• 콘크리트학회논문집
• /
• 제12권1호
• /
• pp.89-99
• /
• 2000

The objective of this study is to investigate the bond strength properties of antiwashout underwater concrete. The arrangement of bars (vertical bar, horizontal upper bar, horizontal lower bar), condition of casting and curing (fresh water, sea water), type of fine aggregate (river sand, blended sand(river sand : sea sand = 1:1), and proportioning strength of concrete (210, 240, 270, 300, 330kgf/$\textrm{cm}^2$)are chosen as the experimental parameters. The test results(ultimate bond stress) are compared with bond and development provisions of the ACI Building Code(ACI 318-89) and proposed equations from previous research(which was proposed by Orangun et. al). The experimental results show that ultimate bond stress of antiwashout underwater concrete which arranged bar on the horizontal lower, used the blend sand, and was cast and cured in the fresh water are higher that other conditions. The ultimate bond stress were increased in proportion to {{{{( SQRT {fcu }) }}3 2. From this study, rational analytic formula for the ultimate bond stress are to be from compressive strength of concrete.

• 한국주조공학회지
• /
• 제24권2호
• /
• pp.63-70
• /
• 2004

Foundry techniquews for large steel casting depends on the skills of foundrymen considerably. Especially, the problem of reducing casring surface defects is difficult to clear numerically. Statistical analysis by using wuantification theory for hot tear and sand inclusion, and multiple regression analysis for dimensional defects have been shown to be examples of solving this difficulty. Many causes of surface defects can be evaluated by these analyses. These evaluations serve as the base data of defect reduction and contribute to the constant improvement of casting quality and quality enhancement activity. The system to perform quality enhancement activity was developed and it proved very useful for transfering foundry techniques and skills from the old to young generations.

• 한국융합학회논문지
• /
• 제12권2호
• /
• pp.185-191
• /
• 2021

본 자동차 실린더 블록 주조시 실린더 보어 내에서 발생하는 열로부터 구조적 변형을 방지하는데 필요한 워터 자켓 코어용 주물사의 특성을 분석하였다. 샌드 코어의 특성평가를 위하여 인장강도 시험기, 입도 지수(AFS-GFN), 광학현미경을 사용하였다. 주물사의 SiO2 함량이 높으면 고온팽창에 의한 치수 불량, 베이닝 불량이 발생하며, 너무 낮으면 코어 파손, 기포, 화학적 소착 등이 발생하였다. 입도 지수와 입형이 코어강도와 레진 소비량에 영향을 미치고, 이로 인한 불량 유형 변화가 발생하였다. 건조사가 염분이 높을수록 코어 강도는 감소하며, 알칼리성일수록 코어 강도가 감소하였다. 레진 함량 1.6~1.8%에서 1시간 경화 이후에 코어 강도 증가는 대략 최대를 보였다.

• 한국주조공학회지
• /
• 제17권6호
• /
• pp.569-576
• /
• 1997

Coating materials for Evaporative Pattern Casting (EPC) process have been developed to investigate the effect of refractories on coating material properties. Three types of developed and one foreign coating materials were used. The former designated as A, B, C and the latter named S.K. The refractory of coating material A is spherical shape of zirconia, and the ones of B, C and S.K. is flake shape of mica. Strength, permeability at room and elevated temperature, anti-sand attachability and carbon residuary were evaluated at each coating materials. Permeability measurement device for elevated temperature was also designed. The zirconia type of coating material had excellent permeability, on the other hand the mica type had good strength and anti-sand attachability. It was found that the refractories were not broken during casting, so permeability indicated same trend at both room and elevated temperature. Based on results, coating material contained small size of mica which is designated as B has the best combination for cast iron.

• 한국정밀공학회지
• /
• 제33권6호
• /
• pp.469-475
• /
• 2016

In this work, casting processes, such as filling and solidification, were simulated in order to accurately predict volume shrinkage defects in large-sized sand gravity casting. Turbulent flow of melted materials and a difference of solidification speed can cause volume shrinkage defects. In order to solve this problem and to understand the phenomenon, a porous filter application was studied. Two different porosities of 10 and 20 p.p.i filters were introduced into the gating system, and in view of the results so far achieved, the defect was dramatically reduced by 22%, compared to that without the use of the filter.

• 한국주조공학회지
• /
• 제26권4호
• /
• pp.174-179
• /
• 2006

This study aims to investigate the microstructures and mechanical properties of DCI manufactured by sand and metal mold casting. To prohibit the formation of the chill, carbon, silicon and rare earth($0{\sim}0.2\;wt%$) were controlled and temperature of metal mold was constantly kept at $160^{\circ}C$. The sizes, counts and nodularity ratios of nodules were analyzed by image analysis device. Wear test using pin-on-disc wear tester was carried out under the conditions of load 47.2N, velocity 0.4 m/s and distance 2000 m. Tensile test using Instron type testing machine was performed with velocity of 0.1 mm/min according to the KS B 0802. The formation of the chill was not observed when percentage of the carbon and silicon were 3.8 and 2.5. Mechanical properties of GCD manufactured by metal mold were better than sand casting.

• 한국자동차공학회논문집
• /
• 제18권6호
• /
• pp.1-6
• /
• 2010

Aluminum rear lower arm is designed for luxury sedan and manufactured by hollow sand casting in the present study. Here we present the relationship between local microstructure and coupon tensile test in the rear lower arm. The characteristics of the local tensile deformation are supposed to be dependent upon Si distribution and DAS (dendrite arm spacing). Si distribution affects the yield strength and DAS affects the elongation of local area in the part, respectively.

• 한국정밀공학회지
• /
• 제18권3호
• /
• pp.47-52
• /
• 2001

Rapid Prototyping(RP) has been widely applied in designing and developing process of new products. RP can reduce the lead time and expense required to bring a new product form initial concept to production. Among several RP process can dramatically reduce the total build time and be applied for fabrication of large-sized and free form object because it uses in LOM the paper thickness is 0.05∼0.38mm as deposition feature segment. In this study, mechanical properties of pattern with LOM system is studied for optimal design of sand mold casting. The main result is that tensile, compressive strength and pattern size are significantly affected by temperature of hot roll.

• 한국주조공학회지
• /
• 제18권5호
• /
• pp.481-487
• /
• 1998

Shell sand is widely used to make a complex shape castings due to its good collapsibility. When molten metal is poured into the mold, various gases are generated by the thermal decomposition of binder in the shell core. Casting defects such as blow hole and blister come from these gases. If it is possible to predict the evolution of gas quantitatively, it may provide effective solutions for minimizing the casting defects. To examine the gas evolution by shell core quantitatively, casting experiment and calculation were carried out. Gas pressure and gas volume evolved by shell core were measured in the experiment, and temperature distribution in the shell core was obtained by heat transfer analysis. From the result above, prediction on the gas volume evolved during pouring was tried. As forming pressure of the shell core increased and forming temperature decreased, the gas evolution increased. There was a close relationship between the calculated gas volume evolved and the measured one.

• 한국주조공학회지
• /
• 제37권6호
• /
• pp.181-185
• /
• 2017

In the present study, the effect of cooling rate on the formation of the porosity in the thick aluminum sand casting was investigated. Nowadays, due to considerations of weight and cost reduction, large scale thick aluminum casting has replaces steel frames for vacuum chambers for semiconductor production. Several thick aluminum castings were manufactured using chill with temperature measurements. The castings were inspected using 3D computed tomography in order to quantify the porosity defect density in the castings. Effects of the thickness of the chill on the porosity defect density were discussed.