In this study, the high-temperature oxidation properties of austenitic 316L stainless steel manufactured by laser powder bed fusion (LPBF) is investigated and compared with conventional 316L manufactured by hot rolling (HR). The initial microstructure of LPBF-SS316L exhibits a molten pool ~100 ㎛ in size and grains grown along the building direction. Isotropic grains (~35 ㎛) are detected in the HR-SS316L. In high-temperature oxidation tests performed at 700℃ and 900℃, LPBF-SS316L demonstrates slightly superior high-temperature oxidation resistance compared to HR-SS316L. After the initial oxidation at 700℃, shown as an increase in weight, almost no further oxidation is observed for both materials. At 900℃, the oxidation weight displays a parabolic trend and both materials exhibit similar behavior. However, at 1100℃, LPBF-SS316L oxidizes in a parabolic manner, but HR-SS316L shows a breakaway oxidation behavior. The oxide layers of LPBF-SS316L and HR-SS316L are mainly composed of Cr₂O₃, Fe-based oxides, and spinel phases. In LPBF-SS316L, a uniform Cr depletion region is observed, whereas a Cr depletion region appears at the grain boundary in HR-SS316L. It is evident from the results that the microstructure and the high-temperature oxidation characteristics and behavior are related.

• 대한의용생체공학회:학술대회논문집
• /
• 대한의용생체공학회 1994년도 추계학술대회
• /
• pp.175-177
• /
• 1994

The wear corrosion behaviour of a nitrogen ion implanted super stainless steel (S.S.S, 22Cr - 20Ni - 6Mo - 0.25N) was compared with those of S.S.S, 316L SS and TiN coated 316L SS. The Cr and Ni amounts won out from the materials were investigated using an electrothermal atomic absorption spectrometry. We observed that the Cr dissolution rate of the S.S.S was similar to that of 316L SS, however, the Ni release of the S.S.S was feater than 316L SS. The metal ions released from the nitrogen ion implanted S.S.S surface were significantly reduced. The wear corrosion behaviour of the stainless steels was not correlated with the results shown by a static metal ion release test.

• 한국전기화학회:학술대회논문집
• /
• 한국전기화학회 2001년도 연료전지심포지움 2001논문집
• /
• pp.237-242
• /
• 2001

용융탄산염 연료전지에서 분리판으로 사용되는 316L 스테인리스 스틸의 내식성을 향상시키기 위해 Ni과 Al을 전기도금법에 의해 코팅하였으며 열처리를 통해 스테인리스 스틸표면에 $Ni_2Al_3$, NiAl 등의 금속간화합물을 형성시켰다. $62mol\%Li_2CO_3-38mol\%K_2CO_3$ 전해질 내에서 100시간 동안 침지실험을 수행한 결과 Al의 도금두께가 $10{\mu}m$ 이상인 경우에는 내식성이 상당히 향상되었음을 확인하였다.

• 방사성폐기물학회지
• /
• 제18권2호
• /
• pp.169-177
• /
• 2020

Here, the stability of stainless steel 316 (SS-316) was investigated to identify its applicability in the oxide reduction process, as a component in related equipment, to produce a complicated gas mixture composed of O₂ and Cl₂ under an argon (Ar) atmosphere. The effects of the mixed gas composition were investigated at flow rates of 30 mL/min O₂, 20 mL/min O₂ + 10 mL/min Cl₂, 10 mL/min O₂ + 20 mL/min Cl₂, and 30 mL/min Cl₂, each at 600℃, during a constant argon flow rate of 170 mL/min. It was found that the corrosion of SS-316 by the chlorine gas was suppressed by the presence of oxygen, while the reaction proceeded linearly with the reaction time regardless of gas composition. Surface observation results revealed an uneven surface with circular pits in the samples that were fed mixed gases. Thermodynamic calculations proposed the combination of Fe and Ni chlorination reactions as an explanation for this pit formation phenomenon. An exponential increase in the corrosion rate was observed with an increase in the reaction temperature in a range of 300 ~ 600℃ under a flow of 30 mL/min Cl₂ + 170 mL/min Ar.

• Nuclear Engineering and Technology
• /
• 제56권6호
• /
• pp.2131-2140
• /
• 2024

The chloride-induced stress corrosion cracking (CISCC) is one of the major integrity concerns in dry storage canisters made of austenitic stainless steels (ASSs). In this study, an advanced duplex stainless steel (DSS) with a composition of Fe-19Cr-4Ni-2.5Mo-4.5Mn (ADCS) was developed and its performance was compared with that of commercial ASS and DSS alloys. The chemical composition of ADCS was determined to obtain greater pitting and CISCC resistance as well as a proper combination of strength and ductility. Then, the thermomechanical processing (TMP) condition was applied, which resulted in higher strength than ASSs (304L SS and 316L SS) and better ductility than DSSs (2101 LDSS and 2205 DSS). The potentiodynamic polarization and electrochemical impedance spectra (EIS) results represented the better pitting corrosion resistance of ADCS compared to 304L SS and 316L SS by forming a better passive layer. The CISCC tests using four-point loaded specimens showed that cracks were initiated at 24 h for 304L SS and 144 h for 316L SS, while crack was not found until 1008 h for ADCS. Overall, the developed alloy, ADCS, showed better combination of CISCC resistance and mechanical properties as dry storage canister materials than commercial alloys.

