• Korean Journal of Materials Research
• /
• v.7 no.2
• /
• pp.107-113
• /
• 1997

$SrBi_{2}Ta_{2}O_{9}(SBT)$ thin films wcre prepared on $Pt/Ti/SiO_{2}/Si$ suhsrrate by pL~snia-enhanced chemical vapor deposition. Sr and Ta huhhling temperatures were kept ,it $120^{\circ}C$ Iron1 X- ray tiiffriict!on. n~icrostruc~ure. and composjrional analysis of SH7' films, respectivels Hi I~ut~t~lmg tempcl.arure was varied SR'I' thin tilrns dcpositcd ar i3i buhbling temperature of $130^{\circ}C$ have dielccrric constanr of 150 anti dissipation factor of 0 02 at IOOkFic. I .eakagc wrrent density of films was ahour $1.0{\times}10^{-8}A/cm^2$ at 20kV/cm. 1.eakage current i11amcrc1istic.s of Sli'l' films nras c.ontrolled by I'oole Frcnkel emission Kenianent polariziit~on and mercivc field oi SR\ulcorner' films annealed at $550^{\circ}C$ were $9{\mu}C/cm^2$ and 70kV/cm, respectively.

• Journal of the Korean Ceramic Society
• /
• v.39 no.10
• /
• pp.1001-1006
• /
• 2002

Bond strength of $SrZrO_3$ resistive oxide barrier on Ag sheathed Bi(2223) tapes prepared by the sol-gel and dip-coating method was evaluated with an aid of Taguchi method and $L_18(2^1{\times}3^7)$ orthogonal arrays to determine the optimal process combination of levels of factors that best satisfy the bigger is better quality characteristic. The observed optimal condition is as follows: Sr/Zr mol ratio(0.3/0.7), amount of organic vehicle(5 wt%), drying temperature and time(160${\circ}C$, 10 min), heat treatment temperature and time(500${\circ}C$, 20 min), respectively. ANOVA analysis suggested that the influence of the factors within ${\alpha}$=0.1 was significant with a 90% confidence level.

• Journal of Food Hygiene and Safety
• /
• v.6 no.3
• /
• pp.171-177
• /
• 1991

According to the Established Regulations of National Institute of Safety Research, the skin-irritation test of BST-SR (Lucky Ltd.) was perfonned for seven days in New Zealand White Rabbits. During treatment periods no significant clinical symptom was observed. Significant changes such as erythema, scar tissue and edema were not shown on the applicating sites. According to Primary Irritation Index of Draize, skin irritation rate was assessed as "Zero". The eye irritation of BST-SR (Lucky Ltd.) was examined in nine New Zealand White rabbits, based on the Established Regulation of National Institute of Safety Research. 0.1 ml of test material was dropped on right eye, and after 20~30 seconds, three rabbits' eyes were cleaned with wann saline for 1 minute. Other six rabbits' eyes were left uncleaned. The untreated left eyes were negative control. The lesions of cornea, iris and conjuntiva were assessed by the Grade table (from the Regulation of National Institute of Safety Research), and it is concluded that BST-SR has no eye-irritation.

• Korean Journal of Materials Research
• /
• v.20 no.3
• /
• pp.155-160
• /
• 2010

In this study, we investigated primary biocompatibility and osteogenic gene expression of porous granular BCP bone substitutes with or without strontium (Sr) doping. In vitro biocompatibility was investigated on fibroblasts like L929 cells and osteoblasts like MG-63 cells using a cell viability assay (MTT) and one cell morphological observation by SEM, respectively. MTT results showed a cell viability percent of L929 fibroblasts, which was higher in Sr-BCP granules (98-101%) than in the non-doped granules (92-96%, p < 0.05). Osteoblasts like MG-63 cells were also found to proliferate better on Sr-doped BCP granules (01-111%) than on the non-doped ones (92-99%, p < 0.05) using an MTT assay. As compared with pure BCP granules, SEM images of MG-63 cells grown on sample surfaces confirmed that cellular spreading, adhesion and proliferation were facilitated by Sr doping on BCP. Active filopodial growth of MG-63 cells was also observed on Sr-doped BCP granules. The cells on Sr-doped BCP granules were well attached and spread out. Gene expression of osteonectin, osteopontin and osteoprotegrin were also evaluated using reverse transcriptase polymerase chain reaction (RT-PCR), which showed that the mRNA phenotypes of these genes were well maintained and expressed in Sr-doped BCP granules. These results suggest that Sr doping in a porous BCP granule can potentially enhance the biocompatibility and bone ingrowth capability of BCP biomaterials.

• Journal of the Korean Ceramic Society
• /
• v.20 no.2
• /
• pp.107-114
• /
• 1983

Formation of Strontium titanate from the products of coprecipitation takes place at 110$0^{\circ}C$ which is 200-30$0^{\circ}C$ lower than that from mechanical mixtures of $SrCO_3$ and $TiO_2$. This is apparently due to the nature of the compounds formed by the reaction of mixtures of aqueous solutions of $SrCl_2$ and $TiCl_4$ with an ammoniacal solution of ammoni-um carbonate and ammonium hydroxide. A procedure is described for preparing strontium titanyl oxalate tetrahydrate in the several mole ratio of $TiCl_4$ to $SrCl_2$. STrontium titanyl oxalates decompose to titanate at elevated temperature. The coprecipitates and the fired specimen were subjected to examined thermal and X-ray analyses and microstruc-ture by SEM.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11a
• /
• pp.34-37
• /
• 2001

In this study, the capacitance-voltage properties of (Sr$_{1-x}$ .Ca$_{x}$)TiO$_3$(0.05$\leq$x$\leq$0.20)-based grain boundary layer ceramics were investigated. The ceramics were fabricated by the conventional mixed oxide method. The sintering temperature and time were 1480~150$0^{\circ}C$ and 4 hours, respectively. The 2nd phase formed by the thermal diffusion of CuO from the surface leads to very excellent dielectric properties, that is, $\varepsilon$$_{r}$>50000, tan$\delta$<0.05, $\Delta$C<$\pm$10%. The capacitance is almost unchanged below about 20[V] but it decreases slowly about 20[V]. The results of the capacitance-voltage properties indicated that the grain boundary was composed of the continuous insulating layers.ulating layers.s.

