• 한국세라믹학회지
• /
• 제34권11호
• /
• pp.1165-1172
• /
• 1997

ZrB2 powders were prepared from a mixture of ZrO2, B2O3 and Mg by self-propagating high temperature synthesis method. The combustion product was successfully obtained from a mixture of ZrO2:B2O3:Mg=1:2:8.5 molar ratio. By-product, MgO was effectively removed by leaching with 1M HCl solution at 9$0^{\circ}C$ for over 5hours. After leaching, the Mg content was 0.86~1.42 wt%, and the mean particle size was 4.72${\mu}{\textrm}{m}$. The addition of 7.5 wt%(14Ni:1.0C) as a sintering aid greatly densified ZrB2 bodies compared with that of only Ni. The ZrB2 sintered bodies containing 7.5 wt%(14Ni:1.0C) was 94.3% of the theoretical density. In this case, ZrB2 existed as a major phase and had a bend strength of 300 MPa and a vickers hardness of 2000 kg/$\textrm{mm}^2$.

• 자원리싸이클링
• /
• 제12권4호
• /
• pp.51-57
• /
• 2003

케퍼시터용 Ta 분말제조공정에서 발생하는 waste 분말을 이용하여 TaC 분말을 자전고온합성법에 의하여 합성하였다. waste TA는 합성반응의 활성 및 산화방지를 위하여 전처리공정에서 미분쇄 및 탈산처리가 필요하였다. 합성반응에서는 TaC 단일상은 6∼7wt.％C의 조성범위에서 얻을 수 있었다. 또한 반응온도는 시료의 압축력에 영향을 받으며, 압축력 1600psi에서 최고반응온도를 나타냈다.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 1994년도 추계학술대회 논문집
• /
• pp.303-308
• /
• 1994

The finite element method has been used to model and analyze the heat transfer phenomena during manufacturing process of MoSi $_{2}$ by SHS. For this urpose nonlinear transient heat transfer analyses by using ANSYS have been performed to compute the temperature distributiuon and the peak temperature in the test specimen. The effects of manufacturing process parameters such as a pre-heating temperature, the velocity of reaction zone have also been investigated. The results of the analysis have been compared with the experimental results.

• 한국세라믹학회지
• /
• 제31권6호
• /
• pp.637-642
• /
• 1994

Using SHS(Self-propagating High-temperature Synthesis) method, the optimum synthetic condition of titanium carbonitride was established by controlling the parameters such as relative density of mixture (Ti+C), nitrogen pressure, additive amounts of titanium hydride(TiH1.924) and protecting heat loss. Under 1 atm nitrogen pressure, nitridation ratio with changing relative density of the sample compacts has a maximum (87.2%) at about 55%, and in the case of enveloping the pellet with a quartz tube, the highest nitridation ratio of 90% was obtained at about 68%. At relative density of 55%, nitridation ratio with the nitrogen pressure has a miximum (87.3%) at 7 atm. As the amounts of additive titanium hydride increased, nitridation ratio decreased at below 7 atm nitrogen pressure and, increased at above this pressure until percent of addition percent reached 15 wt% and decreased abruptly upon futher increases in titanium hydride. In the synthesis of TiCxNy by combustion reaction, heat transfer from combustion zone to preheating zone and nitrogen gas penetration into the compact were found to be important factors affecting the TiCxNy formation. It was difficult to obtain high nitridation ratio when the conbustion temperature was either too high or too low, and it seems that the retention of high temperature after a combustion wave sweeped through the reactant mixture pellet is critical to obtain a satisfactory nitridation ratio.

• 한국결정성장학회지
• /
• 제30권5호
• /
• pp.200-207
• /
• 2020

SHS 법으로 MoSi₂ 분말, (Mo_1/2W_1/2)Si₂ 분말 및 WSi₂ 분말을 합성하고 이 분말들을 500℃, 1,000℃, 1,200℃, 1,300℃, 1,400℃, 1,500℃ 및 1,600℃에서 열처리한 다음, 결정구조 및 열중량 변화 등을 관찰하였다. Mo-W-Si계의 silicide 분말은 500℃의 저온에서도 산화 반응이 일어나며, 저온 산화 및 분해로 생성되는 결정상은 MoO₃이었다. 1,200℃ 이상에서 열처리를 한 경우에 분해반응으로 생성된 SiO₂의 결정상은 상온에서 흔히 관찰되는 α-quartz가 아닌 α-cristobalite 상으로 생성되었다. W이 포함되면 저온과 고온에서 분해 반응이 더 많이 일어나는 것으로 나타났으며, 분말을 성형하여 소결한 시편의 경우에 MoSi₂와 (Mo_1/2W_1/2)Si₂는 저온이나 고온에서 1시간 열처리를 하더라도 저온산화에 의한 분해와 그에 따른 질량 변화 반응을 관찰하기 어려웠지만 WSi₂는 저온 산화에 의하여 소결 자체가 어려웠다.

