 30 %, When the substrate temperature was higher, the resistivity of $SnO_2:Sb$ films was decreased, while the absorption edge shifted to shorter wavelength, indicating higher optical band gap. Heat treatment over $600^{\circ}C$ resulted in poorer electrical and optical properties due to SnO phase (102) plane.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.28 no.11
• /
• pp.690-693
• /
• 2015

In this paper, in order to develop excellent Pb-free composition ceramics for ultrasonic sensor. The $SnO_2$-doped ($Na_{0.525}K_{0.443}Li_{0.037})(Nb_{0.883}Sb_{0.08}Ta_{0.037})O_3$)(abbreviated as NKL-NST) ceramics have been synthesized using the ordinary solid state reaction method. The effect of $SnO_2$-doping on their dielectric and piezoelectric properties was investigated. The ceramics doped with 0 wt% $SnO_2$ have the optimum values of piezoelectric constant($d_{33}$), piezoelectric figure of merit($d_{33}.g_{33}$), planar piezoelectric coupling coefficient($k_p$) and density : $d_{33}=195[pC/N]$, $d_{33}.g_{33}=5.62pm^2/N.kp=0.40$, $density=4.436[g/cm^3]$. suitable for duplex ultrasonic sensor application.

• Proceedings of the Korean Ceranic Society Conference
• /
• 2002.10a
• /
• pp.183.1-183
• /
• 2002