• Current Optics and Photonics
• /
• v.1 no.2
• /
• pp.118-124
• /
• 2017

Color rendering index (CRI) and luminous efficacy (LE) are two key performance factors of white LEDs (WLED). While most recent works in optics focus on methodology to improve these factors, little attention has been dedicated to chemical composition of materials. This paper studies the effect of $Sr_{2.4}1F_{2.59}B_{20.03}O_{74.8}:Eu_{0.12},Sm_{0.048}$ phosphor (SrSm), in terms of concentration and particle size on CRI and LE of 8500 K - WLEDs. Importantly, the molar mass of the componential ions in SrSm are calculated to shed light on the connection between the chemical composition of the material of interest and the performance of WLEDs. Results show that CRI can be improved to a value of around 86 by boosting red-light components in WLEDs, for all 3 major configurations: conformal, in-cup, and remote phosphor. CRI value tends to decrease with larger size of particles, while LE value goes in the reverse direction. On the other hand, both CRI and LE appear to be reduced at higher concentration of SrSm. This light attenuation is analyzed by using the Lambert-Beer law and Mie-scattering theory.

• Journal of the Korean Ceramic Society
• /
• v.49 no.1
• /
• pp.100-104
• /
• 2012

Barium zincoborate (BZB) glass was added to $Ba_{0.5}Sr_{0.5}TiO_3$, and sintered at $875^{\circ}C$ for 2 h in air. When the BZB glass was added in quantities ranging from 15 to 20 wt%, the relative bulk density ranged from 93.1% to 94.2%, while the density decreased to roughly 81% thereafter up to 30 wt% glass addition. Quantitative XRD analysis showed that the $Ba_{0.5}Sr_{0.5}TiO_3$ filler was significantly dissolved into the BZB glass. However, no secondary phase was identified by XRD up to 30 wt% glass addition. The dielectric constant was about 130 to 140 at 1MHz up to 20 wt% BZB glass addition, while it decreased to about 60 thereafter, which may be ascribed to decreased density, partial dissolution of the $Ba_{0.5}Sr_{0.5}TiO_3$, and associated changes in the glass composition. The dielectric loss of the 20 wt% glass added specimen was 0.008.

• The Journal of Korean Academy of Prosthodontics
• /
• v.41 no.5
• /
• pp.626-639
• /
• 2003

Statement of problem : Recently, in attempts to reinforce the acrylic resin and to reduce the polymerization shrinkage, it has been reported that adding vinyloligo-silsesquioxane (vinyl-POSS) to PMMA significantly compensates for polymerization shrinkage and somewhat increases the fracture resistance. Purpose : There haven't been any studies on abrasion that can affect the adaptation of the denture in long-term use. In this study abrasion resistance was compared between acrylic resin with vinyl-POSS and commercialized acrylic resin for denture base. In addition, the difference in abrasion resistance according to molding methods was compared. Material and method : Using PaladentR 20 including vinyl-POSS. PaladentR 20, Lucitone 199R, SR IvocapR, denture bases were fabricated using compression molding technique and continuous-pressure injection technique. Surface hardness and abrasion were measured for each group, and the worn surfaces were observed under a scanning electron microscope. Results : 1. When surface hardness was measured for each material and molding technique, there was no statistically significant difference among the materials. (p<0.05) 2. When same denture base material and molding technique were used, the abrasion due to toothpaste solution was 5 times as severe as the abrasion due to soap solution. 3, When toothpaste solution was used, the abrasion decreased in the order of PaladentR20, PaladentR 20 including vinyl-POSS, SR IvocapR, and Lucitone 199R. However statistically significant difference was seen only among PaladentR 20, SR IvocapR, and Lucitone 199R. (p<0.05). 4. When soap solution was used, the abrasion was more severe in PaladentR 20 and including vinyl-POSS PaladentR 20 groups than in SR IvocapR and Lucitone 199R groups. (p<0.05). Conclusion : Addition of vinyl-POSS doesn't improve the abrasion resistance, and the abrasion resistance was similar to those of existing materials. Additional studies under different conditions are needed. For clinical application of vinyl-POSS, further investigations with different requirements and conditions are necessary.

• Korean Journal of Crystallography
• /
• v.7 no.1
• /
• pp.20-29
• /
• 1996

Sr0.6Ca0.4CuO2 single crystal has been synthesized by flux method and characterized by the single crystal X-ray diffraction. The compound has the orthorhombic system and the space group is Cmcm(63), lattice parameters are a=3.4645Å, b=16.1417Å, c=3.8727Å. In the (Sr1-xCax)CuO2 compound the limit of Ca from substitution for Sr was determined by the change of bond length. For this, X-ray diffraction, scanning electron microscopy (SEM), energy dispersive X-ray fluorescence (EDAX) and electron probe micro-analysis (EPMA) were used. From the change of Cu-O bond length as the Ca substitution, we concluded the limit of Ca incorporation Xca≒0.73.