• 한국세라믹학회지
• /
• 제42권1호
• /
• pp.69-75
• /
• 2005

고온자전연소법에 의한 질화알루미늄 합성에 있어서, 반응물(Al) 형상과 희석제(AlN) 입도 등의 형상학적 조건이 반응생성물에 미치는 영향을 조사하였다. 평균 입경(34$\mu$m)이 같은 두 종류의 Al 분말(입상, 편상)과 평균입경이 다른 4종류의 AM분말을 희석제로 사웅하여 반응 성형체를 준비하였다. 반응성형체의 충진밀도는 이론밀도의 $35\%로 고정하였고, 초기 질소압은 $1\~10MPa$, 희석을은 $0.4\~0.7$로 변화시키면서 반응을 실시하였다. 반응물과 희석제의 입도를 비슷하게 조절함으로써, 상대적으로 질소압이 낮은 1MPa의 조건에서도 순도 $98\% 이상, 입경 수십 $\mu$m의 AlN 합성이 가능함을 확인하였다. 이러한 고순도, 고입경화는 연소파 진행 후, 성형체 내부로 질소가스 투입 용이성의 차이에 의한 현상이라고 판단된다.

• 한국세라믹학회지
• /
• 제48권6호
• /
• pp.559-564
• /
• 2011

In order to investigate the behavior of $SiO_2$ in the molybdenum silicide powders, crystal structure of these powders was measured by XRD, in addition, surface composition and surface phase (or chemical states) and microstructure were analysed by XPS and TEM, respectively. Mo-silicide powders containing $SiO_2$ were synthesized by SHS (Self-Propagating High-Temperature Synthesis) technique. In XRD result, according to increase of $SiO_2$ contents, the crystal structure for synthesized $MoSi_2$ powders was still typical $MoSi_2$ bct without any other phases. By XPS analysis, the surface of Mo and Si source powders was covered with $MoO_3$ and $SiO_2$, respectively, and the surface of synthesized $MoSi_2$ powder was also covered with $MoO_3$ and $SiO_2$, which were stable oxides at room temperature. However, according to increase of $SiO_2$ addition, $MoSi_2$ phase in XPS spectra decreased and $SiO_2$ phase increased relatively in synthesized $MoSi_2$ powders. From the results by XPS and XRD, we found that the existent $SiO_2$ has amorphous structure. In the microstructure, the small particulates of the synthesized products added $SiO_2$ agglomerated together to form larger clusters (from ~10 nm to ~1 ${\mu}m$). From TEM, XPS, and XRD results, we found that the out layer of agglomeration of synthesized $MoSi_2$ powder is surrounded by amorphous $SiO_2$.

• 한국심리학회지 : 문화 및 사회문제
• /
• 제17권4호
• /
• pp.415-434
• /
• 2011

여가생활은 우리의 삶의 질을 향상시키는 중요한 역할을 한다. 그러나 기존 연구들은 여가가 미치는 영향력을 종단적으로 살펴보지 못하여 그 인과관계를 정확히 확인할 수 없었다. 특히나 평균 수명이 80세에 달하는 오늘날 중년기는 노년기 못지않게 새로운 관심 영역으로 떠오르고 있다. 이에 본 연구에서는 중년기의 여가생활이 행복과 건강에 미치는 영향력을 종단적으로 알아보았다. 연구에 참여한 사람들은 총 145명으로 서울지역에 거주하는 40세에서 65세 사이의 중년기에 해당하였다. 설문은 10개월을 간격으로 재실시 되었으며, 여가생활에 관한 질문은 여가만족도와 여가참여시간을 조사하였다. 행복과 건강에 관한 설문 내용은 주관적 행복감, 심리적 건강 불편증상, 신체적 건강 불편증상, 및 수면의 질 등으로 구성되었다. 분석방법은 위계적 회귀 분석을 이용하여 1차 조사 시기의 여가만족도와 여가참여시간이 1차 때의 각 종속변인을 통제한 후에도 여전히 2차 시기의 종속변인에 영향력을 미치는지를 조사하였다. 분석 결과, 여가만족도는 10개월 후의 주관적 행복감, 심리적 건강 불편 증상, 그리고 수면의 질에 유의미한 영향을 미치는 것으로 나타났고, 여가참여시간은 주관적 행복감, 심리적 및 신체적 건강 불편증상에 유의미하게 영향을 주었다. 이러한 연구 결과를 바탕으로 중년기 여가 활성화를 위한 방안과 본 연구의 시사점을 논의하였다.

• 한국세라믹학회지
• /
• 제29권7호
• /
• pp.577-585
• /
• 1992

TiB2 and TiC were prepared from the mixture of metal titanium, boron and graphite powders in Argon atmosphere by Self-propagating High-temperature Synthesis method. The sintered properties of TiB2-TiC composite as a function of TiC content and sintering temperature were investigated in TiB2 matrix. The sintered properties were the most excellent at 10 wt% TiC content in TiB2-TiC composite. The relative density, M.O.R strength, hardness and fracture toughness of TiB2-10 wt% TiC composite sintered at 190$0^{\circ}C$ for 90 min by hot-pressing under the pressure of 30 MPa were 98.6%, 634 MPa, 2128.1 kg/$\textrm{mm}^2$ and 4.09 MN/m3/2, respectively.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2003년도 추계학술발표강연 및 논문개요집
• /
• pp.93-93
• /
• 2003

Tungsten and tungsten heavy alloys have widespread application as radiation shielding devices and heavy duty electrical contacts. High density and good room temperature mechanical properties have generated interest in evaluating tungsten and tungsten alloys as kinetic energy penetrators against armor. Nowdays ultra fine-grained tungsten powders are in great interest because higly dense structures can be obtained at low temperature, pressure and lower sintering time. Several physical md chemical methods are available for the synthesis of nanometric metal Powders: ball milling, laser abalation, vapor condensation, chemical precipitation, metallic wire explosion i.e. However production rates of the above mentioned methods are low and further efforts are needed to find out large-scale synthesis methods. From this point of view solid state combustion method ( known as SHS) represents undoubted interest.