• 한국진공학회지
• /
• 제15권3호
• /
• pp.325-330
• /
• 2006

ITER (International Thermonuclear Experimental Reactor) 조달용 일차벽의 제조 건전성을 검증하기 위해서, 일차벽을 구성하는 Cu/SS mock-up을 제작하여 고열부하 시험을 수행하였다. Cu/SS mock-up은 CuCrZr과 SS316L이 사용되었으며, 두 금속은 $1050^{\circ}C$, 150 MPa의 조건에서 고온등방가압법 (HIP, Hot Isostatic Pressing) 과정을 통해 접합되었다. 시험에 사용된 고열부하 장치는 일본 원자력연구소의 JEBIS (JAEA Electron Beam Irradiation Stand)를 이용하였으며, 시험 조건은 FEM 코드인 ANSYS 해석을 통해 결정하였다. 시험은 $5MW/m^2$의 고열부하를 15초간 인가하고, 30초간 냉각하는 방법으로 수행되었으며, 시험 종료 후 얻어진 시험결과와 해석결과가 잘 일치함을 확인하였다.

• 한국표면공학회지
• /
• 제50권1호
• /
• pp.35-41
• /
• 2017

$TiO_2$, $Al_2O_3$, and $TiO_2-Al_2O_3$ nanolaminated films were grown by atomic layer deposition (ALD) on the 316L stainless steel (SS316L) substrates at a temperature of $150^{\circ}C$. The growth kinetics of $ALD-TiO_2$ and $Al_2O_3$ thin films were systematically investigated in order to precisely control the thickness of each layers in the $TiO_2-Al_2O_3$ nanolaminated films using a high-resolution transmission electron microscopy. And, the exact deposition rates of $ALD-TiO_2$ on $Al_2O_3$ surface and $ALD-Al_2O_3$ on $TiO_2$ surface were revealed to be 0.0284 nm/cycle and 0.11 nm/cycle, respectively. At given growth conditions, the microstructures of $TiO_2$, $Al_2O_3$ and $TiO_2-Al_2O_3$ nanolaminated films were amorphous. The potentiodynamic polarization test revealed that the $TiO_2-Al_2O_3$ nanolaminated film coated SS316L had a best corrosion resistance, although all ALDcoated SS316L exhibited a clear improvement of the corrosion resistance compared with a bare SS316L.

• 대한기계학회논문집A
• /
• 제33권4호
• /
• pp.401-408
• /
• 2009

This study is performed to check the three dimensional characteristics of residual stress in the dissimilar metal weld. Although two dimensional analysis has been widely used for the assessment of weld residual stress, it has limitations to understand the stress distribution of the third direction. 3-D analysis was done to understand residual stress distribution of the welded plate. A simple butt-welded plate was considered to show the stress variation on all direction. A mock-up plate weldment was fabricated with SA-508 and F316L, which are widely used in nuclear power plants. The analysis results were validated with the measured values in the mock-up.

• Nuclear Engineering and Technology
• /
• 제54권12호
• /
• pp.4474-4480
• /
• 2022

Deep geological disposal using a multibarrier system is a promising solution for treating high-level radioactive (HLRW) waste. The HLRW canister represents the first barrier for the migration of radionuclides into the biosphere, therefore, the corrosion behavior of canister materials is of significance. In this study, the electrochemical behaviors of SS316L, Ti-Gr.2, Alloy 22, and Cu in naturally aerated KAERI underground research tunnel (KURT) groundwater solutions were examined. The corrosion potential, current, and impedance spectra of the test materials were recorded using electrochemical methods. According to polarization and impedance measurements, Cu exhibits relatively higher corrosion rates and a lower corrosion resistance ability than those exhibited by the other materials in the given groundwater condition. In the anodic dissolution tests, SS316L exposed to the groundwater solution exhibited the most uniform corrosion, as indicated by its surface roughness. This phenomenon could be attributed to the extremely low concentration of chloride ions in KURT groundwater.

• Nuclear Engineering and Technology
• /
• 제55권4호
• /
• pp.1468-1475
• /
• 2023

Enhancement of wear resistance of components used in fast reactors is necessary for long service life of the components. Plasma nitriding is a promising surface modification technology to impart high hardness and improved wear resistance of various steel components. This study discusses the characterization of chrome nitrided SS316L casing ring used in secondary sodium pump of fast breeder reactor and its stability under long term sodium exposure. Microstructural and hardness analysis showed that stress relieved component could be chrome nitrided successfully to a thickness of about 100 ㎛. Assessment of in-sodium performance of the chrome nitrided casing ring subjected to long term exposure up to 5000h at 550℃, showed retention of chrome nitrided layer with a case depth almost similar to that before sodium exposure. A slight decrease in the hardness was observed due to prolonged high temperature sodium exposure. Tribological studies indicate very low coefficient of friction indicating the retention of good wear resistance of the coating even after long term sodium exposure.